A flame retardant containing multiple antiflaming elements usually exhibits high-efficient flame retardancy. Here, a novel P/N/Si-containing ammonium polyphosphate derivative(APTES-APP) is synthesized from ammonium po...A flame retardant containing multiple antiflaming elements usually exhibits high-efficient flame retardancy. Here, a novel P/N/Si-containing ammonium polyphosphate derivative(APTES-APP) is synthesized from ammonium polyphosphate(APP) and silane coupling agent(3-aminopropyl)triethoxysilane(APTES)via cation exchange, which is quite different in the chemical structure from APTES-modified APP for retaining silicon hydroxyls. APTES-APP is highly efficient for the epoxy resin. 8%(mass) APTES-APP imparts excellent flame retardancy to the epoxy resin, with a V-0 rating at the UL-94 test(1.6 mm)and an LOI value of 26%(vol). The peak heat release rate and total smoke production of the flameretardant epoxy resin are decreased by 68.1% and 31.3%, respectively. The synergy of P/N/Si contributes to the well-expanded char residue with a strong and dense surface layer, which is a very good barrier against heat and mass transfer. Besides, there is no significant deterioration in the mechanical properties of flame-retardant epoxy resin thanks to silicon hydroxyls forming hydrogen bonds with epoxy molecules. Meanwhile, other molecules can be grafted onto APTES-APP via these silicon hydroxyls, if needed.Briefly, this work has developed a new strategy for amino silane as flame retardants. In conjunction with a low-cost and simple preparation method, APTES-APP has a promising prospect in the high-performance flame-retardant epoxy.展开更多
The purpose of this study is to investigate the effect of the concentration of silane coupling solution on the tensile strength of basalt fiber and the interfacial properties of basalt fiber reinforced polymer composi...The purpose of this study is to investigate the effect of the concentration of silane coupling solution on the tensile strength of basalt fiber and the interfacial properties of basalt fiber reinforced polymer composites.The surface treatment of basalt fibers was carried out using an aqueous alcohol solution method.Basalt fibers were subjected to surface treatment with 3-Methacryloxypropyl trimethoxy silane at 0.5 wt.%,1 wt.%,2 wt.%,4 wt.%and 10 wt.%.The basalt monofilament tensile tests were carried out to investigate the variation in strength with the concentration of the silane coupling agent.The microdroplet test was performed to examine the effect of the concentration of the silane coupling agent on interfacial strength of basalt reinforced polymer composites.The film was formed on the surface of the basalt fiber treated silane coupling agent solution.The tensile strength of basalt fiber increased because the damaged fiber surface was repaired by the firm of silane coupling agent.The firm was effective in not only the surface protection of basalt fiber but also the improvement on the interfacial strength of fiber-matrix interface.However,the surface treatment using the high concentration silane coupling agent solution has an adverse effect on the mechanical properties of the composite materials,because of causing the degradation of the interfacial strength of the composite materials.展开更多
The reaction of ZnO nanoparticles grafted with KH570 silane coupling agent was carried out in water-alcohol mixed solvent. Several characterization methods were applied to analyzing the results of surface modification...The reaction of ZnO nanoparticles grafted with KH570 silane coupling agent was carried out in water-alcohol mixed solvent. Several characterization methods were applied to analyzing the results of surface modification such as Soxhlet extraction, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), thermogravimetry (TG), differential scanning calorimetry (DSC) and zeta potential (ζ). The results of FT-IR and TG-DSC show that the desired reaction chains have been covalently bonded on the surface of ZnO nanoparticles. Zetasizer results reveal that the maximal absolute value of ζ of the modified ZnO particles in acetone medium was 67.0 mV, which was much higher than that of the unmodified ZnO particles. So the surface of nanosized ZnO changed from hydrophilicity to hydrophobicity and the dispersity of ZnO nanoparticles were improved simultaneously. Finally, the mechanism of graft modification was discussed.展开更多
The influence of silane coupling agent on the film forming of galvanized steel treated with cerium salt was studied by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS), and the corrosi...The influence of silane coupling agent on the film forming of galvanized steel treated with cerium salt was studied by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS), and the corrosion resistance of conversion films was analyzed by electro interstitial scanning (EIS). The results show that silane coupling agent KH-570 has significant influence on the compactness and homogeneity of cerium conversion films, and the process of film forming is promoted by increasing the content of tervalent and tetravalent cerium oxide. The impedance value of the cerium conversion film, especially modified with KH-570, is greater than that of the base metal, which reveals that it is necessary to add silane coupling agent to the film-forming solution in order to improve the corrosion resistance of the conversion film.展开更多
