Effect of brazing temperature on microstructure and tensile strength ofγ-TiAl joint vacuum brazed with micro-nano Ti−Cu−Ni−Nb−Al−Hf filler

A novel micro-nano Ti−10Cu−10Ni−8Al−8Nb−4Zr−1.5Hf filler was used to vacuum braze Ti−47Al−2Nb−2Cr−0.15B alloy at 1160−1220℃ for 30 min.The interfacial microstructure and formation mechanism of TiAl joints and the relationships among brazing temperature,interfacial microstructure and joint strength were emphatically investigated.Results show that the TiAl joints brazed at 1160 and 1180℃ possess three interfacial layers and mainly consist of α_(2)-Ti_(3)Al,τ_(3)-Al_(3)NiTi_(2) and Ti_(2)Ni,but the brazing seams are no longer layered and Ti_(2)Ni is completely replaced by the uniformly distributed τ_(3)-Al_(3)NiTi_(2) at 1200 and 1220℃ due to the destruction of α_(2)-Ti_(3)Al barrier layer.This transformation at 1200℃ obviously improves the tensile strength of the joint and obtains a maximum of 343 MPa.Notably,the outward diffusion of Al atoms from the dissolution of TiAl substrate dominates the microstructure evolution and tensile strength of the TiAl joint at different brazing temperatures.

Time-dependent effects in transient liquid phase bonding of 304L and Cp-Ti using an Ag-Cu interlayer

One of the challenges for bimetal manufacturing is the joining process.Hence,transient liquid phase(TLP)bonding was performed between 304L stainless steel and Cp-Ti using an Ag-Cu interlayer with a thickness of 75μm for bonding time of 20,40,60,and 90 min.The bonding temperature of 860℃ was considered,which is under the β transus temperature of Cp-Ti.During TLP bonding,various intermetallic compounds(IMCs),including Ti_(5)Cr_(7)Fe_(17),(Cr,Fe)_(2)Ti,Ti(Cu,Fe),Ti_(2)(Cu,Ag),and Ti_(2)Cu from 304L toward Cp-Ti formed in the joint.Also,on the one side,with the increase in time,further diffusion of elements decreases the blocky IMCs such as Ti_(5)Cr_(7)Fe_(17),(Cr,Fe)_(2)Ti,Ti(Cu,Fe)in the 304L diffusion-affected zone(DAZ)and reaction zone,and on the other side,Ti_(2)(Cu,Ag)IMC transformed into fine morphology toward Cp-Ti DAZ.The microhardness test also demonstrated that the(Cr,Fe)_(2)Ti+Ti_(5)Cr_(7)Fe_(17) IMCs in the DAZ on the side of 304L have a hardness value of HV 564,making it the hardest phase.The maximum and minimum shear strength values are equal to 78.84 and 29.0 MPa,respectively.The cleavage pattern dominated fracture surfaces due to the formation of brittle phases in dissimilar joints.

Mechanical property of cylindrical sandwich shell with gradient core of entangled wire mesh

To explore the wide-frequency damping and vibration-attenuation performances in the application of aerospace components,the cylindrical sandwich shell structure with a gradient core of entangled wire mesh was proposed in this paper.Firstly,the gradient cores of entangled wire mesh in the axial and radial directions were prepared by using an in-house Numerical Control weaving machine,and the metallurgical connection between skin sheets and the gradient core was performed using vacuum brazing.Secondly,to investigate the mechanical properties of cylindrical sandwich shells with axial or radial gradient cores,quasi-static and dynamic mechanical experiments were carried out.The primary evaluations of mechanical properties include secant stiffness,natural frequency,Specific Energy Absorption(SEA),vibration acceleration level,and so on.The results suggest that the vibration-attenuation performance of the sandwich shell is remarkable when the high-density core layer is at the end of the shell or abuts the inner skin.The axial gradient material has almost no influence on the vibration frequencies of the shell,whereas the vibration frequencies increase dramatically when the high-density core layer approaches the skin.Moreover,compared to the conventional sandwich shells,the proposed functional grading cylindrical sandwich shell exhibits more potential in mass reduction,stiffness designing,and energy dissipation.

