Owing to the advantages of simple structure,low power consumption and high-density integration,memristors or memristive devices are attracting increasing attention in the fields such as next generation non-volatile me...Owing to the advantages of simple structure,low power consumption and high-density integration,memristors or memristive devices are attracting increasing attention in the fields such as next generation non-volatile memories,neuromorphic computation and data encryption.However,the deposition of memristive films often requires expensive equipment,strict vacuum conditions,high energy consumption,and extended processing times.In contrast,electrochemical anodizing can produce metal oxide films quickly(e.g.10 s) under ambient conditions.By means of the anodizing technique,oxide films,oxide nanotubes,nanowires and nanodots can be fabricated to prepare memristors.Oxide film thickness,nanostructures,defect concentrations,etc,can be varied to regulate device performances by adjusting oxidation parameters such as voltage,current and time.Thus memristors fabricated by the anodic oxidation technique can achieve high device consistency,low variation,and ultrahigh yield rate.This article provides a comprehensive review of the research progress in the field of anodic oxidation assisted fabrication of memristors.Firstly,the principle of anodic oxidation is introduced;then,different types of memristors produced by anodic oxidation and their applications are presented;finally,features and challenges of anodic oxidation for memristor production are elaborated.展开更多
Intermetallic phases were found to influence the anodic oxidation and corrosion behavior of 5A06 aluminum alloy. Scattered in- termetallic particles were examined by scanning electron microscopy (SEM) and energy dis...Intermetallic phases were found to influence the anodic oxidation and corrosion behavior of 5A06 aluminum alloy. Scattered in- termetallic particles were examined by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) after pretreatment. The anodic film was investigated by transmission electron microscopy (TEM), and its corrosion resistance was analyzed by electrochemical impedance spectroscopy (EIS) and Tafel polarization in NaC1 solution. The results show that the size of A1-Fe-Mg-Mn particles gradually decreases with the iron content. During anodizing, these intermetallic particles are gradually dissolved, leading to the complex porosity in the anodic film beneath the particles. After anodizing, the residual particles are mainly silicon-containing phases, which are embedded in the an- odic film. Electrochemical measurements indicate that the porous anodic film layer is easily penetrated, and the barrier plays a dominant role in the overall protection. Meanwhile, self-healing behavior is observed during the long immersion time.展开更多
The anodic oxidation of aqueous solutions containing dimethyl phthalate (DMP) up to 125 mg/L with sodium sulfate (Na2SO4) as supporting electrolyte within the pH range 2.0-10.0 was studied using a one-compartment ...The anodic oxidation of aqueous solutions containing dimethyl phthalate (DMP) up to 125 mg/L with sodium sulfate (Na2SO4) as supporting electrolyte within the pH range 2.0-10.0 was studied using a one-compartment batch reactor employing a boron-doped diamond (BDD) as anode. Electrolyses were carded out at constant current density (1.5-4.5 mA/cm^2). Complete mineralization was always achieved owing to the great concentration of hydroxyl radical (-OH) generated at the BDD surface. The effects of pH, apparent current density and initial DMP concentration on the degradation rate of DMP, the specific charge required for its total mineralization and mineralization current efficiency were investigated systematically. The mineralization rate of DMP was found to be pH-independent and to increase with increasing applied current density. Results indicated that this electrochemical process was subjected, at least partially, to the mass transfer of organics onto the BDD surface. Kinetic analysis of the temporal change of DMP concentration during electrolysis determined by High Performance Liquid Chromatography (HPLC) revealed that DMP decay under all tested conditions followed a pseudo first-order reaction. Aromatic intermediates and generated carboxylic acids were identified by Gas Chromatography- Mass Spectrometry (GC-MS) and a general pathway for the electrochemical incineration of DMP on BDD was proposed.展开更多
Anatase titanium dioxide is an active photocatalyst, but it is difficult to immobilize on the substrate. A crystalline TiO2 porous film was prepared directly on the surface of pure titanium by anodic oxidation in this...Anatase titanium dioxide is an active photocatalyst, but it is difficult to immobilize on the substrate. A crystalline TiO2 porous film was prepared directly on the surface of pure titanium by anodic oxidation in this work. Constant voltage and constant current anodic oxidation were adopted with sulphuric acid used as the electrolyte, pure titanium as the anode and copper as the cathode. The morphology and structure of the porous film on the substrate were analyzed with the aid of Field Emission Scanning Electron Microscopy (FESEM) and X-ray Diffraction (XRD). The effects of the parameters of anodic oxidation (such as voltage, the concentration of sulphuric acid, anodization time and current density) on the aperture and the crystalline phase of the TiO2 porous film were systematically investigated. The results indicate that the increase of current density facilitates the augment of the aperture and the generation of anatase and mille. In addition, the forming mechanism of anatase and mille TiO2 porous films was discussed.展开更多
