Advancements in sensor technology have significantly enhanced atmospheric monitoring.Notably,metal oxide and carbon(MO_(x)/C)hybrids have gained attention for their exceptional sensitivity and room-temperature sensing...Advancements in sensor technology have significantly enhanced atmospheric monitoring.Notably,metal oxide and carbon(MO_(x)/C)hybrids have gained attention for their exceptional sensitivity and room-temperature sensing performance.However,previous methods of synthesizing MO_(x)/C composites suffer from problems,including inhomogeneity,aggregation,and challenges in micropatterning.Herein,we introduce a refined method that employs a metal–organic framework(MOF)as a precursor combined with direct laser writing.The inherent structure of MOFs ensures a uniform distribution of metal ions and organic linkers,yielding homogeneous MO_(x)/C structures.The laser processing facilitates precise micropatterning(<2μm,comparable to typical photolithography)of the MO_(x)/C crystals.The optimized MOF-derived MO_(x)/C sensor rapidly detected ethanol gas even at room temperature(105 and 18 s for response and recovery,respectively),with a broad range of sensing performance from 170 to 3,400 ppm and a high response value of up to 3,500%.Additionally,this sensor exhibited enhanced stability and thermal resilience compared to previous MOF-based counterparts.This research opens up promising avenues for practical applications in MOF-derived sensing devices.展开更多
This study presents a novel process for the fabrication of metal-intermetallic composites with a 3D bicontinuous structure, achieved through a combination of liquid metal dealloying(LMD) and subsequent alloying. Initi...This study presents a novel process for the fabrication of metal-intermetallic composites with a 3D bicontinuous structure, achieved through a combination of liquid metal dealloying(LMD) and subsequent alloying. Initially, porous Ti structures are produced using the LMD process, followed by immersion in a molten Mg-3Al(wt%) metal. Due to the higher thermodynamic miscibility of Al with Ti compared to Mg, the concentration of Al in the Ti matrix increases as the immersion time increases. This results in a sequential phase transition within the Ti matrix: α-Ti → Ti_(3)Al → Ti Al. The phase transition considerably affects the hardness and strength of the composite material,with the Mg-Ti_(3)Al-Ti Al composite exhibiting a maximum hardness nearly twice as high as that of the conventional Mg-Ti composite. This innovative process holds potential for the development of various bicontinuous metal-intermetallic composites.展开更多
Composite materials exhibit the impressive mechanical properties of high damping and stiffness,which cannot be attained by employing conventional single materials.Along these lines,a novel material architecture is pre...Composite materials exhibit the impressive mechanical properties of high damping and stiffness,which cannot be attained by employing conventional single materials.Along these lines,a novel material architecture is presented in this work in order to fabricate composites with enhanced mechanical characteristics.More specifically,entangled metallic wire materials were used as the active matrix,whereas polyurethane was employed as the reinforcement elements.As a result,an entangled metallic wire material-polyurethane composite with high damping and stiffness was prepared by enforcing the vacuum infiltration method.On top of that,the mechanical properties(loss factor,energy consumption,and average stiffness)of the proposed composite materials were characterized by performing dynamic tests,and its fatigue characteristics were verified by the micro-interface bonding,as well as the macro-damage factor.The impact of the density,preloading spacing,loading amplitude,and exciting frequency on the mechanical properties of the composites were also thoroughly analyzed.The extracted results indicate that the mechanical properties of the composites were significantly enhanced than those of the pure materials due to the introduction of interface friction.Moreover,the average stiffness of the composites was about 10 times the respective value of the entangled metallic wire material.Interestingly,a rise in the loading period leads to some failure between the composite interfaces,which reduces the stiffness property but enhances the damping dissipation properties.Finally,a comprehensive dynamic mechanical model of the composites was established,while it was experimentally verified.The proposed composites possess higher damping features,i.e.,stiffness characteristics,and maintain better fatigue characteristics,which can broaden the application range of the composites.In addition,we provide a theoretical and experimental framework for the research and applications in the field of metal matrix composites.展开更多
Aluminum based metal matrix composites were fabricated using stir casting where silicon carbide and alumina were the reinforcements. Different types of properties (physical-density, mechanical-tensile, hardness, chemi...Aluminum based metal matrix composites were fabricated using stir casting where silicon carbide and alumina were the reinforcements. Different types of properties (physical-density, mechanical-tensile, hardness, chemical-corrosion etc.) were measured and compared with base metals/alloys. The properties were significantly varied. The highest density was obtained for pure aluminium with 5% Al<sub>2</sub>O<sub>3</sub> whereas the lowest was obtained for AA-4032 alloy. The highest hardness was obtained for AA-4032 with 5% Al<sub>2</sub>O<sub>3</sub> whereas the lowest was obtained for pure Al with 5% Al<sub>2</sub>O<sub>3</sub>. The highest strength was obtained for AA-6061 with 5% coarse SiC whereas the lowest was obtained for pure Al. The highest impact strength was obtained for AA-4032 with 5% Al<sub>2</sub>O<sub>3</sub> whereas the lowest was obtained for AA-6061. The corrosion resistance of all composites was lower than that of the base materials.展开更多
