Micromagnetic Structure of Co-Rich Amorphous Microwires

Results on the magneto-optical investigation of near-surface micromagnetic structure (MMS) of Co69Fe4Si12B15 amorphous wires 10～50 μm in diameter are presented. The wires were prepared by the rapid solidification technique. The magnetic field H was applied along or perpendicular to the wire length. By scanning the light spot of 1 μm-diameter along the wire length, distributions of magnetization components (both parallel and perpendicular to the applied magnetic field) and also local hysteresis characteristics of the wires were measured. It was experimentally established that owing to the compressive stresses from quenching coupled with negative magnetostriction of Co-rich amorphous materials, the examined microwires have a circumferential magnetic anisotropy. In consequence, there are the near-surface alternate left- and right-handled circular domains in these samples. The dependencies of the circular domain width on the wire diameter and length were found. It was discovered that in the axial magnetic field local hysteresis loops are unhysteretic. It was proved that in this case the dominant mechanism of the wire magnetization reversal is rotation of local magnetization vectors in circular domains.

Microstructure and magnetocaloric properties of melt-extracted SmGdDyCoAl high-entropy amorphous microwires

This paper presents a systematic investigation of the microstructure and magnetocaloric properties of melt-extracted Sm_(20)Gd_(20)Dy_(20)Co_(20)Al_(20)high-entropy microwires.The fabricated wires exhibited an amorphous structure,and the temperature interval of the undercooled liquid AT was 45 K.The microwires underwent a second-order magnetic transition from a ferromagnetic to a paramagnetic state near the Curie temperature(T_(C)=52 K),The maximum magnetic entropy change(-ΔS_M^(max)),the relative cooling power and the refrigeration capacity reached 6.34 J·kg^(-1)·K^(-1).422.09 J·kg^(-1)and 332.94 J·kg^(-1),respectively,under a magnetic field change of 5 T.In addition,the temperature-averaged entropy changes with two temperature lifts(3 and 10 K)were 6.32 and 6.27 J·kg^(-1)·K^(-1),respectively.The good magnetocalorie performance highlights the significant potential for the Sm_(20)Gd_(20)Dy_(20)Co_(20)Al_(20)microwires to be used as magnetic refrigerant materials in low-temperature region applications.This work will serve as a valuable reference for future investigations on low-temperature high-entropy magnetocaloric materials.

Giant magneto-impedance effect of two paralleled amorphous microwires

Giant magneto-impedance （GMI） is effectively enhanced by the mutual magnetic interaction between two amorphous microwires. A comparative study on GMI properties of a single wire and two wires arranged in par- allel mode was reported in this work. Two-peak （TP） of impedance characteristic is presented when the dc external field changed from 0 to 320 A,m-＇ in two-wire system, which is attributed to successive magnetization process in two wires induced by their magnetic interaction. And the evolution of single peak to TP phenomenon, when the distance between two wires is upto 8 ram, evidences a distance dependence of transformation from successive magnetization to simultaneous via a corresponding dis- tance dependence of magnetostatic interactions. It is pro- posed that the recombination of magnetic interaction and the shielding effect results in a distance dependency of GMI response. When the distance is 8 ram, the magneti- zation process is close to synchronous between two wires, which give rises to higher circular permeability and better GMI response. The impedance ratio AZ/Z increases from 74.5 % of single wire to 172.4 % at 10 MHz. However, when the distance is upto 12 mm, the magnetic interaction is weak and magnetization process is completely independent, and GMI response decreases, relatively. This indicates that the GMI response could be effectively improved in a two-wire connection with an optical distance, which is promising and useful for the application of high-performance GMI sensors.

Annealing effects on the microwave permittivity and permeability properties of Fe_(79)Si_(16)B_5 microwires and their microwave absorption performances

This paper reports that amorphous magnetic microwires （Fe79Si16Bs） have been fabricated by a melt-extraction technique and have been annealed at 600℃ and 750℃ respectively. Differential scanning calorimeter measurements show that nanocrystalline magnetic phase （α-Fe） has been formed in the amorphous matrix when it was annealed at 600℃. Hard magnetic phase （Fe2B） was formed in the microwires annealed at 750℃, which increases the magnetic coercivity. Microwave permittivity and permeability are found to be dependent on the microstruetures. The permittivity fitting results show that multi Lorentzian dispersion processes exist. For microwires annealed at 750℃, their resonance peaks due to the domain wall movements and natural resonance are found higher than those of microwires annealed at 600℃. The microwave absorption performance of microwires annealed at 600℃ is found better than microwires annealed at 750℃.