The coarse pore system, interfacial transition zone （ITZ） between aggregate and paste matrix and volume fraction of unhydrated cement in concrete （w/c=0.3） containing mineral admixtures were quantitatively charact...The coarse pore system, interfacial transition zone （ITZ） between aggregate and paste matrix and volume fraction of unhydrated cement in concrete （w/c=0.3） containing mineral admixtures were quantitatively characterized by the scanning electron microscope-backscattered electron （SEM-BSE） image analysis technique. The experimental results show that compound addition of slag and fly ash decreases the coarse porosity from 10.17% to 3.74% and the threshold diameter of coarse pore size from 345 μm to 105 μm compared with concrete （w/c=0.30） without mineral admixtures; Moreover with compound addition of fly ash and slag, the volume proportion of unhydrated cement in paste matrix is reduced by 30%, the maximum amount of coarse pores in the ITZ between aggregate and paste decreases from 13.11% to 5.57% and the thickness of ITZ is reduced by 37% , compared with concrete without mineral admixtures.展开更多
The Ni samples were electroformed from additive-free(AF) and saccharin-containing(SC) sulfamate solutions, respectively. In situ backscattered electron(BSE) imaging, electron backscatter diffraction(EBSD), and electro...The Ni samples were electroformed from additive-free(AF) and saccharin-containing(SC) sulfamate solutions, respectively. In situ backscattered electron(BSE) imaging, electron backscatter diffraction(EBSD), and electron-probe microanalysis(EPMA) were used to investigate the effect of annealing on the deformation behaviors of the AF and SC samples. The results indicate that columnar grains of the as-deposited AF sample had an approximated average width of 3 μm and an approximated aspect ratio of 8. The average width of columnar grains of the as-deposited SC sample was reduced to approximately 400 nm by the addition of saccharin to the electrolyte. A few very-large grains distributed in the matrix of the SC sample after annealing. No direct evidence indicated that S segregated at the grain boundaries before or after annealing. The average value of the total elongations of the SC samples decreased from 16% to 6% after annealing, whereas that of the AF samples increased from 18% to 50%. The dislocation recovery in grain-boundary areas of the annealed AF sample was reduced, which contributed to the appearance of microvoids at the triple junctions. The incompatibility deformation between very-large grains and fine grains contributed to the brittle fracture behavior of the annealed SC Ni.展开更多
文摘The coarse pore system, interfacial transition zone （ITZ） between aggregate and paste matrix and volume fraction of unhydrated cement in concrete （w/c=0.3） containing mineral admixtures were quantitatively characterized by the scanning electron microscope-backscattered electron （SEM-BSE） image analysis technique. The experimental results show that compound addition of slag and fly ash decreases the coarse porosity from 10.17% to 3.74% and the threshold diameter of coarse pore size from 345 μm to 105 μm compared with concrete （w/c=0.30） without mineral admixtures; Moreover with compound addition of fly ash and slag, the volume proportion of unhydrated cement in paste matrix is reduced by 30%, the maximum amount of coarse pores in the ITZ between aggregate and paste decreases from 13.11% to 5.57% and the thickness of ITZ is reduced by 37% , compared with concrete without mineral admixtures.
基金financially supported by the China Scholarship Council(No.201606460015)the support of the H.Nakano laboratory of Kyushu University for the study
文摘The Ni samples were electroformed from additive-free(AF) and saccharin-containing(SC) sulfamate solutions, respectively. In situ backscattered electron(BSE) imaging, electron backscatter diffraction(EBSD), and electron-probe microanalysis(EPMA) were used to investigate the effect of annealing on the deformation behaviors of the AF and SC samples. The results indicate that columnar grains of the as-deposited AF sample had an approximated average width of 3 μm and an approximated aspect ratio of 8. The average width of columnar grains of the as-deposited SC sample was reduced to approximately 400 nm by the addition of saccharin to the electrolyte. A few very-large grains distributed in the matrix of the SC sample after annealing. No direct evidence indicated that S segregated at the grain boundaries before or after annealing. The average value of the total elongations of the SC samples decreased from 16% to 6% after annealing, whereas that of the AF samples increased from 18% to 50%. The dislocation recovery in grain-boundary areas of the annealed AF sample was reduced, which contributed to the appearance of microvoids at the triple junctions. The incompatibility deformation between very-large grains and fine grains contributed to the brittle fracture behavior of the annealed SC Ni.