Residual stress and welding distortion of Al/steel butt joint by arc-assisted laser welding-brazing

The thermo-elastic.plastic finite element method(FEM)is used to simulate the thermo-mechanical behavior of Al/steel tungsten inert gas(TIG)arc-assisted laser welding-brazing(A-LWB)butt joint.The influence of material nonlinearity,geometrical nonlinearity and work hardening on the welding process is studied,and the differences in the welding temperature field,residual stress and welding distortion by A-LWB and by single laser welding-brazing(SLWB)are analyzed.The results show that the thermal cycle,residual stress distribution and welding distortion by the numerical simulation are in good agreement with the measured data by experiments,which verifies the effectiveness of FEM.Compared with the SLWB,A-LWB can make the high-temperature distribution zone of weld in width direction wider,decrease the transverse tensile stress in the weld and reduce the distribution range of longitudinal tensile stress.And the welding deformation also decreases to some extent.

Bulging Distortion of Austenitic Stainless Steel Sheet on the Partially Penetrated Side of Non-Penetration Lap Laser Welding Joint

Non-penetration laser welding of lap joints in austenitic stainless steel sheets is commonly preferred in fields where the surface quality is of utmost importance.However,the application of non-penetration welded austenitic stainless steel parts is limited owing to the micro bulging distortion that occurs on the back surface of the partial penetration side.In this paper,non-penetration lap laser welding experiments,were conducted on galvanized and SUS304 austenitic stainless steel plates using a fiber laser,to investigate the mechanism of bulging distortion.A comparative experiment of DC01 galvanized steel-Q235 carbon steel lap laser welding was carried out,and the deflection and distortion profile of partially penetrated side of the sheets were measured using a noncontact laser interferometer.In addition,the cold-rolled SUS304 was subjected to heat holding at different temperatures and water quenching after bending to characterize its microstructure under tensile and compressive stress.The results show that,during the heating stage of the thermal cycle of laser lap welding,the partial penetration side of the SUS304 steel sheet generates compressive stress,which extrudes the material in the heat-affected zone to the outside of the back of the SUS304 steel sheet,thereby forming a bulge.The findings of these experiments can be of great value for controlling the distortion of the partial penetrated side of austenitic stainless steel sheet during laser non-penetration lap welding.

Effect of process parameters on the morphology of aluminum/copper alloy lap joints by red and blue hybrid laser welding

In order to overcome the problems of many pores,large deformation and unstable weld quality of traditional laser welded aluminumcopper alloy joints,a red-blue dual-beam laser source and a swinging laser were introduced for welding.T2 copper and 6063 aluminum thin plates were lap welded by coaxial dual-beam laser welding.The morphology of weld cross section was compared to explore the influence of process parameters on the formation of lap joints.The microstructure characteristics of the weld zone were observed and compared by optical microscope.The results show that the addition of laser beam swing can eliminate the internal pores of the weld.With the increase of the swing width,the weld depth decreases,and the weld width increases first and then decreases.The influence of welding speed on the weld cross section morphology is similar to that of swing width.With the increase of welding speed,the weld width increases first and then decreases,while the weld depth decreases all the time.This is because that the red laser is used as the main heat source to melt the base metals,with the increase of red laser power,the weld depth increases.As an auxiliary laser source,blue laser reduces the total energy consumption,consequently,the effective heat input increases and the spatter is restrained effectively.As a result,the increase of red laser power has an enhancement effect on the weld width and weld depth.When the swing width is 1.2 mm,the red laser power is 550 W,the blue laser power is 500 W,and the welding speed is 35 mm/s,the weld forming is the best.The lap joint of T2 copper and 6063 aluminum alloy thin plate can be connected stably with the hybrid of blue laser.The effect rules of laser beam swing on the weld formation were obtained,which improved the quality of the joints.

Image processing of weld pool and keyhole in Nd:YAG laser welding of stainless steel based on visual sensing

In order to obtain good welding quality, it is necessary to apply quality control because there are many influencing factors in laser welding process. The key to realize welding quality control is to obtain the quality information. Abundant weld quality information is contained in weld pool and keyhole. Aiming at Nd：YAG laser welding of stainless steel, a coaxial visual sensing system was constructed. The images of weld pool and keyhole were obtained. Based on the gray character of weld pool and keyhole in images, an image processing algorithm was designed. The search start point and search criteria of weld pool and keyhole edge were determined respectively.