In order to analyze the influence of the anodizing process on the thermal load of an aluminum alloy piston,dedicated temperature tests have been carried out using the Hardness Plug method and the results for the anodi...In order to analyze the influence of the anodizing process on the thermal load of an aluminum alloy piston,dedicated temperature tests have been carried out using the Hardness Plug method and the results for the anodized piston have been compared with those obtained separately for an original aluminum piston.In addition,numerical simulations have been conducted to analyze the temperature field and thermal stress distribution.Simulations and experiments show that the maximum temperature of the anodized piston is 16.36%and 5.4%smaller than that of the original piston under the condition of maximum torque and maximum power,respectively.The thermal stress of the temperature field of both pistons is within 50 Mpa,which meets the strength requirements of the material at high temperature.However,the area with significant thermal stress of the anodized piston is significantly smaller than that of the original piston.Combined with the fatigue analysis data,it can be seen that the safety factor of the anodized piston greater than 1.8 is 99.13%.Therefore,adopting the anodizing process not only reduces the piston thermal load,but also helps to extend its life and improve its reliability.展开更多
The effects of insoluble eutectic Si particles on the growth of anodic oxide films on ZL114A aluminum alloy substrates were in- vestigated by optical microscopy (OM) and scanning electron microscopy (SEM). The ano...The effects of insoluble eutectic Si particles on the growth of anodic oxide films on ZL114A aluminum alloy substrates were in- vestigated by optical microscopy (OM) and scanning electron microscopy (SEM). The anodic oxidation was performed at 25℃ and a con- stant voltage of 15 V in a solution containing 50 g/L sulfuric acid and 10 g/L adipic acid. The thickness of the formed anodic oxidation film was approximately 7.13 μm. The interpore distance and the diameters of the major pores in the porous layer of the film were within the ap- proximate ranges of 10~20 nm and 5-10 nm, respectively. Insoluble eutectic Si particles strongly influenced the morphology of the anodic oxidation films. The anodic oxidation films exhibited minimal defects and a uniform thickness on the ZL114A substrates; in contrast, when the front of the oxide oxidation films encountered eutectic Si particles, defects such as pits and non-uniform thickness were observed, and pits were observed in the films.展开更多
The aim of this work was to investigate the effects of calcination/acid-activation on the composition, structure, and photocatalytic (PC) reduction property of an anodic oxidation TiO2/Ti film catalyst. The surface ...The aim of this work was to investigate the effects of calcination/acid-activation on the composition, structure, and photocatalytic (PC) reduction property of an anodic oxidation TiO2/Ti film catalyst. The surface morphology and phase composition were examined by scanning electron microscopy and X-ray diffraction. The catalytic property of the film catalysts was evaluated through the removal rate of potassium chromate during the PC reduction process. The results showed that the film catalysts were composed of anatase and rutile TiO2 with a micro-porous surface structure. The calcination treatment increased the content of TiO2 in the film, changed the relative ratio of anatase and rutile TiO2, and decreased the size of the micro pores of the film catalysts. The removal rate of potassium chromate was related to the technique parameters of calcination/acid-activation treatment. When the anodic oxidation TiO2/Ti film catalyst was calcined at 873 K for 30 min and then acid-activated in the concentrated H2SO4 for 60 min, it presented the highest catalytic property, with the removal rate of potassium chromate of 96.3% during the PC reduction process under the experimental conditions.展开更多
Micron sized hexagon- and flower-like nanostructures of lead oxide(α-PbO2) have been synthesized by very simple and cost effective route of anodic oxidation of lead sheet. These structures were easily obtained by t...Micron sized hexagon- and flower-like nanostructures of lead oxide(α-PbO2) have been synthesized by very simple and cost effective route of anodic oxidation of lead sheet. These structures were easily obtained by the simple variation of applied voltage from 2-6 V between the electrodes. Lead sheet was used as an anode and platinum sheet served as a cathode. Anodic oxidation at 2 V resulted in the variable edge sized(1-2 μm) hexagon-like structures in the electrolyte. When the applied potential was increased to 4 V a structure of distorted hexagons consisting of some flower-like structures were obtained. Further increment of potential up to 6 V resulted in flower like structures of α-PbO2 having six petals. The diameter of the flower-like structures was 200-500 nm and the size of a petal was 100-200 nm.展开更多
