In order to gain a sufficient wear resistance for applications, the biomimetic non-smooth units in concave were fabricated on the surfaces of 20CrMnTi steel using a biomimetic laser remelting technology. The diameter ...In order to gain a sufficient wear resistance for applications, the biomimetic non-smooth units in concave were fabricated on the surfaces of 20CrMnTi steel using a biomimetic laser remelting technology. The diameter and distribution of the concaves were optimized using orthogonal experiment. The microstructures of the biomimetic non-smooth units were examined. The anti-wear behaviors were investigated by the rolling wear test with lubricant. The results of wear tests indicated that the biomimetic surfaces exhibit a higher anti-wear ability than the smooth surfaces. The biomimetic surface with concaves of 250 μm in diameter and transverse distance of 270 μm and longitudinal distance of 400 μm exhibits the best anti-wear property. The enhancement of wear resistance can be mainly attributed to the action of biomimetic non-smooth units and the super fined microstructure and hardness in the biomimetic unit zones.展开更多
基金supported by the National Nature Science Foundation of China (Grant No 50635030)the Key Scientific and Technological Project of Jilin Province (Grant No 09ZDGG001)
文摘In order to gain a sufficient wear resistance for applications, the biomimetic non-smooth units in concave were fabricated on the surfaces of 20CrMnTi steel using a biomimetic laser remelting technology. The diameter and distribution of the concaves were optimized using orthogonal experiment. The microstructures of the biomimetic non-smooth units were examined. The anti-wear behaviors were investigated by the rolling wear test with lubricant. The results of wear tests indicated that the biomimetic surfaces exhibit a higher anti-wear ability than the smooth surfaces. The biomimetic surface with concaves of 250 μm in diameter and transverse distance of 270 μm and longitudinal distance of 400 μm exhibits the best anti-wear property. The enhancement of wear resistance can be mainly attributed to the action of biomimetic non-smooth units and the super fined microstructure and hardness in the biomimetic unit zones.