Solid-state electrolytes(SSEs)are widely considered the essential components for upcoming rechargeable lithium-ion batteries owing to the potential for great safety and energy density.Among them,polymer solid-state el...Solid-state electrolytes(SSEs)are widely considered the essential components for upcoming rechargeable lithium-ion batteries owing to the potential for great safety and energy density.Among them,polymer solid-state electrolytes(PSEs)are competitive candidates for replacing commercial liquid electrolytes due to their flexibility,shape versatility and easy machinability.Despite the rapid development of PSEs,their practical application still faces obstacles including poor ionic conductivity,narrow electrochemical stable window and inferior mechanical strength.Polymer/inorganic composite electrolytes(PIEs)formed by adding ceramic fillers in PSEs merge the benefits of PSEs and inorganic solid-state electrolytes(ISEs),exhibiting appreciable comprehensive properties due to the abundant interfaces with unique characteristics.Some PIEs are highly compatible with high-voltage cathode and lithium metal anode,which offer desirable access to obtaining lithium metal batteries with high energy density.This review elucidates the current issues and recent advances in PIEs.The performance of PIEs was remarkably influenced by the characteristics of the fillers including type,content,morphology,arrangement and surface groups.We focus on the molecular interaction between different components in the composite environment for designing high-performance PIEs.Finally,the obstacles and opportunities for creating high-performance PIEs are outlined.This review aims to provide some theoretical guidance and direction for the development of PIEs.展开更多
Composite solid electrolytes(CSEs)with poly(ethylene oxide)(PEO)have become fairly prevalent for fabricating high-performance solid-state lithium metal batteries due to their high Li~+solvating capability,flexible pro...Composite solid electrolytes(CSEs)with poly(ethylene oxide)(PEO)have become fairly prevalent for fabricating high-performance solid-state lithium metal batteries due to their high Li~+solvating capability,flexible processability and low cost.However,unsatisfactory room-temperature ionic conductivity,weak interfacial compatibility and uncontrollable Li dendrite growth seriously hinder their progress.Enormous efforts have been devoted to combining PEO with ceramics either as fillers or major matrix with the rational design of two-phase architecture,spatial distribution and content,which is anticipated to hold the key to increasing ionic conductivity and resolving interfacial compatibility within CSEs and between CSEs/electrodes.Unfortunately,a comprehensive review exclusively discussing the design,preparation and application of PEO/ceramic-based CSEs is largely lacking,in spite of tremendous reviews dealing with a broad spectrum of polymers and ceramics.Consequently,this review targets recent advances in PEO/ceramicbased CSEs,starting with a brief introduction,followed by their ionic conduction mechanism,preparation methods,and then an emphasis on resolving ionic conductivity and interfacial compatibility.Afterward,their applications in solid-state lithium metal batteries with transition metal oxides and sulfur cathodes are summarized.Finally,a summary and outlook on existing challenges and future research directions are proposed.展开更多
Graphene-reinforced aluminum (AI) matrix composites were successfully prepared via solution mixing and powder metallurgy in this study. The mechanical properties of the composites were studied using microhardness an...Graphene-reinforced aluminum (AI) matrix composites were successfully prepared via solution mixing and powder metallurgy in this study. The mechanical properties of the composites were studied using microhardness and tensile tests. Compared to the pure Al alloy, the graphene/Al composites showed increased strength and hardness. A tensile strength of 255 MPa was achieved for the graphene/Al com- posite with only 0.3wt% graphene, which has a 25% increase over the tensile strength of the pure Al matrix. Raman spectroscopy, Fourier transform infrared spectroscopy, scanning electron microscopy, and transmission electron microscopy were used to investigate the morphol- ogies, chemical compositions, and microstructures of the graphene and the graphene/A1 composites. On the basis of fractographic evidence, a relevant fracture mechanism is proposed.展开更多
An attempt has been made to study the influence of wear parameters like applied load, sliding speed, sliding distance and percentage of reinforcement on the dry sliding wear of the metal matrix composites. A plan of e...An attempt has been made to study the influence of wear parameters like applied load, sliding speed, sliding distance and percentage of reinforcement on the dry sliding wear of the metal matrix composites. A plan of experiments, based on techniques of Taguchi, was performed to acquire data in controlled way. An orthogonal array and the analysis of variance were employed to investigate the influence of process parameters on the wear of composites. The objective is to establish a correlation between dry sliding wear of composites and wear parameters. These correlations were obtained by multiple regressions. Finally, confirmation tests were conducted to verify the experimental results foreseen from the mentioned correlations.展开更多
Al-Si metal matrix composites (MMCs) reinforced with 20 vol.% alumina-silicate shot fibers (Al2O3-SiO2(sf)) were fabricated by an infiltration squeeze method. Pure Pr metal was added into these composites. The effect ...Al-Si metal matrix composites (MMCs) reinforced with 20 vol.% alumina-silicate shot fibers (Al2O3-SiO2(sf)) were fabricated by an infiltration squeeze method. Pure Pr metal was added into these composites. The effect of Pr addition on the microstructure evolution of Al-Si MMCs was investigated by SEM,TEM,and EDS. Pr addition is favorable to make uniform microstructures with the modified eutectic Si crystal. PrAlSi phase with high contents of Pr and Si is observed on the interface between the fiber and the matrix. The addition of Pr promotes interface SiO2 reduction,and SiO2 comes from the crystallization of Al2O3-SiO2 short fibers.展开更多
The particle characteristics of 15%SiC particles reinforced metal matrix composites(MMC)made by powder metallurgy route were studied by using a statistical method.In the analysis,the approach for estimation of the cha...The particle characteristics of 15%SiC particles reinforced metal matrix composites(MMC)made by powder metallurgy route were studied by using a statistical method.In the analysis,the approach for estimation of the characteristics of particles was presented.The study was carried out by using the mathematic software MATLAB to calculate the area and perimeter of each particle, in which the image processing technique was employed.Based on the calculations,the sizes and shape factors of each particle were investigated respectively.Additionally,the finite element model(FEM)was established on the basis of the actual microstructure.The contour plots of von Mises effective stress and strain in matrix and particles were presented in calculations for considering the influence of microstructure on the deformation behavior of MMC.Moreover,the contour maps of the maximum stress of particles and the maximum plastic strain of matrix in the vicinity of particles were introduced respectively.展开更多