Currently, landfills are the main method used for the final disposal of urban solid waste. The degradation processes that waste goes through in these sites, alongside rainwater that percolates through them, generate h...Currently, landfills are the main method used for the final disposal of urban solid waste. The degradation processes that waste goes through in these sites, alongside rainwater that percolates through them, generate highly polluting liquids (leachate). In the treatment of leachate, advanced oxidation processes (AOP) can significantly reduce the concentrations of different pollutants. Due to the high documented potential around AOPs, in this study, the effectiveness of anodic oxidation in the removal of the remaining organic load in leachates pretreated in a biological system was evaluated. Graphite electrodes were used as anode and cathode. The efficiency of anodic oxidation, in terms of the removal of chemical oxygen demand (COD) and color, was evaluated under different current densities (7, 12, 17 and 22 mA/cm2) and pH values (3, 4.5 and 6). Under the best conditions found (22 mA/cm2 and pH of 6) and with an oxidation time of 5 hours, a maximum removal of 68% in COD and 91% in color was achieved, which represented a quality in the final effluent of 271 mg/L and 151 Pt-Co in COD and color, respectively. Therefore, considering that graphite is an economic and widely available material, the results obtained show anodic oxidation, with the use of graphite electrodes, as a technically viable alternative as a final purification stage for pretreated leachates.展开更多
Electrode materials with high desalination capacity and long-term cyclic stability are the focus of capacitive deionization(CDI) community. Understanding the causes of performance decay in traditional carbons is cruci...Electrode materials with high desalination capacity and long-term cyclic stability are the focus of capacitive deionization(CDI) community. Understanding the causes of performance decay in traditional carbons is crucial to design a high-performance material. Based on this, here, nitrogen-doped activated carbon(NAC) was prepared by pyrolyzing the blend of activated carbon powder(ACP) and melamine for the positive electrode of asymmetric CDI. By comparing the indicators changes such as conductivity, salt adsorption capacity, pH, and charge efficiency of the symmetrical ACP-ACP device to the asymmetric ACP-NAC device under different CDI cycles, as well as the changes of the electrochemical properties of anode and cathode materials after long-term operation, the reasons for the decline of the stability of the CDI performance were revealed. It was found that the carboxyl functional groups generated by the electro-oxidation of anode carbon materials make the anode zero-charge potential(E_(pzc)) shift positively,which results in the uneven distribution of potential windows of CDI units and affects the adsorption capacity. Furthermore, by understanding the electron density on C atoms surrounding the N atoms, we attribute the increased cyclic stability to the enhanced negativity of the charge of carbon atoms adjacent to quaternary-N and pyridinic-oxide-N.展开更多
Different additives were added into the potassium fluorozirconate solution to prepare different nickelfree sealing reagents,with which the anodic oxidation film of aluminum alloy was sealed at room temperature.The pho...Different additives were added into the potassium fluorozirconate solution to prepare different nickelfree sealing reagents,with which the anodic oxidation film of aluminum alloy was sealed at room temperature.The phosphor chromic acid weight loss method was used to evaluate the sealing effects.Using electron scanning microscopy(SEM),the surface and cross-sectional micromorphologies of the anodic oxidation films sealed by different fluorozirconate sealants were observed.The position and state of zirconium element distribution in the film hole were investigated by the further quantitative and distribution analysis of Zr element.This study provides an experimental evidence for the theoretical studies of fluorozirconate-sealed anodic oxidation films.It is shown that the fluorozirconate has good sealing effects and has a wide prospect for sealing the aluminum alloy samples.Its products were highly corrosion resistant,and were filled in the openings of the micropores in the oxide film.展开更多
The nitrile functionality is a key building block in synthetic chemistry, and has wide applications in pharmaceuticals. However, traditional methodologies for the synthesis of nitriles are limited to harsh reaction co...The nitrile functionality is a key building block in synthetic chemistry, and has wide applications in pharmaceuticals. However, traditional methodologies for the synthesis of nitriles are limited to harsh reaction conditions. Herein, we report a new and efficient access to aryl nitriles by an electrochemical synthesis. Compared with the conventional synthetic methods, this electrochemical synthesis is more environmentally friendly and easier to handle.展开更多
