Carbide formation in austempered ductile iron (ADI) alloyed with Ni and Cu has been studied by use of TEM. The results show that η carbide precipitates in the bainitic ferrite when austempered at 350℃.for 6h, but no...Carbide formation in austempered ductile iron (ADI) alloyed with Ni and Cu has been studied by use of TEM. The results show that η carbide precipitates in the bainitic ferrite when austempered at 350℃.for 6h, but no carbide was found at the austenite/.ferrite interfaces. When austempered at 300℃, two kinds of. s carbides appear in the bainitic ferrite when austempering time reached I h, and X carbide also precipitates at the austenite /ferrite interfaces when austempering time was extended up to 6h. The bainitic. ferrite and the retained austenite follow the Nishiyama- Wasserman relationship,展开更多
Austempered ductile iron(ADI)is composed of an ausferritic matrix with graphite nodules and has a wide range of applications because of its high mechanical strength,fatigue resistance,and wear resistance compared to o...Austempered ductile iron(ADI)is composed of an ausferritic matrix with graphite nodules and has a wide range of applications because of its high mechanical strength,fatigue resistance,and wear resistance compared to other cast irons.The amount and size of the nodules can be controlled by the chemical composition and austenitizing temperature.As the nodules have lower stiffness than the matrix and can act as stress concentrators,they influence crack propagation.However,the crack propagation mechanism in ADI is not yet fully understood.In this study,we describe a numerical investigation of crack propagation in ADIs subjected to cyclic loading.The numerical model used to calculate the stress intensity factors in the material under the given conditions is built with the aid of Abaqus commercial finite element code.The crack propagation routine,which is based on the Paris law,is implemented in Python.The results of the simulation show that the presence of a nodule generates a shear load on the crack tip.Consequently,even under uniaxial tensile loading,the presence of the nodule yields a non-zero stress intensity factor in mode II,resulting in a deviation in the crack propagation path.This is the primary factor responsible for changing the crack propagation direction towards the nodule.Modifying the parameters,for example,increasing the nodule size or decreasing the distance between the nodule and crack tip,can intensify this effect.In simulations comparing two different ADIs with the same graphite fraction area,the crack in the material with more nodules reaches another nodule in a shorter propagation time(or shorter number of cycles).This suggests that the high fatigue resistance observed in ADIs may be correlated with the number of nodules intercepted by a crack and the additional energy required to nucleate new cracks.In summary,these findings contribute to a better understanding of crack propagation in ADIs,provide insights into the relationship between the presence of nodules and the fatigue resistance of these materials,and support studies that associate the increased fatigue resistance with a higher number of graphite nodules.These results can also help justify the enhanced fatigue resistance of ADIs when compared to other cast irons.展开更多
The fast cooling rate of thin ductile iron castings requires special consideration to produce carbide-free castings. Extraordinary care was taken to select the charge to produce castings of 100-mm long round bars with...The fast cooling rate of thin ductile iron castings requires special consideration to produce carbide-free castings. Extraordinary care was taken to select the charge to produce castings of 100-mm long round bars with 16-mm diameter. The castings show the presence of carbides in the bars. Seven melts were made with different temperatures and with different compositions to get rid of carbides. After chemical analyses,it was found that the extra purity of the charge with less than 0.008wt% sulfur in the castings was the cause of carbides. To remove the carbides from the castings,sulfur should be added to the charge.展开更多
The wear resistances of austempered ductile iron (ADI) were improved through intxoduction of a new phase (carbide) into the ma- txix by addition of chromium. In the present investigation, low-caxbon-equivalent duc...The wear resistances of austempered ductile iron (ADI) were improved through intxoduction of a new phase (carbide) into the ma- txix by addition of chromium. In the present investigation, low-caxbon-equivalent ductile iron (LCEDI) (CE = 3.06%, and CE represents cax- bon-equivalent) with 2.42% chromium was selected. LCEDI was austeintized at two difl'erent temperatures (900 and 975~C) a^ld soaked for 1 h and then quenched in a salt bath at 325~C for 0 to 10 h. Samples were analyzed using optical microscopy and X-ray diffraction. Wear tests were carded out on a pin-on-disk-type machine. The efl'ect of austenization temperature on the wear resistance, impact strength, and the mi- crostructure was evaluated. A stxucture-property correlation based on the observations is established.展开更多
