Synthesis,Characterization of NaA Zeolite from Blast Furnace Slag(BFS)via Alkaline Fusion and Hydrothermal Treatment

A blast furnace slag zeolite(BFSZ)material was successfully synthesized from BFS by alkaline fusion and hydrothermal treatment.Via the analyses of XRD,FT-IR,FE-SEM,XRF,CEC and BET surface area measurement,when zeolite was synthesized at a crystallization temperature of 100℃with initial Si/Al ratio of 1:1,the main composition in the product is Na-A zeolite.Under the above conditions,the BFSZ was synthesized with CEC of 3.06 meq/g and maximum BET surface area of 37.55 m^(2)·g^(-1).Moreover,the incorporating of BFS-derived minor metals(such as Mg,Fe,and Ca)are found to be of little importance for the synthesis of BFSZ.Thus the obtained BFSZ material has a great adsorption performance for removing Mn^(2+),Cu^(2+),and NH_(4)^(+)ions diluted in water,owing to the higher CEC.

Extraction of Valuable Metals from Titanium-bearing Blast Furnace Slag by Acid Leaching

To realize the resource utilization of the valuable metals in the titanium-containing blast furnace slag,the process route of “hydrochloric acid leaching-electrolysis-carbonization and carbon dioxide capture-preparation of calcium carbonate” was proposed.In this study,the influences of process conditions on the leaching rates of calcium,magnesium,aluminum,and iron and the phases of the leaching residue were investigated for the leaching process.The experimental results show that the HCl solution could selectively leach the elements from the titanium-containing blast furnace slag.The better leaching conditions are the HCl solution concentration of 4 mol/L,the leaching time of 30 min,the ratio of liquid volume to solid gas of 10 mL/g,and the stirring paddle speed of 300 r/min.Under the conditions,the leaching rates of calcium,magnesium,aluminum,and iron can reach 85.87%,73.41%,81.35%,and 59.08%,and the leaching rate of titanium is 10.71%.The iron and the aluminum are removed from the leachate to obtain iron-aluminum water purification agents,and the magnesium is removed from the leachate to obtain magnesium hydroxide.The leaching residue phase is dominated by perovskite,followed by magnesium silicate and tricalcium aluminate,and the titaniumrich material could be obtained from the leaching residue by desiliconization.

Analysis and Prospect of Waste Heat Utilization from Blast Furnace Slag Flushing

Estimating the residual heat of blast furnace slag flushing in China,classifying and introducing the current proposed methods of slag flushing waste heat utilization,and listing existing cases.In order to better save energy and water in the slag flushing process of blast furnaces,an ideal comprehensive cascade utilization system scheme for annual recovery of waste heat is proposed.Based on the measured waste heat data of a steel plant,design calculations are carried out to further analyze the economic feasibility of the new scheme and provide reference for its promotion and application.

A Novel Sensing Imaging Equipment Under Extremely Dim Light for Blast Furnace Burden Surface:Starlight High-Temperature Industrial Endoscope

Blast furnace(BF)burden surface contains the most abundant,intuitive and credible smelting information and acquiring high-definition and high-brightness optical images of which is essential to realize precise material charging control,optimize gas flow distribution and improve ironmaking efficiency.It has been challengeable to obtain high-quality optical burden surface images under high-temperature,high-dust,and extremelydim(less than 0.001 Lux)environment.Based on a novel endoscopic sensing detection idea,a reverse telephoto structure starlight imaging system with large field of view and large aperture is designed.Combined with a water-air dual cooling intelligent self-maintenance protection device and the imaging system,a starlight high-temperature industrial endoscope is developed to obtain clear optical burden surface images stably under the harsh environment.Based on an endoscope imaging area model,a material flow trajectory model and a gas-dust coupling distribution model,an optimal installation position and posture configuration method for the endoscope is proposed,which maximizes the effective imaging area and ensures large-area,safe and stable imaging of the device in a confined space.Industrial experiments and applications indicate that the proposed method obtains clear and reliable large-area optical burden surface images and reveals new BF conditions,providing key data support for green iron smelting.

