Preparation of Poly(o-toluidine)/Nano ZrO2/Epoxy Composite Coating and Its Application for Corrosion Protection of Steel

The main objective was to study the anticorrosion performance of poly（o-toluidine）/nano ZrO2/epoxy composite coating.Poly（o-toluidine）/nano ZrO2 composite was prepared by in situ polymerization of o-toluidine monomer in the presence of nano ZrO2 particles.Fourier transformation infrared spectroscopy（FT-IR）,UV-visible spectroscopy（UV-vis）,X-ray diffraction（XRD）,Scanning electron microscopy（SEM）,and Thermogravimetric analysis（TGA） were used to characterize the composition and structure of the composite.Poly（o-toluidine）/nano ZrO2 composite was mixed with epoxy resin through a solution blending method and the three components poly（o-toluidine）/nano ZrO2/epoxy composite coating was coated onto the surface of steel sample by the brush coating method.The anticorrosion performance of poly（o-toluidine）/nano ZrO2/epoxy composite coating on steel sample was studied by polarization curve and electrochemical impendence spectroscopy in 3.5% Na Cl solution as corrosion environment and also compared with that of poly（o-toluidine）/epoxy composite coating and pure epoxy coating.It was observed that the composite coating containing poly（otoluidine）/nano ZrO2 composite has got higher corrosion protection ability than that of poly（o-toluidine）.The electrochemical measurement results demonstrated that poly（o-toluidine） fillers improve the electrochemical anticorrosion performance of epoxy coating and the addition of nano ZrO2 particles increases the tortuosity of the diffusion pathway of corrosive substances.

Preparation and Characterization of Controlled Heparin Release Waterborne Polyurethane Coating Systems

In this study, to improve hemocompatibility of biomedical materials, a waterborne polyurethane （WPU）haepafin release coating system （WPU/heparin） is fabricated via simply blending biodegradable WPU emulsions with heparin aqueous solutions. The surface compositions and hydrophilicity of these WPU/heparin blend coatings are characterized by attenuated total reflectance infrared spectroscopy （ATR-FTIR） and water contact angle measurements. These WPU/heparin blend coatings show effectively controlled release of heparin, as determined by the toluidine blue method. Furthermore, the biocompatibility and anticoagulant activity of these blend coatings are evaluated based on the protein adsorption, platelet adhesion, activated partial thromboplastin time （APTT）, thrombin time （TT）, hemolysis, and cytotoxicity. The results indicate that better hemocompatibility and cytocompatilibity are obtained due to blending heparin into this waterborne polyurethane. Thus, the WPU/heparin blend coating system is expected to be valuable for various biomedical applications.