Microstructural Evolution of Infrared Brazed CP-Ti Using Ti-Cu-Ni Brazes

Microstructural evolution of infrared vacuum brazed CP-Ti using two Ti-based braze alloys,Ti-15Cu-15Ni and Ti-15Cu-25Ni,has been investigated.The infrared brazed joint consisted of eutectic Ti 2 Cu/Ti 2 Ni intermetallic compounds and Ti-rich matrix.The eutectic Ti 2 Cu/Ti 2 Ni intermetallic compounds disappeared from the joint after being annealed at 900 C for 1 h.In contrast,the depletion rate of both Cu and Ni from the braze alloy into CP-Ti substrate at 750 C annealing was greatly decreased as compared with that annealed at 900 C.Blocky Ti 2 Cu/Ti 2 Ni phases were observed even if the specimen was annealed at 750 C for 15 h.Because the Ni content of the Ti-15Cu-25Ni braze alloy is much higher than that of the Ti-15Cu-15Ni alloy,the amount of eutectic Ti 2 Cu/Ti 2 Ni phases in Ti-15Cu-25Ni brazed joint is more than that in Ti-15Ci-15Ni brazed joint.However,similar microstructural evolution can be obtained from the infrared brazed joint annealed at various temperatures and/or time for both filler metals.

Microstructure and properties of induction brazing nickel base/WC composite coating

BNi-2/WC composite wear-resisting coating was prepared on carbon steel by the method of induction brazing.The microstructure and phase composition of the composite coating were analyzed,and the bonding strength and wear-resisting performance of the coating were tested.During the process of induction brazing,the tungsten carbide partially dissolves and reacts with the filler metal alloy to form NiW compound phase,which realizes the metallurgical combination of tungsten carbide and filler metal alloy.The matrix of the filler metal alloy consists of Ni solid solution and Ni_(3)B/Ni_(3)Si eutectic phase,and the metallurgical diffusion reaction occurs between the filler metal alloy and the steel matrix.The mechanical analysis results show that the self-strength of the composite coating reaches 140 MPa and the bonding strength of the filler metal alloy to the steel matrix reaches 360 MPa.The dry sand rubber wheel wear testing machine showed that the coating weight loss was only 0.2824 g,which was only 1/5 of the weight loss of 65 Mn matrix under the same conditions.

Simulation and Optimization of the Fluid Solidification Process in Brazed Plate Heat Exchangers

When a brazed plate heat exchanger is used as an evaporator,the working mass in the channel may undergo soli-dification,thereby hindering the refrigeration cycle.In this study the liquid solidification process and its optimi-zation in a brazed plate heat exchanger are investigated numerically for different inlet velocities;moreover,different levels of corrugation are considered.The results indicate that solidificationfirst occurs around the con-tacts,followed by the area behind the contacts.It is also shown that deadflow zones exist in the sharp areas and such areas are prone to liquid solidification.After optimization,the solidification area attains its smallest value when a corrugation spacingλ=4.2 mm is considered.

Low-temperature soldering process of AlN/Cu enhanced by Ti addition

Aluminum Nitride(AlN)ceramics were soldered to Cu substrate using active metallized Sn0.3Ag0.7Cu-x%Ti(wt.%,where x=2,4,6,8)at 250℃.This process yielded a robust and closely integrated metallized layer on the AlN ceramic’s surface.Employing SnAgCu solder paste within an air atmosphere,joints were formed for durations of 60s and 300 s.Through meticulous microscopic analysis,optimal metallization parameters were identified,resulting in the successful connection between metallized AlN ceramics and Cu substrate at a low temperature.The microstructure interface investigation further elucidated the impact of connection time on the low-temperature soldered joint of metallized AlN ceramics.

