Vacuum brazing TiAl intermetallic to K4169 alloy using amorphous filler metals Ti_(56.25–x)Zr_(x)Ni_(25)Cu1_(8.75)

A series of Ti_(56.25-x)Zr_(x)Ni_(25)Cu1_(8.75)(x=0–25,at.%) filler metals were designed based on a cluster-plus-glue-atom model to vacuum braze TiAl intermetallic to K4169 alloy. The impact of Zr content on the interfacial microstructure and shear strength of joints was examined. And the relationship between the interfacial lattice structure and the fracture behavior of the joint was investigated. The findings reveal a sectionalized characteristic with three reaction zones (Zone I, Zone II and Zone III) in the microstructure of the TiAl intermetallic to K4169 alloy joint. As the Zr content in filler metals increased, the diffusion of Ti transitioned from long-distance to short-distance in Zone I, changing the initial composition from TiNi_(3) /TiNi/NiNb/(Cr, Fe, Ni)SS to NiCrFe/(Cr, Fe, Ni)SS /TiNi. In Zone II, the initial composition altered from TiNi_(3) /TiNi to TiNi/Ti_(2) Ni/TiNi_(3) /TiCu/TiNi. The interface between Zones II and III altered from a non-coherent and semi-coherent interface of TiNi/TiAl/Ti_(3) Al with significant residual stress to a semi-coherent interface of TiNi/TiNi_(3) /TiAl_(2) /Ti_(3) Al with a gradient distribution. The shear strength of the joint initially decreased and then increased. When the Zr content of filler metal was 25 at.%, the shear strength of the joint reached 288 MPa. The crack initiation position changed from non-coherent TiNi/TiAl interface with high angle grain boundaries (HAGBs) and lattice mismatch of 65.86 at.% to a semi-coherent Ti3 Al/TiAl2 interface with a lattice mismatch of 20.07 at.% when the Zr content increased. The brittle fracture was present on the fracture surfaces of all brazed joints.

Interfacial features of TiAl alloy/316L stainless steel joint brazed with Zr−Cu−Ni−Al amorphous filler metal

TiAl alloy and 316L stainless steel were vacuum-brazed with Zr−50.0Cu−7.1Ni−7.1Al(at.%)amorphous filler metal.The influence of brazing time and temperature on the interfacial microstructure and shear strength of the resultant joints was investigated.The brazed seam consisted of three layers,including two diffusion layers and one residual filler metal layer.The typical microstructure of brazed TiAl alloy/316L stainless steel joint was TiAl alloy substrate/α2-(Ti3Al)/AlCuTi/residual filler metal/Cu9Zr11+Fe23Zr6/Laves-Fe2Zr/α-(Fe,Cr)/316L stainless steel substrate.Discontinuous brittle Fe2Zr layer formed near the interface between the residual filler metal layer andα-(Fe,Cr)layer.The maximum shear strength of brazed joints reached 129 MPa when brazed at 1020℃ for 10 min.The diffusion activation energies ofα2-(Ti3Al)andα-(Fe,Cr)phases were−195.769 and−112.420 kJ/mol,respectively,the diffusion constants for these two phases were 3.639×10^(−6) and 7.502×10^(−10)μm^(2)/s,respectively.Cracks initiated at Fe2Zr layer and propagated into the residual filler metal layer during the shear test.The Laves-Fe2Zr phase existing on the fracture surface suggested the brittle fracture mode of the brazed joints.

Strength and interfacial microstructure of Si3N4 joint brazed with amorphous Ti-Zr-Ni-Cu filler metal

In this paper, the vacuum brazing of Si3N4 ceramic was carried out with Ti40Zr25Ni15Cu20 amorphous filler metal. The interfacial microstructure was investigated by scanning electron microscopy （ SEM ）, energy dispersive spectroscopy （EDS） etc. According to the analysis, the interface reaction layer was mode up of TiN abut on the ceramic and the Ti-Si, Zr-Si compounds. The influence of brazing temperature and holding time on the joint strength was also studied. The results shows that the joint strength first increased and then decreased with the increasing of holding time and brazing temperature. The joint strength was significantly affected by the thickness of the reaction layer. Under the same experimental conditions, the joint brazed with amorphous filler metal exhibits much higher strength compared with the one brazed with crystalline filler metal with the same composition. To achieve higher joint strength at relatively low temperature, it is favorable to use the amorphous filler metal than the crystalline filler metal.