期刊文献+
共找到214篇文章
< 1 2 11 >
每页显示 20 50 100
Research progress and future prospects in the service security of key blast furnace equipment
1
作者 Yanxiang Liu Kexin Jiao +3 位作者 Jianliang Zhang Cui Wang Lei Zhang Xiaoyue Fan 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2024年第10期2121-2135,共15页
The safety and longevity of key blast furnace(BF)equipment determine the stable and low-carbon production of iron.This pa-per presents an analysis of the heat transfer characteristics of these components and the uneve... The safety and longevity of key blast furnace(BF)equipment determine the stable and low-carbon production of iron.This pa-per presents an analysis of the heat transfer characteristics of these components and the uneven distribution of cooling water in parallel pipes based on hydrodynamic principles,discusses the feasible methods for the improvement of BF cooling intensity,and reviews the pre-paration process,performance,and damage characteristics of three key equipment pieces:coolers,tuyeres,and hearth refractories.Fur-thermoere,to attain better control of these critical components under high-temperature working conditions,we propose the application of optimized technologies,such as BF operation and maintenance technology,self-repair technology,and full-lifecycle management techno-logy.Finally,we propose further researches on safety assessments and predictions for key BF equipment under new operating conditions. 展开更多
关键词 blast furnace EQUIPMENT service security blast furnace campaign SELF-REPAIR
下载PDF
Practice for Extending Blast Furnace Campaign Life at Wuhan Iron and Steel Corporation 被引量:4
2
作者 ZHANG Shou rong 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2006年第6期1-7,20,共8页
One of the problems encountered in 60's to 80's of 20th century in China's steel industry was short life of blast furnace shaft as well as the excessive erosion of blast furnace hearth. A series of research work wa... One of the problems encountered in 60's to 80's of 20th century in China's steel industry was short life of blast furnace shaft as well as the excessive erosion of blast furnace hearth. A series of research work was carried out in order to extend blast furnace campaign life. The concept of research and development was integrated in the construction of