The theory and approach of the surface modified of asphalt fire-retardant with silane coupling agent were introduced. The optimum silane dosage was determined, and the structure and properties of the asphalt fire-reta...The theory and approach of the surface modified of asphalt fire-retardant with silane coupling agent were introduced. The optimum silane dosage was determined, and the structure and properties of the asphalt fire-retardant before and after the surface modification were characterized by infrared spectrum and thermo gravimetric analysis. The dispersion effect of asphalt flre-retardant was studied. The influence of the surface modification on the hydrophilicity and lipophilicity of the asphalt fire-retardant was analyzed. The experimental results showed that there were physical and chemical interactions between the silane coupling agent and the asphalt fire-retardant, which reduced the surface polarity of the asphalt fire retardant. The optimum silane coupling agent dosage was 0.95% of the asphalt fire retardant. The surface modification improved the thermal stability, dispersibility and lipophilicity of the asphalt fire retardant, which enhanced the compatibility between asphalt fire retardant and asphalt.展开更多
The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane coupling agents KH-570, KH-590, and KH-792. The optimized ...The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane coupling agents KH-570, KH-590, and KH-792. The optimized geome-tries of molecular modified silica reinforced SBR were obtained by using B3LYP calculation of density functional theory with the 6-31+G basis sets. The natural bond orbital analyses were carried out. The Si—O bond length of silica modified by KH-792 was the shortest and the electronegative of O was the highest. It indicated that the connection between silica and KH-792 was the tightest. Higher tensile strength and elongation of reinforced SBR was obtained by silica modified with the KH-792. It was caused by large delocalization of lone pair electrons of the two N atoms in KH-792. The S—C bond length in silica modified by KH-590 was longer than the ordinary S—C bond length. Then the sulfur free radical (·S·) was produced more easily in vulcanization. The degree of crosslink was increased by the cross-linkage of the rubber molecule and the sulfur free radical. That was why the highest stress and tear strength of reinforced SBR was produced when silane coupling agent KH-590 was used. The calculation results was in accord with experimental data.展开更多
We experimentally studied the fine lightweight aggregate with the particle size range of 3.15-4.75 mm used as functional bridge between FRP sheet and concrete substrate. However, problems would appear and how to deal ...We experimentally studied the fine lightweight aggregate with the particle size range of 3.15-4.75 mm used as functional bridge between FRP sheet and concrete substrate. However, problems would appear and how to deal with the interfacial transition zone(ITZ) and make it stronger is the key point for this concept. Considering that silane coupling agent(SCA) can provide a better bond on a silicon-containing material surface, it was introduced as a modifying material to further improve the bond quality of the ITZ between lightweight aggregate and cement paste. Results indicated that the water absorptivity of lightweight aggregate can be controlled by SCA solutions, and the pull-off bond strength, mechanical strength, and microhardness were increased, which was attributed to the optimized microstructure under the condition of an appropriate concentration of SCA.展开更多
Fe3O4 nanoparticles were prepared by chemistry co-precipitation and the mean crystal size was 17.9 nm measured by XRD. After it had been treated by silane-coupling agents KH570, magnetic micro-spheres dispersed in org...Fe3O4 nanoparticles were prepared by chemistry co-precipitation and the mean crystal size was 17.9 nm measured by XRD. After it had been treated by silane-coupling agents KH570, magnetic micro-spheres dispersed in organic medium glycol were gained and the mean size of Fe3O4 nanopowders was 33.7 nm. So it can be concluded that magnetic micro-sphere is made of a few Fe3O4 crystals. Many factors of modification were researched, such as the time of ball milling, the content of Fe3O4 and the content of KH570. The modification of Fe3O4 is relative to the time of ball milling, but the dominant function is affected by the content of Fe3O4 and KH570. When the content of Fe3O4 is known, there is a suitable content of KH570. Different content of Fe3O4 will make the different suitable content of KH570, but the range of latter is less than former, which is relative to the distribution of KH570 on Fe3O4 surface or in the solution.展开更多