Durability of Seawater Mixed Concrete with Different Replacement Ratio of BFS （Blast Furnace Slag） and FA （Fly Ash）

Using seawater in concrete can be considered as one of the sustainable approaches in construction industry not only to save the freshwater resource but also to promote the use of abandoned seawater resource, especially in the construction at the uninhabited area close to the sea where the procurement of fresh water is difficult. In this study, durability against chloride attack of seawater mixed concrete with different replacement ratio of BFS （blast furnace slag） and FA （fly ash） is discussed and the life time until the occurrence of corrosion crack is evaluated. The results show that： （1） Chloride penetration rate of seawater mixed specimens with BFS and FA is lower than that of freshwater mixed OPC （ordinary Portland cement） specimens; （2） Oxygen permeability of seawater mixed specimens with BFS and FA is almost the same or lower than that of freshwater mixed OPC specimens; （3） Total life time （corrosion incubation period and propagation period） of seawater mixed specimens with BFS and FA is almost the same or only slightly shorter than that of freshwater mixed OPC specimens. From the results, it was confirmed that the usage of seawater in concrete mixing is feasible in concrete with the appropriate BFS and FA replacement ratio.

Efficient Use of Steel Slag in Alkali-Activated Blast Furnace Slag Based Geopolymer

Energy shortage and the emission of greenhouse gases have become a global problem of urgent concern.Therefore,there is an urgent need to develop a low carbon building material.Geopolymers have become a hot topic due to their environmental sustainability and the feasibility of immobilizing industrial waste.In this paper,steel slag(SS)fines were investigated as auxiliary materials of blast furnace slag(BFS)based geopolymer.The hydration heat properties,flowability,compressive strength,sorptivity coefficient,X-ray diffraction(XRD),and scanning electron microscopy(SEM)of the geopolymer pastes were determined.The results showed that the incorporation of SS weakened the reactivity of the BFS-based geopolymer paste and improved the flow values of the paste.The compressive strength of the geopolymer with 20%SS content reached 117 MPa at 28 d.The geopolymer specimens with high compressive strength showed a low sorptivity coefficient.The microscopic results showed that the addition of the appropriate amount of SS reduced the cracks,improved the density of the geopolymer,and produced a geopolymer composite with excellent mechanical properties.

Effect of Blast Furnace Sludge (BFS) Characteristics on Suitable Recycling Process Determining

The present study aims to give a detailed characterization of blast furnace sludge (BFS) by using different techniques, in order to determine the most effective recycling method to recover valuable metals from this waste. BFS is composed mainly of hematite, as its iron-bearing phase, and carbon, in addition to fractions of silicate and carbonate materials. The studied BFS shows relatively high contents of iron (Fe) (390 g.kg-1), and carbon (C) (290 g.kg-1), due to abundance of hematite and coke, while the concentration of zinc (Zn) (2.5 g.kg-1) is low. The XRD analyses indicated that, hematite is more concentrated in the fine fraction (<20 μm), while the coarser fraction (90 - 250 μm) is dominated by calcite, quartz and X-ray amorphous coke. SEM-EDX analyses confirmed that particles rich in iron and zinc were detected in the fine fraction (<20 μm) of the sludge. Due to high Fe and C content in BFS, it can be utilized as self-reducing material and briquetting represent a potential method for recycling of blast furnace sludge.

Preparation of UV-visible light responsive photocatalyst from titania-bearing blast furnace slag modified with(NH_4)_2SO_4

Sulfate-modified titanium dioxide-bearing blast furnace slag（STBBFS） photocatalysts were prepared by the high energy ball milling method with（NH4）2SO4 and titanium dioxide-bearing blast furnace slag（TBBFS） as raw materials.X-ray photoelectron spectroscopy（XPS）,X-ray diffraction（XRD）,scanning electron microscopy（SEM）,thermogravimetric analysis（TGA）,UV-visible diffuse reflectance absorption spectra（UV-Vis）,adsorption experiment and photocatalytic degradation measurement were conducted to characterize the structure,surface status,light absorption capacity,adsorption capacity and photocatalytic activity of the obtained photocatalysts.The adsorption equilibrium was described by the Langmuir isotherm model with a maximum adsorption capacity of 8.25 mg/g of Cr（VI） ions onto the STBBFS photocatalysts.As a result,sulfation of TBBFS improved the photocatalytic activities of STBBFSx photocatalysts.At a low calcination temperature,the photocatalytic activity of STBBFS300 photocatalyst was markedly higher compared with TBBFSx prepared at high calcination temperature,indicating that the photocatalytic activity of STBBFSx photocatalyst was determined by the balanced result between adsorption capacity and perovskite content.