Particulate reinforced metallic matrix composites have attracted considerable attention due to their lightweight, high strength, high specific modulus, and good wear resistance. A1/B4C composite strips were produced i...Particulate reinforced metallic matrix composites have attracted considerable attention due to their lightweight, high strength, high specific modulus, and good wear resistance. A1/B4C composite strips were produced in this work by a modified accumulative roll bonding process where the strips were rotated 90° around the normal direction between successive passes. Transmission electron microscopy and X-ray diffraction analyses reveal the development of nanostructures in the Al matrix after seven passes. It is found that the B4C reinforcement distribution in the matrix is improved by progression of the process. Additionally, the tensile yield strength and elongation of the processed materials are increased with the increase of passes.展开更多
(Zr41.2Ti13.sCu12.sNi10Be22.5)100-~Nb~ (at%, x=0 and 8) bulk metallic glasses (BMGs) were coated on the surface of Q195 steel wires by a continuous coating process. The potentiodynamic polarization tests of thes...(Zr41.2Ti13.sCu12.sNi10Be22.5)100-~Nb~ (at%, x=0 and 8) bulk metallic glasses (BMGs) were coated on the surface of Q195 steel wires by a continuous coating process. The potentiodynamic polarization tests of these BMGs were conducted in 3.5wt% NaC1 aqueous solution. It is found that the addition of 8at% Nb into Zr41.2Ti13.sCu12.sNi10Be22.5 alloy results in the improvement of corrosion resistance with the pitting potential of -52 mV, the open circuit potential of-446 mV, and the corrosion current density of 9.86x 10-6 mA/cm2. This may be attributed to that Nb is beneficial to passivate and stabilize Zr and Ti.展开更多
To improve the wettability of common fiUer metals on Al metal matrix composites ( AI-MMCs ) , three kinds of active ternary filler metals, Al-Si-Ti, Zn-Al-Ti and Cu-Al-Ti systems, were prepared by the addition of Ti...To improve the wettability of common fiUer metals on Al metal matrix composites ( AI-MMCs ) , three kinds of active ternary filler metals, Al-Si-Ti, Zn-Al-Ti and Cu-Al-Ti systems, were prepared by the addition of Ti. Excessive melting temperature made the gravity segregation of Ti remarkable in ingot. The effect of Ti content on the melting point for AI-Si-Ti ternary system was not as sensitive as that for Al-Ti binary system. The Al-12Si-1Ti filler metal showed good ability to form brazing foil during rapid cooling, ductile fracture surface and similar shear strength to conventional Al-12Si filler metal. Moreover, the Al2 03 reinforcements on initial surface could be covered by the Al-12Si-1Ti filler metal without interfacial gaps after sessile drop test. For Zn-9.5Al-0. 5 Ti braze alloy, severe vaporization of Zn and severe segregation of Ti Occurred. During wettability test for traditional Al-12Si and Zn-9.5Al-0. 5Ti, although some Si or Zn could penetrate into the composite, interfacial gap still remained. The prepared Cu-19Al-1 Ti interlayer consisted of primary phase of Al4Cu9 and network Cu-Al-Ti ternary intermetaUic compound, showing poor ability to form foil and very brittle nature. These results demonstrated that Al-Si-Ti system should be promising for Al-MMCs.展开更多
The thermal residual stresses and the stress distributions of short fiber reinforced metal matrix composite under tensile and compressive loadings were studied using large strain axisymmetric elasto plastic finite ele...The thermal residual stresses and the stress distributions of short fiber reinforced metal matrix composite under tensile and compressive loadings were studied using large strain axisymmetric elasto plastic finite element method. It is demonstrated that the thermal residual stresses can result in asymmetrical stress distributions and matrix plasticity. The thermal residual stresses decrease the stress transfer in tension and enhance the stress transfer in compression. The fiber volume fraction has more important effects on the thermal residual stresses and the stress distributions under tensile and compressive loadings than the fiber aspect ratio and the fiber end distance. [展开更多
Important progresses in the study of laser additive manufacturing on metal matrix composites(MMCs)have been made.Recent efforts and advances in additive manufacturing on 5 types of MMCs are presented and reviewed.The ...Important progresses in the study of laser additive manufacturing on metal matrix composites(MMCs)have been made.Recent efforts and advances in additive manufacturing on 5 types of MMCs are presented and reviewed.The main focus is on the material design,the combination of reinforcement and the metal matrix,the synthesis principle during the manufacturing process,and the resulted microstructures as well as properties.Thereafter,the trend of development in future is forecasted,including:Formation mechanism and reinforcement principle of strengthening phase;Material and process design to actively achieve expected performance;Innovative structure design based on the special properties of laser AM MMCs;Simulation,monitoring and optimization in the process of laser AM MMCs.展开更多
Magnesium matrix composites (MMC) reinforced with 5wt% tricalcium phosphate (TCP) particles were prepared by powder metallurgy. Pure magnesium (CP-Mg) was fabricated by the same procedure for comparison. Scannin...Magnesium matrix composites (MMC) reinforced with 5wt% tricalcium phosphate (TCP) particles were prepared by powder metallurgy. Pure magnesium (CP-Mg) was fabricated by the same procedure for comparison. Scanning electron microscopy and en- ergy-dispersive X-ray spectroscopy analyses revealed that TCP particles were distributed homogeneously in the MMC. In order to investi- gate the corrosion properties, MMC samples were immersed in a simulated body fluid (SBF) at 310~0.5 K for 72 h. The mass loss of the samples in SBF and the pH values of the SBF were evaluated. Moreover, electrochemical measurements were conducted in the SBF. It was shown that the corrosion rate of the MMC decreased with the addition of TCP compared with CP-Mg. Hydroxyapatite was formed on the surface of MMC samples after immersion in the SBF for 72 h but not on the surface of CP-Mg.展开更多
