The bonded MoS_(2)solid lubricant coating is an effective measure to mitigate the fretting wear of AISI 1045 steel.In this work,the amino functionalized MoS_(2)was protonated with acetic acid to make the MoS_(2)positi...The bonded MoS_(2)solid lubricant coating is an effective measure to mitigate the fretting wear of AISI 1045 steel.In this work,the amino functionalized MoS_(2)was protonated with acetic acid to make the MoS_(2)positively charged.The directional arrangement of protonated MoS2 in the coating was achieved by electrophoretic deposition under the electric field force.The bonded directionally aligned MoS_(2)solid lubricant coating showed high adaptability to various loads and excellent lubrication performance under all three working conditions.At a load of 10 N,the friction coefficient and wear volume of the coating with 5 wt%protonated MoS_(2)decreased by 20.0%and 37.2%compared to the pure epoxy coating,respectively,and by 0.07%and 16.8%than the randomly arranged MoS_(2)sample,respectively.The remarkable lubricating properties of MoS_(2)with directional alignment were attributed to its effective load-bearing and mechanical support,barrier effect on longitudinal extension of cracks,and the formation of a continuous and uniform transfer film.展开更多
基金the financial support of National Natural Science Foundation of China(Nos.52075458 and U2141211)Sichuan Science Foundation for Distinguished Young Scholars(No.2023NSFSC1957)the Analytical and Testing Center of Southwest Jiaotong University for support of the scanning electron microscopy(SEM)and Raman measurements.
文摘The bonded MoS_(2)solid lubricant coating is an effective measure to mitigate the fretting wear of AISI 1045 steel.In this work,the amino functionalized MoS_(2)was protonated with acetic acid to make the MoS_(2)positively charged.The directional arrangement of protonated MoS2 in the coating was achieved by electrophoretic deposition under the electric field force.The bonded directionally aligned MoS_(2)solid lubricant coating showed high adaptability to various loads and excellent lubrication performance under all three working conditions.At a load of 10 N,the friction coefficient and wear volume of the coating with 5 wt%protonated MoS_(2)decreased by 20.0%and 37.2%compared to the pure epoxy coating,respectively,and by 0.07%and 16.8%than the randomly arranged MoS_(2)sample,respectively.The remarkable lubricating properties of MoS_(2)with directional alignment were attributed to its effective load-bearing and mechanical support,barrier effect on longitudinal extension of cracks,and the formation of a continuous and uniform transfer film.