Analysis of high-power disk laser welding stability based on classification of plume and spatter characteristics

Classification of plume and spatter images was studied to evaluate the welding stability. A high-speed camera was used to capture the instantaneous images of plume and spatters during high power disk laser welding. Characteristic parameters such as the area and number of spatters, the average grayscale of a spatter image, the entropy of a spatter grayscale image, the coordinate ratio of the plume centroid and the welding point, the polar coordinates of the plume centroid were defined and extracted. Karhunen-Loeve transform method was used to change the seven characteristics into three primary characteristics to reduce the dimensions. Also, K-nearest neighbor method was used to classify the plume and spatter images into two categories such as good and poor welding quality. The results show that plume and spatter have a close relationship with the welding stability, and two categories could be recognized effectively using K-nearest neighbor method based on Karhunen-Loeve transform.

Determination of energy coupling to material in laser welding by a novel “sandwich” method

A mathematical energy coupling model was developed to analyze the light transmission in the keyhole and energy distribution on the keyhole wall.The main characteristics of the model include：1） a prototype of the keyhole and the inverse Bremsstrahlung absorption coefficient in the keyhole plasma are obtained from the experiments;2） instead of using a parallel incident beam,a focused laser beam with real Gaussian intensity distribution is implemented;3） both Fresnel absorption and inverse Bremsstrahlung absorption during multiple reflections are considered.The calculation results show that the distribution of absorbed laser intensity by the keyhole wall is not uniform.The maximum laser energy is absorbed by the bottom of the keyhole,although no rays irradiate directly onto the bottom.According to analysis of beam focusing characteristics,the location of the focal plane plays a more important role in the laser energy absorption by the front wall than by the rear wall.

Porosity sensitivity of A356 Al alloy during fiber laser welding

In order to decrease the metallurgical porosity and keyhole-induced porosity during deep penetration laser welding of Al and its alloys, and increase the mechanical properties of work-piece, the effects of welding parameters such as laser power, welding speed and defocusing value on both kinds of porosities were systemically analyzed respectively, and the shape and fluctuation of plume of the keyhole were observed to reflect the stability of the keyhole. The results show that increasing laser power or decreasing laser spot size can lead to the rising of both number and occupied area of pores in the weld; meanwhile, the plume fluctuates violently over the keyhole, which is always companied with the intense metallic vapor, liquid metal spatter and collapsing in the keyhole, thus more pores are generated in the weld. The porosity in the weld reaches the minimum at welding velocity of 2.0 m/min when laser power is 5 kW and defocusing value is 0.

Stitch welding of Ti-6Al-4V titanium alloy by fiber laser

Stitch welding of plate covered skeleton structure of Ti-6Al-4V titanium alloys has a variety of applications in aerospace vehicle manufacture. The laser stitch welding of Ti-6Al-4V titanium alloys was carried out by a 4 kW ROFIN fiber laser. Influences of laser welding parameters on the macroscopic geometry, porosity, microstructure and mechanical properties of the stitch welded seams were investigated by digital microscope, optical microscope, scanning electron microscope and universal tensile testing machine. The results showed that the three-pipe nozzle with gas flow rate larger than 5 L/min could avoid oxidization, presenting better shielding effect in comparison with the single-pipe nozzle. Porosity formation could be suppressed with the gap between plate and skeleton less than 0.1 mm, while the existing porosity can be reduced with remelting. The maximum shear strength of stitch welding joint with minimal porosity was obtained by employing laser power of 1700 W, welding speed of 1.5 m/min and defocusing distance of ＋8 ram.

Microstructures and Toughness of Weld Metai of Ultrafine Grained Ferritic Steel by Laser Welding

3 mm thick 400 MPa grade ultrafine grained ferritic steel plates were bead-on-plate welded by CO2 laser with heat input of 120-480 J/mm. The microstructures of the weld metal mainly consist of bainite, which form is lower bainite plates or polygonal ferrite containing quantities of dispersed cementite particles, mixed with a few of low carbon martensite laths or ferrite, depending on the heat input. The hardness and the tensile strength of the weld metal are higher than those of the base metal, and monotonously increase as the heat input decreases. No softened zone exists in heat affected zone (HAZ). Compared with the base metal, although the grains of laser weld are much larger, the toughness of the weld metal is higher within a large range of heat input. Furthermore, as the heat input increases, the toughness of the weld metal rises to a maximum value, at which point the percentage of lower bainite is the highest, and then drops.

