The effects of aramid/carbon on tensile properties of multilayered biaxial weft knitted( MBWK) fabric reinforced composites are analyzed by experiments. The tensile tests are inducted by the SHIMADZU AG-250 KNE univer...The effects of aramid/carbon on tensile properties of multilayered biaxial weft knitted( MBWK) fabric reinforced composites are analyzed by experiments. The tensile tests are inducted by the SHIMADZU AG-250 KNE universal material testing machine and Aramis V6 digital image correlation( DIC) technique.More specifically,the composite samples own four hybrid ratios(Na∶ Nc= 12∶ 0,8 ∶ 4,6 ∶ 6 and 4 ∶ 8). The results showed that the aramid/carbon hybrid MBWK fabric reinforced composites showed nearly linear response until reaching the maximum load and the inserting yarns distribution on the surface of MBWK fabrics reinforced composites had a great influence on the strain pattern distribution. Besides,the tensile strength,the tensile modulus and the elongation at breakage of 0° samples and 90° samples increased with the decreasing of aramid/carbon hybrid ratio. In a word,the changes of tensile strength, tensile modulus and elongation at breakage have a lot to do with the difference of aramid/carbon hybrid ratio.展开更多
Seven kinds of weft knitted fabrics from glass fiber yarns were used as reinforcement to make fabric/epoxy composite laminates. Tensile tests were carried out to examine and compare the mechanical properties in course...Seven kinds of weft knitted fabrics from glass fiber yarns were used as reinforcement to make fabric/epoxy composite laminates. Tensile tests were carried out to examine and compare the mechanical properties in course and wale direction of these composites. On the basis of experimental results, attempts have been made to analyze some main factors influencing stress-strain curve, ultimate tensile strength and initial elastic modulus of specimens.展开更多
Several different kinds of weft knitted fabrics from glass fiber yarns were used as reinforcement to make fabric/polyester composite laminates. Flexural tests were carried out to examine stress- deflection process and...Several different kinds of weft knitted fabrics from glass fiber yarns were used as reinforcement to make fabric/polyester composite laminates. Flexural tests were carried out to examine stress- deflection process and compare the mechanical properties in course and wale directions of these composites. The experimental results indicate that the numbers of load-bearing yarn in course and wale direction and the fabric density are the main factors influencing the ultimate tensile strength and initial elastic modulus of specimens.展开更多
Polypropylene, carbon, aramid and polyethylene fibers reinforced cement composites were fabricated respectively. Their fracture behaviors were observed using scanning electron microscopy and the bonding between fiber ...Polypropylene, carbon, aramid and polyethylene fibers reinforced cement composites were fabricated respectively. Their fracture behaviors were observed using scanning electron microscopy and the bonding between fiber and matrix was observed in detail.展开更多
基金Tianjin Municipal Science and Technology Commission for the Financial Supports,China(No.11ZCKFSF00500)China's General Administration of Quality Supervision,Inspection and Quarantine for the Financial Supports,China(No.201210260)
文摘The effects of aramid/carbon on tensile properties of multilayered biaxial weft knitted( MBWK) fabric reinforced composites are analyzed by experiments. The tensile tests are inducted by the SHIMADZU AG-250 KNE universal material testing machine and Aramis V6 digital image correlation( DIC) technique.More specifically,the composite samples own four hybrid ratios(Na∶ Nc= 12∶ 0,8 ∶ 4,6 ∶ 6 and 4 ∶ 8). The results showed that the aramid/carbon hybrid MBWK fabric reinforced composites showed nearly linear response until reaching the maximum load and the inserting yarns distribution on the surface of MBWK fabrics reinforced composites had a great influence on the strain pattern distribution. Besides,the tensile strength,the tensile modulus and the elongation at breakage of 0° samples and 90° samples increased with the decreasing of aramid/carbon hybrid ratio. In a word,the changes of tensile strength, tensile modulus and elongation at breakage have a lot to do with the difference of aramid/carbon hybrid ratio.
文摘Seven kinds of weft knitted fabrics from glass fiber yarns were used as reinforcement to make fabric/epoxy composite laminates. Tensile tests were carried out to examine and compare the mechanical properties in course and wale direction of these composites. On the basis of experimental results, attempts have been made to analyze some main factors influencing stress-strain curve, ultimate tensile strength and initial elastic modulus of specimens.
文摘Several different kinds of weft knitted fabrics from glass fiber yarns were used as reinforcement to make fabric/polyester composite laminates. Flexural tests were carried out to examine stress- deflection process and compare the mechanical properties in course and wale directions of these composites. The experimental results indicate that the numbers of load-bearing yarn in course and wale direction and the fabric density are the main factors influencing the ultimate tensile strength and initial elastic modulus of specimens.
基金Supported by China Natural Science Foundation(29874030)
文摘Polypropylene, carbon, aramid and polyethylene fibers reinforced cement composites were fabricated respectively. Their fracture behaviors were observed using scanning electron microscopy and the bonding between fiber and matrix was observed in detail.