Ti-Cu alloy has potential to be used in plastic surgery and dental implants due to its strong antibacterialproperties,high strength and good corrosion resistance.In this paper,Ti-5Cu was anodic-oxidized to enhance the...Ti-Cu alloy has potential to be used in plastic surgery and dental implants due to its strong antibacterialproperties,high strength and good corrosion resistance.In this paper,Ti-5Cu was anodic-oxidized to enhance the surface compatibility.The influence of the oxidation on the corrosion resistance,antibacterial properties and biological properties was investigated.X-ray diffraction(XRD)and X-ray photoelectron spectroscopy(XPS)results showed that a double-layer oxide coating with dense inner layer and porous outside layer was formed on Ti-Cu sample.The oxide coating consisted mainly of TiO2,CuzO and small amount of CuO,improved the corrosion resistance of Ti-Cu alloy by one order of magnitude due to the formation of the dense oxide inner layer,but high Cu ion release was detected.The plate count results showed that the antibac-terial activity of Ti-Cu sample was improved to≥99%due to the comprehensive function of CuO and Cu_(2)O in the coating and Cu^(2+)release.Cell test results showed that thecoating exhibited good cell compatibility,the porous sur-face structure improved the adhesion of cells,and Cu ion release promoted the cell proliferation.展开更多
This work was conducted to study the ability of anodic oxidation of azo dye C.I. Acid Red 73 (ART3) using the yttrium-doped Ti/SnO2-Sb electrodes. The effects of Sb doping level, yttrium doping level, thermal decomp...This work was conducted to study the ability of anodic oxidation of azo dye C.I. Acid Red 73 (ART3) using the yttrium-doped Ti/SnO2-Sb electrodes. The effects of Sb doping level, yttrium doping level, thermal decomposition temperature and cycle times of dip-coating thermal decomposition on the properties of the electrodes were investigated. The results showed that the excellent electrochemical activity of Ti/SnO2-Sb-Y electrode can be achieved at a 7:1 molar ratio of Sn:Sb and thermal decomposition temperature of 550~C. Moreover when the cycle times of dip-coating and thermal decomposition were up to 10 times, the performance of the electrode tends to be stable. The Ti/SnO2-Sb electrodes doped with yttrium (0.5 tool-%) showed the most excellent electrochemical activity. In addition, the influences of operating variables, including current density, initial pH, dye concentration and support electrolyte, on the colour removal, chemical oxygen demand (COD) removal and current efficiency were also investigated. Our results confirmed that the current efficiency increased with the concentrations of dye and sodium chloride. Moreover, increasing the current density and the initial pH would reduce the current efficiency.展开更多
Polyacrylonitrile (PAN) based carbon fibers with different surface morphology were electrochemically treated in 3 wt% NH4HCO3 aqueous solution with current density up to 3.47 A/m 2 at room temperature, and surface s...Polyacrylonitrile (PAN) based carbon fibers with different surface morphology were electrochemically treated in 3 wt% NH4HCO3 aqueous solution with current density up to 3.47 A/m 2 at room temperature, and surface structures, surface morphology and residual mechanical properties were characterized. The crystallite size (La) of carbon fibers would be interrupted due to excessive electrochemical etching, while the crystallite spacing (d(002)) increased as increasing current density. The disordered structures on the surface of carbon fiber with rough surface increased at the initial oxidation stage and then removed by further electrochemical etching, which resulting in continuous increase of the extent of graphitization on the fiber surface. However, the electrochemical etching was beneficial to getting ordered morphology on the surface for carbon fiber with smooth surface, especially when the current density was lower than 1.77 A/m 2 . The tensile strength and tensile modulus could be improved by 17.27% and 5.75%, respectively, and was dependent of surface morphology. The decreasing density of carbon fibers probably resulted from the volume expansion of carbon fibers caused by the abundant oxygen functional groups intercalated between the adjacent graphite layers.展开更多
A novel bromination of α,β-unsaturated carboxylic acids was developed via a decarboxylation by virtue of a direct anodic electro-oxidation.In this method,ammonium bromide was employed as a bromine source and the rea...A novel bromination of α,β-unsaturated carboxylic acids was developed via a decarboxylation by virtue of a direct anodic electro-oxidation.In this method,ammonium bromide was employed as a bromine source and the reaction features transition-metal-free,short time,and no additional supporting electrolyte.展开更多
The anodic oxidation of nickel in molten (Li 0.62 ,K 0.38 ) 2CO 3 was investigated by means of cyclic voltammetry, X ray diffraction and X ray photoelectron spectroscopy. The results indicate that two reac...The anodic oxidation of nickel in molten (Li 0.62 ,K 0.38 ) 2CO 3 was investigated by means of cyclic voltammetry, X ray diffraction and X ray photoelectron spectroscopy. The results indicate that two reactions are involved in the anodic process: one is Ni+O 2- =NiO+2e -, the other reaction is Ni(Ⅱ)=Ni(Ⅲ)+e -.展开更多