Laser-pulsed MIG hybrid welding technology of A6N01S aluminum alloy

Welding research of A6N01S-T5 aluminum alloy profile for high-speed train was done by using laser-MIG hybrid welding and MIG welding individually. And the weld appearance,welding distortion,mechanical properties of the joints and microstructures were analyzed. The test results demonstrated that high-efficient welding for the profile can be achieved by using laser-MIG hybrid welding,the speed of which can be over 3. 0 m/min. The processing had a good gap bridging ability,even if the gap of the butt joint was up to 2. 0 mm,a good weld appearance can also be got. While the hybrid welding speed was greater than 2. 5 m/min,the welding distortion of the laser-tandem MIG hybrid joints was just about 33% of that of the MIG joints,but the welding efficiency was over 3 times of MIG welding. And tensile strength of the hybrid joints was 85% of that of A6N01S-T5 base metal,9% higher than that of the MIG joints. Fatigue properties was tested individually with pulsed tensile fatigue method in the condition of 1 × 10~7 lifetime. The test results demonstrated that the fatigue strength of the joints was a little lower than that of base material,which could be up to 115 MPa. But the fatigue strength of hybrid welding joints was 107. 5 MPa,which was 23% higher than 87 MPa of MIG welding joints.

INVESTIGATION OF LASER BEAM WELDING PROCESS OF AZ61 MAGNESIUM-BASED ALLOY

Laser welling process of AZ61 magnesium alloys is investigated using a special CO2 laser experimental system. The effect of processing parameters including laser power, welling speed, and protection gas flow at the top and bottom is researched. The results show that an ideal well bead can be formed by choosing the processing parameters properly. An optimized parameter range is obtained by a large number of experiments. Among them, laser power and welling speed are the two main parameters that determine the well width and dimensions. The protect gas flow rate has a slight effect on the well width, but it directly effects the surface color of the well. The test results for typical welds indicate that the microhardness and tensile strength of the well zone are better than that of the base metal A fine-grained well region has been observed and no obvious heat-affected zone is found. The well zone mainly consists of small α-Mg phase, （α ＋ Al12Mg17）, and other eutectic phases. The small grains and the eutectic phases in the joint are believed to play an important role in the increase of the strength of wells for AZ61 magnesium alloys.

YAG laser welding with surface activating flux

YAG laser welding with surface activating flux has been investigated, and the influencing factors and mechanism are discussed. The results show that both surface activating flux and surface active element S have fantastic effects on the YAG laser weld shape, that is to obviously increase the weld penetration and D/W ratio in various welding conditions. The mechanism is thought to be the change of weld pool surface tension temperature coefficient, thus, the change of fluid flow pattern in weld pool due to the flux.

Study on the effect of welding current during laser beam-resistance seam welding of aluminum alloy 5052

The effect of welding current on the weld shape and tensile shear load during laser beam-resistance seam welding （LB-RSW） of aluminum alloy 5052 is studied. Experimental results show that the penetration depth, weld width ,tensile shear load and the ratio of penetration depth to weld width of LB-RSW are bigger than those of laser beam welding（ LBW） under the same conditions and the former three parameters increase as welding current rises. The weld shape of LB-RSW below 5 kA welding current is nearly the same as that of LBW. The weld morphology is protuberant under the condition of 5 kA welding current and 0. 8 m/min welding speed. Furthermore, the microstructure of the weld seam of LB-RSW is coarser than that of LBW.

Characteristic of laser-MIG hybrid welding with filling additional cold wire for aluminum alloy

The weld appearance, deposition rate, welding efficiency, stability of arc, laser keyhole characteristic, and weld property were studied by using a novel laser-MIG hybrid welding process with filling wire of aluminum alloy. The results were also compared with those by conventional laser-MIG hybrid welding process. It was found that with the suitable process parameters this novel welding process for aluminum alloy was stable and final weld bead had fine appearance. Compared to conventional laser-MIG hybrid welding process, during this novel welding process the stability of arc, the laser keyhole characteristic and the weld property were similar, while the keyhole cycle frequency and keyhole opening area had differences of 1.23% and 15.34%, respectively, and the welding efficiency increased by about 31% without increasing heat input.

Effect of filler wire on the joint properties of AZ31 magnesium alloys using CO_2 laser welding

Laser welding with filler wire of AZ31 magnesium alloys is investigated using a CO2 laser experimental system. The effect of three different filler wires on the joint properties is researched. The results show that the weld appearance can be effectively improved when using laser welding with filler wire. The microhardness and tensile strength of joints are almost the same us those of the base metal when ER AZ31 or ER AZ61 wire is adopted. However, when the filler wire of ER 5356 aluminum alloy is used, the mechanical properties of flints become worse. For ER AZ31 and ER AZ61 filler wires, the microstructure of weld zone slws small dendrite grains. In comparison, for ER 5356 filler wire, the weld shows a structure of snowy dendrites and many intermetallic compounds and eutectic phases distribute in the dendrites. These intermetallic constituents with low melting point increase the tendency of hot crack and result in fiagile joint properties. Therefore, ER AZ31 and ER AZ61 wire are more suitable filler material than ER 5356 for CO2 laser welding of AZ31 magnesium alloys.

