Force chains based mesoscale simulation is conducted to investigate the response behavior of aluminumpolytetrafluoroethylene(Al-PTFE)granular composites under a low-velocity impact.A two-dimensional model followed the...Force chains based mesoscale simulation is conducted to investigate the response behavior of aluminumpolytetrafluoroethylene(Al-PTFE)granular composites under a low-velocity impact.A two-dimensional model followed the randomly normal distribution of real Al particles size is developed.The dynamic compressive process of Al-PTFE composites with varied Al mass fraction is simulated and validated against the experiments.The results indicate that,force chains behavior governed by the number and the size of agglomerated Al particles,significantly affects the impact response of the material.The failure mode of the material evolves from shear failure of matrix to debonding failure of particles with increasing density.A high crack area of the material is critical mechanism to arouse the initiation reaction.The damage maintained by force chains during large plastic strain builds up more local stresses concentration to enhance a possible reaction performance.In addition,simulation is performed with identical mass fraction but various Al size distribution to explore the effects of size centralization and dispersion on the mechanical properties of materials.It is found that smaller sized Al particle of composites are more preferred than its bulky material in ultimate strength.Increasing dispersed degree is facilitated to create stable force chains in samples with comparable particle number.The simulation studies provide further insights into the plastic deformation,failure mechanism,and possible energy release capacity for Al-PTFE composites,which is helpful for further design and application of reactive materials.展开更多
Formation behaviors of rod-like reactive shaped charge penetrator(RRSCP)and their effects on damage capability are investigated by experiments and numerical simulations.The pulsed X-ray technology and a spaced aluminu...Formation behaviors of rod-like reactive shaped charge penetrator(RRSCP)and their effects on damage capability are investigated by experiments and numerical simulations.The pulsed X-ray technology and a spaced aluminum/steel plate with the thicknesses of 5 mm/100 mm are used.Three types of sphericalsegment aluminum-polytetrafluoroethylene-copper(Al-PTFE-Cu)reactive liners with Cu contents of 0%,46.6%,and 66%are fabricated and tested.The experimental results show that the reactive liners can form excellent rod-shaped penetrators with tail skirts under the shaped charge effect,but the tail skirts disappear over time.Moreover,rupturing damage to the aluminum plate and penetration to the steel plate are caused by the RRSCP impact.From simulation analysis,the RRSCP is formed by a mechanically and chemically coupled response with the reactive liner activated by shock in its outer walls and bottom and then backward overturning,forming a leading reactive penetrator and a following chemical energy cluster.The unique formation structure determines the damage modes of the aluminum plate and the steel plate.Further analysis indicates that the formation behaviors and damage capability of Al-PTFE-Cu RRSCP strongly depend on Cu content.With increasing Cu content,the velocity,activation extent,and reaction extent of Al-PTFE-Cu RRSCP decrease,which contribute to elongation and alleviate the negative effects of chemical reactions on elongation,significantly increasing the length-diameter ratio and thus enhancing the capability of steel plate penetration.However,the lower activation extent and energetic density will weaken the RRSCP's capability of causing rupturing damage to the aluminum plate.展开更多
基金the National Natural Science Foundation of China(No.U1730112).
文摘Force chains based mesoscale simulation is conducted to investigate the response behavior of aluminumpolytetrafluoroethylene(Al-PTFE)granular composites under a low-velocity impact.A two-dimensional model followed the randomly normal distribution of real Al particles size is developed.The dynamic compressive process of Al-PTFE composites with varied Al mass fraction is simulated and validated against the experiments.The results indicate that,force chains behavior governed by the number and the size of agglomerated Al particles,significantly affects the impact response of the material.The failure mode of the material evolves from shear failure of matrix to debonding failure of particles with increasing density.A high crack area of the material is critical mechanism to arouse the initiation reaction.The damage maintained by force chains during large plastic strain builds up more local stresses concentration to enhance a possible reaction performance.In addition,simulation is performed with identical mass fraction but various Al size distribution to explore the effects of size centralization and dispersion on the mechanical properties of materials.It is found that smaller sized Al particle of composites are more preferred than its bulky material in ultimate strength.Increasing dispersed degree is facilitated to create stable force chains in samples with comparable particle number.The simulation studies provide further insights into the plastic deformation,failure mechanism,and possible energy release capacity for Al-PTFE composites,which is helpful for further design and application of reactive materials.
基金the National Natural Science Foundation of China(No.12172052 and No.12132003).
文摘Formation behaviors of rod-like reactive shaped charge penetrator(RRSCP)and their effects on damage capability are investigated by experiments and numerical simulations.The pulsed X-ray technology and a spaced aluminum/steel plate with the thicknesses of 5 mm/100 mm are used.Three types of sphericalsegment aluminum-polytetrafluoroethylene-copper(Al-PTFE-Cu)reactive liners with Cu contents of 0%,46.6%,and 66%are fabricated and tested.The experimental results show that the reactive liners can form excellent rod-shaped penetrators with tail skirts under the shaped charge effect,but the tail skirts disappear over time.Moreover,rupturing damage to the aluminum plate and penetration to the steel plate are caused by the RRSCP impact.From simulation analysis,the RRSCP is formed by a mechanically and chemically coupled response with the reactive liner activated by shock in its outer walls and bottom and then backward overturning,forming a leading reactive penetrator and a following chemical energy cluster.The unique formation structure determines the damage modes of the aluminum plate and the steel plate.Further analysis indicates that the formation behaviors and damage capability of Al-PTFE-Cu RRSCP strongly depend on Cu content.With increasing Cu content,the velocity,activation extent,and reaction extent of Al-PTFE-Cu RRSCP decrease,which contribute to elongation and alleviate the negative effects of chemical reactions on elongation,significantly increasing the length-diameter ratio and thus enhancing the capability of steel plate penetration.However,the lower activation extent and energetic density will weaken the RRSCP's capability of causing rupturing damage to the aluminum plate.