A Cu-based bulk amorphous alloy composite reinforced by carbon nanotube

Bulk Cu50Zr40Ti10 amorphous alloy composites reinforced with carbon nanotube （CNT） were successfully fabricated by hot pressing technique. Their density, thermal conductivity, and mechanical properties were systemically investigated. The density and the compression strength of the compacts both decrease with increasing CNT content. The thermal conductivity of the compacts decreases when the CNT content is less than 0.10% or exceeds 0.60% （mass fraction）, while increases when the CNT content is in the range of 0.1%-0.6%. The strain limit and the modulus of the compacts are obviously improved when the CNT content is less than 1.0% and then decrease significantly when the CNT content exceeds 1.00%. The optimum CNT addition is less than 0.20% at the comprehensive properties point of view.

Effect of consolidation parameters on mechanical properties of Cu-based bulk amorphous alloy consolidated by hot pressing

Cu50Zr40Ti10 bulk amorphous alloys were fabricated by hot pressing gas-atomized Cu50Zr40Ti10 amorphous powder under different consolidation conditions without vacuum and inert gas protection. The consolidation conditions of the Cu50Zr40Ti10 amorphous powder were investigated based on an L9（34） orthogonal design. The compression strength and strain limit of the Cu50Zr40Ti10 bulk amorphous alloys can reach up to 1090.4 MPa and 11.9 %, respectively. The consolidation pressure significantly influences the strain limit and compression strength of the compact. But the mechanical properties are not significantly influenced by the consolidation temperature. In addition, the preforming pressure significantly influences not the compression strength but the strain limit. The optimum consolidation condition for the Cu50Zr40Ti10 amorphous powder is first precompacted under the pressure of 150 MPa, and then consolidated under the pressure of 450 MPa and the temperature of 380 °C.

Electrolyte manipulation on Cu-based electrocatalysts for electrochemical CO_(2) reduction

Electrocatalytic reduction of CO_(2)is crucial for environmental sustainability and renewable energy storage,with Cu-based catalysts excelling in producing high-value C_(2+)products.However,a comprehensive analysis of how specific electrolyte influences Cu-based catalysts is lacking.This review addresses this gap by focusing on how electrolytes impact surface reconstruction and the CO_(2) reduction process on Cu-based electrocatalysts,identifying specific electrolyte compositions that enhance the density and stability of active sites,and providing insights into how different electrolyte environments modulate the selectivity and efficiency of C_(2+)product formation.The review begins by exploring how electrolytes induce favorable surface reconstruction in Cu-based catalysts,affecting surface roughness through dissolution-redeposition of Cu species and interactions with halogens and molecular additives.It also covers changes in crystalline facets of Cu and Cu_(2)O,and oxidation states,highlighting transitions from Cu^(0) to Cu^(δ+)and the stabilization of Cu^(+).The role of electrolytes in the C–C coupling process is examined,emphasizing their effects in modulating mass and charge transfer,CO_(2) adsorption,intermediate evolution,and product desorption.Subsequently,the mechanisms by non-aqueous electrolytes,including organic solvents,ionic liquids,and mixed electrolytes,affecting CO_(2) reduction are analyzed,highlighting the unique advantages and challenges of each type.The review concludes by addressing current challenges,proposing solutions,and research directions,such as optimizing electrolyte composition by integrating diverse cations and anions and employing advanced in-situ characterization techniques.These insights can significantly enhance CO_(2)reduction performance on Cu-based electrocatalysts,advancing efficient and sustainable green energy technologies.

Cu-based materials for electrocatalytic CO_(2) to alcohols:Reaction mechanism,catalyst categories,and regulation strategies

Electrocatalytic CO_(2) reduction reaction(CO_(2)RR)technology,which enables carbon capture storage and resource utilization by reducing CO_(2) to valuable chemicals or fuels,has become a global research hotspot in recent decades.Among the many products of CO_(2)RR(carbon monoxide,acids,aldehydes and alcohols,olefins,etc.),alcohols(methanol,ethanol,propanol,etc.)have a higher market value and energy density,but it is also more difficult to produce.Copper is known to be effective in catalyzing CO_(2) to high valueadded alcohols,but with poor selectivity.The progress of Cu-based catalysts for the selective generation of alcohols,including copper oxides,bimetals,single atoms and composites is reviewed.Meanwhile,to improve Cu-based catalyst activity and modulate product selectivity,the modulation strategies are straighten out,including morphological regulation,crystalline surface,oxidation state,as well as elemental doping and defect engineering.Based on the research progress of electrocatalytic CO_(2) reduction for alcohol production on Cu-based materials,the reaction pathways and the key intermediates of the electrocatalytic CO_(2)RR to methanol,ethanol and propanol are summarized.Finally,the problems of traditional electrocatalytic CO_(2)RR are introduced,and the future applications of machine learning and theoretical calculations are prospected.An in-depth discussion and a comprehensive review of the reaction mechanism,catalyst types and regulation strategies were carried out with a view to promoting the development of electrocatalytic CO_(2)RR to alcohols.