BF (blast furnace) No. 5 at WISCO (Wuhan Iron and Steel Corporation), and in October, 1991, the BF No. 5 was blown in. The blast furnace has worked smoothly for more than 15 years without any medium repair even guniting. It is expected that the campaign life of BF No. 5 would be longer than 16 years with a production over 11 000 t per unit inner volume (m^2). A new blast furnace with an inner volume of 3 400 m^3 is under construction, and is designed with a campaign life of 20 years without any medium repair. The campaign life of blast furnaces in China has been extended in recent years. 展开更多
关键词 blast furnace campaign life EROSION
下载PDF
Monitoring Method for Blast Furnace Wall With Copper Staves 被引量:5
3
作者 CHENG Su-sen QIAN Liang ZHAO Hong-bo 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2007年第4期1-5,共5页
A monitoring method that has been designed for the first time for blast furnace wall with copper staves manufactured in China was introduced. Combining the method of "inverse problem" and the concept "non-inverse p... A monitoring method that has been designed for the first time for blast furnace wall with copper staves manufactured in China was introduced. Combining the method of "inverse problem" and the concept "non-inverse problem", the monitoring program for blast furnace wall with copper staves has been realized, which can be used to calculate online the accretion thickness and temperature of hot surface of copper staves after obtaining the values of thermocouples of copper staves. The accretion state obtained in the actual investigation has proved that the result of the program is correct. The monitoring program shows that the accretion would easily fluctuate when the accretion layer is extremely thick or thin, thereby the stable and smooth operation of the blast furnace is hindered. By maintaining appropriate accretion thickness, both long campaigns and high productivity of the blast furnace can be achieved; furthermore, it can also optimize the operation of blast furnace and maximize its production. Approximately 30--50 mm in thickness of accretion layer is maintained on the wall of Shougang blast furnace 2, which can meet the requirement for obtaining both long campaign and high productivity. 展开更多