Effects of activating flux on CO_2 laser welding process of 6013 Al alloy

In order to increase the absorption of laser energy and improve the weld appearance in laser welding of Al alloy, 1.8 mm- 6013 Al alloy plate was welded by activating flux CO2 laser welding. Activating flux includes oxide and fluoride, which was coated on the workpiece surface before welding. The experimental results show that the activating flux can effectively improve the absorption of CO2 laser energy and increase the amount of the molten base metal. The improvement on the absorption of laser energy by oxide activating flux is greater than that by fluoride activating flux or two-component activating flux, but the slag detachability made from both the single activating flux and two-activating flux is poor. The gas pore sensitivity with oxide activating flux is much higher than that with fluoride activating flux in CO2 laser welding of 6013 Al alloy.

Study of Dynamic Features of Surface Plasma in High-Power Disk Laser Welding

High-speed photography was used to obtain the dynamic changes in the surface plasma during a high-power disk laser welding process. A color space clustering algorithm to extract the edge information of the surface plasma region was developed in order to improve the accuracy of image processing. With a comparative analysis of the plasma features, i.e., area and height, and the characteristics of the welded seam, the relationship between the surface plasma and the stability of the laser welding process was characterized, which provides a basic understanding for the real-time monitoring of laser welding.

Supervised descent method for weld pool boundary extraction during fiber laser welding process

In order to obtain a high-quality weld during the laser welding process, extracting the characteristic parameters of weld pool is an important issue for automated welding. In this paper, the type 304 austenitic stainless steel is welded by a 5 kW high-power fiber laser and a high-speed camera is employed to capture the topside images of weld pools. Then we propose a robust visual-detection approach for the molten pool based on the supervised descent method. It provides an elegant framework for representing the outline of a weld pool and is especially efficient for weld pool detection in the presence of strong uncertainties and disturbances. Finally, welding experimental results verified that the proposed approach can extract the weld pool boundary accurately, which will lay a solid foundation for controlling the weld quality of fiber laser welding process.

Microstructure,properties and first principles calculation of titanium alloy/steel by Nd: YAG laser self-fluxing welding

The experiment of Nd： YAG pulsed laser self-fluxing welding for 304 stainless steel/Ti6Al4V titanium alloy dissimilar metal was carried out. The microstructure properties of welded joint were analyzed by SEM, EDS and XRD. The equilibrium lattice constants, enthalpies of formation, cohesive energies, mechanical properties, Debye temperatures and valence electron structures of Ti-Fe intermetallic compounds （IMCs） were calculated by the first principle pseudopotential plane wave method based on density functional theory （DFT）. According to the thermodynamic data of Ti-Fe-Cr compounds, the Gibbs free energy per mole of compound at different temperatures was calculated and their thermal stability was compared. The results show that there are no macroscopic cracks in the welded joints, and the IMCs distributed evenly along the welding interface exhibits 3 distinct layers of microstructure with different colors. The welds interface generates IMCs of TiFe, TiFe 2 and a small amount of Ti 5Cr 7Fe 17 IMCs. Ti-Fe IMCs with high thermodynamic stability and easy alloying formation. The results of Gibbs free energies show that the sequence of precipitates in the interface is Ti 5Cr 7Fe 17 , TiFe 2 and TiFe in high temperature during the metallurgical reaction. The G/B values of Ti-Fe IMCs are greater than the critical value of 0.5, indicating that it is an intrinsic brittleness.

Effects of laser beam welding parameters on mechanical properties and microstructure of AZ31B magnesium alloy

The effects of laser beam welding process parameters such as laser power,welding speed and focal position on mechanical properties and microstructure of AZ31B magnesium alloy were studied.Nine joints were fabricated using different levels of laser power,welding speed and focal position.Tensile properties of the welded joints were evaluated and correlated with the weld zone microstructure and hardness.It is found that the joints fabricated using a laser power of 2 500 W,welding speed of 5.5 m/min and focal position of-1.5 mm yield superior tensile properties compared with the other joints.The formation of very fine grains in weld region,higher fusion zone hardness and uniformly distributed finer precipitates are the main reasons for superior tensile properties of these joints.