Sodium beta alumina（Na-β-alumina） films were synthesized by heat treatment of NaAl6O（9.5）and γ-NaA1O2 films at temperatures of 1 373-1 573 K.Single-phase γ-NaA1O2 and NaAl6O（9.5） films were prepared by laser ...Sodium beta alumina（Na-β-alumina） films were synthesized by heat treatment of NaAl6O（9.5）and γ-NaA1O2 films at temperatures of 1 373-1 573 K.Single-phase γ-NaA1O2 and NaAl6O（9.5） films were prepared by laser chemical vapor deposition at the deposition temperatures of 976 and 1 100 K,respectively.Subsequent heat treatment of the films resulted in the formation of Na-β-alumina with α-Al2O3 at temperatures above 1 373 K for NaAl6O（9.5） and 1 473 K for γ-NaA1O2.On heat treatment at temperatures of 1 473-1 573 K,the faceted morphology with terraces of the as-deposited（110）-oriented γ-NaAlO2 films transformed to a porous morphology with platelet grains comprising Na-β-alumina and α-Al2O3.On heat treatment at temperatures of1 373-1 473 K,the pyramidal,faceted grains of as-deposited NaAl6O（9.5） films transformed to planer,shapeanisotropic morphology in the film of mixed Na-β-alumina and α-Al2O3.A dense morphology was observed in both the as-deposited and heat-treated NaAl6O（9.5） films.展开更多
基金Funded by the Ministry of Education,Culture,Sports,Science and Technology,a Grant-in-Aid for Challenging Exploratory Research(No.26560235)the ARCMG–IMR Cooperative Program(No.14G0402)of Tohoku Universitythe China Scholarship Council and the 111 Project(No.B13035)of China
文摘Sodium beta alumina（Na-β-alumina） films were synthesized by heat treatment of NaAl6O（9.5）and γ-NaA1O2 films at temperatures of 1 373-1 573 K.Single-phase γ-NaA1O2 and NaAl6O（9.5） films were prepared by laser chemical vapor deposition at the deposition temperatures of 976 and 1 100 K,respectively.Subsequent heat treatment of the films resulted in the formation of Na-β-alumina with α-Al2O3 at temperatures above 1 373 K for NaAl6O（9.5） and 1 473 K for γ-NaA1O2.On heat treatment at temperatures of 1 473-1 573 K,the faceted morphology with terraces of the as-deposited（110）-oriented γ-NaAlO2 films transformed to a porous morphology with platelet grains comprising Na-β-alumina and α-Al2O3.On heat treatment at temperatures of1 373-1 473 K,the pyramidal,faceted grains of as-deposited NaAl6O（9.5） films transformed to planer,shapeanisotropic morphology in the film of mixed Na-β-alumina and α-Al2O3.A dense morphology was observed in both the as-deposited and heat-treated NaAl6O（9.5） films.