Background: Anesthetists should measure the concentration of supplemental oxygen to determine whether patients’ partial pressure of arterial oxygen (PaO2) is correct during general anesthesia. However, the standard P...Background: Anesthetists should measure the concentration of supplemental oxygen to determine whether patients’ partial pressure of arterial oxygen (PaO2) is correct during general anesthesia. However, the standard PaO2 value in obese patients in the supine position is unknown. We evaluated the PaO2 with respect to the Broca-Katsura obesity index. Materials and Methods: From January 2001 to December 2013, we evaluated 472 patients aged ≥16 years old that underwent general anesthesia in the supine position. The anesthetic charts of 472 patients with an American Society of Anesthesiologists physical status of I or II were retrospectively reviewed to investigate the PaO2. Results: In patients aged 16 to 2 was 165.7 ± 25.6 mmHg at a Broca-Katsura index of 2 was 152.1 ± 23.8 mmHg at a Broca-Katsura index of 2 tended to decrease with age from 16 to 2 tended to decrease with age from 16 to <65 years at a Broca-Katsura index of 20% to <40%.展开更多
Objective:To explore the easily applicable indicators of practical value to evaluate the prognosis of acute respiratory distress syndrome（ARDS）.Methods:Blood and biochemical tests and bloodgas analyses were performe...Objective:To explore the easily applicable indicators of practical value to evaluate the prognosis of acute respiratory distress syndrome（ARDS）.Methods:Blood and biochemical tests and bloodgas analyses were performed upon entry into the ICUs,12 h,24 h,48 h and 72 h after that in 72 ARDS patients（who were admitted to the ICUs of our hospital from January 2000 to December 2009）.Then APACHEⅡscores were achieved by combining relevant physiological parameters and laboratory results.Results:There was a statistical difference between the death group and survival group at different time points upon entering the ICUs in terms of APACHEⅡscore, alveolar-arterial oxygen difference and arterial blood lactate clearance rate.PaO<sub>2</sub>/FiO<sub>2</sub> values were recorded to be statistically different between the death group and survival group 24 h,48 h and 72 h,respectively after entry into the ICUs.In addition,registered linear regression existed between APACHEⅡscore,alveolar-arterial oxygen difference or PaO<sub>2</sub>/FiO<sub>2</sub> value and time. APACHEⅡscore 24 h and 72 h after entering ICUs predicted mortality with an area under the ROC curve（AUC） standing respectively at 0.919 and 0.9SS.Arterial blood lactate clearance rate 12 h, 24 h,48 h and 72 h after entering ICUs predicted mortality with an area under the ROC curve （AUC） at 0.918,0.918,0.909 and 0.991,respectively.Conclusions:APACHEⅡscore applied in combination with arterial blood lactate clearance rate is of clinical significance in assessing the prognosis of ARDS patients.展开更多
Ti_(2)AlC,a MAX phase ceramic,has an attractive self-healing ability to restore performance via the oxidation-induced crack healing mechanism upon healing at high temperatures in air(high oxygen partial pressures).How...Ti_(2)AlC,a MAX phase ceramic,has an attractive self-healing ability to restore performance via the oxidation-induced crack healing mechanism upon healing at high temperatures in air(high oxygen partial pressures).However,such healing ability to repair damages in vacuum or low oxygen partial pressure conditions remains unknown.Here,we report on the self-healing behavior of Ti_(2)AlC at a low oxygen partial pressure of about 1 Pa.The experimental results showed that the strength recovery depends on both healing temperature and time.After healing at 1400℃for 1–4 h,the healed samples exhibited the recovered strengths even exceeding the original strength of 375 MPa.The maximum recovered strength of~422 MPa was achieved in the healed Ti_(2)AlC sample after healing at 1400 for 4 h,about 13%higher than the original strength.Damages were healed by the formed℃TiCx from the decomposition of Ti_(2)AlC.The decomposition-induced crack healing as a new mechanism in the low oxygen partial pressure condition was disclosed for the MAX ceramics.The present study illustrates that key components made of Ti_(2)AlC can prolong their service life and keep their reliability during use at high temperatures in low oxygen partial pressures.展开更多