关键词 blast furnace copper stave wall monitoring ACCRETION long campaign high productivity
下载PDF
大型高炉炉缸浇注修复技术研究与应用
4
作者 张福明 贾国利 +2 位作者 张勇 赵满祥 焦克新 《炼铁》 CAS 北大核心 2024年第5期1-7,共7页
为了有效延长炉役中后期高炉寿命,开发了高炉炉缸内衬浇注修复技术,在首钢股份3座高炉上应用,取得了显著的应用成效和经济效益。系统阐述了高炉炉缸内衬浇注修复技术关键技术及特点,开展了炉缸内衬浇注修复多场仿真模拟研究。简要分析... 为了有效延长炉役中后期高炉寿命,开发了高炉炉缸内衬浇注修复技术,在首钢股份3座高炉上应用,取得了显著的应用成效和经济效益。系统阐述了高炉炉缸内衬浇注修复技术关键技术及特点,开展了炉缸内衬浇注修复多场仿真模拟研究。简要分析了高炉停炉及相关技术,如高炉快速停炉降温技术、残铁口精准定位技术、炉缸侵蚀内型数字化成像技术;重点分析了炉缸内衬浇注修复技术,如炉缸内衬浇注料选择、炉缸内衬浇注结构设计优化、炉缸内衬整体浇注修复技术、炉缸内衬侵蚀模型的重构等,同时指出了本项技术的关键操作要素和未来预期的应用效果。 展开更多
关键词 大型高炉 炉缸内衬 浇注修复 长寿
下载PDF
高炉炉缸铁水流场影响因素的数值模拟研究
5
作者 卢正东 李承志 《宝钢技术》 CAS 2024年第2期9-18,共10页
对高炉炉缸铁水流场影响因素开展数值模拟研究。结果表明:铁水剪切应力较高区域主要集中在炉缸出铁口下方;提高高炉利用系数会增大炉缸壁面上的剪切应力;在高炉正常生产情况下,死料柱孔隙率和铁口直径变化对炉缸侧壁铁水剪切应力影响较... 对高炉炉缸铁水流场影响因素开展数值模拟研究。结果表明:铁水剪切应力较高区域主要集中在炉缸出铁口下方;提高高炉利用系数会增大炉缸壁面上的剪切应力;在高炉正常生产情况下,死料柱孔隙率和铁口直径变化对炉缸侧壁铁水剪切应力影响较小;增加铁口深度和减小铁口倾角可以有效降低铁水对炉缸侧壁的剪切应力。实际生产中,保持良好原燃料条件,适度增加铁口深度,采取小铁口倾角出铁有利于减缓铁水对炉缸内衬的冲刷,从而实现炉缸长寿的目标。 展开更多
关键词 高炉 炉缸 流场 剪切应力 长寿
下载PDF
Design and Operation Control for Long Campaign Life of Blast Furnaces 被引量:7
6
作者 ZHANG Fu-ming 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2013年第9期53-60,共8页
At the beginning of 1990s, Shougang blast furnaces (BFs) No. 2, No. 4, No. 3 and No. 1 were rebuilt se quently for new technological modernization in succession. The campaign life of BFs No. 1, No. 3 and No. 4 reach... At the beginning of 1990s, Shougang blast furnaces (BFs) No. 2, No. 4, No. 3 and No. 1 were rebuilt se quently for new technological modernization in succession. The campaign life of BFs No. 1, No. 3 and No. 4 reaches 16.4, 17.6 and 15.6 years, respectively, and the hot metal output of one campaign reaches 33.8, 35.48 and 26.37 Mt, respectively; the hot metal output of BF effective volume of one campaign reaches 13328, 13991 and 12560 t/m^3, respectively, which reaches the international advanced level of BF high efficiency and long campaign life. In BF desig-ning, several advanced BF long campaign technologies were adopted. BF proper inner profile was optimized, reasona- ble inner profile was adopted, and closed circulating soften water cooling technology was applied in 4 BFs. Double row cooling pipe high efficiency cooling stave was developed which could prolong the service life of bosh, belly and stack. Hot pressed carbon brick and ceramic cup