We used silane coupling agents to improve the bonding ability between wheat straw particles and UF resin, and investigated surface properties (wettability and surface roughness) and hardness of parti-cleboard made f...We used silane coupling agents to improve the bonding ability between wheat straw particles and UF resin, and investigated surface properties (wettability and surface roughness) and hardness of parti-cleboard made from UF-bonded wheat straw (Triticum aestivum L.) combined with poplar wood as affected by silane coupling agent content and straw/poplar wood particle ratios. We manufactured one-layered particleboard panels at four different ratios of straw to poplar wood par-ticles (0%, 15%, 30% and 45% wheat straw) and silane coupling agent content at three levels of 0, 5% and 10%. Roughness measurements, average roughness (Ra), mean peak-to-valley height (Rz), and root mean square roughness (Rq) were measured on unsanded samples by using a fine stylus tracing technique. We obtained contact angle measurements by using a goniometer connected to a digital camera and computer sys-tem. Boards containing greater amounts of poplar particles had superior hardness compared to control samples and had lower wettability. Panels made with higher amounts of silane had lower Rq values.展开更多
A novel silane coupling agent bearing sulfobetaine group, N,N-diethyl-N-(3-sulfopropyl)-aminopropyl- trimethoxysilane (DESATS), was first designed, synthesized and characterized. Its solution property was studied ...A novel silane coupling agent bearing sulfobetaine group, N,N-diethyl-N-(3-sulfopropyl)-aminopropyl- trimethoxysilane (DESATS), was first designed, synthesized and characterized. Its solution property was studied by means of dynamic light scattering. DESATS was successfully bonded onto the surface of the glass and proved by ESCA. Platelet adhesion assay in vitro indicated that the nonthrombogenicity of glass slide modified with DESATS is greatly improved.展开更多
A new kind of silane coupling agent, N- (β-aminoethyl ) - γ-aminopropyl triet hoxysilane, was used for DNA direct attachment on the surfaces of glass supports, then the immobilized DNA was hybridized with horseradis...A new kind of silane coupling agent, N- (β-aminoethyl ) - γ-aminopropyl triet hoxysilane, was used for DNA direct attachment on the surfaces of glass supports, then the immobilized DNA was hybridized with horseradish peroxidase (HRP)-labeled probe, and detected by using enhanced chemiluminescent method. In comparison with γ-aminopropyl triethoxysilane, the detection limits (S/N) of DNA were 10 pg and 75 pg respectively. Several experimental conditions of DNA attachING to glass supports were investigated, and the system of hybridization of nucleic acid on the surfaces of glass supports was developed.展开更多
Polyurethane/desulfurization ash(PU/DA)composites were synthesized using"one-pot method",with the incorporation of a silane coupling agent(KH550)as a"molecular bridge"to facilitate the integration ...Polyurethane/desulfurization ash(PU/DA)composites were synthesized using"one-pot method",with the incorporation of a silane coupling agent(KH550)as a"molecular bridge"to facilitate the integration of DA as hard segments into the PU molecular chain.The effects of DA content(φ)on the mechanical properties,thermal stability,and hydrophobicity of PU,both before and after the addition of KH550,were thoroughly examined.The results of microscopic mechanism analysis confirmed that KH550 chemically modified the surface of DA,facilitating its incorporation into the polyurethane molecular chain,thereby significantly enhancing the compatibility and dispersion of DA within the PU matrix.When the mass fraction of modified DA(MDA)reached 12%,the mechanical properties,thermal stability,and hydrophobicity of the composites were substantially improved,with the tensile strength reaching 14.9 MPa,and the contact angle measuring 100.6°.展开更多
The surface modification of clay fines was carried out by using silanecoupling agent. By means of IR spectra etc, a study was made on the combined state ofcoupling agent and clay. A rubber--clay composite material wit...The surface modification of clay fines was carried out by using silanecoupling agent. By means of IR spectra etc, a study was made on the combined state ofcoupling agent and clay. A rubber--clay composite material with excellent performancehas been prepared.展开更多