Microstructure of Cu-based Amorphous Composite Coatings on AZ91D Magnesium Alloy by Laser Cladding

To improve the sliding wear resistance of AZ91D magnesium alloy, Cu-based amorphous composite coatings made of CuaTTi34Zr11Nis and Cu47Ti34Zr11Ni8＋20 wt pct SiC powders were fabricated on AZ91D magnesium alloy by laser cladding, respectively. SEM （scanning electron microscopy）, EDS （energy dispersive X-ray spectroscopy）, XRD （X-ray diffraction） and TEM （transmission electron microscopy） techniques were employed to study the phases of the coatings. The results show that the coatings mainly consist of amorphous phase and different intermetallic compounds. The reason of formation of amorphous phase and the function of SiC particles were explained in details.

Highly selective CO methanation over amorphous Ni-Ru-B/ZrO_2 catalyst

Amorphous Ni-Ru-B/ZrO2 catalyst was prepared by the means of chemical reduction, and selective CO methanation as a strategy for CO removal in fuel processing applications was investigated over the amorphous Ni-Ru-B/ZrO2 catalyst. The result showed that, at the temperature of 210-230 ℃, the catalyst was shown to be capable of reducing CO in a hydrogen-rich reformate to less than 10 ppm, while keeping the CO2 conversion below 1.55% and the hydrogen consumption below 6.50%. ？2009 Xin Fa Dong. Published by Elsevier B.V. on behalf of Chinese Chemical Society. All rights reserved.

Hydrogenation of Cinnamaldehyde to Cinnamyl Alcohol over An Ultrafine Co-B Amorphous Catalyst

A novel Co-B amorphous alloy catalyst in the form of ultrafine particles was prepared by chemical reduction of CoCl2 with aqueous NaBH4, which exhibited excellent activity and selectivity during the hydrogenation of cinnamaldehyde to cinnamyl alcohol in liquid phase. The optimum yield of cinnamyl alcohol was 87.6%, much better than the yield of using Raney Ni, Raney Co and other Co-based catalysts.

Study on the Nanosized Amorphous Ru-Fe-B/ZrO_2 Alloy Catalyst for Benzene Selective Hydrogenation to Cyclohexene

A novel nanosized amorphous Ru-Fe-B/ZrO2 alloy catalyst for benzene selective hydrogenation to cyclohexene was investigated. The superior properties of this catalyst were attributed to the combination of the nanosize and the amorphous character as well as to its textural character. In addition, the concentration of zinc ions, the content of ZrO2 in the slurry, and the pretreatment of the catalyst were found to be effective in improving the activity and the selectivity of the catalyst.

Effect of Lanthanum on Performance of RuB Amorphous Alloy Catalyst for Benzene Selective Hydrogenation

The effect of La on the performance of a supported RuB amorphous alloy catalyst for benzene selective hydrogenation was studied by means of activity and selectivity tests, such as HRTEM, SAED, XPS, and XRD. The results show that the addition of La to RuB amorphous alloy catalyst can evidently increase the activity and improve the thermal stability of RuB amorphous alloy to refrain its crystallization. The promoting effect of La on the activity of RuB amorphous alloy catalyst is because of the high dispersion of the active components.

Selective CO methanation over amorphous Ni-Ru-B/ZrO_2 catalyst for hydrogen-rich gas purification

Amorphous Ni-Ru-B/ZrO2 catalysts were prepared by chemical reduction method. The effects of Ni-Ru-B loading and Ru/Ni mole ratio on the catalytic performance for selective CO methanation from reformed fuel were studied, and the catalysts were characterized by BET, ICP, XRD and TPD. The results showed that Ru strongly affected the catalytic activity and selectivity by increasing the thermal stability of amorphous structure, promoting the dispersion of the catalyst particle, and intensifying the CO adsorption. For the catalysts with Ru/Ni mole ratio under 0.15, the CO methanation conversion and selectivity increased significantly with the increasing Ru/Ni mole ratio. Among all the catalysts investigated, the 30 wt% Ni-Ru-B loading amorphous Ni61Ru9B30/ZrO2 catalyst with 0.15 Ru/Ni mole ratio presented the best catalytic performance, over which higher than 99.9% of CO conversion was obtained in the temperature range of 230℃-250℃, and the CO2 conversion was kept under the level of 0.9%.