The formation mechanism of the spheroidal carbide in the ultra-low carbon ductile cast iron fabricated by the metal mold casting technique was systematically investigated. The results demonstrated that the spheroidal ...The formation mechanism of the spheroidal carbide in the ultra-low carbon ductile cast iron fabricated by the metal mold casting technique was systematically investigated. The results demonstrated that the spheroidal carbide belonged to eutectic carbide and crystallized in the isolated eutectic liquid phase area. The formation process of the spheroidal carbide was related to the contact and the intersection between the primary dendrite and the secondary dendrite of austenite. The oxides of magnesium, rare earths and other elements can act as heterogeneous nucleation sites for the spheroidal carbide. It was also found that the amount of the spheroidal carbide would increase with an increase in carbon content. The cooling rate has an important influence on the spheroidal carbide under the same chemical composition condition.展开更多
The aim of present work is to investigate the influencing factors on mechanical property stability of Cu-Mo-Ni alloyed austempered ductile iron (ADI). The results show that after austenitized at 900℃ for 2 h follow...The aim of present work is to investigate the influencing factors on mechanical property stability of Cu-Mo-Ni alloyed austempered ductile iron (ADI). The results show that after austenitized at 900℃ for 2 h followed by austempered at 370℃for another 2 h, the mechanical property of the alloyed ADI can reach the Germanite GGG-100 standard, i.e. σb≮1000 MPa,δ≮5%, at 95% confidence level. And the satisfactory mechanical properties were obtained when the alloyed ADI was austenitized at 850℃ to 1 000 ℃ for 1-4 h, and austempered at 355℃ to 400℃ for another 1 h to 4 h. The microstructures, including nodule number, white bright zone content (martensite-containing interdendritic segregation zone) and retained austenite content, can significantly influence the mechanical properties of the ADI. In order to obtain the good combinations of strength and ductility, the volume fraction of white bright zone should he less than 5%, and the retained austenite contents maintain hetween 30 % and 40%. The application of inoculation techniques to increase graphite nodule number can effectively reduce the white bright zone content in the structure.展开更多
Austempered ductile iron(ADI) parts have a unique combination of high strength and toughness with excellent design flexibility and low cost. These excellent properties are directly related to its microstructure called...Austempered ductile iron(ADI) parts have a unique combination of high strength and toughness with excellent design flexibility and low cost. These excellent properties are directly related to its microstructure called "ausferrite" that is the result of austempering heat treatment applied to ductile irons. Alloying elements increase ADI austemperability and change speeds of austempering reactions. Thus, they can affect ADI resultant microstructure and mechanical properties. In this paper, the effects of alloying elements on ADI mechanical properties, microstructural changes, two-stage austempering reactions, processing windows, austemperability, and other aspects are reviewed.展开更多
This paper presents the effects of chemical compositions of austempered ductile iron(ADI)on casting quality,heat treatment process parameters and mechanical properties of final products.Through experiment and producti...This paper presents the effects of chemical compositions of austempered ductile iron(ADI)on casting quality,heat treatment process parameters and mechanical properties of final products.Through experiment and production practice,the impacts of carbon equivalent on ADI and its mechanical properties have been studied. Proper content ranges for carbon and silicon have been obtained to avoid ADI casting shrinkage and graphite floatation,as well as to achieve the optimal mechanical properties.According to the impact of silicon content on austenite phase transformation,the existing form of carbon in ADI has been analyzed,and also the formula and diagram showing the relationship between austenitizing temperature and carbon content in austenite have been deduced.The chemical composition range for high performance ADI and its control points have been recommended, to serve as a reference for production process.展开更多