The chemical composition and high wear resistance of steel slag(SS)make it a potential alternative to traditional inorganic fillers.3-Aminopropyltriethoxysilane(KH550)modified steel slag(MSS)was successfully prepared,...The chemical composition and high wear resistance of steel slag(SS)make it a potential alternative to traditional inorganic fillers.3-Aminopropyltriethoxysilane(KH550)modified steel slag(MSS)was successfully prepared,and its application in epoxy(EP)anti-corrosion coating was introduced.Due to the grafting of silane coupling agent functional groups onto the surface of SS,MSS exhibited improved solubility in xylene organic solvent and reduced agglomeration.When the MSS content was 15 wt.%,the contact angle of the MSS/EP composite coating was 101°,and the abrasion was only 0.07 g,compared with 56.2°and 0.13 g,respectively,for the pure EP coating.The corrosion resistance of coatings was investigated by performing the electrochemical test(impedance)after immersion in a 3.5 wt.%NaCl solution.The electrochemical test results showed that the impedance modulus of the 15 wt.%MSS/EP composite coating at low frequency(Z_(f)=0.01 Hz)was approximately 1.08×10^(7)Ωcm^(2),which was two orders of magnitude higher than that of the pure EP coating.展开更多
The surface treatment of silca fume with silane coupling agent prior w incorporation in a cement mortar resulted in composites exhibiting increuses in loss tangent by 5%-200% and storage modulus by 10%-20% , relative...The surface treatment of silca fume with silane coupling agent prior w incorporation in a cement mortar resulted in composites exhibiting increuses in loss tangent by 5%-200% and storage modulus by 10%-20% , relative to the value obtained by using as-received silica fume. The scanning electron microscopy (SEM) images iindicate that there is a morphological difference in the cement paste with treated and as-received silica fume, The, X-ray diffraction (XRD), infrared (IR) spectrum analyses and mercury intrusion porosimetry ( MIP ) have provided evidence to understand the reaction mechanism between treated silica .fume and the hydrate product of cement. This has led to the establishment of an initial microscopic model describing the damping behavior of cement matrix.展开更多
Currently there has been a growing interest in substituting traditional synthetic polymers with biobased renewable polymers for adhesive applications. However, biobased renewable polymers such as starch suffer from fe...Currently there has been a growing interest in substituting traditional synthetic polymers with biobased renewable polymers for adhesive applications. However, biobased renewable polymers such as starch suffer from few draw-backs like poor water resistance and mechanical strength. To become important potential alternatives of synthetic polymers, starch must have comparable physical, chemical, thermal and mechanical properties to that of synthetic polymers. To achieve this, starch has been modified by a series of crosslinkers like boric acid, citric acid, glyoxal, gluteraldehyde, etc. and silane modification. Silane modification by chloropropyl trimethoxysilane, γ-Methacryloxypropyl trimethoxy silane and vinyl trimethoxy silane is a suitable method to improve the performance in terms of mechanical and thermally. Silane forms covalent bonds with starch during starch modification resulted in enhanced shear strength and storage stability. A new research on biodegradable, renewable, environmentally friendly silane modification of starch-based wood adhesive that was prepared by reacting with various silanes. This paper, we reviewed silane as a modifying agent for starch-based wood adhesive.展开更多
This paper, through XPS and IR analyses on the surface of sealing glass, identifies that the surface treatment of sealing glass by silane is a chemical process. On the basis of the analyses, the authors suggest an ide...This paper, through XPS and IR analyses on the surface of sealing glass, identifies that the surface treatment of sealing glass by silane is a chemical process. On the basis of the analyses, the authors suggest an ideal chemical bonding status between silane and glass surface.展开更多
基金financially supported by the National Natural Science Foundation of China (22178242)。
文摘A flame retardant containing multiple antiflaming elements usually exhibits high-efficient flame retardancy. Here, a novel P/N/Si-containing ammonium polyphosphate derivative(APTES-APP) is synthesized from ammonium polyphosphate(APP) and silane coupling agent(3-aminopropyl)triethoxysilane(APTES)via cation exchange, which is quite different in the chemical structure from APTES-modified APP for retaining silicon hydroxyls. APTES-APP is highly efficient for the epoxy resin. 8%(mass) APTES-APP imparts excellent flame retardancy to the epoxy resin, with a V-0 rating at the UL-94 test(1.6 mm)and an LOI value of 26%(vol). The peak heat release rate and total smoke production of the flameretardant epoxy resin are decreased by 68.1% and 31.3%, respectively. The synergy of P/N/Si contributes to the well-expanded char residue with a strong and dense surface layer, which is a very good barrier against heat and mass transfer. Besides, there is no significant deterioration in the mechanical properties of flame-retardant epoxy resin thanks to silicon hydroxyls forming hydrogen bonds with epoxy molecules. Meanwhile, other molecules can be grafted onto APTES-APP via these silicon hydroxyls, if needed.Briefly, this work has developed a new strategy for amino silane as flame retardants. In conjunction with a low-cost and simple preparation method, APTES-APP has a promising prospect in the high-performance flame-retardant epoxy.