With the rapid development of two-phase heat exchangers,the further improvement of the capillary performance of their internal wick faces a great challenge.As an important technology in the surface treatment of alumin...With the rapid development of two-phase heat exchangers,the further improvement of the capillary performance of their internal wick faces a great challenge.As an important technology in the surface treatment of aluminum alloys,anodic oxidation has been widely used to develop various functional nanostructures.In this study,nanopores with diameters of 30–40 nm were fabricated on the surface of aluminum fibers through anodic oxidation under an oxalic acid system.Results showed that anodizing increased the specific surface area of the aluminum braid by 163 times,and changed its surface wettability from hydrophobic to superhydrophilic.A significant reduction in the effective capillary radius can substantially increase the capillary force of aluminum braids on the basis of capillary theory.Therefore,the nanoporous aluminum braids can be used as a novel wick in the vapor chamber to improve its capillary performance.Capillary rate-of-rise tests with ethanol and acetone were performed to characterize the capillary of this novel wick structure.Infrared thermal imaging was utilized to monitor the capillary rise of aluminum braided wicks.The capillary force of the anodized wicks was greater than that of a normal wick,and the maximum capillary rise height was 81 mm.The nanoporous aluminum braided wicks prepared by anodizing could be applied in heat transfer.展开更多
基金supported by the National Key Research and Development Program of China (Grant No.2018YFE0203802)Natural Science Foundation of Hubei Province, China (Grant No.2022CFA031)Dongguan Innovative Research Team Program (2020607101007)。
文摘Owing to the advantages of simple structure,low power consumption and high-density integration,memristors or memristive devices are attracting increasing attention in the fields such as next generation non-volatile memories,neuromorphic computation and data encryption.However,the deposition of memristive films often requires expensive equipment,strict vacuum conditions,high energy consumption,and extended processing times.In contrast,electrochemical anodizing can produce metal oxide films quickly(e.g.10 s) under ambient conditions.By means of the anodizing technique,oxide films,oxide nanotubes,nanowires and nanodots can be fabricated to prepare memristors.Oxide film thickness,nanostructures,defect concentrations,etc,can be varied to regulate device performances by adjusting oxidation parameters such as voltage,current and time.Thus memristors fabricated by the anodic oxidation technique can achieve high device consistency,low variation,and ultrahigh yield rate.This article provides a comprehensive review of the research progress in the field of anodic oxidation assisted fabrication of memristors.Firstly,the principle of anodic oxidation is introduced;then,different types of memristors produced by anodic oxidation and their applications are presented;finally,features and challenges of anodic oxidation for memristor production are elaborated.
基金financially supported by the National Natural Science Foundation of China(No.51271012)
文摘Intermetallic phases were found to influence the anodic oxidation and corrosion behavior of 5A06 aluminum alloy. Scattered in- termetallic particles were examined by scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) after pretreatment. The anodic film was investigated by transmission electron microscopy (TEM), and its corrosion resistance was analyzed by electrochemical impedance spectroscopy (EIS) and Tafel polarization in NaC1 solution. The results show that the size of A1-Fe-Mg-Mn particles gradually decreases with the iron content. During anodizing, these intermetallic particles are gradually dissolved, leading to the complex porosity in the anodic film beneath the particles. After anodizing, the residual particles are mainly silicon-containing phases, which are embedded in the an- odic film. Electrochemical measurements indicate that the porous anodic film layer is easily penetrated, and the barrier plays a dominant role in the overall protection. Meanwhile, self-healing behavior is observed during the long immersion time.
基金This work was financially supported by the Natural Science Foundation of Jiangsu Province (No. BK2004129) the Aviation Science Foundation of China (No. 04H52059).
基金supported by the National Natural Science Foundation of China (No 50778172) the Funds for Creative Research Groups of China (No 50621804)
文摘The anodic oxidation of aqueous solutions containing dimethyl phthalate (DMP) up to 125 mg/L with sodium sulfate (Na2SO4) as supporting electrolyte within the pH range 2.0-10.0 was studied using a one-compartment batch reactor employing a boron-doped diamond (BDD) as anode. Electrolyses were carded out at constant current density (1.5-4.5 mA/cm^2). Complete mineralization was always achieved owing to the great concentration of hydroxyl radical (-OH) generated at the BDD surface. The effects of pH, apparent current density and initial DMP concentration on the degradation rate of DMP, the specific charge required for its total mineralization and mineralization current efficiency were investigated systematically. The mineralization rate of DMP was found to be pH-independent and to increase with increasing applied current density. Results indicated that this electrochemical process was subjected, at least partially, to the mass transfer of organics onto the BDD surface. Kinetic analysis of the temporal change of DMP concentration during electrolysis determined by High Performance Liquid Chromatography (HPLC) revealed that DMP decay under all tested conditions followed a pseudo first-order reaction. Aromatic intermediates and generated carboxylic acids were identified by Gas Chromatography- Mass Spectrometry (GC-MS) and a general pathway for the electrochemical incineration of DMP on BDD was proposed.