Laminated metal composites(LMCs) are a unique composite material and have great application prospects in automobiles, ships, aircraft,and other manufacturing industries. As lightweight materials, the Mg/Al LMCs are ex...Laminated metal composites(LMCs) are a unique composite material and have great application prospects in automobiles, ships, aircraft,and other manufacturing industries. As lightweight materials, the Mg/Al LMCs are expected to combine the advantages of both Mg and Al alloys to broaden their application prospects. Roll-bonding is the most popular process for the fabrication of Mg/Al LMCs due to high production efficiency and good product quality stability. The roll-bonding process involves the deformation of the substrates and the formation of the interfacial diffusion layer. The latter will directly determine the interface bonding strength of Mg/Al LMCs. Bonding strength is very sensitive to the thickness of the reaction layer in the diffusion layer. When the thickness of the reaction layer exceeds 5 μm, the bonding strength decreases sharply. Therefore, controlling the thickness of the reaction layer is very important for the design of rolling parameters.The latest research also showed that the addition of intermediate layer metal and the construction of three-dimensional interfaces can further improve the interface bonding strength. How to apply these methods to roll-bonding is the focus of future research. Recently, a new rolling technique, corrugated roll/plat roll rolling+flat roll/flat roll rolling has been developed to fabricate Mg/Al LMCs. It can effectively promote the deformation of the hard layer and generate a wavy interface, resulting in the enhancement of the bonding quality and rolling quality.In the current review, the effects of rolling parameters and subsequent annealing on the interface structure of Mg/Al LMCs were elaborated in detail. The application of some special rolling techniques in the preparation of Mg/Al LMCs was also summarized. The latest research results on the relationship between interface structure and mechanical properties of Mg/Al LMCs were reviewed. Finally, further research directions in this field were proposed.展开更多
Reticulated polyurethane was chosen as the preceramic material for preparing the porous preform using the replication process. The immersing and sintering processes were each performed twice for fabricating a high-por...Reticulated polyurethane was chosen as the preceramic material for preparing the porous preform using the replication process. The immersing and sintering processes were each performed twice for fabricating a high-porosity and super-strong skeleton. The aluminum magnesium matrix composites reinforced with three-dimensional network structure were prepared using the infiltration technique by pressure assisting and vacuum driving. Light interfacial reactions have played a profitable role in most of the ceramic-metal systems. The metal matrix composites interpenetrated with the ceramic phase have a higher wear resistance than the metal matrix phase. The volume fraction of ceramic reinforcement has a significant effect on the abrasive wear, and the wear rate can be decreased with the increase of the volume fraction of reinforcement.展开更多
Graphene has been extensively explored to enhance functional and mechanical properties of metalmatrix nanocomposites for wide-range applications due to their superior mechanical,electrical and thermal properties.This ...Graphene has been extensively explored to enhance functional and mechanical properties of metalmatrix nanocomposites for wide-range applications due to their superior mechanical,electrical and thermal properties.This article discusses recent advances of key mechanisms,synthesis,manufacture,modelling and applications of graphene metal matrix nanocomposites.The main strengthening mechanisms include load transfer,Orowan cycle,thermal mismatch,and refinement strengthening.Synthesis technologies are discussed including some conventional methods(such as liquid metallurgy,powdermetallurgy,thermal spraying and deposition technology)and some advanced processing methods(such as molecular-level mixing and friction stir processing).Analytical modelling(including phenomenological models,semi-empirical models,homogenization models,and self-consistent model)and numerical simulations(including finite elements method,finite difference method,and boundary element method)have been discussed for understanding the interface bonding and performance characteristics between graphene and different metal matrices(Al,Cu,Mg,Ni).Key challenges in applying graphene as a reinforcing component for the metal matrix composites and the potential solutions as well as prospectives of future development and opportunities are highlighted.展开更多
In this study, the processing and mechanical properties of porous metal matrix composites(MMCs) composed of spheroidal cast iron chips(GGG40) and bronze chips(CuSn10) and formed by hot isostatic pressing were investig...In this study, the processing and mechanical properties of porous metal matrix composites(MMCs) composed of spheroidal cast iron chips(GGG40) and bronze chips(CuSn10) and formed by hot isostatic pressing were investigated. Bronze chips(CuSn10) were used as a matrix component, and spheroidal cast iron(GGG40) chips were used as a reinforcement component. The MMCs were produced with different CuSn10 contents(90 wt%, 80 wt%, 70 wt%, and 60 wt%). The hot isostatic pressing process was performed under three different pressures and temperatures. The produced MMCs were characterized using density tests, Brinell hardness tests, and compression tests. In addition, the consolidation mechanism was investigated by X-ray diffraction(XRD) analysis and scanning electron microscopy. The test results were compared with those for bulk CuSn10 and bulk GGG40. Mechanical tests results revealed that the metallic chips can be recycled by using hot pressing and that the mechanical properties of the produced MMCs were similar to those of bulk CuSn10. XRD and microscopy studies showed that no intermetallic compounds formed between the metallic chips. The results showed that the CuSn10 and GGG40 chips were consolidated by mechanical interlocking.展开更多
基金supported by the National Research Foundation of Korea(NRF)grants funded by the Ministry of Science and ICT(MSIT)(RS-2023-00251283,and 2022M3D1A2083618)by the Ministry of Education(2020R1A6A1A03040516).
