The CO_(2)catalytic hydrogenation represents a promising approach for gas-phase CO_(2)utilization in a direct manner.Due to its excellent hydrogenation ability,nickel has been widely studied and has shown good activit...The CO_(2)catalytic hydrogenation represents a promising approach for gas-phase CO_(2)utilization in a direct manner.Due to its excellent hydrogenation ability,nickel has been widely studied and has shown good activities in CO_(2)hydrogenation reactions,in addition to its high availability and low price.However,Ni-based catalysts are prone to sintering under elevated temperatures,leading to unstable catalytic performance.In the present study,various characterization techniques were employed to study the structural evolution of Ni/SiO_(2)during CO_(2)hydrogenation.An anti-sintering phenomenon is observed for both 9%Ni/SiO_(2)and 1%Ni/SiO_(2)during CO_(2)hydrogenation at 400℃.Results revealed that Ni species were re-dispersed into smaller-sized nanoparticles and formed Ni^(0)active species.While interestingly,this anti-sintering phenomenon leads to distinct outcomes for two catalysts,with a gradual increase in both reactivity and CH_(4)selectivity for 9%Ni/SiO_(2)presumably due to the formation of abundant surface Ni°from redispersion,while an apparent decreasing trend of CH_(4)selectivity for 1%Ni/SiO_(2)sample,presumably due to the formation of ultra-small nanoparticles that diffuse and partially filled the mesoporous pores of the silica support over time.Finally,the redispersion phenomenon was found relevant to the H_(2)gas in the reaction environment and enhanced as the H_(2)concentration increased.This finding is believed to provide in-depth insights into the structural evolution of Ni-based catalysts and product selectivity control in CO_(2)hydrogenation reactions.展开更多
A series of PtCuCeMgAl quintuple hydrotalcite-like compounds with different Ce contents were synthesized by one-pot method. After calcining and reduction, CeO_2-modified Mg(Al)O-supported Pt–Cu alloy catalysts were o...A series of PtCuCeMgAl quintuple hydrotalcite-like compounds with different Ce contents were synthesized by one-pot method. After calcining and reduction, CeO_2-modified Mg(Al)O-supported Pt–Cu alloy catalysts were obtained. To understand the effect of Cu and Ce, the structure and physico-chemistry properties of the catalysts were characterized and analyzed, and the catalytic behaviors were investigated in a direct dehydrogenation of propane to propene. The results show that the Pt^(4+), Cu^(2+), and Ce^(3+) ions can be incorporated into the brucite-like layers and the Ce content significantly affects the interaction strength between Pt and Cu and the dehydrogenation performance of propane. Under the reaction conditions, the highest propane conversion(45%) with 89% selectivity to propene and a 40% propene yield were achieved with a 0.3 wt% Ce-modified PtCu/Mg(Al)O catalyst. The improved catalytic performance is related to the easy formation of Pt–Cu alloy phase, excellent resistance to sintering, and coke deposits of active components modified by CeO_2.展开更多
Limestone can be used for CO_2 capture and sequestration(CCS) in flue gas effectively. However, its CCS capability will dramatically decline after several cycles due to the surface "sintering". In this work,...Limestone can be used for CO_2 capture and sequestration(CCS) in flue gas effectively. However, its CCS capability will dramatically decline after several cycles due to the surface "sintering". In this work, the limestone was modified with palygorskite to reduce sintering phenomenon between the absorbent particles during the CCS process and the carbonation rate of the limestone can be enhanced effectively. Palygorskite is a natural mineral with nano-fibrous structure which can reduce the mutual contact of limestone particles during the CCS process. The results were detected by TGA, SEM, MIP, FTIR and particle size analyzer respectively. The best CO_2 capture performance of modified absorbent was 13.11% improvement with only 5 wt% palygorskite added during the CCS process after 15 cycles compared with natural absorbent. It was found that excellent microscopic structures of absorbent modified with palygorskite was created, and the surface sintering was postponed leading to CO_2 capture performance enhanced under the same conditions.展开更多