文摘Anatase titanium dioxide is an active photocatalyst, but it is difficult to immobilize on the substrate. A crystalline TiO2 porous film was prepared directly on the surface of pure titanium by anodic oxidation in this work. Constant voltage and constant current anodic oxidation were adopted with sulphuric acid used as the electrolyte, pure titanium as the anode and copper as the cathode. The morphology and structure of the porous film on the substrate were analyzed with the aid of Field Emission Scanning Electron Microscopy (FESEM) and X-ray Diffraction (XRD). The effects of the parameters of anodic oxidation (such as voltage, the concentration of sulphuric acid, anodization time and current density) on the aperture and the crystalline phase of the TiO2 porous film were systematically investigated. The results indicate that the increase of current density facilitates the augment of the aperture and the generation of anatase and mille. In addition, the forming mechanism of anatase and mille TiO2 porous films was discussed.
文摘In order to analyze the influence of the anodizing process on the thermal load of an aluminum alloy piston,dedicated temperature tests have been carried out using the Hardness Plug method and the results for the anodized piston have been compared with those obtained separately for an original aluminum piston.In addition,numerical simulations have been conducted to analyze the temperature field and thermal stress distribution.Simulations and experiments show that the maximum temperature of the anodized piston is 16.36%and 5.4%smaller than that of the original piston under the condition of maximum torque and maximum power,respectively.The thermal stress of the temperature field of both pistons is within 50 Mpa,which meets the strength requirements of the material at high temperature.However,the area with significant thermal stress of the anodized piston is significantly smaller than that of the original piston.Combined with the fatigue analysis data,it can be seen that the safety factor of the anodized piston greater than 1.8 is 99.13%.Therefore,adopting the anodizing process not only reduces the piston thermal load,but also helps to extend its life and improve its reliability.
基金financially supported by the National Nature Science Foundation of China (No. 21371019)the Aero Science Foundation of China (No. 2011ZE51057)
文摘The effects of insoluble eutectic Si particles on the growth of anodic oxide films on ZL114A aluminum alloy substrates were in- vestigated by optical microscopy (OM) and scanning electron microscopy (SEM). The anodic oxidation was performed at 25℃ and a con- stant voltage of 15 V in a solution containing 50 g/L sulfuric acid and 10 g/L adipic acid. The thickness of the formed anodic oxidation film was approximately 7.13 μm. The interpore distance and the diameters of the major pores in the porous layer of the film were within the ap- proximate ranges of 10~20 nm and 5-10 nm, respectively. Insoluble eutectic Si particles strongly influenced the morphology of the anodic oxidation films. The anodic oxidation films exhibited minimal defects and a uniform thickness on the ZL114A substrates; in contrast, when the front of the oxide oxidation films encountered eutectic Si particles, defects such as pits and non-uniform thickness were observed, and pits were observed in the films.
基金supported by the National High Technology Research and Development Program of China (No. 2007AA03Z337)the Harbin Special Creation Foundation for Science and Technology of Fellow in China (No. 2006RFQXG032)
文摘The aim of this work was to investigate the effects of calcination/acid-activation on the composition, structure, and photocatalytic (PC) reduction property of an anodic oxidation TiO2/Ti film catalyst. The surface morphology and phase composition were examined by scanning electron microscopy and X-ray diffraction. The catalytic property of the film catalysts was evaluated through the removal rate of potassium chromate during the PC reduction process. The results showed that the film catalysts were composed of anatase and rutile TiO2 with a micro-porous surface structure. The calcination treatment increased the content of TiO2 in the film, changed the relative ratio of anatase and rutile TiO2, and decreased the size of the micro pores of the film catalysts. The removal rate of potassium chromate was related to the technique parameters of calcination/acid-activation treatment. When the anodic oxidation TiO2/Ti film catalyst was calcined at 873 K for 30 min and then acid-activated in the concentrated H2SO4 for 60 min, it presented the highest catalytic property, with the removal rate of potassium chromate of 96.3% during the PC reduction process under the experimental conditions.
基金financial support from USACH-Chile, Council of Scientific and Industrial Research (CSIR) and University Grant Commission (UGC) New Delhi, India
文摘Micron sized hexagon- and flower-like nanostructures of lead oxide(α-PbO2) have been synthesized by very simple and cost effective route of anodic oxidation of lead sheet. These structures were easily obtained by the simple variation of applied voltage from 2-6 V between the electrodes. Lead sheet was used as an anode and platinum sheet served as a cathode. Anodic oxidation at 2 V resulted in the variable edge sized(1-2 μm) hexagon-like structures in the electrolyte. When the applied potential was increased to 4 V a structure of distorted hexagons consisting of some flower-like structures were obtained. Further increment of potential up to 6 V resulted in flower like structures of α-PbO2 having six petals. The diameter of the flower-like structures was 200-500 nm and the size of a petal was 100-200 nm.