文摘Advancements in sensor technology have significantly enhanced atmospheric monitoring.Notably,metal oxide and carbon(MO_(x)/C)hybrids have gained attention for their exceptional sensitivity and room-temperature sensing performance.However,previous methods of synthesizing MO_(x)/C composites suffer from problems,including inhomogeneity,aggregation,and challenges in micropatterning.Herein,we introduce a refined method that employs a metal–organic framework(MOF)as a precursor combined with direct laser writing.The inherent structure of MOFs ensures a uniform distribution of metal ions and organic linkers,yielding homogeneous MO_(x)/C structures.The laser processing facilitates precise micropatterning(<2μm,comparable to typical photolithography)of the MO_(x)/C crystals.The optimized MOF-derived MO_(x)/C sensor rapidly detected ethanol gas even at room temperature(105 and 18 s for response and recovery,respectively),with a broad range of sensing performance from 170 to 3,400 ppm and a high response value of up to 3,500%.Additionally,this sensor exhibited enhanced stability and thermal resilience compared to previous MOF-based counterparts.This research opens up promising avenues for practical applications in MOF-derived sensing devices.
基金supported by the National Research Council of Science & Technology (NST) grant by the Korea Government (MSIT) (grant no.CRC23011-000)by the National Research Foundation of Korea (NRF) funded by the Ministry of Science,ICT,and Future Planning (MSIP,South Korea) (grant no.NRF-2021R1C1C1007645)。
文摘This study presents a novel process for the fabrication of metal-intermetallic composites with a 3D bicontinuous structure, achieved through a combination of liquid metal dealloying(LMD) and subsequent alloying. Initially, porous Ti structures are produced using the LMD process, followed by immersion in a molten Mg-3Al(wt%) metal. Due to the higher thermodynamic miscibility of Al with Ti compared to Mg, the concentration of Al in the Ti matrix increases as the immersion time increases. This results in a sequential phase transition within the Ti matrix: α-Ti → Ti_(3)Al → Ti Al. The phase transition considerably affects the hardness and strength of the composite material,with the Mg-Ti_(3)Al-Ti Al composite exhibiting a maximum hardness nearly twice as high as that of the conventional Mg-Ti composite. This innovative process holds potential for the development of various bicontinuous metal-intermetallic composites.
基金National Natural Science Foundation of China(Grant No.52175162,51805086 and 51975123)Natural Science Foundation of Fujian Province(Grant No.2019J01210)Health education joint project of Fujian Province(Grant No.2019-WJ-01)。
文摘Composite materials exhibit the impressive mechanical properties of high damping and stiffness,which cannot be attained by employing conventional single materials.Along these lines,a novel material architecture is presented in this work in order to fabricate composites with enhanced mechanical characteristics.More specifically,entangled metallic wire materials were used as the active matrix,whereas polyurethane was employed as the reinforcement elements.As a result,an entangled metallic wire material-polyurethane composite with high damping and stiffness was prepared by enforcing the vacuum infiltration method.On top of that,the mechanical properties(loss factor,energy consumption,and average stiffness)of the proposed composite materials were characterized by performing dynamic tests,and its fatigue characteristics were verified by the micro-interface bonding,as well as the macro-damage factor.The impact of the density,preloading spacing,loading amplitude,and exciting frequency on the mechanical properties of the composites were also thoroughly analyzed.The extracted results indicate that the mechanical properties of the composites were significantly enhanced than those of the pure materials due to the introduction of interface friction.Moreover,the average stiffness of the composites was about 10 times the respective value of the entangled metallic wire material.Interestingly,a rise in the loading period leads to some failure between the composite interfaces,which reduces the stiffness property but enhances the damping dissipation properties.Finally,a comprehensive dynamic mechanical model of the composites was established,while it was experimentally verified.The proposed composites possess higher damping features,i.e.,stiffness characteristics,and maintain better fatigue characteristics,which can broaden the application range of the composites.In addition,we provide a theoretical and experimental framework for the research and applications in the field of metal matrix composites.
文摘Aluminum based metal matrix composites were fabricated using stir casting where silicon carbide and alumina were the reinforcements. Different types of properties (physical-density, mechanical-tensile, hardness, chemical-corrosion etc.) were measured and compared with base metals/alloys. The properties were significantly varied. The highest density was obtained for pure aluminium with 5% Al<sub>2</sub>O<sub>3</sub> whereas the lowest was obtained for AA-4032 alloy. The highest hardness was obtained for AA-4032 with 5% Al<sub>2</sub>O<sub>3</sub> whereas the lowest was obtained for pure Al with 5% Al<sub>2</sub>O<sub>3</sub>. The highest strength was obtained for AA-6061 with 5% coarse SiC whereas the lowest was obtained for pure Al. The highest impact strength was obtained for AA-4032 with 5% Al<sub>2</sub>O<sub>3</sub> whereas the lowest was obtained for AA-6061. The corrosion resistance of all composites was lower than that of the base materials.
