Kinetics of austenite growth and bainite transformation during reheating and cooling treatments of high strength microalloyed steel produced by sub-rapid solidification

First,strip cast samples of high strength microalloyed steel with sub-rapid solidification characteristics were prepared by simulated strip casting technique.Next,the isothermal growth of austenite grain during the reheating treatment of strip casts was observed in situ through confocal laser scanning microscope(CLSM).The results indicated that the time exponent of grains growth suddenly rise when the isothermal temperature higher than 1000℃.And the activation energy for austenite grain growth were calculated to be 538.0 kJ/mol in the high temperature region(above 1000℃)and 693.2 kJ/mol in the low temperature region(below 1000℃),respectively.Then,the kinetics model of austenite isothermal growth was established,which can predict the austenite grain size during isothermal hold very well.Besides,high density of second phase particles with small size was found during the isothermal hold at the low temperature region,leading to the refinement of austenite grain.After isothermal hold at different temperature for 1800 s,the bainite transformation in microalloyed steel strip was also observed in situ during the continuous cooling process.And growth rates of bainite plates with different nucleation positions and different prior austenite grain size(PAGS)were calculated.It was indicated that the growth rate of the bainite plate is not only related to the nucleation position but also to the PAGS.

Bainite Transformation Under Continuous Cooling of Nb-Microalloyed Low Carbon Steel

Utilizing Gleeble-1500 thermomechanical simulator, the influences of hot deformation parameters on continuous cooling bainite transformation in Nb-microalloyed low carbon steel were investigated. The results indicate that bainite starting temperature decreases with raising cooling rate and increases with increasing deformation temperature. Deformation has an accelerative effect on the bainite transformation when the specimens are deformed at 950 ℃. When the deformation temperature increases, the effect of deformation on bainite starting temperature is weakened. The amount of bainite is influenced by strain, cooling rate, and deformation temperature. When the specimens are deformed below 900 ℃, equiaxed ferrites are promoted and the bainite transformation is suppressed.

In situ measured growth rates of bainite plates in an Fe-C-Mn-Si superbainitic steel

The growth rates of bainite plates in an Fe-C-Mn-Si superbainitie steel were investigated by in situ observation. The lengthening rates of ferrite bainite during both cooling and isothermal holding processes were observed and the growth rates of bainite plates nucleating at grain boundaries, within grains and on preformed bainite were measured. It is indicated that the lengthening rates of bainite plates during the cooling and isothermal processes were different, and that the growth rates of bainite plates nucleating at different types of sites also demon- strated diversity. The bainite plates initiating at [vain boundaries during cooling grew the fastest, while the plates nucleating on preformed bainite did the slowest. However, the growth rate of the bainite plates nucleating at grain boundaries during isothermal transformation de- creased the most, whereas the bainite plates initiating within grains grew the fastest. In addition, the growth rate of ferrite bainite in the study supported the diffusion transformation mechanism of bainite from the viewooint of ~rowth rate.

Effects of Deformation on Bainite Transformation During Continuous Cooling of Low Carbon Steels

Hot deformation experiments were carried out on Gleeble 1500 thermo-mechanical simulator. The bainite transformation after deformation was investigated by optical microstructure analysis. The results indicated that the deformation accelerated the bainite transformation when the deformation was carried out at high temperature and no or little ferrite was precipitated before bainite transformation; when the deformation was carried out at low temperature, the deformation hindered the bainite transformation because a lot of ferrite precipitated before bainite transformation.

Kinetics of bainite-to-austenite transformation during continuous reheating in low carbon microalloyed steel

A dilatometer was used to study the kinetics of bainite-to-austenite transformation in low carbon microalloyed steel with the initial microstructure of bainite during the continuous reheating process. The bainite-to-austenite trans- formation was observed to take place in two steps at low heating rate. The first step is the dissolution of bainite, and the second one is the remaining bainite-to-austenite transformation controlled by a dissolution process. The calculation result of the kinetics of austenite formation shows that the two steps occur by diffusion at low heating rate. However, at high heating rate the bainite-to-austenite transformation occurs in a single step, and the process is mainly dominated by shear. The growth rate of austenite reaches the maximum at about 835℃ at different heating rates and the growth rate of austenite as a function of temperature increases with the increase in heating rate.

Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure

The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite （CFB/M） complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrasonic fatigue testing equipment at a frequency of 20 kHz. It is found that there is no horizontal part in the S-N curve and fatigue fracture occurs when the life of specimens exceeds 10^7 cycles. In addition, the origination of fatigue cracks tends to transfer from the surface to interior of specimens as the fatigue cycle exceeds 10^7, and the fatigue crack originations of many specimens are not induced by inclusions, but by some kind of ＂soft structure＂. It is shown that the studied high strength steel performs good ultra-high cycle fatigue properties. The ultra-high fatigue mechanism was discussed and it is suggested that specific CFB/M complex microstructure of the studied steel contributes to its superior properties.

