A composite biomass insulation material,which uses geopolymers as adhesives and forestry waste as fillers,was proposed and experimentally tested.The orthogonal experimental method was adopted to analyze the optimum th...A composite biomass insulation material,which uses geopolymers as adhesives and forestry waste as fillers,was proposed and experimentally tested.The orthogonal experimental method was adopted to analyze the optimum theoretical oxide molar ratios and the mass ratio of mixing water to binder(m_(w2)/m__(B))for preparing geopolymers.The influences of curing regimes(including one-stage and two-stage curing methods)and m_(w2)/m_(B) ratios of the insulation materials on mechanical,thermal,and hydraulic performances were also studied by experiment.The results indicated that the optimum combination scheme of preparing geopolymers was molar ratio x_(SiO_(2))/x_(Na_(2)O)=3.3,x_(SiO_(2))/x_(Al_(2)O_(3))=3.2 and m_(w2)/m_(B)=0.5 with the highest mechanical strength of 34.21 MPa.Besides,the best curing conditions of the composite material were the curing temperatures of 85°C and 70°C under the two-stage curing regime,which could achieve the low heat conductivity of 0.123 and 0.125 W/(m·K),and the high mechanical strength of 1.70 MPa and 1.71 MPa,respectively.The optimum m_(w2)/m_(B)ratios of the biomass material were 0.5 to 0.55 with heat conductivity of 0.114 to 0.125 W/(m·K).This novel composite insulation material has satisfying physical performances,which is helpful for achieving building energy conservation.展开更多
The chemical characteristics,element contents,mineral compositions,and the ameliorative effects on acid soils of five biomass ashes from different materials were analyzed. The chemical properties of the ashes varied d...The chemical characteristics,element contents,mineral compositions,and the ameliorative effects on acid soils of five biomass ashes from different materials were analyzed. The chemical properties of the ashes varied depending on the source biomass material. An increase in the concrete shuttering contents in the biomass materials led to higher alkalinity,and higher Ca and Mg levels in biomass ashes,which made them particularly good at ameliorating effects on soil acidity. However,heavy metal contents,such as Cr,Cu,and Zn in the ashes,were relatively high. The incorporation of all ashes increased soil p H,exchangeable base cations,and available phosphorus,but decreased soil exchangeable acidity. The application of the ashes from biomass materials with a high concrete shuttering content increased the soil available heavy metal contents. Therefore,the biomass ashes from wood and crop residues with low concrete contents were the better acid soil amendments.展开更多
基金funded by the Science and Technology Bureau of Changsha,China(No.kh1902239)National Natural Science Foundations of China(No.52076070No.52008166)。
文摘A composite biomass insulation material,which uses geopolymers as adhesives and forestry waste as fillers,was proposed and experimentally tested.The orthogonal experimental method was adopted to analyze the optimum theoretical oxide molar ratios and the mass ratio of mixing water to binder(m_(w2)/m__(B))for preparing geopolymers.The influences of curing regimes(including one-stage and two-stage curing methods)and m_(w2)/m_(B) ratios of the insulation materials on mechanical,thermal,and hydraulic performances were also studied by experiment.The results indicated that the optimum combination scheme of preparing geopolymers was molar ratio x_(SiO_(2))/x_(Na_(2)O)=3.3,x_(SiO_(2))/x_(Al_(2)O_(3))=3.2 and m_(w2)/m_(B)=0.5 with the highest mechanical strength of 34.21 MPa.Besides,the best curing conditions of the composite material were the curing temperatures of 85°C and 70°C under the two-stage curing regime,which could achieve the low heat conductivity of 0.123 and 0.125 W/(m·K),and the high mechanical strength of 1.70 MPa and 1.71 MPa,respectively.The optimum m_(w2)/m_(B)ratios of the biomass material were 0.5 to 0.55 with heat conductivity of 0.114 to 0.125 W/(m·K).This novel composite insulation material has satisfying physical performances,which is helpful for achieving building energy conservation.
基金supported by the National Key Basic Research Program of China(No.2014CB441003)the National Key Research and Development of China(No.2016YFD0200302)
文摘The chemical characteristics,element contents,mineral compositions,and the ameliorative effects on acid soils of five biomass ashes from different materials were analyzed. The chemical properties of the ashes varied depending on the source biomass material. An increase in the concrete shuttering contents in the biomass materials led to higher alkalinity,and higher Ca and Mg levels in biomass ashes,which made them particularly good at ameliorating effects on soil acidity. However,heavy metal contents,such as Cr,Cu,and Zn in the ashes,were relatively high. The incorporation of all ashes increased soil p H,exchangeable base cations,and available phosphorus,but decreased soil exchangeable acidity. The application of the ashes from biomass materials with a high concrete shuttering content increased the soil available heavy metal contents. Therefore,the biomass ashes from wood and crop residues with low concrete contents were the better acid soil amendments.