基金the National Natural Science Foundation of China(Nos.22279070,U21A20170 and 22175106)the Ministry of Science and Technology of China(Nos.2019YFA0705703,2021YFB2501900 and 2019YFE0100200)+1 种基金the Tsinghua University Initiative Scientific Research Program(20223080001)the Tsinghua-Foshan Innovation Special Fund(2021THFS0216)。
文摘Solid-state electrolytes(SSEs)are widely considered the essential components for upcoming rechargeable lithium-ion batteries owing to the potential for great safety and energy density.Among them,polymer solid-state electrolytes(PSEs)are competitive candidates for replacing commercial liquid electrolytes due to their flexibility,shape versatility and easy machinability.Despite the rapid development of PSEs,their practical application still faces obstacles including poor ionic conductivity,narrow electrochemical stable window and inferior mechanical strength.Polymer/inorganic composite electrolytes(PIEs)formed by adding ceramic fillers in PSEs merge the benefits of PSEs and inorganic solid-state electrolytes(ISEs),exhibiting appreciable comprehensive properties due to the abundant interfaces with unique characteristics.Some PIEs are highly compatible with high-voltage cathode and lithium metal anode,which offer desirable access to obtaining lithium metal batteries with high energy density.This review elucidates the current issues and recent advances in PIEs.The performance of PIEs was remarkably influenced by the characteristics of the fillers including type,content,morphology,arrangement and surface groups.We focus on the molecular interaction between different components in the composite environment for designing high-performance PIEs.Finally,the obstacles and opportunities for creating high-performance PIEs are outlined.This review aims to provide some theoretical guidance and direction for the development of PIEs.
基金financially supported by National Key R&D Program for International Cooperation(No.2021YFE0115100)the project of the National Natural Science Foundation of China(Nos.51872240,51972270 and 52172101)+4 种基金Key Research and Development Program of Shaanxi Province(No.2021ZDLGY14-08 and 2022KWZ-04)Natural Science Foundation of Shaanxi Province(2020JZ-07)the Research Fund of the State Key Laboratory of Solidification Processing(NPU),China(2021-TS-03)the Fundamental Research Funds for the Central Universities(No.3102019JC005 and G2022KY0604)the Research Fund of the State Key Laboratory of Solid Lubrication(CAS),China(LSL-2007)。
文摘Composite solid electrolytes(CSEs)with poly(ethylene oxide)(PEO)have become fairly prevalent for fabricating high-performance solid-state lithium metal batteries due to their high Li~+solvating capability,flexible processability and low cost.However,unsatisfactory room-temperature ionic conductivity,weak interfacial compatibility and uncontrollable Li dendrite growth seriously hinder their progress.Enormous efforts have been devoted to combining PEO with ceramics either as fillers or major matrix with the rational design of two-phase architecture,spatial distribution and content,which is anticipated to hold the key to increasing ionic conductivity and resolving interfacial compatibility within CSEs and between CSEs/electrodes.Unfortunately,a comprehensive review exclusively discussing the design,preparation and application of PEO/ceramic-based CSEs is largely lacking,in spite of tremendous reviews dealing with a broad spectrum of polymers and ceramics.Consequently,this review targets recent advances in PEO/ceramicbased CSEs,starting with a brief introduction,followed by their ionic conduction mechanism,preparation methods,and then an emphasis on resolving ionic conductivity and interfacial compatibility.Afterward,their applications in solid-state lithium metal batteries with transition metal oxides and sulfur cathodes are summarized.Finally,a summary and outlook on existing challenges and future research directions are proposed.
基金financially supported by the National Natural Science Foundation of China (Nos. 51574118, 51571087, 51674292)the Natural Science Foundation of Hunan Province (No. 2015JJ4017)+1 种基金the Project of Innovation-driven Plan in Central South University (No. 2016CX007)the Hunan Provincial Science and Technology Plan Project, China (No. 2016TP1007)
文摘Graphene-reinforced aluminum (AI) matrix composites were successfully prepared via solution mixing and powder metallurgy in this study. The mechanical properties of the composites were studied using microhardness and tensile tests. Compared to the pure Al alloy, the graphene/Al composites showed increased strength and hardness. A tensile strength of 255 MPa was achieved for the graphene/Al com- posite with only 0.3wt% graphene, which has a 25% increase over the tensile strength of the pure Al matrix. Raman spectroscopy, Fourier transform infrared spectroscopy, scanning electron microscopy, and transmission electron microscopy were used to investigate the morphol- ogies, chemical compositions, and microstructures of the graphene and the graphene/A1 composites. On the basis of fractographic evidence, a relevant fracture mechanism is proposed.
文摘An attempt has been made to study the influence of wear parameters like applied load, sliding speed, sliding distance and percentage of reinforcement on the dry sliding wear of the metal matrix composites. A plan of experiments, based on techniques of Taguchi, was performed to acquire data in controlled way. An orthogonal array and the analysis of variance were employed to investigate the influence of process parameters on the wear of composites. The objective is to establish a correlation between dry sliding wear of composites and wear parameters. These correlations were obtained by multiple regressions. Finally, confirmation tests were conducted to verify the experimental results foreseen from the mentioned correlations.
文摘Al-Si metal matrix composites (MMCs) reinforced with 20 vol.% alumina-silicate shot fibers (Al2O3-SiO2(sf)) were fabricated by an infiltration squeeze method. Pure Pr metal was added into these composites. The effect of Pr addition on the microstructure evolution of Al-Si MMCs was investigated by SEM,TEM,and EDS. Pr addition is favorable to make uniform microstructures with the modified eutectic Si crystal. PrAlSi phase with high contents of Pr and Si is observed on the interface between the fiber and the matrix. The addition of Pr promotes interface SiO2 reduction,and SiO2 comes from the crystallization of Al2O3-SiO2 short fibers.