A Novel Ultrafine Ru-B Amorphous Alloy Catalyst for Glucose Hydrogenation to Sorbitol

An ultrafine Ru-B amorphous alloy catalyst was prepared by chemical reduction with KBH4 in aqueous solution, which exhibited perfect selectivity to sorbitol (~100%) and very high activity during the liquid phase glucose hydrogenation, much higher than the corresponding crystallized Ru-B, the pure Ru powder, and Raney Ni catalysts. The correlation of the catalytic activity to both the structural and surface electronic characteristics was discussed briefly.

Amorphous TiO_2-supported Keggin-type ionic liquid catalyst catalytic oxidation of dibenzothiophene in diesel

Supported ionic liquid(IL) catalysts [Cmim]PMoO/Am TiO(amorphous TiO) were synthesized through a one-step method for extraction coupled catalytic oxidative desulfurization(ECODS) system. Characterizations such as FTIR, DRS,wide-angle XRD, Nadsorption–desorption and XPS were applied to analyze the morphology and Keggin structure of the catalysts. In ECODS with hydrogen peroxide as the oxidant, it was found that ILs with longer alkyl chains in the cationic moiety had a better effect on the removal of dibenzothiophene. The desulfurization could reach 100% under optimal conditions, and GC–MS analysis was employed to detect the oxidized product after the reaction. Factors affecting the desulfurization efficiencies were discussed, and a possible mechanism was proposed. In addition, cyclic experiments were also conducted to investigate the recyclability of the supported catalyst. The catalytic activity of [Cmim]PMoO/Am TiOonly dropped from 100% to 92.9% after ten cycles, demonstrating the good recycling performance of the catalyst and its potential industrial application.

Rational design strategies of Cu-based electrocatalysts for CO_(2) electroreduction to C_(2) products

Electrochemical reduction of CO_(2)(CO_(2)RR)to high value-added chemicals is an effective way to remove excess CO_(2) from the atmosphere.Due to the unique propensity of Cu for valuable hydrocarbons,Cu-based electrocatalysts are the most potential catalysts that allow the conversion of CO_(2) into a variety of C_(2) products such as ethylene and ethanol.Rational design of Cu-based catalysts can improve their directional selectivity to C_(2) products.Hence,in this review,we summarize the recent progress in the mechanistic studies of Cu-based catalysts on reducing CO_(2) to C_(2) products.We focus on three key strategies for efficiently enhancing electrocatalytic performance of Cu-based catalysts,including tuning electronic structure,surface structure,and coordination environment.The correlation between the structural characteristics of Cu-based catalysts and their activity and selectivity to C_(2) products is discussed.Finally,we discuss the challenges in the field of CO_(2) electroreduction to C_(2) products and provide the perspectives to design efficient Cu-based catalysts in the future.

Effect of TiO_2 Support on the Composition, Morphology and Catalytic Property of the NiB Amorphous Alloy Catalyst

Both the unsupported and supported NiB amorphous alloy catalysts (NiB and NiB/TiO2) were prepared by the chemical reduction method. Their catalytic activities were tested by the hydrogenation of sulfolene. The interactions between the NiB alloy and TiO2 were discussed for the first time by using XRD, ICP, SEM and TEM.

Effects of Cerium Dopant on Ni-B Amorphous Alloy Catalysts Used in 2-Ethylanthraquinone Hydrogenation

A series of Ce-doped Ni-B amorphous alloy catalysts were prepared by a KBH_4 reduction method, characterized by ICP, BET, XRD, H_2-chemisorption, H_2-TPD, etc., and tested in the hydrogenation of 2-ethylanthraquinone. The results of characterization show that with the addition of Ce the amount of H_2-chemisorption and H_2-TPD areas first increases markedly and then decreases with the maximum appears at the atomic ratio of Ce to Ni of 0.036. The hydrogenation activity also shows the same trend. The effects of Ce are attributed to its dispersion of Ni particles, resulting in the formation of more surface Ni centers. However, much higher Ce contents may result in the decrease of the surface Ni contents. After heat treatment at higher temperatures, the amorphous structure of Ni-B is destroyed.