Research on the heat conduction mechanism of induction brazecoating

Induction brazecoating technology is an important means to improve the surface properties of materials.In this paper,copper plate and corundum are selected as substrates for induction brazecoating respectively.The temperature variation of powder and paste coating is systematically studied,and the heat conduction mode and path in the brazecoating process are analyzed.The results show that rise of the coating temperature mainly depends on the heat absorption from the substrate.The liquid-solid interface conducts heat violently and advances step by step,which promotes the melting spread of metal filler metal.The powdery brazecoating material is in a free state,and there is a gas insulation film between the powder particles and the diamond,making it difficult for substrate to conduct heat to the coating.The binder not only assists forming,shell making and oxygen isolation,but also plays an important role during melting.

PERFORMANCE OF BRAZED DIAMOND CUP-TYPE WHEELS WITH DEFINED GRAIN PATTERN IN GRINDING CEMENTED CARBIDE

A new cup-type grinding wheel of the brazed monolayer diamond is developed with a defined grain pattern on the wheel surface. Grinding performance of the brazed wheel in the surface grinding of cemented carbide is studied. Experimental results show that when continuous dry grinding is employed, grits of the brazed diamond grinding wheel fail mainly in attritious wear and fracture modes and no pull-out ones are found in conventional electroplated and sintered diamond wheels. It indicates the strong retention of brazing alloy to diamond grits and the longer service life of the wheel. In addition, the ground surface has good roughness. The theoretical surface roughness agrees well with experimental results.

Microstructure and shear strength of reactive brazing joints of TiAl/Ni-based alloy

Reactive brazing of TiAl-based intermetallics and Ni-based alloy with Ti foil as interlayer was investigated. The interfacial microstructure and shear strength of the joints were studied. According to the experimental observations, the molten interlayer reacts vigorously with base metals, forming several continuous reaction layers. The typical interfacial microstructure of the joint can be expressed as GH99/（Ni,Cr）ss（γ）/TiNi（β2）＋TiNi2Al（τ4）＋Ti2Ni（δ）/δ＋Ti3Al（α2）＋Al3NiTi2（τ3）/α2＋τ3/TiAl. The maximum shear strength is 258 MPa for the specimen brazed at 1000°C for 10 min. Higher brazing temperature or longer brazing time causes coarsening of the phases in the brazing seam and formation of brittle intermetallic layer, which greatly depresses the shear strength of the joints.

Contact reactive brazing of Al alloy/Cu/stainless steel joints and dissolution behaviors of interlayer

Contact reactive brazing of 6063 Al alloy and 1Cr18Ni9Ti stainless steel was researched by using Cu as interlayer. Effect of brazing time on microstructure of the joints, as well as the dissolution behaviors of Cu interlayer was analyzed. The results show that the product of reaction zone near 1Cr18Ni9Ti is composed of Fe2Al5, FeAl3 intermetallic compound （IMC）, and Cu-Al IMC; the near by area is composed of Al-Cu eutectic structure with Al （Cu） solid solution. With increasing the brazing time, the thickness of IMC layer at the interface increases, while the width of Al-Cu eutectic structure with Al（Cu） solution decreases. Calculation shows the dissolution rate of Cu interlayer is very fast. The complete dissolution time is about 0.47 s for Cu interlayer with 10 μm in thickness used in this study.

Microstructural characteristics of joint region during diffusion-brazing of magnesium alloy and stainless steel using pure copper interlayer

A novel joining method,double-stage diffusion-brazing of an AZ31 magnesium alloy and a 304L austenitic stainless steel,was carried out using a pure copper interlayer.The solid-state diffusion bonding of 304L to copper was conducted at 850 ℃ for 20 min followed by brazing to AZ31 at 520 ℃ and 495 ℃ for various time.Microstructural characteristics of the diffusion-brazed joints were investigated in detail.A defect free interface of Fe-Cu diffusion area appeared between the Cu alloy and the 304L steel.Cu-Mg reaction products were formed between AZ31 and Cu alloys.A layered structure including AZ31/Cu-Mg compounds/Cu/Fe-Cu diffusion layer/304L was present in the joint.With time prolonging,the reduction in the width of Cu layer was balanced by the increase in the width of Cu-Mg compounds zone.Microhardness peaks in the zone between AZ31 and Cu layer were attributed to the formation of Mg-Cu compounds in this zone.

