Lightweight and energy saving autoclaved aerated concrete(AAC) acting as a newbuilding material were prepared by using magnetite tailings from iron ore as main rawmaterials,and the purpose of comprehensive utilization...Lightweight and energy saving autoclaved aerated concrete(AAC) acting as a newbuilding material were prepared by using magnetite tailings from iron ore as main rawmaterials,and the purpose of comprehensive utilization of tailings resources was to improve their utilization efficiency.The effects of curing system on AAC product performance were discussed.The autoclave curing reaction kinetics was studied as well as the generated amount of hydration product trends over autoclave curing temperature and time were analyzed.The results indicated that the properties of AAC was in accordance with Chinese national standard the A3.5 B06 class of GB/T11968-2006 by prepared from magnetite tailing as the main rawmaterials.Meanwhile,autoclave curing process was controlled by the diffusion velocity through the products ' layers of reactants,and the apparent activation energy of autoclave curing process was 19.269 k J/mol.Compressive strength of aerated concrete is improved by mutual cementation between the appropriate amount of calcium silicate hydrate and tobermorite crystal.展开更多
This work aims at designing a set of curing pressure routes to produce laminates with various void contents. The effects of various consolidation pressures resulting in different void contents on mechanical strength o...This work aims at designing a set of curing pressure routes to produce laminates with various void contents. The effects of various consolidation pressures resulting in different void contents on mechanical strength of carbon/epoxy laminates have been examined. Characterization of the voids, in terms of void volume fraction, void distribution, size, and shape, was performed by standard test, ultrasonic inspection and metallographic analysis. The interlaminar shear strength was measured by the short-beam method. An empirical model was used to predict the strength vs porosity. The predicted strengths conform well with the experimental data and voids were found to be uniformly distributed throughout the laminate.展开更多
With the aid of the latest fiber optic sensing technology parameters in the cure process of ther- mosetting resin-matrix composite, such as temperature, viscosity,void and residual stress, can be monitored entirely an...With the aid of the latest fiber optic sensing technology parameters in the cure process of ther- mosetting resin-matrix composite, such as temperature, viscosity,void and residual stress, can be monitored entirely and efficiently.In this paper, experiment results of viscosity measurement in composite cure process in autoclave using fiber optic sensors are presented. Based on the sensed information, a computer program is utilized to control the cure process. With this technology, the cure process becomes more apparent and controllable, which will greatly improve the cured products and reduce the cost.展开更多
基金National 12th Five-Year Science and Technology Planning Project,China(No.2013BAB03B03)
文摘Lightweight and energy saving autoclaved aerated concrete(AAC) acting as a newbuilding material were prepared by using magnetite tailings from iron ore as main rawmaterials,and the purpose of comprehensive utilization of tailings resources was to improve their utilization efficiency.The effects of curing system on AAC product performance were discussed.The autoclave curing reaction kinetics was studied as well as the generated amount of hydration product trends over autoclave curing temperature and time were analyzed.The results indicated that the properties of AAC was in accordance with Chinese national standard the A3.5 B06 class of GB/T11968-2006 by prepared from magnetite tailing as the main rawmaterials.Meanwhile,autoclave curing process was controlled by the diffusion velocity through the products ' layers of reactants,and the apparent activation energy of autoclave curing process was 19.269 k J/mol.Compressive strength of aerated concrete is improved by mutual cementation between the appropriate amount of calcium silicate hydrate and tobermorite crystal.
文摘This work aims at designing a set of curing pressure routes to produce laminates with various void contents. The effects of various consolidation pressures resulting in different void contents on mechanical strength of carbon/epoxy laminates have been examined. Characterization of the voids, in terms of void volume fraction, void distribution, size, and shape, was performed by standard test, ultrasonic inspection and metallographic analysis. The interlaminar shear strength was measured by the short-beam method. An empirical model was used to predict the strength vs porosity. The predicted strengths conform well with the experimental data and voids were found to be uniformly distributed throughout the laminate.
文摘With the aid of the latest fiber optic sensing technology parameters in the cure process of ther- mosetting resin-matrix composite, such as temperature, viscosity,void and residual stress, can be monitored entirely and efficiently.In this paper, experiment results of viscosity measurement in composite cure process in autoclave using fiber optic sensors are presented. Based on the sensed information, a computer program is utilized to control the cure process. With this technology, the cure process becomes more apparent and controllable, which will greatly improve the cured products and reduce the cost.