hearth lining structure were applied and optimized. BF operation was improved continuously to ensure stable and smooth operation of BF. Hearth working condition control was strengthened, burden distribution control technology was applied to achieve reasonable distribution of gas flow, and heat load monitoring was strengthened to maintain BF reasonable working inner profile. Proper maintenance at the end of BF campaign was enhanced. Hearth and bottom service life was prolonged by adding titaniferous material and enhancing hearth cooling. Gunning of lining was carried out periodically for the area above tuyere zone. 展开更多
关键词 blast furnace long campaign life hearth lining cooling stave operation control
原文传递
高炉炉缸砌体结构及烘炉风量对炉缸长寿的影响简析 被引量:1
7
作者 王雪峰 《炼铁》 CAS 北大核心 2023年第1期56-58,共3页
从高炉炉缸砌体结构和烘炉风量两个方面分析了对炉缸长寿的影响。认为:①稳定性相对较差的炉缸砌体结构,会因“象脚区”的侵蚀而导致侧壁炭砖加速出现大量的砖缝,继而出现“钻铁”情况,会大大缩短炉缸的寿命,建议采用整体稳定性更好的... 从高炉炉缸砌体结构和烘炉风量两个方面分析了对炉缸长寿的影响。认为:①稳定性相对较差的炉缸砌体结构,会因“象脚区”的侵蚀而导致侧壁炭砖加速出现大量的砖缝,继而出现“钻铁”情况,会大大缩短炉缸的寿命,建议采用整体稳定性更好的圆筒型炉缸结构。②高炉烘炉时,应关注烘炉的总风量能否将耐材中的水分完全带走,以减少水分及气隙对高炉长寿的影响,对于4000m^(3)以上高炉,单位炉容烘炉风量应达到10000m^(3)/m^(3)以上。 展开更多
关键词 高炉 炉缸长寿 砌体结构 烘炉风量
下载PDF
马钢B高炉炉役后期的生产对策
8
作者 郝团伟 吴宏亮 +1 位作者 高鹏 张越强 《炼铁》 CAS 北大核心 2023年第4期29-33,共5页
马钢B高炉炉役后期主要面临的问题:一是烧结矿、球团矿的钛含量偏高对炉缸活跃性产生了不利影响;二是冷却壁水管破损漏水影响了煤气流分布及安全生产。为保持炉况稳定顺行,采取的生产对策主要有:①加强原燃料管理,改善焦炭质量,减少矿... 马钢B高炉炉役后期主要面临的问题:一是烧结矿、球团矿的钛含量偏高对炉缸活跃性产生了不利影响;二是冷却壁水管破损漏水影响了煤气流分布及安全生产。为保持炉况稳定顺行,采取的生产对策主要有:①加强原燃料管理,改善焦炭质量,减少矿石钛含量及入炉碱金属量;②优化上下部制度,疏松边沿、活跃中心,强化炉前出铁,稳定出铁时间,保证炉缸活跃性;③对炉缸活跃性进行定量评价。B高炉取得了较好的技术经济指标,2021年9月-2022年8月,月均利用系数在2.04~2.28t/(m^(3)·d),焦炭负荷在5.00左右,燃料比在488~500kg/t。 展开更多
关键词 大型高炉 炉役后期 顺行 炉缸活跃性 操作制度
下载PDF
长钢8号高炉炉缸炉底破损调查及长寿经验
9
作者 杨军昌 李迎辉 +3 位作者 陈红俊 张学恩 张林凯 宋国伟 《炼铁》 CAS 北大核心 2023年第4期38-43,共6页
对长钢8号高炉炉缸炉底破损调查及长寿经验进行了总结分析。8号高炉一代炉役寿命9年10个月,单位炉容产铁量10640t/m^(3),停炉后进行的炉缸炉底破损调查结果表明,炉缸与炉底交界处侵蚀最为严重,呈象脚状侵蚀,炉缸炭砖部分环裂,炉底5层满... 对长钢8号高炉炉缸炉底破损调查及长寿经验进行了总结分析。8号高炉一代炉役寿命9年10个月,单位炉容产铁量10640t/m^(3),停炉后进行的炉缸炉底破损调查结果表明,炉缸与炉底交界处侵蚀最为严重,呈象脚状侵蚀,炉缸炭砖部分环裂,炉底5层满铺炭砖完好,炉缸侵蚀的原因主要是铁水环流、铁水溶蚀、有害元素侵蚀和热应力等。8号高炉这一代炉役的长寿经验:一是均衡稳定的生产组织;二是长期稳定顺行的炉况;三是及时采取相应的护炉生产措施,四是合理应用炉体维护技术。 展开更多
关键词 高炉 炉缸 炉底 破损调查 炭砖 长寿 护炉
下载PDF
沙钢2号高炉长寿管理的主要措施 被引量:1
10
作者 吕昌贺 常李 +2 位作者 周大勇 张建良 徐震 《炼铁》 CAS 北大核心 2023年第3期6-11,15,共7页