A high temperature equilibration experiment was carried out to investigate the effect of oxygen partial pres- sure on the phase equilibria and liquidus in CaO-Al2O3- FeOx system with the intermediate oxygen partial pr...A high temperature equilibration experiment was carried out to investigate the effect of oxygen partial pres- sure on the phase equilibria and liquidus in CaO-Al2O3- FeOx system with the intermediate oxygen partial pressures of 10.13 Pa and 1.01 × 10^-3 Pa. The equilibrated phases and their compositions of the quenched samples were analyzed by using SEM/EPMA （Scanning Electron Microscope/Electron Probe Micro Analysis） and XRD （X Ray Diffraction）. The phase equilibrium results include two cases, the two phase coexistence and the three-phase coexistence in the high Al2O3 region with oxygen partial pressure of either 10.13 Pa or 1.01 × 10^-3 Pa. Effects of oxygen partial pressure and temperature on the liquidus along the primary phase fields of CaO · Al2O3 and CaO · 2Al2O3 were nota hle. With the decrease of oxygen partial pressure, the liquid area expands and the liquidus of CaO · Al2O3 and CaO · 2Al2O3 primary fields moves to the Al2O3-FeOx region. On the other hand, the liquid area of CaO Al2O3-FeOx sys tem extends extremely to the high Al2O3 region with the temperature increasing from 1 400 to 1 500℃, especially at lower oxygen partial pressure. The present experiment results are in good agreement with the calculated ones by FactSage.展开更多
A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock r...A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock resistance. The anti-oxidation properties under different oxygen partial pressures （OPP） and thermal shock resistance of the SZS coating were investigated. The results show that the SZS coated sample under low OPP, corresponding to the ambient air, during isothermal oxidation was 0.54% in mass gain after 111 h oxidation at 1500 ° C and less than 0.03% in mass loss after 50 h oxidation in high OPP, corresponding to the air flow rate of 36 L/h. Additionally, the residual compressive strengths （RCS） of the SZS coated samples after oxidation for 50 h in high OPP and 80 h in low OPP remain about 70% and 72.5% of those of original C/C samples, respectively. Moreover, the mass loss of SZS coated samples subjected to the thermal cycle from 1500 ° C in high OPP to boiling water for 30 times was merely 1.61%.展开更多
文摘Background: Anesthetists should measure the concentration of supplemental oxygen to determine whether patients’ partial pressure of arterial oxygen (PaO2) is correct during general anesthesia. However, the standard PaO2 value in obese patients in the supine position is unknown. We evaluated the PaO2 with respect to the Broca-Katsura obesity index. Materials and Methods: From January 2001 to December 2013, we evaluated 472 patients aged ≥16 years old that underwent general anesthesia in the supine position. The anesthetic charts of 472 patients with an American Society of Anesthesiologists physical status of I or II were retrospectively reviewed to investigate the PaO2. Results: In patients aged 16 to 2 was 165.7 ± 25.6 mmHg at a Broca-Katsura index of 2 was 152.1 ± 23.8 mmHg at a Broca-Katsura index of 2 tended to decrease with age from 16 to 2 tended to decrease with age from 16 to <65 years at a Broca-Katsura index of 20% to <40%.
基金sponsored by Guangdong Science and Technology Project(No:2009B03081118)
文摘Objective:To explore the easily applicable indicators of practical value to evaluate the prognosis of acute respiratory distress syndrome（ARDS）.Methods:Blood and biochemical tests and bloodgas analyses were performed upon entry into the ICUs,12 h,24 h,48 h and 72 h after that in 72 ARDS patients（who were admitted to the ICUs of our hospital from January 2000 to December 2009）.Then APACHEⅡscores were achieved by combining relevant physiological parameters and laboratory results.Results:There was a statistical difference between the death group and survival group at different time points upon entering the ICUs in terms of APACHEⅡscore, alveolar-arterial oxygen difference and arterial blood lactate clearance rate.PaO<sub>2</sub>/FiO<sub>2</sub> values were recorded to be statistically different between the death group and survival group 24 h,48 h and 72 h,respectively after entry into the ICUs.In addition,registered linear regression existed between APACHEⅡscore,alveolar-arterial oxygen difference or PaO<sub>2</sub>/FiO<sub>2</sub> value and time. APACHEⅡscore 24 h and 72 h after entering ICUs predicted mortality with an area under the ROC curve（AUC） standing respectively at 0.919 and 0.9SS.Arterial blood lactate clearance rate 12 h, 24 h,48 h and 72 h after entering ICUs predicted mortality with an area under the ROC curve （AUC） at 0.918,0.918,0.909 and 0.991,respectively.Conclusions:APACHEⅡscore applied in combination with arterial blood lactate clearance rate is of clinical significance in assessing the prognosis of ARDS patients.