文摘The particle characteristics of 15%SiC particles reinforced metal matrix composites(MMC)made by powder metallurgy route were studied by using a statistical method.In the analysis,the approach for estimation of the characteristics of particles was presented.The study was carried out by using the mathematic software MATLAB to calculate the area and perimeter of each particle, in which the image processing technique was employed.Based on the calculations,the sizes and shape factors of each particle were investigated respectively.Additionally,the finite element model(FEM)was established on the basis of the actual microstructure.The contour plots of von Mises effective stress and strain in matrix and particles were presented in calculations for considering the influence of microstructure on the deformation behavior of MMC.Moreover,the contour maps of the maximum stress of particles and the maximum plastic strain of matrix in the vicinity of particles were introduced respectively.
文摘Particulate reinforced metallic matrix composites have attracted considerable attention due to their lightweight, high strength, high specific modulus, and good wear resistance. A1/B4C composite strips were produced in this work by a modified accumulative roll bonding process where the strips were rotated 90° around the normal direction between successive passes. Transmission electron microscopy and X-ray diffraction analyses reveal the development of nanostructures in the Al matrix after seven passes. It is found that the B4C reinforcement distribution in the matrix is improved by progression of the process. Additionally, the tensile yield strength and elongation of the processed materials are increased with the increase of passes.
基金supports by the Specialized Research Fund for the Doctoral Program of Higher Education of China(No.20100006120020)the National Nature Science Foundation of China(Nos.51071018and51271018)
文摘(Zr41.2Ti13.sCu12.sNi10Be22.5)100-~Nb~ (at%, x=0 and 8) bulk metallic glasses (BMGs) were coated on the surface of Q195 steel wires by a continuous coating process. The potentiodynamic polarization tests of these BMGs were conducted in 3.5wt% NaC1 aqueous solution. It is found that the addition of 8at% Nb into Zr41.2Ti13.sCu12.sNi10Be22.5 alloy results in the improvement of corrosion resistance with the pitting potential of -52 mV, the open circuit potential of-446 mV, and the corrosion current density of 9.86x 10-6 mA/cm2. This may be attributed to that Nb is beneficial to passivate and stabilize Zr and Ti.
基金The present research was sponsored by the National Natural Science Foundation of China ( No. 50875199), and by State Key Laboratory of Advanced Welding Production Technology, Harbin Institute of Technology, China.
文摘To improve the wettability of common fiUer metals on Al metal matrix composites ( AI-MMCs ) , three kinds of active ternary filler metals, Al-Si-Ti, Zn-Al-Ti and Cu-Al-Ti systems, were prepared by the addition of Ti. Excessive melting temperature made the gravity segregation of Ti remarkable in ingot. The effect of Ti content on the melting point for AI-Si-Ti ternary system was not as sensitive as that for Al-Ti binary system. The Al-12Si-1Ti filler metal showed good ability to form brazing foil during rapid cooling, ductile fracture surface and similar shear strength to conventional Al-12Si filler metal. Moreover, the Al2 03 reinforcements on initial surface could be covered by the Al-12Si-1Ti filler metal without interfacial gaps after sessile drop test. For Zn-9.5Al-0. 5 Ti braze alloy, severe vaporization of Zn and severe segregation of Ti Occurred. During wettability test for traditional Al-12Si and Zn-9.5Al-0. 5Ti, although some Si or Zn could penetrate into the composite, interfacial gap still remained. The prepared Cu-19Al-1 Ti interlayer consisted of primary phase of Al4Cu9 and network Cu-Al-Ti ternary intermetaUic compound, showing poor ability to form foil and very brittle nature. These results demonstrated that Al-Si-Ti system should be promising for Al-MMCs.
文摘The thermal residual stresses and the stress distributions of short fiber reinforced metal matrix composite under tensile and compressive loadings were studied using large strain axisymmetric elasto plastic finite element method. It is demonstrated that the thermal residual stresses can result in asymmetrical stress distributions and matrix plasticity. The thermal residual stresses decrease the stress transfer in tension and enhance the stress transfer in compression. The fiber volume fraction has more important effects on the thermal residual stresses and the stress distributions under tensile and compressive loadings than the fiber aspect ratio and the fiber end distance. [
基金Supported by National Natural Science Foundation of China(Grant Nos.51775525,51605456)Beijing Nova Program(Grant No.Z201100006820094)from Beijing Municipal Science&Technology Commission.
文摘Important progresses in the study of laser additive manufacturing on metal matrix composites(MMCs)have been made.Recent efforts and advances in additive manufacturing on 5 types of MMCs are presented and reviewed.The main focus is on the material design,the combination of reinforcement and the metal matrix,the synthesis principle during the manufacturing process,and the resulted microstructures as well as properties.Thereafter,the trend of development in future is forecasted,including:Formation mechanism and reinforcement principle of strengthening phase;Material and process design to actively achieve expected performance;Innovative structure design based on the special properties of laser AM MMCs;Simulation,monitoring and optimization in the process of laser AM MMCs.
基金the National Key Technologies R&D Program(No.2011BAE22B04)Chong qing Science and Technology Commission(No.2008BB4055)
文摘Magnesium matrix composites (MMC) reinforced with 5wt% tricalcium phosphate (TCP) particles were prepared by powder metallurgy. Pure magnesium (CP-Mg) was fabricated by the same procedure for comparison. Scanning electron microscopy and en- ergy-dispersive X-ray spectroscopy analyses revealed that TCP particles were distributed homogeneously in the MMC. In order to investi- gate the corrosion properties, MMC samples were immersed in a simulated body fluid (SBF) at 310~0.5 K for 72 h. The mass loss of the samples in SBF and the pH values of the SBF were evaluated. Moreover, electrochemical measurements were conducted in the SBF. It was shown that the corrosion rate of the MMC decreased with the addition of TCP compared with CP-Mg. Hydroxyapatite was formed on the surface of MMC samples after immersion in the SBF for 72 h but not on the surface of CP-Mg.