In this work, a series of Pt nanocrystallines(Pt NCs) supported on TiO2 substrate with controlled thickness of carbon layers(C-Pt/TiO2) were synthesized. Well-dispersed Pt NCs were facilely synthesized at room tem...In this work, a series of Pt nanocrystallines(Pt NCs) supported on TiO2 substrate with controlled thickness of carbon layers(C-Pt/TiO2) were synthesized. Well-dispersed Pt NCs were facilely synthesized at room temperature by a photo-reduction process in lytropic liquid crystal(LCs). Surface tuning of the carbon layers on Pt/TiO2 catalysts was achieved by varying the calcination atmospheres(in argon, air, and oxygen) and characterized by XPS and HRTEM. The influence of the coated carbon layers on the catalytic activity of catalysts is investigated by CO oxidation reaction which presented the following ranks: C-Pt/TiO2-O2〉 C-Pt/TiO2-Air 〉 C-Pt/TiO2-Ar. It is found that the carbon layer coating can stabilize the Pt NCs and enable them anti-sintering at high temperature. This finding provides new insight into understanding the C-Pt/TiO2 ternary system for tuning their catalytic performance.展开更多
Impeding high temperature sintering is challengeable for synthesis of carbon-supported single-atom catalysts (C-SACs), which requires high-cost precursor and strictly-controlled procedures. Herein, by virtue of the ul...Impeding high temperature sintering is challengeable for synthesis of carbon-supported single-atom catalysts (C-SACs), which requires high-cost precursor and strictly-controlled procedures. Herein, by virtue of the ultrastrong polarity of salt melts, sintering of metal atoms is effectively suppressed. Meanwhile, doping with inorganic sulfur anions not only produces sufficient anchoring sites to achieve high loading of atomically dispersed Co up to 13.85 wt.%, but also enables their electronic and geometric structures to be well tuned. When served as a cathode catalyst in dye-sensitized solar cells, the C-SAC with Co-N4-S2 moieties exhibits high activity towards the iodide reduction reaction (IRR), achieving a higher power conversion efficiency than that of conventional Pt counterpart. Density function theory (DFT) calculations revealed that the superior IRR activity was ascribed to the unique structure of Co-N4-S2 moieties with lower reaction barriers and moderate binding energy of iodine on the Co center, which was beneficial to I2 dissociation.展开更多
基金supported by the Shanghai Post-Doctoral Excellence Program(No.2021232)Y.He thanks the National Natural Science Foundation of China(No.22202131)+3 种基金the Shanghai Science and Technology Development Funds of“Rising Star”Sailing Program(No.22YF1419400)for the financial supportM.Zhu thanks the research funding sponsored by the National Natural Science Foundation of China(No.22078089)the Shanghai Special Program for Fundamental Research(No.22TQ1400100-7)the Basic Research Program of Science and Technology Commission of Shanghai Municipality(No.22JC1400600)。
文摘The CO_(2)catalytic hydrogenation represents a promising approach for gas-phase CO_(2)utilization in a direct manner.Due to its excellent hydrogenation ability,nickel has been widely studied and has shown good activities in CO_(2)hydrogenation reactions,in addition to its high availability and low price.However,Ni-based catalysts are prone to sintering under elevated temperatures,leading to unstable catalytic performance.In the present study,various characterization techniques were employed to study the structural evolution of Ni/SiO_(2)during CO_(2)hydrogenation.An anti-sintering phenomenon is observed for both 9%Ni/SiO_(2)and 1%Ni/SiO_(2)during CO_(2)hydrogenation at 400℃.Results revealed that Ni species were re-dispersed into smaller-sized nanoparticles and formed Ni^(0)active species.While interestingly,this anti-sintering phenomenon leads to distinct outcomes for two catalysts,with a gradual increase in both reactivity and CH_(4)selectivity for 9%Ni/SiO_(2)presumably due to the formation of abundant surface Ni°from redispersion,while an apparent decreasing trend of CH_(4)selectivity for 1%Ni/SiO_(2)sample,presumably due to the formation of ultra-small nanoparticles that diffuse and partially filled the mesoporous pores of the silica support over time.Finally,the redispersion phenomenon was found relevant to the H_(2)gas in the reaction environment and enhanced as the H_(2)concentration increased.This finding is believed to provide in-depth insights into the structural evolution of Ni-based catalysts and product selectivity control in CO_(2)hydrogenation reactions.