文摘Currently, landfills are the main method used for the final disposal of urban solid waste. The degradation processes that waste goes through in these sites, alongside rainwater that percolates through them, generate highly polluting liquids (leachate). In the treatment of leachate, advanced oxidation processes (AOP) can significantly reduce the concentrations of different pollutants. Due to the high documented potential around AOPs, in this study, the effectiveness of anodic oxidation in the removal of the remaining organic load in leachates pretreated in a biological system was evaluated. Graphite electrodes were used as anode and cathode. The efficiency of anodic oxidation, in terms of the removal of chemical oxygen demand (COD) and color, was evaluated under different current densities (7, 12, 17 and 22 mA/cm2) and pH values (3, 4.5 and 6). Under the best conditions found (22 mA/cm2 and pH of 6) and with an oxidation time of 5 hours, a maximum removal of 68% in COD and 91% in color was achieved, which represented a quality in the final effluent of 271 mg/L and 151 Pt-Co in COD and color, respectively. Therefore, considering that graphite is an economic and widely available material, the results obtained show anodic oxidation, with the use of graphite electrodes, as a technically viable alternative as a final purification stage for pretreated leachates.
文摘Electrode materials with high desalination capacity and long-term cyclic stability are the focus of capacitive deionization(CDI) community. Understanding the causes of performance decay in traditional carbons is crucial to design a high-performance material. Based on this, here, nitrogen-doped activated carbon(NAC) was prepared by pyrolyzing the blend of activated carbon powder(ACP) and melamine for the positive electrode of asymmetric CDI. By comparing the indicators changes such as conductivity, salt adsorption capacity, pH, and charge efficiency of the symmetrical ACP-ACP device to the asymmetric ACP-NAC device under different CDI cycles, as well as the changes of the electrochemical properties of anode and cathode materials after long-term operation, the reasons for the decline of the stability of the CDI performance were revealed. It was found that the carboxyl functional groups generated by the electro-oxidation of anode carbon materials make the anode zero-charge potential(E_(pzc)) shift positively,which results in the uneven distribution of potential windows of CDI units and affects the adsorption capacity. Furthermore, by understanding the electron density on C atoms surrounding the N atoms, we attribute the increased cyclic stability to the enhanced negativity of the charge of carbon atoms adjacent to quaternary-N and pyridinic-oxide-N.
基金financially supported by the National New Material Testing and Evaluation Platform Main Center Project(No.TC170A5SU-1)。
文摘Different additives were added into the potassium fluorozirconate solution to prepare different nickelfree sealing reagents,with which the anodic oxidation film of aluminum alloy was sealed at room temperature.The phosphor chromic acid weight loss method was used to evaluate the sealing effects.Using electron scanning microscopy(SEM),the surface and cross-sectional micromorphologies of the anodic oxidation films sealed by different fluorozirconate sealants were observed.The position and state of zirconium element distribution in the film hole were investigated by the further quantitative and distribution analysis of Zr element.This study provides an experimental evidence for the theoretical studies of fluorozirconate-sealed anodic oxidation films.It is shown that the fluorozirconate has good sealing effects and has a wide prospect for sealing the aluminum alloy samples.Its products were highly corrosion resistant,and were filled in the openings of the micropores in the oxide film.
基金financially supported by the National Natural Science Foundation of China (Nos. 2127222, 91213303, 21172205, J1030412)
文摘The nitrile functionality is a key building block in synthetic chemistry, and has wide applications in pharmaceuticals. However, traditional methodologies for the synthesis of nitriles are limited to harsh reaction conditions. Herein, we report a new and efficient access to aryl nitriles by an electrochemical synthesis. Compared with the conventional synthetic methods, this electrochemical synthesis is more environmentally friendly and easier to handle.
基金This work was financially supported by the National Natural Science Foundation of China(No.31971253)Beijing Municipal Health Commission(Nos.BMHC-2019-9,BMHC-2018-4 and PXM2020-026275-000002).
文摘Ti-Cu alloy has potential to be used in plastic surgery and dental implants due to its strong antibacterialproperties,high strength and good corrosion resistance.In this paper,Ti-5Cu was anodic-oxidized to enhance the surface compatibility.The influence of the oxidation on the corrosion resistance,antibacterial properties and biological properties was investigated.X-ray diffraction(XRD)and X-ray photoelectron spectroscopy(XPS)results showed that a double-layer oxide coating with dense inner layer and porous outside layer was formed on Ti-Cu sample.The oxide coating consisted mainly of TiO2,CuzO and small amount of CuO,improved the corrosion resistance of Ti-Cu alloy by one order of magnitude due to the formation of the dense oxide inner layer,but high Cu ion release was detected.The plate count results showed that the antibac-terial activity of Ti-Cu sample was improved to≥99%due to the comprehensive function of CuO and Cu_(2)O in the coating and Cu^(2+)release.Cell test results showed that thecoating exhibited good cell compatibility,the porous sur-face structure improved the adhesion of cells,and Cu ion release promoted the cell proliferation.
