Surface modification of poly [1-(trimethylsilyl)-1-propyne] (PTMSP) membranes bybromine vapor has been studied. It is shown that Br/C atomic ratio at the surfaces increased withthe time of bromination until about 60 m...Surface modification of poly [1-(trimethylsilyl)-1-propyne] (PTMSP) membranes bybromine vapor has been studied. It is shown that Br/C atomic ratio at the surfaces increased withthe time of bromination until about 60 min, then it reached a plateau. The results of XPS and IRstudies indicated that the addition of bromine to double bonds and the replacement of H on CH_3 bybromine had taken place so that a new peak at 286.0 eV (C--Br)in C_(1s) spectra and some newbands, e. g. at 1220 and 580cm^(-1) in IR spectra were formed. The fact,t Po_2, permeability ofoxygen, decreased and α_(O_2/N_2), separation factor of oxygen relative to nitrogen, increased withbromination time, shows that surface modification of PTMSP by bromine may be an efficient approach to prepare PTMSP membranes used for practical gas separations.展开更多
基金The project is supported by the National Natural Science Foundation of China
文摘Surface modification of poly [1-(trimethylsilyl)-1-propyne] (PTMSP) membranes bybromine vapor has been studied. It is shown that Br/C atomic ratio at the surfaces increased withthe time of bromination until about 60 min, then it reached a plateau. The results of XPS and IRstudies indicated that the addition of bromine to double bonds and the replacement of H on CH_3 bybromine had taken place so that a new peak at 286.0 eV (C--Br)in C_(1s) spectra and some newbands, e. g. at 1220 and 580cm^(-1) in IR spectra were formed. The fact,t Po_2, permeability ofoxygen, decreased and α_(O_2/N_2), separation factor of oxygen relative to nitrogen, increased withbromination time, shows that surface modification of PTMSP by bromine may be an efficient approach to prepare PTMSP membranes used for practical gas separations.