Earth-abundant amorphous catalysts for electrolysis of water

The generation of hydrogen through the electrolysis of water has attracted attention as a promising way to produce and store energy using renewable energy sources.In this process,a catalyst is very important to achieve a high‐energy conversion efficiency for the electrolysis of water.A good catalyst for water electrolysis should exhibit high catalytic activity,good stability,low cost and good scalability.Much research has been devoted to developing efficient catalysts for both the hydrogen evolution reaction(HER)and oxygen evolution reaction(OER).Traditionally,it has been accepted that a material with high crystallinity is important to serve as a good catalyst for HER and/or OER.Recently,catalysts for HER and/or OER in the electrolysis of water splitting based on amorphous materials have received much interest in the scientific community owing to the abundant unsaturated active sites on the amorphous surface,which form catalytic centers for the reaction of the electrolysis of water.We summarize the recent advances of amorphous catalysts for HER,OER and overall water splitting by electrolysis and the related fundamental chemical reactions involved in the electrolysis of water.The current challenges confronting the electrolysis of water and the development of more efficient amorphous catalysts are also discussed.

Ni-B/TiO_2 Amorphous Catalyst Used in Heavy Arenes of Petrochemicals Hydrogenation

A supported Ni-B/TiO2 amorphous catalyst was prepared by impregnation and reduction. It was characterized by XRD, SAED, DSC, XPS, etc.. The catalytic activity of catalyst was measured through the hydrogenation of heavy arenes in petrochemicals for the first time.

Identification of the structure of Ni active sites for ethylene oligomerization on an amorphous silica-alumina supported nickel catalyst

The structure of Ni active sites supported on amorphous silica-alumina supports with different contents of Al_(2)O_(3)loadings in relation to their activities in ethylene oligomerization were investigated.Two kinds of Ni sites were detected by in situ FTIR-CO and H_(2)-TPR experiments,that are Ni^(2+)cations as grafted on weak acidic silanols and Ni^(2+)cations at ion-exchange positions.The ethylene oligomerization activities of these Ni/ASA catalysts were found an ascending tendency as the Al_(2)O_(3)loading decreased,which could be attributed to the enriched concentration of Ni^(2+)species on acidic silanols with a weaker interaction with the amorphous silica-alumina support.These Ni^(2+)species were more easily to be evolved into Ni^(+)species,which has been identified to be the active sites of ethylene oligomerization.Thus,it seems reasonable to conclude that Ni^(2+)species grafted on acidic silanols were the precursors of active sites.

Preparation and Application of Supported Amorphous Alloy Catalyst CoP/TiO_2

A new supported amorphous catalyst CoP/TiO2 was prepared by chemical reduction and characterized by ICP, XRD, TEM, BET and DSC. Its application in decomposing PH3 to high purity phosphor and its catalytic activity were studied. The decomposition rate is over 95% at 450 ℃. For comparison, unsupported CoP amorphous catalyst was prepared by the same method. The result suggests that CoP/TiO2 exhibits higher thermal stability and catalytic activity than CoP, which is attributed to the high dispersion of CoP alloy particles on the support-TiO2.

Amorphous CoSnO_3@rGO nanocomposite as an efficient cathode catalyst for long-life Li-O_2 batteries

An amorphous CoSnO3@rGO nanocomposite fabricated using a surfactant‐assisted assembly method combined with thermal treatment served as a catalyst for non‐aqueous lithium‐oxygen(Li‐O2)batteries.In contrast to the specific surface area of the bare CoSnO3 nanoboxes(104.3 m2 g–1),the specific surface area of the CoSnO3@rGO nanocomposite increased to approximately 195.8 m2 g–1 and the electronic conductivity also improved.The increased specific surface area provided more space for the deposition of Li2O2,while the improved electronic conductivity accelerated the decomposition of Li2O2.Compared to bare CoSnO3,the overpotential reduced by approximately 20 and 60 mV at current densities of 100 and 500 mA g?1 when CoSnO3@rGO was used as the catalyst.A Li‐O2 battery using a CoSnO3@rGO nanocomposite as the cathode catalyst cycled indicated a superior cyclic stability of approximately 130 cycles at a current density of 200 mA g–1 with a limited capacity of 1000 mAh g–1,which is 25 cycles more than that of the bare amorphous CoSnO3 nanoboxes.