Fabrication of in-situ synthesized ceramic reinforced Ni-based alloy composite coatings by reactive braze coating processing

In-situ synthesized ceramic such as TiC,Cr7C3 and Cr5B3 reinforced Ni-based alloy composite coating was fabricated on the surface of mild steel substrate by reactive braze coating processing with colloidal graphite,Cr,Ni,ferro-boron,Si and titanium powders as the raw materials at low temperature of 1000℃,and a new kind of coating materials was developed.By means of SEM,EDS,XRD and surface hardness tester,the microstructures,phases,hardness and wear-resistance of the coating were analyzed,respectively.The results revealed that the coating was mainly composed of the ceramic in-situ synthesized reinforcement phases of TiC,Cr7C3 and Cr5B3 and the binder phases in-situ synthesized of Ni31Si12 and(Ni,Fe)solid solution;The ceramic reinforcement phases of TiC,Cr7C3 and Cr5B3 were randomly distributed in the binder phases of Ni31Si12 and(Ni,Fe)solid solution;The coating had about 15vol%pores and can possibly be applied as a self-lubrication coating;The coating and the substrate were integrated together by metallurgical bonding;The coating had a hardness up to 91-94HR15N.

Fabrication of Ti-Ni-Mo-Si composite coating by reactive braze coating process

Ti-Ni-Mo-Si composite coating was fabricated on mild steel by reactive braze coating process with Ti61. 9Ni24. 6Si4. 411409.1 （ wt. % ） powders as the raw materials. Microstr^cture of the coating was characterized by optical microscopy, scanning electron microscopy, X-ray diffraction and energy dispersive spectroscopy and micro-hardness tester. Results indicate that the Ti-Ni-Mo-Si composite coating is metallurgically bonded to the mild steel substrate and has high hardness. The microstructure of the coating consists of the reinforcement of Ti5 Si3 and Mo9 Ti4 particles and the matrix of eutectic NiTi2. Due to the poor wettability of NiTi2 liquid at low temperature, TisSi3 and Mo9 Ti4 do not uniformly distribute in the NiTi2 matrix.

A study on reactive braze coating of (TiC+Cr_3C_2)/Fe composite coatings

A new hardfacing process, reactive braze coating process (RBCC) was studied, and (TiC+Cr_3C_2)/Fe composite coatings were prepared by RBCC using carbon, Cr_3C_2, iron, ferrochromium and titanium powder as the raw materials in vacuum braze furnace. The results show that TiC is in-situ synthesized in the coatings. The methods of introducing Cr_3C_2 have great effects on the distribution of TiC. Adding Cr_3C_2 directly to the raw materials for coatings, fine TiC particles aggregate into discoids parallel to the coating surface, whereas, in-situ synthesizing Cr_3C_2 in coatings, the aggregations of TiC are lumpish. During braze coating, Cr_3C_2 particles directly added dissolve and precipitate to become needle-shaped. The coatings have an even and smooth surface and are combined with their mild steel substrates by a metallurgical bonding.

Evolution behavior of phase and performance in Ni-based coating layer based on high temperature thermal field

Effect of post-welding heat treatment on the microstructure and properties of BNi-2 brazing coating was analyzed. The phase transformation in the heat treatment process was analyzed by high temperature metallographic microscope, scanning electron microscope and X-ray diffraction, and the microhardness after the post heat treatment was tested by microhardness tester. The results show that the microstructure of brazing BNi-2 brazing coating is mainly CrB phase, Ni solid solution phase and eutectic phase of Ni_(3)B and Ni_(3)Si. After brazing,the overall hardness value is higher, generally higher than 510 HV, and the microhardness in some areas is higher than 700 HV. After quenching, the solid solution phase of Ni increased, and the eutectic phase of Ni and Ni_(3)Si decreased, leading to the softening of the brazing coating, the area whose microhardness in the range of 342 HV–454 HV increased. After tempering the brazed coating samples, the eutectic phases of Ni and Ni_(3)Si grew and the hardness recovered, but the overall hardness distribution was still lower than the brazing one. The results of the brazing post-heat treatment test show that the post-welding heat treatment will bring adverse effects on the hardness distribution of the coating, which may affect the wear resistance of the coating.