Aluminum oxide(Al_(2)O_(3))ceramics have been widely utilized as circuit substrates owing to their exceptional performance.In this study,boron nitride microribbon(BNMR)/Al_(2)O_(3)composite ceramics are prepared using...Aluminum oxide(Al_(2)O_(3))ceramics have been widely utilized as circuit substrates owing to their exceptional performance.In this study,boron nitride microribbon(BNMR)/Al_(2)O_(3)composite ceramics are prepared using spark plasma sintering(SPS).This study examines the effect of varying the amount of toughened phase BNMR on the density,mechanical properties,dielectric constant,and thermal conductivity of BNMR/Al_(2)O_(3)composite ceramics while also exploring the mechanisms behind the toughening and increased thermal conductivity of the fabricated ceramics.The results showed that for a BNMR content of 5 wt%,BNMR/Al_(2)O_(3)composite ceramics displayed more enhanced characteristics than pure Al_(2)O_(3)ceramics.In particular,the relative density,hardness,fracture toughness,and bending strength were 99.95%±0.025%,34.11±1.5 GPa,5.42±0.21 MPa·m^(1/2),and 375±2.5 MPa,respectively.These values represent increases of 0.76%,70%,35%,and 25%,respectively,compared with the corresponding values for pure Al_(2)O_(3)ceramics.Furthermore,during the SPS process,BNMRs are subjected to high temperatures and pressures,resulting in the bending and deformation of the Al_(2)O_(3)matrix;this leads to the formation of special thermal pathways within it.The dielectric constant of the composite ceramics decreased by 25.6%,whereas the thermal conductivity increased by 45.6%compared with that of the pure Al_(2)O_(3)ceramics.The results of this study provide valuable insights into ways of enhancing the performance of Al_(2)O_(3)-based ceramic substrates by incorporating novel BNMRs as a second phase.These improvements are significant for potential applications in circuit substrates and related fields that require high-performance materials with improved mechanical properties and thermal conductivities.展开更多
In this study, we have investigated how the dielectric loss tangent and permittivity of AlN ceramics are affected by factors such as powder mixing methods, milling time, sintering temperature, and the addition of a se...In this study, we have investigated how the dielectric loss tangent and permittivity of AlN ceramics are affected by factors such as powder mixing methods, milling time, sintering temperature, and the addition of a second conductive phase. All ceramic samples were pre-pared by spark plasma sintering (SPS) under a pressure of 30 MPa. AlN composite ceramics sintered with 30wt%-40wt%SiC at 1600℃ for 5 min exhibited the best dielectric loss tangent, which is greater than 0.3. In addition to AlN and β-SiC, the samples also contained 2H-SiC and Fe5Si3, as detected by X-ray difraction (XRD). The relative densities of the sintered ceramics were higher than 93%. Experimental results indicate that nano-SiC has a strong capability of absorbing electromagnetic waves. The dielectric constant and dielectric loss of AlN-SiC ce-ramics with the same content of SiC decreased as the frequency of electromagnetic waves increased from 1 kHz to 1 MHz.展开更多
The Si3N4-BN composites have been prepared via die pressing and precursor infiltration and pyrolysis route using borazine as precursor, and the effect of sintering additives on properties of the composites has been in...The Si3N4-BN composites have been prepared via die pressing and precursor infiltration and pyrolysis route using borazine as precursor, and the effect of sintering additives on properties of the composites has been investigated. After sintering additives are adopted, the a to β phase transition of Si3N4 and the mechanical properties of the composites at both room temperature and high temperature are all increased with small extent. When using Y2O3+Al2O3 as additives, the phase transition of Si3N4 and the mechanical properties of the composites have better results. The β-Si3N4 content is 17.47%. The flexural strength, elastic modulus and fracture toughness of the composites are 188.74 MPa, 84.34 GPa and 2.96 MPa.m1/2, respectively. After exposed at 1 000 ℃ in the air for 15 min, the flexural strength of the composites is 154.62 MPa with a residual ratio of 81.92%. The elongated β-Si3N4 grains appear in all composites with different sintering additives. Relatively more rod like β-Si3N4 grains can be observed in composites with Y2O3+Al2O3 as additives, making it to possess better mechanical properties.展开更多