Measurements of dry sliding wear are presented for ductile irons with composition Fe-3.56C-2.67Si-0.25Mo-0.5Cu and Ni contents of 0.8 and 1.5 in wt.% with applied loads of 50, 100 and 150 N for austempering temperatur...Measurements of dry sliding wear are presented for ductile irons with composition Fe-3.56C-2.67Si-0.25Mo-0.5Cu and Ni contents of 0.8 and 1.5 in wt.% with applied loads of 50, 100 and 150 N for austempering temperatures of 270, 320, and 370 °C after austenitizing at 870 °C for 120 min. The mechanical property measurements show that the grades of the ASTM 897M: 1990 Standard can be satisfied for the selected austempering conditions. The results show that wear resistance is independent of austempering temperature with an applied load of 50 N, but there is a strong dependence at higher austempering temperatures with applied loads of 100 and 150 N. Observations indicate that wear is due to subsurface fatigue with cracks nucleated at deformed graphite nodules.展开更多
Effects of graphite nodule diameter on the water embrittlement of austempered ductile iron (ADI) is studied. The water embrittlement mechanism is discussed. Due to water adhesion, local embrittlement occurs on the sur...Effects of graphite nodule diameter on the water embrittlement of austempered ductile iron (ADI) is studied. The water embrittlement mechanism is discussed. Due to water adhesion, local embrittlement occurs on the surface of ADI specimen, resulting in early fracture and significant reduction in tensile strength and elongation. The water embrittlement is the cracking of stress induced martensite formed during tensile deformation caused by hydrogen diffusion decomposed from water and as a result tensile strength and elongation of ADI are remarkably reduced. The segregation of alloying elements in ductile iron is weakened with decreasing nodule diameter, reducing the residual austenite in grain boundaries, then decreasing the amount of stress induced martensite during tensile plastic deformation and finally restraining ADI water embrittlement.展开更多
The erosion behavior of austempered ductile irons austenized at different temperatures was studied. The results indicate that the erosion rate well correlates with the mechanical properties. At high impact angles, inc...The erosion behavior of austempered ductile irons austenized at different temperatures was studied. The results indicate that the erosion rate well correlates with the mechanical properties. At high impact angles, increasing ductility and mechanical energy density results in decreasing erosion rate, whereas increasing hardness reduces the erosion rate at low impact angles. 2008 University of Science and Technology Beijing. All rights reserved.展开更多
The Impact toughness and fracture toughness of Austempered Ductile Iron (ADI) are described. The notched and un-notched Charpy impact toughness of ADI at room temperature are somewhat lower than that of steel castings...The Impact toughness and fracture toughness of Austempered Ductile Iron (ADI) are described. The notched and un-notched Charpy impact toughness of ADI at room temperature are somewhat lower than that of steel castings or forged steel pieces, however, they are approximately three times higher than that of normal pearlitic ductile iron. The impact toughness of ADI decreases with decreasing temperature; but at-40℃ it still maintains about 70% of the value at room temperature. The properties of fracture toughness are important in safety design and failure analysis. In this study all fracture toughness data of ADI are higher than that of conventional ductile iron, and are equivalent to or better than that of steel castings or forged steel pieces with the tensile strength equivalent to ADI.展开更多
Shot peening is one of the most common surface treatments to improve the fatigue behavior of metallic parts. In this study the effect of shot peening process on the fatigue behavior of an alloyed austempered ductile i...Shot peening is one of the most common surface treatments to improve the fatigue behavior of metallic parts. In this study the effect of shot peening process on the fatigue behavior of an alloyed austempered ductile iron (ADI) has been studied. Austempering heat treatment consisted of austenitizing at 875℃ for 90 min followed by austempering at three different temperatures of 320, 365 and 400℃. Rotating-bending fatigue test was carried out on samples after shot peening by 0.4-0.6 mm shots. XRD and SEM analysis, micro hardness and roughness tests were carried out to study the fatigue behavior of the samples. Results indicate that the fatigue strengths of samples austempered at 320, 365 and 400℃ are increased by 27.3%, 33.3% and 48.4%, respectively, after shot peening process.展开更多