基金supported by the National Natural Science Foundation of China(No.21776214)the Natural Science Foundation of Jiangsu Province(No.BK20161166)the State Key Laboratory of Chemical Resource Engineering
文摘A series of PtCuCeMgAl quintuple hydrotalcite-like compounds with different Ce contents were synthesized by one-pot method. After calcining and reduction, CeO_2-modified Mg(Al)O-supported Pt–Cu alloy catalysts were obtained. To understand the effect of Cu and Ce, the structure and physico-chemistry properties of the catalysts were characterized and analyzed, and the catalytic behaviors were investigated in a direct dehydrogenation of propane to propene. The results show that the Pt^(4+), Cu^(2+), and Ce^(3+) ions can be incorporated into the brucite-like layers and the Ce content significantly affects the interaction strength between Pt and Cu and the dehydrogenation performance of propane. Under the reaction conditions, the highest propane conversion(45%) with 89% selectivity to propene and a 40% propene yield were achieved with a 0.3 wt% Ce-modified PtCu/Mg(Al)O catalyst. The improved catalytic performance is related to the easy formation of Pt–Cu alloy phase, excellent resistance to sintering, and coke deposits of active components modified by CeO_2.
基金Supported by the National Natural Science Foundation of China(51274159)Special Funds for The Major Science and Technology Innovation of Shaanxi Province(2012zkc06-2)
文摘Limestone can be used for CO_2 capture and sequestration(CCS) in flue gas effectively. However, its CCS capability will dramatically decline after several cycles due to the surface "sintering". In this work, the limestone was modified with palygorskite to reduce sintering phenomenon between the absorbent particles during the CCS process and the carbonation rate of the limestone can be enhanced effectively. Palygorskite is a natural mineral with nano-fibrous structure which can reduce the mutual contact of limestone particles during the CCS process. The results were detected by TGA, SEM, MIP, FTIR and particle size analyzer respectively. The best CO_2 capture performance of modified absorbent was 13.11% improvement with only 5 wt% palygorskite added during the CCS process after 15 cycles compared with natural absorbent. It was found that excellent microscopic structures of absorbent modified with palygorskite was created, and the surface sintering was postponed leading to CO_2 capture performance enhanced under the same conditions.
基金financially supported by the National Key Technology R&D Program of China (No. 2017YFB0310704)the National Natural Science Foundation of China (Nos. 21773112, 21173119 and 21303083)+2 种基金Natural Science Foundation of the Higher Education Institutions of Jiangsu Province (No. 17KJB150001)the Natural Science Foundation of Jiangsu Province (No. BK20130563)the Fundamental Research Funds for the Central Universities
文摘In this work, a series of Pt nanocrystallines(Pt NCs) supported on TiO2 substrate with controlled thickness of carbon layers(C-Pt/TiO2) were synthesized. Well-dispersed Pt NCs were facilely synthesized at room temperature by a photo-reduction process in lytropic liquid crystal(LCs). Surface tuning of the carbon layers on Pt/TiO2 catalysts was achieved by varying the calcination atmospheres(in argon, air, and oxygen) and characterized by XPS and HRTEM. The influence of the coated carbon layers on the catalytic activity of catalysts is investigated by CO oxidation reaction which presented the following ranks: C-Pt/TiO2-O2〉 C-Pt/TiO2-Air 〉 C-Pt/TiO2-Ar. It is found that the carbon layer coating can stabilize the Pt NCs and enable them anti-sintering at high temperature. This finding provides new insight into understanding the C-Pt/TiO2 ternary system for tuning their catalytic performance.
基金This work was financially supported by the National Natural Science Foundation of China(Nos.51773025 and 21701168)the Natural Foundation of Liaoning Province(Materials Joint Foundation,No.20180510027)+1 种基金Dalian Science and Technology Innovation Fund(No.019J12GX032)We gratefully acknowledge the BL14W1 Beamline of Shanghai Synchrotron Radiation Facility(SSRF)in Shanghai,China and the 1W1B Beamline of Beijing Synchrotron Radiation Facility(BSRF)in Beijing,China for providing the beam time.
文摘Impeding high temperature sintering is challengeable for synthesis of carbon-supported single-atom catalysts (C-SACs), which requires high-cost precursor and strictly-controlled procedures. Herein, by virtue of the ultrastrong polarity of salt melts, sintering of metal atoms is effectively suppressed. Meanwhile, doping with inorganic sulfur anions not only produces sufficient anchoring sites to achieve high loading of atomically dispersed Co up to 13.85 wt.%, but also enables their electronic and geometric structures to be well tuned. When served as a cathode catalyst in dye-sensitized solar cells, the C-SAC with Co-N4-S2 moieties exhibits high activity towards the iodide reduction reaction (IRR), achieving a higher power conversion efficiency than that of conventional Pt counterpart. Density function theory (DFT) calculations revealed that the superior IRR activity was ascribed to the unique structure of Co-N4-S2 moieties with lower reaction barriers and moderate binding energy of iodine on the Co center, which was beneficial to I2 dissociation.