Mechanisms of phosphate removal from aqueous solution by blast furnace slag and steel furnace slag

We report the adsorption of phosphate and discuss the mechanisms of phosphate removal from aqueous solution by burst furnace slag (BFS) and steel furnace slag (SFS). The results show that the adsorption of phosphate on the slag was rapid and the majority of adsorption was completed in 5~10 min. The adsorption capacity of phosphate by the slag was reduced dramatically by acid treatment. The relative contribution of adsorption to the total removal of phosphate was 26%~28%. Phosphate adsorption on BFS and SFS follows the Freundlich isotherm, with the related constants of k 6.372 and 1/n 1.739 for BFS, and of k 1.705 and 1/n 1.718 for SFS. The pH and Ca2+ concentration were decreased with the addition of phosphate, suggesting the formation of calcium phosphate precipitation. At pH 2.93 and 6.93, phosphate was desorbed by about 36%~43% and 9%~11%, respectively. These results indicate that the P adsorption on the slag is not completely reversible and that the bond between the slag particles and adsorbed phosphate is strong. The X-ray diffraction (XRD) patterns of BFS and SFS before and after phosphate adsorption verify the formation of phosphate salts (CaHPO4·2H2O) after adsorption process. We conclude that the removal of phosphate by BFS and SFS is related to the formation of phosphate calcium precipitation and the adsorption on hydroxylated oxides. The results show that BFS and SFS removed phosphate nearly 100%, indicating they are promising adsorbents for the phosphate removal in wastewater treatment and pollution control.

Synthesis of (Ca, Mg)-α′-Sialon-AlN-BN powders from boron-rich blast furnace slag by microwave carbothermal reduction-nitridation

(Ca, Mg)-α′-Sialon-AlN-BN powders were synthesized by the carbothermal reduction and nitridation (CRN) method using boron-rich slag, one of the intermediate products from pyrometallurgy separation of pageit, as the staring material. The influences of synthesis temperature and holding time on the phase composition and microstructure during the microwave CRN were studied by XRD, SEM and EDS. The comparison between two heating techniques, conventional and microwave heating, on the synthesized powder was presented as well. The experimental results revealed that the phase compositions and microstructures of the synthesized products were greatly affected by the synthesis temperature and holding time. With an increase in the synthesis temperature or holding time, the relative amount of α′-Sialon increased and α′-Sialon became the main crystalline phase at 1400 °C for 6 h. The synthesized products also contained AlN, BN and a small amount of β-SiC. Elongated α′-Sialon grains, short rod AlN grains, aggregate nanoscale BN grains were observed in the synthesized powders. The reaction temperature of microwave heating method was reduced by 80 °C, the reaction time was shortened by 2 h, and more elongated α′-Sialon grains with large aspect ratio were observed.

Influence of aluminium nitride as a foaming agent on the preparation of foam glass-ceramics from high-titanium blast furnace slag

To effectively reuse high-titanium blast furnace slag （TS）, foam glass-ceramics were successfully prepared by powder sintering at 1000℃. TS and waste glass were used as the main raw materials, aluminium nitride （AIN） as the foaming agent, and borax as the fluxing agent. The influence of the amount of A1N added （lwt%-5wt%） on the crystalline phases, microstructure, and properties of the produced foam glass-ceramics was studied. The results showed that the main crystal phases were perovskite, diopside, and augite. With increasing A1N content, a transformation from diopside to augite occurred and the crystallinity of the pyroxene phases slightly decreased. Initially, the aver- age pore size and porosity of the foam glass-ceramics increased and subsequently decreased; similarly, their bulk density and compressive strength decreased and subsequently increased. The optimal properties were obtained when the foam glass-ceramics were prepared by adding 4wt% AIN.

Status and development of mineral wool made from molten blast furnace slag

This study describes the characteristics of mineral wool and its applications,and also introduces the traditional process of mineral wool made from molten blast furnace （BF） slag. Compared with high energy consumption of the traditional process,the production of mineral wool by using molten BF slag will be able to take full advantage of the sensible heat of molten slag, and also reduce production costs. However, there are also further issues to resolve such as how to obtain the required amount of molten BF slag and how to make it homogeneous. Based on the physical and chemical properties of the molten BF slag,the investigation into the relationship between temperature and viscosity under different acidity coefficients of the slag and silicon mixture was conducted. Combined with the crystallization and phase diagram of slag wool, its heat resistance, water resistance, durability and corrosion resistance were analyzed. Finally, trends of the technology development are proposed.