BONDING INTERFACE AND WEAR BEHAVIOR OF CBN GRAINS BRAZED USING NANO-TiC POWDER MODIFIED FILLER

A new kind of composite fillers,composed of Ag-Cu-Ti alloy and nano-TiC powders,is utilized to braze cubic boron nitride （CBN） grains and tool substrate. The bonding system,including the interfacial microstructure and reactive products between CBN grains and filler layer,is observed by optical microscope and scanning electron microscope （SEM）. Resistant-to-wear experiments of the brazed grains are performed. Results show that the nano-TiC powders evenly distribute in the filler layer so that the resultants grow compactly and uniformly on the surface of CBN grain. This indicates that the chemical bond is established between CBN grains and nano-TiC modified filler. Accordingly,the bonding strength of the grains is ensured. The CBN grains are worn smoothly without grain pull-out.

Development of Al-12Si-xTi system active ternary filler metals for Al metal matrix composites

To improve the wettability of Al metal matrix composites（Al-MMCs） by common filler metals,Al-12Si-xTi（x=0.1,0.5,1,3.0;mass fraction,%） system active ternary filler metals were prepared.It was demonstrated that although the added Ti existed within Ti（Al1-xSix）3（0≤x≤0.15） phase,the shear strength and shear fracture surface of the developed Al-12Si-xTi brazes were quite similar to those of traditional Al-12Si braze due to the presence of similar microstructure of Al-Si eutectic microstructure with large volume fraction.So,small Ti addition（～1%） did not make the active brazes brittle and hard compared with the conventional Al-12Si braze.The measured melting range of each Al-12Si-xTi foil was very similar,i.e.,580-590 ℃,because the composition was close to that of eutectic.For wettability improvement,with increasing Ti content,the interfacial gap between the Al2O3 reinforcement and filler metal（R/M） could be eliminated,and the amount of the remainder of the active fillers on the composite substrate decreased after sessile drop test at 610 ℃ for 30 min.So,the wettability improvement became easy to observe repeatedly with increasing Ti content.Additionally,the amount and size of Ti（AlSi）3 phase were sensitive to the Ti content（before brazing） and Si content（after brazing）.

Microstructure and properties of Cu/Al joints brazed with Zn-Al filler metals

The mechanical properties and microstructural distribution of the Cu/A1 brazing joints formed by torch-brazing with different Zn-A1 filler metals were investigated. The microstructure of the Zn-A1 alloys was studied by optical microscopy and scanning electron microscopy, and the phase constitution of the Cu/A1 joints was analyzed by energy dispersion spectrometry. The results show that the spreading area of the Zn-A1 filler metals on the Cu and A1 substrates increases as the A1 content increases. The mechanical results indicate that the shear strength reaches a peak value of 88 MPa when A1 and Cu are brazed with Zn-15AI filler metal. Microhardness levels from HV122 to HV515 were produced in the three brazing seam regions corresponding to various microstructure features. The Zn- and Al-rich phases exist in the middle brazing seam regions. However, two interface layers, CuZn3 and A12Cu are formed on the Cu side when the A1 content in the filler metals is 2% and more than 15%, respectively. The relationship between intermetallic compounds on Cu side and Zn-xA1 filler metals was investigated.

EFFECTS OF BRAZING ATMOSPHERES ON INTERFACIAL MICROSTRUCTURE BETWEEN DIAMOND GRITS AND BRAZING ALLOY

The samples of brazed diamond grits with NiCr brazing alloy are prepared in vacuum and argon gas. The microstructures are analyzed with scanning electron microscope （SEM）, energy dispersive X-ray spectroscopy （EDS） and X-ray diffraction（XRD）. The effects of brazing atmospheres on the as-brazed NiCr brazing alloy composite structures and interracial microstructure are studied between diamond grits and brazing alloy. Results show that： （1） There are different composite structures of as-brazed NiCr brazing alloy under different oxygen partial pressures in vacuum and argon gas. B203 exists on the surface of the brazed samples under argon gas furnace brazing. It indicates that oxygen plays an important role in the resultants of as-brazed NiCr brazing alloy during the brazing process. （2） There are different interfacial microstructures in different brazing atmospheres, but the main reaction product is chromium carbides. The chromium carbides in argon gas furnace brazing grow in a disordered form, but those in vacuum furnace brazing grow radiated. And the scale of grains in argon gas is smaller than those in vacuum.