文摘The purpose of this study is to investigate the effect of the concentration of silane coupling solution on the tensile strength of basalt fiber and the interfacial properties of basalt fiber reinforced polymer composites.The surface treatment of basalt fibers was carried out using an aqueous alcohol solution method.Basalt fibers were subjected to surface treatment with 3-Methacryloxypropyl trimethoxy silane at 0.5 wt.%,1 wt.%,2 wt.%,4 wt.%and 10 wt.%.The basalt monofilament tensile tests were carried out to investigate the variation in strength with the concentration of the silane coupling agent.The microdroplet test was performed to examine the effect of the concentration of the silane coupling agent on interfacial strength of basalt reinforced polymer composites.The film was formed on the surface of the basalt fiber treated silane coupling agent solution.The tensile strength of basalt fiber increased because the damaged fiber surface was repaired by the firm of silane coupling agent.The firm was effective in not only the surface protection of basalt fiber but also the improvement on the interfacial strength of fiber-matrix interface.However,the surface treatment using the high concentration silane coupling agent solution has an adverse effect on the mechanical properties of the composite materials,because of causing the degradation of the interfacial strength of the composite materials.
基金the Foundation of National Key Technologies R&D Program-Shanghai World Exposition Special Project (Grant No.04DZ05803)the Special Project of Shanghai Nano-technology (Grant No.05nm05011)
文摘The reaction of ZnO nanoparticles grafted with KH570 silane coupling agent was carried out in water-alcohol mixed solvent. Several characterization methods were applied to analyzing the results of surface modification such as Soxhlet extraction, Fourier transform infrared spectroscopy (FT-IR), transmission electron microscopy (TEM), thermogravimetry (TG), differential scanning calorimetry (DSC) and zeta potential (ζ). The results of FT-IR and TG-DSC show that the desired reaction chains have been covalently bonded on the surface of ZnO nanoparticles. Zetasizer results reveal that the maximal absolute value of ζ of the modified ZnO particles in acetone medium was 67.0 mV, which was much higher than that of the unmodified ZnO particles. So the surface of nanosized ZnO changed from hydrophilicity to hydrophobicity and the dispersity of ZnO nanoparticles were improved simultaneously. Finally, the mechanism of graft modification was discussed.
文摘The influence of silane coupling agent on the film forming of galvanized steel treated with cerium salt was studied by scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS), and the corrosion resistance of conversion films was analyzed by electro interstitial scanning (EIS). The results show that silane coupling agent KH-570 has significant influence on the compactness and homogeneity of cerium conversion films, and the process of film forming is promoted by increasing the content of tervalent and tetravalent cerium oxide. The impedance value of the cerium conversion film, especially modified with KH-570, is greater than that of the base metal, which reveals that it is necessary to add silane coupling agent to the film-forming solution in order to improve the corrosion resistance of the conversion film.
基金Funded by the National Natural Science Foundation of China(No.50978263)
文摘The theory and approach of the surface modified of asphalt fire-retardant with silane coupling agent were introduced. The optimum silane dosage was determined, and the structure and properties of the asphalt fire-retardant before and after the surface modification were characterized by infrared spectrum and thermo gravimetric analysis. The dispersion effect of asphalt flre-retardant was studied. The influence of the surface modification on the hydrophilicity and lipophilicity of the asphalt fire-retardant was analyzed. The experimental results showed that there were physical and chemical interactions between the silane coupling agent and the asphalt fire-retardant, which reduced the surface polarity of the asphalt fire retardant. The optimum silane coupling agent dosage was 0.95% of the asphalt fire retardant. The surface modification improved the thermal stability, dispersibility and lipophilicity of the asphalt fire retardant, which enhanced the compatibility between asphalt fire retardant and asphalt.
