Commercial high purity corundum brick,corundum-mullite brick,mullite brick,calcium hexaaluminate brick and calcium hexaaluminate-corundum brick were studied to investigate their reaction state and alkali vapor corrosi...Commercial high purity corundum brick,corundum-mullite brick,mullite brick,calcium hexaaluminate brick and calcium hexaaluminate-corundum brick were studied to investigate their reaction state and alkali vapor corrosion mechanism at 1370 and 1500℃.The results show that:(1)served in hot alkali vapor,the high-purity corundum brick has no obvious slag layer but expands dramatically;(2)the corundum-mullite brick shows obvious reactive expansion at 1370℃and melting corrosion happens at 1500℃;(3)at 1370℃alkali vapor and mullite brick react and form a slag layer without volume effect;when the temperature increases to 1500℃,the reaction melting corrosion intensifies;(4)the calcium hexaaluminate brick and the calcium hexaaluminate-corundum brick form a thin slag layer in alkali vapor,and the sample surface absorbs Na+to form a dense layer with small volume effect.展开更多
文摘Commercial high purity corundum brick,corundum-mullite brick,mullite brick,calcium hexaaluminate brick and calcium hexaaluminate-corundum brick were studied to investigate their reaction state and alkali vapor corrosion mechanism at 1370 and 1500℃.The results show that:(1)served in hot alkali vapor,the high-purity corundum brick has no obvious slag layer but expands dramatically;(2)the corundum-mullite brick shows obvious reactive expansion at 1370℃and melting corrosion happens at 1500℃;(3)at 1370℃alkali vapor and mullite brick react and form a slag layer without volume effect;when the temperature increases to 1500℃,the reaction melting corrosion intensifies;(4)the calcium hexaaluminate brick and the calcium hexaaluminate-corundum brick form a thin slag layer in alkali vapor,and the sample surface absorbs Na+to form a dense layer with small volume effect.