(1-x)CoTiNb2O8-x ZnNb2O6 microwave dielectric ceramics were prepared via the conventional solid-state reaction route with the aim of reducing thetf value and improving the thermal stability.The phase composition and t...(1-x)CoTiNb2O8-x ZnNb2O6 microwave dielectric ceramics were prepared via the conventional solid-state reaction route with the aim of reducing thetf value and improving the thermal stability.The phase composition and the microstructure were investigated using X-ray diffraction,Raman spectra,and scanning electron microscopy.A set of phase transitions which were induced by composition had been confirmed via the sequence:rutile structure→coexistence of rutile and columbite phase→columbite phase.For(1-x)CoTiNb2O8-x ZnNb2O6 microwave dielectric ceramics,the addition of ZnNb2O6 content(x=0–1)led to the decrease ofer from 62.98 to 23.94.As a result of the high Q×?of ZnNb2O6 ceramics,the increase of ZnNb2O6 content also led to the lower sintering temperatures and the higher Q×?values.Thetf value was reduced from+108.04(x=0)to–49.31 ppm/℃(x=1).Among them,high density 0.5CoTiNb2O8-0.5ZnNb2O6 ceramics were obtained at 1175℃with excellent microwave dielectric properties of εr 39.2,Q×? 40013 GHz,and tf+3.57 ppm/℃.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 51772022)
文摘(1-x)CoTiNb2O8-x ZnNb2O6 microwave dielectric ceramics were prepared via the conventional solid-state reaction route with the aim of reducing thetf value and improving the thermal stability.The phase composition and the microstructure were investigated using X-ray diffraction,Raman spectra,and scanning electron microscopy.A set of phase transitions which were induced by composition had been confirmed via the sequence:rutile structure→coexistence of rutile and columbite phase→columbite phase.For(1-x)CoTiNb2O8-x ZnNb2O6 microwave dielectric ceramics,the addition of ZnNb2O6 content(x=0–1)led to the decrease ofer from 62.98 to 23.94.As a result of the high Q×?of ZnNb2O6 ceramics,the increase of ZnNb2O6 content also led to the lower sintering temperatures and the higher Q×?values.Thetf value was reduced from+108.04(x=0)to–49.31 ppm/℃(x=1).Among them,high density 0.5CoTiNb2O8-0.5ZnNb2O6 ceramics were obtained at 1175℃with excellent microwave dielectric properties of εr 39.2,Q×? 40013 GHz,and tf+3.57 ppm/℃.