文摘The properties of styrene-butadiene rubber (SBR) reinforced by modified silica was investigated according to national standards. Silica was modified by silane coupling agents KH-570, KH-590, and KH-792. The optimized geome-tries of molecular modified silica reinforced SBR were obtained by using B3LYP calculation of density functional theory with the 6-31+G basis sets. The natural bond orbital analyses were carried out. The Si—O bond length of silica modified by KH-792 was the shortest and the electronegative of O was the highest. It indicated that the connection between silica and KH-792 was the tightest. Higher tensile strength and elongation of reinforced SBR was obtained by silica modified with the KH-792. It was caused by large delocalization of lone pair electrons of the two N atoms in KH-792. The S—C bond length in silica modified by KH-590 was longer than the ordinary S—C bond length. Then the sulfur free radical (·S·) was produced more easily in vulcanization. The degree of crosslink was increased by the cross-linkage of the rubber molecule and the sulfur free radical. That was why the highest stress and tear strength of reinforced SBR was produced when silane coupling agent KH-590 was used. The calculation results was in accord with experimental data.
基金Funded by the National Natural Science Foundation of China(No.51172173)
文摘We experimentally studied the fine lightweight aggregate with the particle size range of 3.15-4.75 mm used as functional bridge between FRP sheet and concrete substrate. However, problems would appear and how to deal with the interfacial transition zone(ITZ) and make it stronger is the key point for this concept. Considering that silane coupling agent(SCA) can provide a better bond on a silicon-containing material surface, it was introduced as a modifying material to further improve the bond quality of the ITZ between lightweight aggregate and cement paste. Results indicated that the water absorptivity of lightweight aggregate can be controlled by SCA solutions, and the pull-off bond strength, mechanical strength, and microhardness were increased, which was attributed to the optimized microstructure under the condition of an appropriate concentration of SCA.
基金This work was financially supported by the Graduate Innovation Plan Projects of Jiangsu Province in 2005.
文摘Fe3O4 nanoparticles were prepared by chemistry co-precipitation and the mean crystal size was 17.9 nm measured by XRD. After it had been treated by silane-coupling agents KH570, magnetic micro-spheres dispersed in organic medium glycol were gained and the mean size of Fe3O4 nanopowders was 33.7 nm. So it can be concluded that magnetic micro-sphere is made of a few Fe3O4 crystals. Many factors of modification were researched, such as the time of ball milling, the content of Fe3O4 and the content of KH570. The modification of Fe3O4 is relative to the time of ball milling, but the dominant function is affected by the content of Fe3O4 and KH570. When the content of Fe3O4 is known, there is a suitable content of KH570. Different content of Fe3O4 will make the different suitable content of KH570, but the range of latter is less than former, which is relative to the distribution of KH570 on Fe3O4 surface or in the solution.
文摘We used silane coupling agents to improve the bonding ability between wheat straw particles and UF resin, and investigated surface properties (wettability and surface roughness) and hardness of parti-cleboard made from UF-bonded wheat straw (Triticum aestivum L.) combined with poplar wood as affected by silane coupling agent content and straw/poplar wood particle ratios. We manufactured one-layered particleboard panels at four different ratios of straw to poplar wood par-ticles (0%, 15%, 30% and 45% wheat straw) and silane coupling agent content at three levels of 0, 5% and 10%. Roughness measurements, average roughness (Ra), mean peak-to-valley height (Rz), and root mean square roughness (Rq) were measured on unsanded samples by using a fine stylus tracing technique. We obtained contact angle measurements by using a goniometer connected to a digital camera and computer sys-tem. Boards containing greater amounts of poplar particles had superior hardness compared to control samples and had lower wettability. Panels made with higher amounts of silane had lower Rq values.
基金This work was support by the Special Funds for Major State Basic Research Projects of China(G1999064705).
文摘A novel silane coupling agent bearing sulfobetaine group, N,N-diethyl-N-(3-sulfopropyl)-aminopropyl- trimethoxysilane (DESATS), was first designed, synthesized and characterized. Its solution property was studied by means of dynamic light scattering. DESATS was successfully bonded onto the surface of the glass and proved by ESCA. Platelet adhesion assay in vitro indicated that the nonthrombogenicity of glass slide modified with DESATS is greatly improved.
基金a grant from National Science Foundation of China (No. 39990570).
文摘A new kind of silane coupling agent, N- (β-aminoethyl ) - γ-aminopropyl triet hoxysilane, was used for DNA direct attachment on the surfaces of glass supports, then the immobilized DNA was hybridized with horseradish peroxidase (HRP)-labeled probe, and detected by using enhanced chemiluminescent method. In comparison with γ-aminopropyl triethoxysilane, the detection limits (S/N) of DNA were 10 pg and 75 pg respectively. Several experimental conditions of DNA attachING to glass supports were investigated, and the system of hybridization of nucleic acid on the surfaces of glass supports was developed.