基金supported by Guangdong Major Project of Basic and Applied Basic Research,No. 2020B0301030006。
文摘Laminated metal composites(LMCs) are a unique composite material and have great application prospects in automobiles, ships, aircraft,and other manufacturing industries. As lightweight materials, the Mg/Al LMCs are expected to combine the advantages of both Mg and Al alloys to broaden their application prospects. Roll-bonding is the most popular process for the fabrication of Mg/Al LMCs due to high production efficiency and good product quality stability. The roll-bonding process involves the deformation of the substrates and the formation of the interfacial diffusion layer. The latter will directly determine the interface bonding strength of Mg/Al LMCs. Bonding strength is very sensitive to the thickness of the reaction layer in the diffusion layer. When the thickness of the reaction layer exceeds 5 μm, the bonding strength decreases sharply. Therefore, controlling the thickness of the reaction layer is very important for the design of rolling parameters.The latest research also showed that the addition of intermediate layer metal and the construction of three-dimensional interfaces can further improve the interface bonding strength. How to apply these methods to roll-bonding is the focus of future research. Recently, a new rolling technique, corrugated roll/plat roll rolling+flat roll/flat roll rolling has been developed to fabricate Mg/Al LMCs. It can effectively promote the deformation of the hard layer and generate a wavy interface, resulting in the enhancement of the bonding quality and rolling quality.In the current review, the effects of rolling parameters and subsequent annealing on the interface structure of Mg/Al LMCs were elaborated in detail. The application of some special rolling techniques in the preparation of Mg/Al LMCs was also summarized. The latest research results on the relationship between interface structure and mechanical properties of Mg/Al LMCs were reviewed. Finally, further research directions in this field were proposed.
基金This work was financially supported by the Natural Science Foundation of Shandong Province, China (Y2006F03).
文摘Reticulated polyurethane was chosen as the preceramic material for preparing the porous preform using the replication process. The immersing and sintering processes were each performed twice for fabricating a high-porosity and super-strong skeleton. The aluminum magnesium matrix composites reinforced with three-dimensional network structure were prepared using the infiltration technique by pressure assisting and vacuum driving. Light interfacial reactions have played a profitable role in most of the ceramic-metal systems. The metal matrix composites interpenetrated with the ceramic phase have a higher wear resistance than the metal matrix phase. The volume fraction of ceramic reinforcement has a significant effect on the abrasive wear, and the wear rate can be decreased with the increase of the volume fraction of reinforcement.
基金The authors would like to acknowledge the financial supports from Xi'an Science Research Project of China(No.2020KJRC0089)Shaanxi Coal Industry Group United Fund of China(No.2019JLM-2)+4 种基金National Natural Science Foundation of China,China(No.51901192)Key Research and Development Projects of Shaanxi Province(No.2019GY-164)Science and Technology Project of Weiyang District of Xi'an City(No.201857)Shaanxi Youth Star Program of Science and Technology(No.2020KJXX-061)as well as Newton Mobility Grant(No.IE161019)through Royal Society and the National Natural Science Foundation of China.
文摘Graphene has been extensively explored to enhance functional and mechanical properties of metalmatrix nanocomposites for wide-range applications due to their superior mechanical,electrical and thermal properties.This article discusses recent advances of key mechanisms,synthesis,manufacture,modelling and applications of graphene metal matrix nanocomposites.The main strengthening mechanisms include load transfer,Orowan cycle,thermal mismatch,and refinement strengthening.Synthesis technologies are discussed including some conventional methods(such as liquid metallurgy,powdermetallurgy,thermal spraying and deposition technology)and some advanced processing methods(such as molecular-level mixing and friction stir processing).Analytical modelling(including phenomenological models,semi-empirical models,homogenization models,and self-consistent model)and numerical simulations(including finite elements method,finite difference method,and boundary element method)have been discussed for understanding the interface bonding and performance characteristics between graphene and different metal matrices(Al,Cu,Mg,Ni).Key challenges in applying graphene as a reinforcing component for the metal matrix composites and the potential solutions as well as prospectives of future development and opportunities are highlighted.
基金financially supported by the Scientific and Technological Research Council of Turkey(TUBITAK,No.113M141)
文摘In this study, the processing and mechanical properties of porous metal matrix composites(MMCs) composed of spheroidal cast iron chips(GGG40) and bronze chips(CuSn10) and formed by hot isostatic pressing were investigated. Bronze chips(CuSn10) were used as a matrix component, and spheroidal cast iron(GGG40) chips were used as a reinforcement component. The MMCs were produced with different CuSn10 contents(90 wt%, 80 wt%, 70 wt%, and 60 wt%). The hot isostatic pressing process was performed under three different pressures and temperatures. The produced MMCs were characterized using density tests, Brinell hardness tests, and compression tests. In addition, the consolidation mechanism was investigated by X-ray diffraction(XRD) analysis and scanning electron microscopy. The test results were compared with those for bulk CuSn10 and bulk GGG40. Mechanical tests results revealed that the metallic chips can be recycled by using hot pressing and that the mechanical properties of the produced MMCs were similar to those of bulk CuSn10. XRD and microscopy studies showed that no intermetallic compounds formed between the metallic chips. The results showed that the CuSn10 and GGG40 chips were consolidated by mechanical interlocking.