基金supported by the National Natural Science Foundation of China(No.52275171)the PreResearch Program in National 14th Five-Year Plan(No.80923010304).
文摘Ti_(2)AlC,a MAX phase ceramic,has an attractive self-healing ability to restore performance via the oxidation-induced crack healing mechanism upon healing at high temperatures in air(high oxygen partial pressures).However,such healing ability to repair damages in vacuum or low oxygen partial pressure conditions remains unknown.Here,we report on the self-healing behavior of Ti_(2)AlC at a low oxygen partial pressure of about 1 Pa.The experimental results showed that the strength recovery depends on both healing temperature and time.After healing at 1400℃for 1–4 h,the healed samples exhibited the recovered strengths even exceeding the original strength of 375 MPa.The maximum recovered strength of~422 MPa was achieved in the healed Ti_(2)AlC sample after healing at 1400 for 4 h,about 13%higher than the original strength.Damages were healed by the formed℃TiCx from the decomposition of Ti_(2)AlC.The decomposition-induced crack healing as a new mechanism in the low oxygen partial pressure condition was disclosed for the MAX ceramics.The present study illustrates that key components made of Ti_(2)AlC can prolong their service life and keep their reliability during use at high temperatures in low oxygen partial pressures.
基金Item Sponsored by National Natural Science Foundation of China(50974034,51074039)
文摘A high temperature equilibration experiment was carried out to investigate the effect of oxygen partial pres- sure on the phase equilibria and liquidus in CaO-Al2O3- FeOx system with the intermediate oxygen partial pressures of 10.13 Pa and 1.01 × 10^-3 Pa. The equilibrated phases and their compositions of the quenched samples were analyzed by using SEM/EPMA （Scanning Electron Microscope/Electron Probe Micro Analysis） and XRD （X Ray Diffraction）. The phase equilibrium results include two cases, the two phase coexistence and the three-phase coexistence in the high Al2O3 region with oxygen partial pressure of either 10.13 Pa or 1.01 × 10^-3 Pa. Effects of oxygen partial pressure and temperature on the liquidus along the primary phase fields of CaO · Al2O3 and CaO · 2Al2O3 were nota hle. With the decrease of oxygen partial pressure, the liquid area expands and the liquidus of CaO · Al2O3 and CaO · 2Al2O3 primary fields moves to the Al2O3-FeOx region. On the other hand, the liquid area of CaO Al2O3-FeOx sys tem extends extremely to the high Al2O3 region with the temperature increasing from 1 400 to 1 500℃, especially at lower oxygen partial pressure. The present experiment results are in good agreement with the calculated ones by FactSage.
基金Project supported by the Nonferrous Metal Oriented Advanced Structural Materials and Manufacturing Cooperative Innovation Center,ChinaProject(51205417)supported by the National Natural Science Foundation of China
文摘A SiC/ZrSiO4？SiO2 （SZS） coating was successfully fabricated on the carbon/carbon （C/C） composites by pack cementation, slurry painting and sintering to improve the anti-oxidation property and thermal shock resistance. The anti-oxidation properties under different oxygen partial pressures （OPP） and thermal shock resistance of the SZS coating were investigated. The results show that the SZS coated sample under low OPP, corresponding to the ambient air, during isothermal oxidation was 0.54% in mass gain after 111 h oxidation at 1500 ° C and less than 0.03% in mass loss after 50 h oxidation in high OPP, corresponding to the air flow rate of 36 L/h. Additionally, the residual compressive strengths （RCS） of the SZS coated samples after oxidation for 50 h in high OPP and 80 h in low OPP remain about 70% and 72.5% of those of original C/C samples, respectively. Moreover, the mass loss of SZS coated samples subjected to the thermal cycle from 1500 ° C in high OPP to boiling water for 30 times was merely 1.61%.