基金The authors are grateful for the financial support from the National Natural Science Foundation of China (Grant No. 21276177), and the Natural Science Foundation of Tianjin (Grant No. 10JCYBJC04900).
文摘This work was conducted to study the ability of anodic oxidation of azo dye C.I. Acid Red 73 (ART3) using the yttrium-doped Ti/SnO2-Sb electrodes. The effects of Sb doping level, yttrium doping level, thermal decomposition temperature and cycle times of dip-coating thermal decomposition on the properties of the electrodes were investigated. The results showed that the excellent electrochemical activity of Ti/SnO2-Sb-Y electrode can be achieved at a 7:1 molar ratio of Sn:Sb and thermal decomposition temperature of 550~C. Moreover when the cycle times of dip-coating and thermal decomposition were up to 10 times, the performance of the electrode tends to be stable. The Ti/SnO2-Sb electrodes doped with yttrium (0.5 tool-%) showed the most excellent electrochemical activity. In addition, the influences of operating variables, including current density, initial pH, dye concentration and support electrolyte, on the colour removal, chemical oxygen demand (COD) removal and current efficiency were also investigated. Our results confirmed that the current efficiency increased with the concentrations of dye and sodium chloride. Moreover, increasing the current density and the initial pH would reduce the current efficiency.
基金supported by the National Basic Research Program of China (No. 2011CB605602)
文摘Polyacrylonitrile (PAN) based carbon fibers with different surface morphology were electrochemically treated in 3 wt% NH4HCO3 aqueous solution with current density up to 3.47 A/m 2 at room temperature, and surface structures, surface morphology and residual mechanical properties were characterized. The crystallite size (La) of carbon fibers would be interrupted due to excessive electrochemical etching, while the crystallite spacing (d(002)) increased as increasing current density. The disordered structures on the surface of carbon fiber with rough surface increased at the initial oxidation stage and then removed by further electrochemical etching, which resulting in continuous increase of the extent of graphitization on the fiber surface. However, the electrochemical etching was beneficial to getting ordered morphology on the surface for carbon fiber with smooth surface, especially when the current density was lower than 1.77 A/m 2 . The tensile strength and tensile modulus could be improved by 17.27% and 5.75%, respectively, and was dependent of surface morphology. The decreasing density of carbon fibers probably resulted from the volume expansion of carbon fibers caused by the abundant oxygen functional groups intercalated between the adjacent graphite layers.
基金the National Nature Science Foundation of China(Nos.21472177,21672200,21432009,J1310010)the Strategic Priority Research Program of the Chinese Academy of Sciences(No.XDB20000000)
文摘A novel bromination of α,β-unsaturated carboxylic acids was developed via a decarboxylation by virtue of a direct anodic electro-oxidation.In this method,ammonium bromide was employed as a bromine source and the reaction features transition-metal-free,short time,and no additional supporting electrolyte.
文摘The anodic oxidation of nickel in molten (Li 0.62 ,K 0.38 ) 2CO 3 was investigated by means of cyclic voltammetry, X ray diffraction and X ray photoelectron spectroscopy. The results indicate that two reactions are involved in the anodic process: one is Ni+O 2- =NiO+2e -, the other reaction is Ni(Ⅱ)=Ni(Ⅲ)+e -.
基金the Natural Science Foundation of Guangdong Province,China(No.2021B1515020087)the National Natural Science Foundation of China(No.51775197).
文摘With the rapid development of two-phase heat exchangers,the further improvement of the capillary performance of their internal wick faces a great challenge.As an important technology in the surface treatment of aluminum alloys,anodic oxidation has been widely used to develop various functional nanostructures.In this study,nanopores with diameters of 30–40 nm were fabricated on the surface of aluminum fibers through anodic oxidation under an oxalic acid system.Results showed that anodizing increased the specific surface area of the aluminum braid by 163 times,and changed its surface wettability from hydrophobic to superhydrophilic.A significant reduction in the effective capillary radius can substantially increase the capillary force of aluminum braids on the basis of capillary theory.Therefore,the nanoporous aluminum braids can be used as a novel wick in the vapor chamber to improve its capillary performance.Capillary rate-of-rise tests with ethanol and acetone were performed to characterize the capillary of this novel wick structure.Infrared thermal imaging was utilized to monitor the capillary rise of aluminum braided wicks.The capillary force of the anodized wicks was greater than that of a normal wick,and the maximum capillary rise height was 81 mm.The nanoporous aluminum braided wicks prepared by anodizing could be applied in heat transfer.