3Y-TZP/3wt%Al_(2)O_(3) powder was coated with varying amounts of BN using the urea and borate reaction sintering method,and then multiphase ceramics were prepared by hot pressing sintering.The micro-topography and the...3Y-TZP/3wt%Al_(2)O_(3) powder was coated with varying amounts of BN using the urea and borate reaction sintering method,and then multiphase ceramics were prepared by hot pressing sintering.The micro-topography and the compositional analysis of synthesized ceramics were conducted through scanning electron microscopy,transmission electron microscopy and X-ray diffraction.A mechanical tester was used to analyze the Vickers hardness,fracture toughness,and bending strength of the synthesized ceramics.The results showed that the ceramic with a BN content of 12wt%showed the best processability,but had diminished mechanical properties(such as fracture toughness and bending strength).The ceramic with a BN content of 9wt%showed better processability than those with 3wt%and 6wt%BN.However,the fracture toughness was affected by the addition of 9wt%BN,making this ceramic only usable as a base material for a three-unit fixed bridge.In contrast,the ceramics with a BN content of 3wt%or 6wt%fulfilled the criteria for use in multi-unit restoration,but their low processability made them unsuitable for milling after sintering.展开更多
Hexagonal boron nitride ceramic(h-BN) based on the nitridation of B powders was obtained by reaction sintering method. The effects of sintering temperature on the mechanical properties and microstructure of the resu...Hexagonal boron nitride ceramic(h-BN) based on the nitridation of B powders was obtained by reaction sintering method. The effects of sintering temperature on the mechanical properties and microstructure of the resultant products were investigated and the reaction mechanism was discussed. Results showed that the reaction between B and N2 occurred vigorously at temperatures ranging from 1 000 ℃ to 1 300 ℃, which resulted in the generation of t-BN. When the temperature exceeded 1 450 ℃, transformation from t-BN to h-BN began to occur. As the sintering temperature increased, the spherical particles of t-BN gradually transformed into fine sheet particles of h-BN. These particles subsequently displayed a compact arrangement to achieve a more uniform microstructure, thereby increasing the strength.展开更多
基金the financial support from National Natural Science Foundation of China(No.52262010)the Guangxi Natural Science Foundation of China(No.2023GXNSFAA026384)the Guilin Scientific Research and Technology Development Program(No.2020011203-3).
文摘Aluminum oxide(Al_(2)O_(3))ceramics have been widely utilized as circuit substrates owing to their exceptional performance.In this study,boron nitride microribbon(BNMR)/Al_(2)O_(3)composite ceramics are prepared using spark plasma sintering(SPS).This study examines the effect of varying the amount of toughened phase BNMR on the density,mechanical properties,dielectric constant,and thermal conductivity of BNMR/Al_(2)O_(3)composite ceramics while also exploring the mechanisms behind the toughening and increased thermal conductivity of the fabricated ceramics.The results showed that for a BNMR content of 5 wt%,BNMR/Al_(2)O_(3)composite ceramics displayed more enhanced characteristics than pure Al_(2)O_(3)ceramics.In particular,the relative density,hardness,fracture toughness,and bending strength were 99.95%±0.025%,34.11±1.5 GPa,5.42±0.21 MPa·m^(1/2),and 375±2.5 MPa,respectively.These values represent increases of 0.76%,70%,35%,and 25%,respectively,compared with the corresponding values for pure Al_(2)O_(3)ceramics.Furthermore,during the SPS process,BNMRs are subjected to high temperatures and pressures,resulting in the bending and deformation of the Al_(2)O_(3)matrix;this leads to the formation of special thermal pathways within it.The dielectric constant of the composite ceramics decreased by 25.6%,whereas the thermal conductivity increased by 45.6%compared with that of the pure Al_(2)O_(3)ceramics.The results of this study provide valuable insights into ways of enhancing the performance of Al_(2)O_(3)-based ceramic substrates by incorporating novel BNMRs as a second phase.These improvements are significant for potential applications in circuit substrates and related fields that require high-performance materials with improved mechanical properties and thermal conductivities.
