Preparation and Characterization of Two-component Waterborne Polyurethane Comprised of Water-soluble Acrylic Resin and HDI Biuret

A two-component waterborne polyurethane(2K-WPU) was prepared by mixing water-soluble acrylic resin and hexamethylene diisocyanate biuret, and then diluted for phase inversion with water. Compared with water-soluble acrylic resin, the phase inversion of 2K-WPU occurs at lower water content. It is indicated by TEM that 2K-WPU parti-cles show a core-shell structure, in which HDI biuret is encapsulated by hydrophilic acrylic resin. 2K-WPU emulsion with HDI biuret has larger particle size and narrower distribution index, while for 2K-WPU emulsion with HDI iso-cyanurate, the latex not only has large particle size, but also has two-peak distribution. FTIR shows that the reaction be-tween HDI biuret and acrylic resin can complete in 12h. In addition, studies on effect of composition of acrylic resin on performance of 2K-WPU show that narrowing the polar difference between water-soluble acrylic resin and HDI biuret and improving the miscibility of two components are the key to prepare the transparent and high gloss films with high crosslinking density.

Synthesis of a Novel UV Curable Aqueous Dispersion Polyurethane PDHA-PEDA-PU and the Properties of Cured Film

A novel ultraviolet （UV） curable aqueous dispersion polyurethane PDHA-PEDA-PU was synthesized based on isophorone diisocyanate （IPDI）, polyester dihydric alcohol （PDHA）, dimethylol propionic acid （DMPA）, pentaerythritol diacrylate （PEDA）, 2-hydroxyethyl acrylate （HEA） and triethylamine （TEA）. Acrylate groups were incorporated in the side and end of PDHA-PEDA-PU chain. The C=C content in the chain can be controlled easily through the change of IPDI/PDHA/PEDA ratio. Fourier transform infrared spectroscopy （FTIR） was used to identify the structure of prepolymer, aqueous dispersion and cured polyurethane. The curing rule of the polyurethane for different C=C content has been investigated depending on the change of C=C content during the curing process. The hardness, thermal stability and scrub resistance to MEK of UV cured PDHA-PEDA-PU were also discussed for the samples with different C=C content.

Use of the Newly Synthesized Aqueous Polyurethane Acrylate Binders for Printing Cotton and Polyester Fabrics

The use of the four new synthesized polyurethane acrylate binders in the pigment print paste for screen printing cotton and polyester fabrics and pigment fixation through the polymerization process of the binder by using the thermofixation technique as well as the UV curing technique was studied. The effect of changing time and temperature of thermofixation, and the time of UV curing on the color strength, and prints fastness properties were also studied. The results showed that, the newly synthesized polyurethane acrylate binders could be successfully used for pigment fixation on cotton and polyester using the two fixation techniques and in general their prints possessed better color strength values as compared to those obtained upon using the selected commercial binders.

A Novel Aqueous Polyurethane Containing Short Fluoroalkyl Chains:Synthesis and Application on Cotton Fabrics

As very useful superficial mediflcation agents, the common long perfluoroalkyl -- containing agents are facing the ecological problems, such as persistence, bioacumulatlen, and/or toxicity in the environment. In order to overcome the problems, we designed and synthesized a polyether dioi containing short perfluoroaikyl side chains, which was condensed with diisocyanate to form fluorine-containing aqueous polyurethane. This aqueous polyurethane was applied on cotton fabrics by conventional pad-dry-cure process. The treated cotton fabrics showed good water repellent property with the contact angle reached 131°, and also IXBSessed good washing durability.

Part 1: Synthesis and Evaluation of Novel Nano Scale Powdered Polyurethane Acrylate Binders

Some new an aqueous polyurethane acrylate (waterborne binder) based on polyethylene glycol with different M. wt. mixed with polyol were carried out. Seven different polyurethane acrylate co-polymers were prepared aiming at substituting the two hydroxyl groups of polyethylene glycol (6000, 12,000 and 20,000 g/mol) and two primary hydroxyl groups of polyol through their reaction with corresponding calculated amounts of either isophorone diisoyanate or toluene diisocyanate and caped the remaining isocyanate group with either hydroxy ethyl acrylate or hydroxy propyl methacrylate to get on the polyurethane acrylate polymers [PUA]. From DSC measurement the result of Tg of synthesized PUA are in range from -8.78℃ to 36.4℃. So they can classify as soft binders. The infrared spectra, rheological properties, viscosity measurement, the weight average molecular weight, of the synthesize binders were investigated.

Synthesis and fluorescence enhancement behavior of a novel fluorescent aqueous polyurethane emulsion DDAQ-TDI-PU

A novel fluorescent aqueous polyurethane emulsion DDAQ-TDI-PU was synthesized by blocking the anthraquinone moiety of 1,4-diamino-2,3-diphenoxyanthraquinone（DDAQ） into polyurethane chain using 2,4-tolylene diisocyanate（TDI）,poly（propylene glycol） and 2,2-dimethylol propionic acid.The chain structure of DDAQ-TDI-PU was confirmed by means of Fourier transform infrared spectroscopy and UV-vis analysis.Comparing to the UV-vis spectrum of DDAQ,DDAQ-TDI-PU showed a hypsochromic shift from the absorption maxima of 518,558,609 nm to 510,548,586 nm,respectively.It was found that the fluorescence intensity of DDAQ-TDI-PU emulsion was enhanced greatly comparing with that of DDAQ.The fluorescence of DDAQ-TDI-PU was very stable not only for the long term storage but also for the fluorescence quencher.

Strength performance of mortise and loose-tenon furniture joints under uniaxial bending moment

We determined the effects of adhesive type and loose tenon dimensions （length and thickness） on bending strength of T-shaped mor- tise and loose-tenon joints. Polyvinyl acetate （PVAc） and two-component polyurethane （PU） adhesives were used to construct joint specimens. The bending moment capacity of joints increased significantly with increased length and thickness of the loose tenon. Bending moment capacity of joints constructed with PU adhesive was approximately 13% higher than for joints constructed with PVAc adhesive. We developed a predictive equation as a function of adhesive type and loose tenon dimensions to estimate the strength of the joints constructed of oriental beech （Fagus orientalis L.） under uniaxial bending load.