沙钢2号高炉第二代炉役已连续高强度生产近10年,炉缸热电偶温度虽有波动,但总体保持在安全受控范围内,产能及相关消耗指标较好,炉缸侵蚀也处于稳定状态,长寿管理取得明显成效。2号高炉长寿管理的主要措施是:(1)改进炉缸炉底耐材砌筑结... 沙钢2号高炉第二代炉役已连续高强度生产近10年,炉缸热电偶温度虽有波动,但总体保持在安全受控范围内,产能及相关消耗指标较好,炉缸侵蚀也处于稳定状态,长寿管理取得明显成效。2号高炉长寿管理的主要措施是:(1)改进炉缸炉底耐材砌筑结构及冷却系统;(2)调整优化操作制度;(3)建立合理的炉体管理制度;(4)改善原燃料质量;(5)加强炉前铁口维护工作。认为,高炉长寿管理是一项综合型的长期系统管理工作,2号高炉建立的正常生产、经济性护炉和强化补炉护炉等炉体管理制度,是实现高炉安全长寿、高效稳定生产的关键。 展开更多
关键词 高炉 炉缸 长寿 操作制度 炉体管理制度
下载PDF
世界高炉炼铁技术的发展现状与趋势 被引量:1
11
作者 张福明 《炼铁》 CAS 北大核心 2023年第5期1-9,共9页
近10年来,国外在炼铁工艺流程结构优化,高炉大型化、现代化、高效化、低碳化等方面取得了显著成就,高炉生产效率不断提高,燃料消耗不断下降,高炉清洁低碳生产技术迈向新的发展阶段。阐述了世界高炉炼铁技术近年来的发展现状,如高炉大型... 近10年来,国外在炼铁工艺流程结构优化,高炉大型化、现代化、高效化、低碳化等方面取得了显著成就,高炉生产效率不断提高,燃料消耗不断下降,高炉清洁低碳生产技术迈向新的发展阶段。阐述了世界高炉炼铁技术近年来的发展现状,如高炉大型化、工艺流程结构优化、高炉长寿技术、高炉低碳炼铁技术等。认为:基于现有高炉炼铁工艺流程,通过装备现代化、大型化和工艺优化,可以取得优异的技术经济指标,进一步提高技术竞争力;延长高炉寿命、提高球团矿人炉比例、提高炉料分布精准控制水平等,是未来高炉改善工艺操作、优化工艺装备的重要技术途径;未来高炉炼铁工艺创新发展的重点是氢基燃料的大量应用,实现碳-氢耦合还原和高效耦合的“三传一反”过程,提高H,在高炉内的利用率。 展开更多
关键词 高炉 炼铁 燃料比 长寿 绿色低碳 氢冶金
下载PDF
沙钢5800m^(3)高炉炉缸长寿浅析
12
作者 朱华 《炼铁》 CAS 北大核心 2023年第2期13-16,20,共5页
沙钢5800m高炉生产运行已超过12年,受限于总图布置,高炉仅有3个铁口,且铁口分布不均匀,生产中曾出现过数次炉缸温度升高及炭砖侵蚀现象。针对5800m高炉炉缸工作不均匀、不容易活跃、存在气隙等问题,经过长期的生产实践,摸索出了适合炉... 沙钢5800m高炉生产运行已超过12年,受限于总图布置,高炉仅有3个铁口,且铁口分布不均匀,生产中曾出现过数次炉缸温度升高及炭砖侵蚀现象。针对5800m高炉炉缸工作不均匀、不容易活跃、存在气隙等问题,经过长期的生产实践,摸索出了适合炉役后期安全生产的措施:①优化出铁制度,加强出铁管理;②提高炉缸活跃性;③炉缸定期压浆和排水;④加强原燃料质量管理。目前,5800m高炉一代炉役铁产量已达到9300/m^(3)以上,炉缸温度在受控范围内,炉缸炭砖没有出现新的侵蚀,炉缸工作状态稳定,利用系数达到2.25(m^(3)·d)。 展开更多
关键词 特大型高炉 炉缸 炭砖 长寿 炉役后期
下载PDF
攀钢高炉炉缸侵蚀的特征及高效长寿技术
13
作者 林千谷 《炼铁》 CAS 北大核心 2023年第6期5-10,15,共7页
攀钢多座高炉的炉体破损调查结果表明,炉缸侵蚀由象脚状向平底锅状转变。炉缸炉底不管是普通黏土砖结构还是复合莫来石陶瓷杯结构,均可在炉缸底部形成一层富含TiC的沉积物,有效保护了炉底,但TiC在炉缸侧壁沉积有限,铁口区域安全仍然是... 攀钢多座高炉的炉体破损调查结果表明,炉缸侵蚀由象脚状向平底锅状转变。炉缸炉底不管是普通黏土砖结构还是复合莫来石陶瓷杯结构,均可在炉缸底部形成一层富含TiC的沉积物,有效保护了炉底,但TiC在炉缸侧壁沉积有限,铁口区域安全仍然是薄弱环节。通过建立原料钛平衡管控制度、全风操作制度、铁水[Ti]与炉渣(TiO_(2))平衡的操作制度、炉缸炉底冷却水管控制度及定修制度等,形成了一套完整的高钛型钒钛磁铁矿高效长寿冶炼控制技术,实现了高炉高效长寿的目标。攀钢新3号高炉一代炉役寿命达到16.9年,单位炉容产铁量达到13006t/m^(3)。 展开更多
关键词 高炉 炉缸侵蚀 钒钛磁铁矿 破损调查 高效长寿
下载PDF
首钢股份3号高炉炉役后期降低燃料消耗实践
14
作者 张俊伟 程洪全 +2 位作者 贾新 王荣刚 林春山 《四川冶金》 CAS 2023年第1期36-39,共4页
首钢股份3号高炉于2010年1月投产,一代炉役寿命已达12年,进入炉役生产后期。生产中存在操作炉型既定,高炉炉况接受调整困难;炉缸炉底侵蚀严重,加钛护炉为常态;冷却强度下降,在炉墙处形不成稳定的渣皮等制约高炉强化冶炼的特征,高炉表现... 首钢股份3号高炉于2010年1月投产,一代炉役寿命已达12年,进入炉役生产后期。生产中存在操作炉型既定,高炉炉况接受调整困难;炉缸炉底侵蚀严重,加钛护炉为常态;冷却强度下降,在炉墙处形不成稳定的渣皮等制约高炉强化冶炼的特征,高炉表现为煤气流分布紊乱,炉缸侧壁温度长期处在高位,被迫控制铁水产量适应,严重影响了高炉顺行,燃料消耗居高不下。通过采取加强原燃料质量管理,提高原燃料质量和入炉粒级;合理地上下部调剂,调整中心和边缘煤气流分布,提高煤气利用率;精细精准化日常管理,保证炉温和炉渣碱度合适稳定,炉外渣铁出匀出净等措施,3号高炉炉况长时间稳定顺行,铁水产量稳步提升,燃料比大幅下降,各项技术经济指标明显改善。 展开更多
