In the present paper, low carbon steel strips with different phosphorus contents were produced using a twin roll strip casting process. The solidification structure was studied and its features were analyzed in detail...In the present paper, low carbon steel strips with different phosphorus contents were produced using a twin roll strip casting process. The solidification structure was studied and its features were analyzed in detail. It was found that the strips possessed a fine microstructure compared with the mould cast steels. With increasing phosphorus content more ferrite has been formed with finer grains.展开更多
This paper focused on the influence of the shape and size of threshing frames as well as the grades of tobacco leaves on the structure of threshed leaves.The testing tobacco leaves all came from the hilly ecological r...This paper focused on the influence of the shape and size of threshing frames as well as the grades of tobacco leaves on the structure of threshed leaves.The testing tobacco leaves all came from the hilly ecological region of Nanling and belonged to burnt sweet,alcoholic sweet and scent category.The comprehensive evaluating value S was taken as the test index.Results showed that,without considering the influence of tobacco grade on leaf structure,the shapes of first-stage thresher five-link frames were all hexagons,and the combination with the sizes of 3.5,3.0,3.5,3.0,3.0 inches had the highest evaluating value S of 2.49.For tobacco grade C2FH,the shapes of first-stage thresher five-link frames were also hexagons,and the evaluating value S reached the highest value of 3.40 with sizes of 3.5,3.0,3.5,3.0,3.0 inches.Comprehensive analysis showed that:3.0 inch frame performed better in controlling the percentage of large-sized strips than 3.5 inch frame did;rhombic frames were better than hexagon frames in reducing the breakage rate of tobacco leaves;different shapes or sizes of nonadjacent two-link frames can help to improve the threshing quality.展开更多
In this study, the matrix structure, state and composition of the mill scales of four typical domestically made 510L hot-rolled strips were observed and analyzed by means of optical microscopy （OM） ,scanning electro...In this study, the matrix structure, state and composition of the mill scales of four typical domestically made 510L hot-rolled strips were observed and analyzed by means of optical microscopy （OM） ,scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The corrosion behavior of the steels with and without mill scales were investigated by means of hot-humid corrosion tests under the condition of relative humidity （ RH ） of 95% at 50℃ and 70℃, respectively. The results show that the matrix structures, state, composition and thickness of mill scales vary in the strips. The rusting starting time of the specimens with scales is generally a bit longer than that of the specimens without scales, but their corrosion mass-gain is higher. For these two kinds of specimens ,their corrosion rate increases significantly with the increase of temperature. The rusting behavior of the 510L strips produced by various plants is different due to the variations of hot-rolling processes and designed chemical compositions. Various relevant aspects should be taken into account in the evaluation of the corrosion behavior of hot-rolled strips.展开更多
基金This work was supported by the Major State Basic Research Development Program of China(973 Program)under the contract number of 2004CB619108the National Natural Science Foundation of China(No.50574018)the NECT-04-0278 Project of the Ministry of Education of China.
文摘In the present paper, low carbon steel strips with different phosphorus contents were produced using a twin roll strip casting process. The solidification structure was studied and its features were analyzed in detail. It was found that the strips possessed a fine microstructure compared with the mould cast steels. With increasing phosphorus content more ferrite has been formed with finer grains.
文摘This paper focused on the influence of the shape and size of threshing frames as well as the grades of tobacco leaves on the structure of threshed leaves.The testing tobacco leaves all came from the hilly ecological region of Nanling and belonged to burnt sweet,alcoholic sweet and scent category.The comprehensive evaluating value S was taken as the test index.Results showed that,without considering the influence of tobacco grade on leaf structure,the shapes of first-stage thresher five-link frames were all hexagons,and the combination with the sizes of 3.5,3.0,3.5,3.0,3.0 inches had the highest evaluating value S of 2.49.For tobacco grade C2FH,the shapes of first-stage thresher five-link frames were also hexagons,and the evaluating value S reached the highest value of 3.40 with sizes of 3.5,3.0,3.5,3.0,3.0 inches.Comprehensive analysis showed that:3.0 inch frame performed better in controlling the percentage of large-sized strips than 3.5 inch frame did;rhombic frames were better than hexagon frames in reducing the breakage rate of tobacco leaves;different shapes or sizes of nonadjacent two-link frames can help to improve the threshing quality.
文摘In this study, the matrix structure, state and composition of the mill scales of four typical domestically made 510L hot-rolled strips were observed and analyzed by means of optical microscopy （OM） ,scanning electron microscopy （SEM） and X-ray diffraction （XRD）. The corrosion behavior of the steels with and without mill scales were investigated by means of hot-humid corrosion tests under the condition of relative humidity （ RH ） of 95% at 50℃ and 70℃, respectively. The results show that the matrix structures, state, composition and thickness of mill scales vary in the strips. The rusting starting time of the specimens with scales is generally a bit longer than that of the specimens without scales, but their corrosion mass-gain is higher. For these two kinds of specimens ,their corrosion rate increases significantly with the increase of temperature. The rusting behavior of the 510L strips produced by various plants is different due to the variations of hot-rolling processes and designed chemical compositions. Various relevant aspects should be taken into account in the evaluation of the corrosion behavior of hot-rolled strips.