Effect of Chromium on CCT Diagrams of Novel Air-Cooled Bainite Steels Analyzed by Neural Network

The quantitative effects of chromium content on continuous cooling transformation （CCT） diagrams of novel air-cooled bainite steels were analyzed using artificial neural network models. The results showed that the chromium may retard the high and medium-temperature martensite transformation.

Development of grain boundary allotriomorphic ferrite/granular bainite duplex steel

A new hot-rolled low alloy high strength steel with grain boundaryallotriomorphic ferrite/granular bainite duplex microstructure has been developed through novelmicrostructure and alloying designs without any noble metal elements such as nickel and molybdenum.Its as-rolled microstructure and mechanical properties, fatigue crack propagation behavior comparedwith single granular bainitic steel as well as continuous cooling transformation, were investigatedin detail. The measured result of CCT (continuous cooling transformation) curve shows that suchduplex microstructure can be easily obtained within a wide air-cooling rate range. More importantly,this duplex microstructure has much better combination of toughness and strength than the singlegranular bainite microstructure. It is found that the grain boundary allotriomorphic ferrite in thisduplex microstructure can blunt the microcrack tip, cause fatigue crack propagation route branchingand curving, and thus it increases the resistance to fatigue crack propagation, improves steeltoughness. The mechanical properties of the above commercial duplex steel plates have achieved orexceeded 870 MPa ultimate tensile strength, 570 MPa yield strength, 18 percent elongation and 34 JCharpy V-notch impact energy at -40 deg C, showing good development potential.

Influence of Holding Time After Deformation on Bainite Transformation in Niobium Microalloyed Steel

Using Gleeble-1500 system, the influence of holding time on bainite transformation in deformed niobium microalloyed steel during continuous cooling was analyzed, and the carbides in upper bainite were also systematically researched. The results show that the occurrence of the static recrystallization decreases the amount of bainite with an increase in the holding time and the emergence of retained austenite （RA） with the longer holding time. Two types of carbides were observed in upper bainite with regard to their precipitation sites. They either existed between the bainite ferrite laths or co-existed with RA. The formation mechanism of two kinds of carbides was analyzed by combining TEM micrographs with the model.

Effect of zirconium addition on the austenite grain coarsening behavior and mechanical properties of 900 MPa low carbon bainite steel

The ultra-fine bainitic microstructure of a 900 MPa low carbon bainitic Cu-Ni-Mo-B steel was obtained by a newly developed relaxation precipitation control （RPC） phase transformation processing. In a pan-cake like prior-austenite grain, the micro- structure consisted of lath bainite, a little of abnormal granular bainite, and acicular ferrite. The effect of zirconium carbonitrides on the austenite grain coarsening behavior was studied by transmission electron microscopy （TEM）. The results show that, the lath is narrower with increasing cooling rate. The ratio of all kinds of bainitic microstructure is proper with the intermediate cooling rate; and Zr-containing precipitates distribute uniformly, which restrains austenite grain growing in heat-affected welding zone.

EFFECT OF THE CONTROLLED ROLLING CONTROLLED COOLING ON STRENGTH AND DUCTILITY OF THE BAINITE MICRO ALLOYED ENGINEERING STEEL

The continuous cooling transformation of hot deformation austenite austenite of test steel and the effect of different processing schedules of controlled rolling and controlled cooling on the strength and ductility have been studied. The theory and the experiment base are presented for controlled rolling and controlled cooling of the SBL micro alloyed engineering steel.

EFFECT OF MICROSTRUCTURE ON CORROSION FATIGUE BEHAVIOUR OF A LOW CARBON BAINITE STEEL

The behaviour towards corrosion fatigue of low carbon bainite steel with various microstructures after tempered at different temperatures has been examined. The susceptibility of the steel to corrosion fatigue may be improved by tempering at 300℃.

Austenite－bainite Medium Mn Steel with Nodular Carbide Modified by La Compound

A new wear-resistant austenite-bainite medium Mn steel with nodular carbide can be obtained by modifying with La compound. The result shows that the equiaxed crystals are refined, and their quantity is increased after the treatment. The nodular carbide in fact is eutectic of austenite and (Fe . Mn)3 C is formed during solidification between austenitic dendrites. When the eutectic grows, the small melting pools between equiaxed crystals limit it's growing. Lanthanum species, are absorbed on eutectic growth interface, controlling eutectic growing.