关键词 大型高炉 后期炉役 装料制度 燃料消耗
下载PDF
高炉炉缸炉底长寿技术 被引量:12
15
作者 任嵬 董丽 +4 位作者 李鹏 丛培源 马骁一 王英武 雷明 《耐火材料》 CAS 北大核心 2012年第3期224-229,共6页
对高炉炉缸和炉底的侵蚀机制、合理的炉缸结构、炉缸和炉底内衬结构及其耐火材料进行了较为全面的介绍,同时建议在高炉生产过程中采取一系列措施来提高炉缸、炉底的寿命:拥有合理的死铁层深度、炉缸高度和铁口深度的炉缸结构,可为高炉... 对高炉炉缸和炉底的侵蚀机制、合理的炉缸结构、炉缸和炉底内衬结构及其耐火材料进行了较为全面的介绍,同时建议在高炉生产过程中采取一系列措施来提高炉缸、炉底的寿命:拥有合理的死铁层深度、炉缸高度和铁口深度的炉缸结构,可为高炉高效长寿和生产的稳定顺行奠定良好基础;根据高炉顺行情况和炉缸、炉底侵蚀状态控制好生铁成分,并采取有效措施减少碱金属等有害元素在炉内的富集及对炉缸、炉底的侵蚀;在线进行压浆能有效消除炉缸砖衬间的缝隙,提高炉缸冷却系统的冷却效果,减缓炉缸砖衬的侵蚀;加含钛物料护炉可以使侵蚀严重的炉底、炉缸转危为安,显著提高高炉寿命。 展开更多
关键词 炉缸 炉底 耐火材料 高炉长寿 侵蚀机制 维护
下载PDF
首钢迁钢1号高炉长寿设计 被引量:13
16
作者 钱世崇 程素森 +1 位作者 张福明 张键 《炼铁》 北大核心 2005年第1期6-9,共4页
通过讨论炉底炉缸长寿技术的发展历程,总结首钢高炉长寿经验,提出高炉炉缸炉底长寿设计的思想和理念——控制炉缸炉底的“象脚状”侵蚀,避开炉缸的过度侵蚀,使炉缸炉底侵蚀向“锅底状”侵蚀的方向发展。首钢迁钢 1号高炉炉缸炉底的设计... 通过讨论炉底炉缸长寿技术的发展历程,总结首钢高炉长寿经验,提出高炉炉缸炉底长寿设计的思想和理念——控制炉缸炉底的“象脚状”侵蚀,避开炉缸的过度侵蚀,使炉缸炉底侵蚀向“锅底状”侵蚀的方向发展。首钢迁钢 1号高炉炉缸炉底的设计,结合数学模型计算,实现了长寿设计。 展开更多
关键词 炉缸 高炉长寿 炉底 开炉 长寿技术 首钢 侵蚀 发展历程 过度 经验
下载PDF
高炉的大型化与长寿化 被引量:12
17
作者 王再义 张立国 +2 位作者 张伟 王相力 邓伟 《炼铁》 北大核心 2012年第1期17-20,共4页
高炉的大型化已成为炼铁技术发展的主流趋势,如何实现大型高炉长寿化是目前亟待解决的问题。同时,就大型高炉的技术指标评价和炉缸炉底设计等方面提出了建议。
关键词 高炉 大型化 长寿 炉缸
下载PDF
高炉炉缸炭砖保护层的形成机理及影响因素 被引量:21
18
作者 王筱留 焦克新 +1 位作者 祁成林 项钟庸 《炼铁》 北大核心 2017年第5期8-14,共7页
阐述了高炉炉缸炭砖保护层4种类型(即富铁层、富渣层、富石墨层和富钛层)的形成机理,并用案例印证了炉缸炭砖保护层是4种类型保护层综合作用的结果。重点阐明了影响炉缸炭砖保护层的若干因素,认为:(1)炉缸炭砖保护层形成和稳定的关键是... 阐述了高炉炉缸炭砖保护层4种类型(即富铁层、富渣层、富石墨层和富钛层)的形成机理,并用案例印证了炉缸炭砖保护层是4种类型保护层综合作用的结果。重点阐明了影响炉缸炭砖保护层的若干因素,认为:(1)炉缸炭砖保护层形成和稳定的关键是砖衬热面温度,为此必须做好有关冷却系统的设计、建安、护炉及生产维护等工作;(2)要维持与冶炼强度相适应的炉腹煤气量来组织生产,以利于形成稳定的炉缸炭砖保护层;(3)控制好铁水成分,以减缓炭砖保护层的消蚀;(4)提高炉缸死料堆的透气性和透液性,有利于炉缸炭砖保护层的形成和稳定;(5)做好炉前出铁工作,是形成稳定保护层的有效保证。 展开更多
关键词 高炉 炉缸 炭砖 保护层 长寿
下载PDF
近年来炼铁生产的回顾及新时期持续发展的路径 被引量:10
19
作者 杨天钧 张建良 +1 位作者 刘征建 焦克新 《炼铁》 北大核心 2017年第4期1-9,共9页
近年来,我国在高炉大型化、淘汰落后产能、钢铁行业的供给侧结构性改革等方面取得了明显进展,指导高炉生产的观念正在转变。但是,高炉炼铁也存在一些亟待解决的问题,诸如:精料方针尚未深入贯彻,高炉长寿问题依然严峻,热风温度还有较大... 近年来,我国在高炉大型化、淘汰落后产能、钢铁行业的供给侧结构性改革等方面取得了明显进展,指导高炉生产的观念正在转变。但是,高炉炼铁也存在一些亟待解决的问题,诸如:精料方针尚未深入贯彻,高炉长寿问题依然严峻,热风温度还有较大提升空间,燃料比偏高等。为此,高炉炼铁技术在发展路径上,一要深入贯彻精料方针;二要努力改善高炉操作,提高煤气利用率;三要重视高炉安全长寿与环境保护;四要提高风温,富氧喷吹,大幅度降低燃料比;五要探索智能炼铁技术;六要注重基础理论研究,不断研发新工艺和新技术。 展开更多
关键词 高炉炼铁 精料 操作 长寿
下载PDF
首钢高炉高效长寿技术设计与应用实践 被引量:11
20
作者 毛庆武 张福明 +1 位作者 姚轼 钱世崇 《炼铁》 北大核心 2011年第5期1-6,共6页
阐述了首钢高炉采用的多项高效长寿技术及取得的应用效果,并对高炉内型、炉缸内衬结构、冷却体系、自动化检测、生产操作管理等技术进行了评述。
关键词 大型高炉 高效 长寿 设计
下载PDF
上一页 1 2 11 下一页 到第