Copper staves have been equipped on nearly all of BF （blast furnaces） with volume over than 1000 m3 in China since their introduction from abroad about more than 10 years ago. Because of short application and lack o...Copper staves have been equipped on nearly all of BF （blast furnaces） with volume over than 1000 m3 in China since their introduction from abroad about more than 10 years ago. Because of short application and lack of experience, phenomena of thickened or naked of copper stave happen occasionally which influence production severely. So it is important to study the model of forming-accretion on BF copper stave and realize real-time monitoring of forming-accretion on different copper staves. Therefore, mathematic model of calculating accretion thickness by heat flow of BF is proposed, and the calculated results indicate that accretion thickness could be kept at a reasonable range of around 50 mm by controlling heat flux around 22.0 kW/mz. The monitoring program based on the model was applied to a certain BF in China successfully, and it is found that slip of BF near the inner wall is one of most important reasons that cause fluctuation of accretion thickness. During the period of scheduled maintenance of the certain BF, the thickness of accretion measured through the static pressure holes is in good accordance with the value calculated by the monitoring program, so the results calculated by the monitoring program can be used to guide industrial production展开更多
A new hydraulic cementitious binder was developed by mainly utilizing industrial byproducts phosphogypsum（PG）and ground granulated blast furnace slag（GGBFS）with small addition of ordinary portland cement（OPC）.Th...A new hydraulic cementitious binder was developed by mainly utilizing industrial byproducts phosphogypsum（PG）and ground granulated blast furnace slag（GGBFS）with small addition of ordinary portland cement（OPC）.The hydration process and microstructure were studied by X-ray diffraction（XRD） and scanning electronic microscopy（SEM）.OPC hydrated first at early age to form primarily C-S-H gel,ettringite and calcium hydroxide（CH）.GGBFS activated by CH and sulfate ions hydrated continuously at later age,producing more and more hydration products,C-S-H gel and ettringite.Thus the paste developed a denser microstructure and its strength increased.The 28 d compressive strength of the mixture of 50%PG,46% GGBFS and 4%OPC exceeded 45 MPa.The setting time was faster and 3 d and 7 d strength were higher when the proportion of OPC increased.But the 28 d strength decreased when OPC exceeded 4%due to large amount of ettringite formed at late hydration age which damaged the microstructure.展开更多
Using ground granulated blast furnace slag as the active stuff of high performance concrete (HPC), the C60 SHPC was prepared. The behaviour of the C60 SHPC and its application in the Car Parking Building of Beijing C...Using ground granulated blast furnace slag as the active stuff of high performance concrete (HPC), the C60 SHPC was prepared. The behaviour of the C60 SHPC and its application in the Car Parking Building of Beijing Capital International Airport were described. Also, the manufacturing techniques of reducing cement consumption, lowering hydration heat, minimizing shrinkage cracks and improving durability of the C60 SHPC were discussed. (Author abstract) 3 Refs.展开更多
文摘Copper staves have been equipped on nearly all of BF （blast furnaces） with volume over than 1000 m3 in China since their introduction from abroad about more than 10 years ago. Because of short application and lack of experience, phenomena of thickened or naked of copper stave happen occasionally which influence production severely. So it is important to study the model of forming-accretion on BF copper stave and realize real-time monitoring of forming-accretion on different copper staves. Therefore, mathematic model of calculating accretion thickness by heat flow of BF is proposed, and the calculated results indicate that accretion thickness could be kept at a reasonable range of around 50 mm by controlling heat flux around 22.0 kW/mz. The monitoring program based on the model was applied to a certain BF in China successfully, and it is found that slip of BF near the inner wall is one of most important reasons that cause fluctuation of accretion thickness. During the period of scheduled maintenance of the certain BF, the thickness of accretion measured through the static pressure holes is in good accordance with the value calculated by the monitoring program, so the results calculated by the monitoring program can be used to guide industrial production
文摘A new hydraulic cementitious binder was developed by mainly utilizing industrial byproducts phosphogypsum（PG）and ground granulated blast furnace slag（GGBFS）with small addition of ordinary portland cement（OPC）.The hydration process and microstructure were studied by X-ray diffraction（XRD） and scanning electronic microscopy（SEM）.OPC hydrated first at early age to form primarily C-S-H gel,ettringite and calcium hydroxide（CH）.GGBFS activated by CH and sulfate ions hydrated continuously at later age,producing more and more hydration products,C-S-H gel and ettringite.Thus the paste developed a denser microstructure and its strength increased.The 28 d compressive strength of the mixture of 50%PG,46% GGBFS and 4%OPC exceeded 45 MPa.The setting time was faster and 3 d and 7 d strength were higher when the proportion of OPC increased.But the 28 d strength decreased when OPC exceeded 4%due to large amount of ettringite formed at late hydration age which damaged the microstructure.
文摘Using ground granulated blast furnace slag as the active stuff of high performance concrete (HPC), the C60 SHPC was prepared. The behaviour of the C60 SHPC and its application in the Car Parking Building of Beijing Capital International Airport were described. Also, the manufacturing techniques of reducing cement consumption, lowering hydration heat, minimizing shrinkage cracks and improving durability of the C60 SHPC were discussed. (Author abstract) 3 Refs.