Effects of Ce addition on microstructure, mechanical properties and corrosion resistance of as-cast AZ80 magnesium alloy

In this study, Ce was introduced into the AZ80 alloy and the effects of Ce addition on the microstructure, mechanical properties and corrosion resistance of the as-cast AZ80 magnesium alloy were investigated. The results show that the addition of Ce into the AZ80 alloy can not only refine the microstructure, but also result in the formation of the needle-like Al4Ce phase. These tiny Al4Ce phases are homogeneously distributed at grain boundaries and within grains. An appropriate Ce addition can also change the β-Mg17Al12 phase at the grain boundaries from continuous network to small island-like. At the same time, with the increase of Ce content from 0 to 2.0wt.%, the macro-hardness of the as-cast alloy is enhanced linearly, while impact toughness, tensile strength and elongation all firstly increase and then decrease. The AZ80 alloy containing 1.0wt.% Ce exhibits the optimal properties. Its macro-hardness, impact toughness, tensile strength and elongation are 61.90 HB, 15.50 J·cm-2, 171.80 MPa and 3.35%, increase by 9.95%, 63%, 13.3% and 36.7%, respectively compared with the base alloy. In addition, Ce can enhance the corrosion resistance of the AZ80 magnesium alloy.

The effects of deformation parameters and cooling rates on the aging behavior of AZ80+0.4%Ce

The extruded AZ80+0.4%Ce magnesium alloy was twisted in the temperature range of 300-380℃by using a Gleeble 3500 thermal simulation test machine with a torsion unit.The deformed cylindrical specimens were cooled at a cooling rate of 10℃/s or 0.1℃/s,respectively,and aged at 170℃.The microstructure analysis results showed that the grain size decreased with increasing specimen radial position from center(SRPC),and that the strong initial basal texture of the extruded magnesium alloy was weakened.Both continuous and discontinuous dynamic recrystallization mechanisms were involved in contributing to the grain refinement for all specimens investigated.And a novel extension twinning induced dynamic recrystallization mechanism was proposed for specimen deformed at 300℃.For the specimens deformed at 300℃and 340℃followed by a slow cooling rate(0.1℃/s),precipitates of various shapes(β-Mg_(17)Al_(12)),with the dominant precipitates being on the grains boundaries,appeared on the surface section.For specimen deformed at 380℃,lamellar precipitates(LPS)in the interiors of the grains were predominant.After aging,the LPS still dominated for specimens twisted at 380℃;however,the LPS gradually decreased with decreasing deformation temperatures from 380℃to 300℃.Dynamically precipitatedβ,especially those decorating the grain boundaries,changed the competition pictures for the LPS and precipitates of other shapes after aging.Interestingly,LPS dominated the areas for the center section of the specimens after aging regardless of deformation temperatures.Low temperature deformation with high SRPC followed by rapid cooling rate increased the micro hardness of the alloy after aging due to refined grain,reduced precipitates size,decreased lamellar spacing as well as strain hardening.