Effects of germanium additions on microstructures and properties of Al-Si filler metals for brazing aluminum

A series of Al?Si?Ge filler metals were studied for brazing aluminum. The microstructures and properties of the filler metals were investigated systematically. The results show that the liquidus temperature of Al?Si?Ge filler metals drops from 592 to 519 °C as the content of Ge increases from 0 to 30% (mass fraction). As the content of Ge increases, bright eutectic Ge forms. However, as the Ge content exceeds 20%, the aggregation growth of the eutectic structure tends to happen and coarsened primary Si?Ge particle forms, which is detrimental to the properties of alloys. The Al?10.8Si?10Ge filler metal has good processability and wettability with the base metal Al. When this filler metal is used to braze 1060 aluminum, the complete joint can be achieved. Furthermore, the shear strength test results show that the fracture of brazed joint with Al?10.8Si?10Ge filler metal occurs in the base metal.

向NI-Cr合金中添加Ni/C制备自润滑金刚石工具（英文）

利用添加3%、5%的Ni-Cr合金在保护气氛炉中制备金刚石试样,钎焊温度为1 050℃,保温5 min。采用扫描电镜分析钎焊金刚石形貌和钎缝的微观组织,维氏硬度计测量接头的硬度。结果表明:添加Ni/C的Ni-Cr合金对金刚石具有较好的润湿性,可以实现高强度连接,碳化物在金刚石表面形核和结晶长大,与金刚石表面的原子分布具有一定位向关系。钎缝中形成的空心Cr7C3和簇状共晶石墨与添加的Ni/C有关,钎焊层中有少量Ni/C剩余,硬度从830HV0.2降低到700HV0.2,这有利于降低钎焊热应力和金刚石后期的出露高度。

Microstructure evolution and mechanical properties of ultrasonic-assisted soldering joints of 2024 aluminum alloys

Ultrasonic-assisted soldering of 2024 aluminum alloys using a filler metal of Zn-5Al alloy was investigated at the temperature of 400 ℃,which is lower than the solution strengthening temperature of Al-Cu alloys.The ultrasonic vibration with power of 200 W and vibration amplitude of 15 μm at the frequency of 21 kHz was applied on the top samples.The ultrasonic vibration promoted the dissolution of Al elements in the base metal.The reduction of volume fraction of the eutectic phases in the bonds was investigated by increasing ultrasonic vibration time.As the ultrasonic vibration time increased from 3 s to 30 s,the volume fraction of the eutectic phase in the bonds decreased from 12.9% to 0.9%,and the shear strength of the joints was up to 149-153 MPa,increased by 20%.The improvement of the mechanical properties of joints was discussed based on the modulus and hardness of the phases in the bonds and the fracture of the joints.

Microstructures of brazing zone between titanium alloy and stainless steel using various filler metals

Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Filler metals were titanium based 40Ti-20Zr-20Cu-20Ni,silver based Ag 5Pd,and nickel based Ni-7Cr-3.1B-4.5Si-3Fe-0.06C (BNi2) and Ni-14Cr-10P-0.06C (BNi7).To select a good filler metal for brazing process,wetting test was performed at 880-1050 °C.It was not brazed using silver based filler metals,but at the conditions using titanium and nickel based filler metals had brazed zone between titanium alloy and stainless steel.However,titanium alloy was eroded during brazing using titanium based filler metals.Nickel based filler metal has a good brazed zone between titanium alloy and stainless steel among the filler metals.