Indirect mineral carbonation of blast furnace slag with(NH4)2SO4 as a recyclable extractant

Large quantities of COand blast furnace slag are discharged in the iron and steel industry. Mineral carbonation of blast furnace slag can offer substantial COemission reduction and comprehensive utilisation of the solid waste. In this study, a recyclable extractant,（NH）SO, was used to extract calcium and magnesium from blast furnace slag（main phases of gehlenite and akermanite） by using low-temperature roasting to fix COthrough aqueous carbonation. The process parameters and efficiency of the roasting extraction, mineralisation, and Al recovery were investigated in detail. The results showed that the extractions of Ca, Mg, and Al can reach almost 100% at an（NH4）SO-to-slag mass ratio of 3:1 and at 370°C in 1 h. Adjusting the p H value of the leaching solution of the roasted slag to 5.5 with the NHreleased during the roasting resulted in 99% Al precipitation, while co-precipitation of Mg was lower than 2%. The Mg-rich leachate after the depletion of Al and the leaching residue（main phases of CaSOand SiO） were carbonated using（NH）COand NHHCOsolutions, respectively, under mild conditions. Approximately 99% of Ca and 89% of Mg in the blast furnace slag were converted into CaCOand（NH）Mg（CO）·4 HO,respectively. The latter can be selectively decomposed to magnesium carbonate at 100-200 °C to recover the NHfor reuse. In the present route, the total COsequestration capacity per tonne of blast furnace slag reached up to 316 kg, and 313 kg of Al-rich precipitate, 1000 kg of carbonated product containing CaCOand SiO, and 304 kg of carbonated product containing calcium carbonate and magnesium carbonate were recovered simultaneously. These products can be used, respectively, as raw materials for the production of electrolytic aluminium, cement, and light magnesium carbonate to replace natural resources.

Characteristics of gaseous product from municipal solid waste gasification with hot blast furnace slag

Possibility of combustible gas production from municipal solid waste （MSW） using hot blast furnace （BF） slag has been studied.The objective of this work is to generate combustible gas from MSW using heated BF slag.In this experiment,the thermal stability of the MSW was analyzed by thermogravimetric analysis,and effects of temperature,gasifying agent （air,N2,steam） and BF slag on the gas products were investigated at 600？900 ？C.The thermogravimetric analysis indicates that the weight loss of MSW includes four stages：evaporation of the moisture,combustion of volatile materials,burning of carbon residue and burnout of ash.The contents of the combustible gas increase with increasing temperature,and the lower calorific value （LCV） increases rapidly at 600？900 ？C.It is found that volume fraction of CO,H2 and CH4 at different atmospheres increases in the order N2〈air〈steam.It is believed that BF slag acts as the catalyst and the heat carrier,which promotes the gasification reactivity of MSW.

Effect of sintering temperature on the microstructure and properties of foamed glass-ceramics prepared from high-titanium blast furnace slag and waste glass

Foamed glass-ceramics were prepared via a single-step sintering method using high-titanium blast furnace slag and waste glass as the main raw materials The influence of sintering temperature(900–1060℃) on the microstructure and properties of foamed glass-ceramics was studied. The results show that the crystal shape changed from grainy to rod-shaped and finally turned to multiple shapes as the sintering temperature was increased from 900 to 1060℃. With increasing sintering temperature, the average pore size of the foamed glass-ceramics increased and subsequently decreased. By contrast, the compressive strength and the bulk density decreased and subsequently increased. An excessively high temperature, however, induced the coalescence of pores and decreased the compressive strength. The optimal properties, including the highest compressive strength(16.64 MPa) among the investigated samples and a relatively low bulk density(0.83 g/cm^3), were attained in the case of the foamed glass-ceramics sintered at 1000℃.

Preparation,characterization and photocatalytic activity of sulfuric acid-modified titanium-bearing blast furnace slag

The feasibility of reducing Cr(VI)from the aqueous solution by sulfuric acid-modified titanium-bearing blast furnace slag(SATBBFS)as a photocatalyst was investigated.The photocatalysts were examined by X-ray diffraction(XRD),UV-vis diffuse reflectance spectra,thermogravimetric analysis(TG)and Fourier transform infrared spectroscopy(FTIR).The photocatalytic activities of the different catalysts were evaluated by the photocatalytic reduction of Cr(VI)under UV-vis light irradiation.The results show that the photocatalytic activities of SATBBFS catalysts are strongly dependent on CaTiO3-to-TiO2 mass ratio,adsorption capacity and surface acidity,and SATBBFS calcined at 400°C shows a higher photocatalytic activity compared with other catalysts.