FATIGUE PROPERTIES OF META-BAINITE IN STEEL 40CrMnSiMoVA

The microstructure,strength,toughness and fatigue properties of an ultra-high strength steel 40CrMnSiMoVA have been investigated.The so-called meta-bainite,composed of thin re- tained austenite films within or between the bainitic ferrite lathes was found in the steel after isothermally quenched at 300℃ for 1h.In comparison with the martensite structure obtained by isothermally quenching in martensite range,the meta-bainite has more excellent strength and plasticity,lower notch sensitivity,stronger strain harden ability,higher fatigue strength, longer strain or impact fatigue life,slower crack propagation rate and more remarkable overload effect on increasing fatigue life.

Effects of ausforming strain on bainite transformation in nanostructured bainite steel

The effects of ausforming strain on bainite transformation in high-carbon low-alloy nanobainite steel were investigated using a Gleeble 3500 thermomechanical simulator machine. The bainite transformation speed at 300°C was found to be accelerated by ausforming at 300, 600, and 700°C under applied strains ranging from 10% to 50% followed by isothermal transformation at 300°C. The ausformed bainite volume fraction varied with the ausforming strain because of the mechanical stabilization of the deformed austenite. Ausforming at low temperatures not only enhanced the bainite ferrite volume fraction but also refined the microstructure substantially. Although the amount of bainite ferrite might have been reduced with increasing strain, the microstructures were refined by ausforming. © 2017, University of Science and Technology Beijing and Springer-Verlag Berlin Heidelberg.

MECHANICAL PROPERTIES IN AN INTERCRITICALLY HEAT-TREATED BAINITE-TRANSFORMED 2%Si STEEL

A significant amount of austenite can be retained by rapid cooling following intercritical annealing and holding at the bainite transformation range in steel with comparatively low carbon and silicon contents. Retained austenite is blocky and very fine and moderately stabilized due to C enrichment. The elongation and the strength-ductility balance of the steel can be enhanced considerably due to strain-induced martensite transformation and transformation-induced plasticity (TRIP) of retained austenite.

TRANSFORMATION OF UPPER BAINITE IN 55SiMnMo STEEL DURING TEMPERING

The transformation of upper bainite of normalized 55SiMnMo steel during tempering has been studied by optical microscopy,X-ray diffraction,transmission electron microscopy and differential scanning calorimetry.Ferrite plate surface is parallel to ferrite{110}and is the coherent interface for α and γ,the crystallographic relationship is(111)_γ,∥(011)_α.The small plate surface of Fe_3C precipitated during tempering is parallel to(100).The strengthening mechanism for carbon-rich austenite in normalized condition is primarily uniform solid so- lution hardening,however,in the tempered state,it is strengthened chiefly by non-uniform one.

Heterogeneous Nuclei of Intergrowth Eutectic in Austenite-Bainite Steel Modified by Ce and Al

The nodular eutectic in the austenite bainite steel is pseudo eutectic of austenite and (Fe,Mn) 3C, which is formed between austenite dendrites at the end of the solidification because of the segregation of C and Mn. By thermodynamics calculation, two dimensional lattice misfitting calculation and observations of transmission electron microscope(TEM) and scanning electron microscope(SEM), it is shown that CeO 2 and CeAlO 3 may act as the heterogeneous nuclei of the nodular eutectic.

SECONDARY HARDENING OF BAINITE IN HIGH SPEED STEEL

The mechanical properties and structure of bainite and martensite after tempering m 6-5-4-2 high speed steel have been investigated.It was found that the secondary hardening effect and resistance to heat softening as well as impact toughness are higher in the bainite than in the martensite.TEM observations show that the(Fe,M)_3C precipitated in the martensite after tempering at temperature near the peak of hardness-tempering temperature curve.However, no(Fe,M)_3C but the dispersive MC and M_2C precipitated in the ferrite and austenite of bainite after tempering at the same temperature.This indicates that the diffusion of alloy ele- ments forming carbide might exist during the process of bainite growing.

Interaction of Hydrogen and Retained Austenite in Bainite/Martensite Dual-Phase High Strength Steel

The hydrogen trapping phenomena in two bainite/martensite dual-phase high strength steels(U20Si and U20DSi)were investigated by electrochemical permeation technique.The hydrogen diffusivity was calculated from data of permeation delay time,and the diffusion coefficient in U20 Si is far less than that in U20 DSi.Moreover,the hydrogen diffusivity decreases as the volume percent of retained austenite increases.The experiment results show that there are different hydrogen trappings and different volume percents of retained austenite in U20 Si and U20 DSi.The retained austenite is precipitated as films.The trap binding energy for the retained austenite and hydrogen is calculated to be 40.4kJ·mol-1.