Effect of CuO on the Formation Mechanism of Calcium Sulphoaluminate

Calcium sulphoaluminate was prepared with chemical reagents in this paper. The formation mechanism of calcium sulphoaluminate and effect of CuO on the formation mechanism of calcium sulphoaluminate were investigated by the chemical analysis, X-ray diffraction （XRD）, and differential scanning calorimetry （DSC）. The results show that there are three ways in the formation of calcium sulphoaluminate. CuO can promote the decomposition of calcium carbonate and decrease the formation temperature of calcium sulphoaluminate（C4A3S）. When the burning temperature is below 1 000 ℃, the addition of CuO can promote the formation of calcium sulphoaluminate, while CuO can not favor the formation of calcium sulphoaluminate above 1 000 ℃.

Thermodynamics and Kinetics of Calcium Sulphoaluminate

The formation process of calcium suphoaluminate（C4A3S） was investigated by the X-ray diffraction technique and then the thermodynamics was analyzed, finally the kinetics of which was studied by SC-132. XRD results show that the formation of C4A3S is accomplished in three different kinds of ways： one is by solid reaction of Ca （OH）2/ CaO, Al2O3 and CaSO4, other two ways are through such interstitial products as CaO·Al2O3 and CaO·2Al2O3. The formation thermodynamics shows that C4A3S begins to form at 900 ℃-1 000 ℃ and increases as temperature rising; the quantity of reaches the highest at 1 300 ℃-1 350 ℃ and then falls at 〉1350℃. Kinetics study shows that the formation rate of C4A3S can be described as first-order kinetics at high temperature, and it belongs to the random nucleation growth mechanism. The apparent activation energy is 456.37 kJ·mol-1 and pre-exponential factor is 1.545×1012.

Effect of Barium Oxide on the Formation and Coexistence of Tricalcium Silicate and Calcium Sulphoaluminate

Formation and coexistence of tricalciurn silicate （C3S） and calcium sulphoaluminate （ C4 A3S^- ） minerals in Portland cement clinker containing calcium sulphoaluminate were investigated. Thef-CaO content, mineral composite and formation of mineral in the clinker were analyzed respectively by chemical analysis, differential scanning calorimetry（DSC） and X-ray diffraction. The results show that, adding a suitable amount of BaO can improve the burnability of raw meal and promote the f-CaO absorption. Tricalcium silicate and calcium sulphoaluminate minerals can form and coexist in clinkers at 1 234-1 317 ℃ by the addition of BaO to the raw meal. A suitable amount of BaO expanded the coexistence temperature of two minerals by 58 ℃.

Effects of LiAl-Layered Double Hydroxides on Early Hydration of Calcium Sulphoaluminate Cement Paste

As a 3D micro-nano material, layered double hydroxides have been widely used in many fields, especially for reinforced composite materials. In this paper, Li Al-LDHs was obtained by a hydrothermal method. In order to investigate the effects of Li Al-LDHs on the early hydration of calcium sulphoaluminate（CSA） cement paste, compressive strength, setting time and hydration heat were tested while X-ray diffraction（XRD）, Fourier transform infrared spectroscopy（FT-IR）, scaning electron microscopy（SEM） and differential scanning calorimetry（DSC） analysis were employed. The results indicated that Li Al-LDHs could significantly improve the early compressive strength and shorten the setting time of calcium sulphoaluminate cement paste with 3 wt% concentration. Besides, the hydration exothermic rate within 5h was accelerated with increasing Li Al-LDHs content. Moreover, the addition of Li Al-LDHs did not result in the formation of a new phase, but increased the quantity of hydration products providing higher compressive strength, shorter setting time and denser microstructure.

Durability of Alite-calcium Barium Sulphoaluminate Cement

The durability of the cement was mainly studied. Under 1.0 MPa of hydraulic pressure for 8 hours, water could penetrate completely through the sample made by portland cement, but could not penetrate through that by alite-barium sulphoaluminate cement. Under the condition of freezing and thawing cycle, the loss ratio of compressive strength of the cement was only about 17.3% at curing 28 d ages, but the loss of portland cement was as high as 29.5%. Alite-calcium barium sulphoaluminate cement also has an excellent resistance to sulfate attack. The coefficients of resistance to sulfate attack of the cement exceeded 1.0. Meanwhile, the composition and microstructure of the hardened paste of alite-calcium barium sulphoaluminate cement were analyzed by XRD and SEM.