Kinetics of the leaching of TiO_2 from Ti-bearing blast furnace slag

Ti-bearing blast furnace slag is a valuable secondary resource containing about 24 percent of TiO2.In this paper a process of leaching Ti-bearing blast furnace slag with sulfuric acid to recover TiO2,and the kinetics of that reaction,are described.Under laboratory conditions the rate is controlled by a chemical reaction.The leaching reaction is in accord with a shrinking unre- acted-core model.The apparent reaction order of the leaching reaction was 1.222 and the apparent activation energy was 87.01 kJ/mol.The model fits the observed data well until 90%of the TiO2 has be leached from the particles.The model disagrees with observations during later periods of the reaction because the solution becomes supersaturated with Ti ions,which precipitate as H2TiO4.The assumptions of constant reactant concentration and that there is no effect from the product layer on diffusion,also cause the model to deviate from the actual values.

Influence of CeO_2 addition on the preparation of foamed glass-ceramics from high-titanium blast furnace slag

Foamed glass-ceramics doped with cerium oxide（CeO_2）were successfully prepared from high-titanium blast furnace slag by one-step sintering.The influence of CeO_2 addition（1.5wt%–3.5wt%）on the crystalline phases,microstructure,and properties of foamed glass-ceramics was studied.Results show that CeO_2 improves the stability of the glass phase and changes the two-dimensional crystallization mechanism into three-dimensional one.XRD analysis indicates the presence of Ca（Mg,Fe）Si_2O_6 and Ca（Ti,Mg,Al）（Si,Al）_2O_（6 ）in all sintered samples.Added with CeO_2,Ti CeO_4 precipitates,and crystallinity increases,leading to increased thickness of pore walls and uniform pores.The comprehensive properties of foamed glass-ceramics are better than that of samples without CeO_2.In particular,the sample added with a suitable amount of CeO_2（2.5wt%）exhibits bulk density that is similar to and compressive strength（14.9 MPa）that is more than twice of foamed glass-ceramics without CeO_2.

Simultaneous preparation of TiO2 and ammonium alum,and microporous SiO2 during the mineral carbonation of titanium-bearing blast furnace slag

In this study,a route for simultaneous mineralization of CO2 and production of titanium dioxide and ammonium alum,and microporous silicon dioxide from titanium-bearing blast furnace slag(TBBF slag)was proposed,which is comprised of(NH4)2 S04 roasting,acid leaching,ammonium alum crystallization,silicic acid flocculation and Ti hydrolysis.The effects of relevant process parameters were systematically investigated.The re sults showed that under the optimal roasting and leaching conditions about 85%of titanium and 84.6%of aluminum could be extracted while only 30%of silicon entered the leachate.84%of Al^3+was crystallized from the leachate in the form of ammonium aluminum sulfate dodecahydrate with a purity up to 99.5 wt%.About 85%of the soluble silicic acid was flocculated with the aid of secondary alcohol polyoxyethylene ether 9(AEO-9)to yield a microporous SiO2 material(97.4 wt%)from the crystallized mother liquor.The Al-and Si-depleted solution was then hydrolyzed to generate a titanium dioxide(99.1 wt%)with uniform particle size distribution.It was figured out that approximately 146 kg TiO2 could be produced from 1000 kg of TBBF slag.Therefore,the improved process is a promising method for industrial application.

PRECIPITATION AND GROWTH OF PEROVSKITE PHASE IN TITANIUM BEARING BLAST FURNACE SLAG

The effects of transformation of slag composition and additive agents on the morphology, the precipitation behavior, the crystal growth, and the volume fraction (VF) of perovskite (CaO·¤TiO_2) crystal in the Ti-bearing blast furnace slags were investigated. As the morphology of perovskite is dispersed in molten slags, the crystal growth mechanism of the melting of fine dendrites and the coarsening of large grains exist throughout the solidification of molten slags. With the increase of CaO and Fe_2O_3 content, VF of perovskite obviously increases. However, high basicity leads to the viscosity of slag, which results in the reduction of the average equivalent diameter (AED). The experimental results showed that the presence of the additives CaF_2 and MnO efficiently decreased the viscosity of the slags, and obviously improved the morphology of perovskite and promoted its growth.