基金Funded by the National Key Research and Development Project(No.2019YFC1908204)the Guiding Projects in Fujian Province(No.2023H0023)the Fuzhou Science and Technology Plan Project(No.2022-P-012)。
文摘Polyurethane/desulfurization ash(PU/DA)composites were synthesized using"one-pot method",with the incorporation of a silane coupling agent(KH550)as a"molecular bridge"to facilitate the integration of DA as hard segments into the PU molecular chain.The effects of DA content(φ)on the mechanical properties,thermal stability,and hydrophobicity of PU,both before and after the addition of KH550,were thoroughly examined.The results of microscopic mechanism analysis confirmed that KH550 chemically modified the surface of DA,facilitating its incorporation into the polyurethane molecular chain,thereby significantly enhancing the compatibility and dispersion of DA within the PU matrix.When the mass fraction of modified DA(MDA)reached 12%,the mechanical properties,thermal stability,and hydrophobicity of the composites were substantially improved,with the tensile strength reaching 14.9 MPa,and the contact angle measuring 100.6°.
文摘The surface modification of clay fines was carried out by using silanecoupling agent. By means of IR spectra etc, a study was made on the combined state ofcoupling agent and clay. A rubber--clay composite material with excellent performancehas been prepared.
基金the University Synergy Innovation Program of Anhui Province(GXXT-2020-072).
文摘The chemical composition and high wear resistance of steel slag(SS)make it a potential alternative to traditional inorganic fillers.3-Aminopropyltriethoxysilane(KH550)modified steel slag(MSS)was successfully prepared,and its application in epoxy(EP)anti-corrosion coating was introduced.Due to the grafting of silane coupling agent functional groups onto the surface of SS,MSS exhibited improved solubility in xylene organic solvent and reduced agglomeration.When the MSS content was 15 wt.%,the contact angle of the MSS/EP composite coating was 101°,and the abrasion was only 0.07 g,compared with 56.2°and 0.13 g,respectively,for the pure EP coating.The corrosion resistance of coatings was investigated by performing the electrochemical test(impedance)after immersion in a 3.5 wt.%NaCl solution.The electrochemical test results showed that the impedance modulus of the 15 wt.%MSS/EP composite coating at low frequency(Z_(f)=0.01 Hz)was approximately 1.08×10^(7)Ωcm^(2),which was two orders of magnitude higher than that of the pure EP coating.
文摘The surface treatment of silca fume with silane coupling agent prior w incorporation in a cement mortar resulted in composites exhibiting increuses in loss tangent by 5%-200% and storage modulus by 10%-20% , relative to the value obtained by using as-received silica fume. The scanning electron microscopy (SEM) images iindicate that there is a morphological difference in the cement paste with treated and as-received silica fume, The, X-ray diffraction (XRD), infrared (IR) spectrum analyses and mercury intrusion porosimetry ( MIP ) have provided evidence to understand the reaction mechanism between treated silica .fume and the hydrate product of cement. This has led to the establishment of an initial microscopic model describing the damping behavior of cement matrix.
文摘Currently there has been a growing interest in substituting traditional synthetic polymers with biobased renewable polymers for adhesive applications. However, biobased renewable polymers such as starch suffer from few draw-backs like poor water resistance and mechanical strength. To become important potential alternatives of synthetic polymers, starch must have comparable physical, chemical, thermal and mechanical properties to that of synthetic polymers. To achieve this, starch has been modified by a series of crosslinkers like boric acid, citric acid, glyoxal, gluteraldehyde, etc. and silane modification. Silane modification by chloropropyl trimethoxysilane, γ-Methacryloxypropyl trimethoxy silane and vinyl trimethoxy silane is a suitable method to improve the performance in terms of mechanical and thermally. Silane forms covalent bonds with starch during starch modification resulted in enhanced shear strength and storage stability. A new research on biodegradable, renewable, environmentally friendly silane modification of starch-based wood adhesive that was prepared by reacting with various silanes. This paper, we reviewed silane as a modifying agent for starch-based wood adhesive.
文摘This paper, through XPS and IR analyses on the surface of sealing glass, identifies that the surface treatment of sealing glass by silane is a chemical process. On the basis of the analyses, the authors suggest an ideal chemical bonding status between silane and glass surface.