Dissolution Equilibrium of Calcium Vapor in Liquid Iron

The dissolution equilibrium of calcium vapor in liquid iron was carried out at 1873 K in a two-temperature zone furnace by using vapor pressure method.A sealed Mo reaction chamber and a self-made CaO crucible were used in this experiment.The thermodynamic parameters obtained are as follows for reaction Ca(g) =[Ca]\nK = 4.27-15040/T△G^0 = 125000-35.5T J/mol The relation between dissolved amount of calcium in liquid iron(1873K) and calcium vapor pressure is expressed as[%Ca]= 0.028 pc.

铁水用金属镁脱硫的热力学分析

计算分析了镁在铁液中汽化、溶解的热力学行为和镁一硫反应的平衡及其影响因素。

铁液中钙蒸气溶解平衡的研究

利用气一液平衡法，在双恒温带钼丝炉及密封钼反应室内，进行了铁液中钙蒸气溶解平衡的研究，得到反应式Ｃａ＿（ｇ）＝［Ｃａ］的溶解平衡常数及标准溶解自由能分别为１ｎＫ＝４．２７－１５０４０／ＴΔＧ￣０＝１２５０００－３５．５ＴＪ／ｍｏｌ１８７３Ｋ下铁液中钙溶解量与钙饱和蒸气压关系为［％Ｃａ］＝０．

金属钙对铁水脱硫的热力学计算和工艺

研究了金属钙在铁水中的蒸发和溶解及对铁水脱硫反应的热力学。提出了脱硫机理和工艺。

脱硫剂对含铌铁液脱硫效果的影响

应用镁、钙基脱硫剂在真空碳管炉内进行含铌铁液脱硫实验,分析对比了不同脱硫剂的脱硫效果,并用Factsage软件进行脱硫热力学计算。结果表明:通过热力学计算镁的脱硫率高于Ca-Si合金、Al-Ca合金和50%CaO-30%Al_2O_3-20%MgO的脱硫率;实验表明了镁中加入CaO能显著提高镁的脱硫效果,Mg+CaO和铝钙脱硫时在铁液中形成形态不同的夹杂物。

强酸性偶氮染料废液的处理工艺

以强酸性红色偶氮染料废液为处理对象,在强酸介质中采用零价铁降解偶氮染料并用碳酸钙中和强酸。探究了降解时间、pH、铁粉的用量对偶氮染料去除率的影响及碳酸钙的用量对强酸中和效果的影响。研究结果表明:当反应时间为30 min,pH值为1.5,零价铁用量为8.0 g/L及碳酸钙用量为5.0 g/L时,红色偶氮染料的去除率为99.2%,废液中强酸可以被有效中和。