基金financially supported by the International S&T Cooperation Program of China(No.2010DFR50360)
文摘In this study, we have investigated how the dielectric loss tangent and permittivity of AlN ceramics are affected by factors such as powder mixing methods, milling time, sintering temperature, and the addition of a second conductive phase. All ceramic samples were pre-pared by spark plasma sintering (SPS) under a pressure of 30 MPa. AlN composite ceramics sintered with 30wt%-40wt%SiC at 1600℃ for 5 min exhibited the best dielectric loss tangent, which is greater than 0.3. In addition to AlN and β-SiC, the samples also contained 2H-SiC and Fe5Si3, as detected by X-ray difraction (XRD). The relative densities of the sintered ceramics were higher than 93%. Experimental results indicate that nano-SiC has a strong capability of absorbing electromagnetic waves. The dielectric constant and dielectric loss of AlN-SiC ce-ramics with the same content of SiC decreased as the frequency of electromagnetic waves increased from 1 kHz to 1 MHz.
基金Founded by the National Natural Science Foundation of China(Nos.90916019 and 50902150)Aid Program for Science and Technology Innovative Research Team in Higher Educational Institutions of Hunan Province and Aid Program for Innovative Group of National University of Defense Technology
文摘The Si3N4-BN composites have been prepared via die pressing and precursor infiltration and pyrolysis route using borazine as precursor, and the effect of sintering additives on properties of the composites has been investigated. After sintering additives are adopted, the a to β phase transition of Si3N4 and the mechanical properties of the composites at both room temperature and high temperature are all increased with small extent. When using Y2O3+Al2O3 as additives, the phase transition of Si3N4 and the mechanical properties of the composites have better results. The β-Si3N4 content is 17.47%. The flexural strength, elastic modulus and fracture toughness of the composites are 188.74 MPa, 84.34 GPa and 2.96 MPa.m1/2, respectively. After exposed at 1 000 ℃ in the air for 15 min, the flexural strength of the composites is 154.62 MPa with a residual ratio of 81.92%. The elongated β-Si3N4 grains appear in all composites with different sintering additives. Relatively more rod like β-Si3N4 grains can be observed in composites with Y2O3+Al2O3 as additives, making it to possess better mechanical properties.
基金financially supported by the National Natural Science Foundation of China(No.81371183).
文摘3Y-TZP/3wt%Al_(2)O_(3) powder was coated with varying amounts of BN using the urea and borate reaction sintering method,and then multiphase ceramics were prepared by hot pressing sintering.The micro-topography and the compositional analysis of synthesized ceramics were conducted through scanning electron microscopy,transmission electron microscopy and X-ray diffraction.A mechanical tester was used to analyze the Vickers hardness,fracture toughness,and bending strength of the synthesized ceramics.The results showed that the ceramic with a BN content of 12wt%showed the best processability,but had diminished mechanical properties(such as fracture toughness and bending strength).The ceramic with a BN content of 9wt%showed better processability than those with 3wt%and 6wt%BN.However,the fracture toughness was affected by the addition of 9wt%BN,making this ceramic only usable as a base material for a three-unit fixed bridge.In contrast,the ceramics with a BN content of 3wt%or 6wt%fulfilled the criteria for use in multi-unit restoration,but their low processability made them unsuitable for milling after sintering.
基金Funded by the Scientific and Technological Development Project of Yantai(2013JH020)
文摘Hexagonal boron nitride ceramic(h-BN) based on the nitridation of B powders was obtained by reaction sintering method. The effects of sintering temperature on the mechanical properties and microstructure of the resultant products were investigated and the reaction mechanism was discussed. Results showed that the reaction between B and N2 occurred vigorously at temperatures ranging from 1 000 ℃ to 1 300 ℃, which resulted in the generation of t-BN. When the temperature exceeded 1 450 ℃, transformation from t-BN to h-BN began to occur. As the sintering temperature increased, the spherical particles of t-BN gradually transformed into fine sheet particles of h-BN. These particles subsequently displayed a compact arrangement to achieve a more uniform microstructure, thereby increasing the strength.