The effect of sub-zero cooling on microstructure and mechanical properties of a low alloyed austempered ductile iron has been investigated. Austempering of samples was performed at 325℃and 400℃after austenitizing at...The effect of sub-zero cooling on microstructure and mechanical properties of a low alloyed austempered ductile iron has been investigated. Austempering of samples was performed at 325℃and 400℃after austenitizing at 875℃and 950℃. The sub-zero treatments were carried out by cooling down the samples to -30℃, -70℃and -196℃. The changes in volume fraction of austenite and mechanical properties were determined after cooling to each temperature. The austenite volume fraction of samples which were austenitized at 875℃and austempered at 325℃remained unchanged, whilst it reduced in samples austenitized at 950℃and 875℃for austempering temperature of 400℃. In these specimens, some austenite transformed to martensite after subzero cooling. Mechanical property measurements showed a slight increase in strength and hardness and decrease in elongation and toughness due to this transformation behavior.展开更多
This study focused on the development of austempered ductile iron(ADI)with desirable combination of mechanical properties for crankshaft applications by the combined effect of vanadium(V)alloying and an optimized heat...This study focused on the development of austempered ductile iron(ADI)with desirable combination of mechanical properties for crankshaft applications by the combined effect of vanadium(V)alloying and an optimized heat treatment process.The produced unalloyed GGG60,0.15%V-alloyed GGG60(V-15),and 0.30%V-alloyed GGG60 samples were subjected to austenitizing at 900℃for 1 h and subsequent austempering processes at 250,300,and 350℃for 15,30,60,90,and 180 min.As a result of these austempering processes,different bainitic structures were obtained,which led to the formation of diverse combinations of mechanical properties.The mechanical properties of the austempered samples were tested comprehensively,and the results were correlated with their microstructures and the stability of the retained austenite phases.From the microstructural observations,the V-alloyed samples exhibited a finer microstructure and a more acicular ferrite phase than unalloyed samples.The V addition delayed the coarsening of the acicular ferrite structures and considerably contributed to the improvement of the mechanical properties of GGG60.Moreover,the X-ray diffraction results revealed that the retained austenite volume and the carbon enrichment of austenite phases in ADI samples were remarkably affected by the addition of vanadium.The increase in volume fraction of retained austenite and its carbon content provided favorable ductility and toughness to V-15,as confirmed by the elongation and impact test results.Consequently,the dual-phase ausferrite microstructure of V-15 that was austempered at 300℃for 60 min exhibited high strength with substantial ductility and toughness for crankshaft applications.展开更多
In the present research, the orthogonal experiment was carried out to investigate the influence of different austempering process parameters(i.e. austenitizing temperature and time, and austempering temperature and ti...In the present research, the orthogonal experiment was carried out to investigate the influence of different austempering process parameters(i.e. austenitizing temperature and time, and austempering temperature and time) on microstructure and mechanical properties of LZQT500-7 ductile iron dense bars with 172 mm in diameter which were produced by horizontal continuous casting(HCC). The results show that the major factors influencing the hardness of austempered ductile iron(ADI) are austenitizing temperature and austempering temperature. The fraction of retained austenite increases as the austenitizing and austempering temperatures increase. When austenitizing temperature is low, acicular ferrite and retained austenite can be effi ciently obtained by appropriately extending the austenitizing time. The proper austmepering time could ensure enough stability of retained austenite and prevent high carbon austenite decomposition. The optimal mechanical properties of ADI can be achieved with the following process parameters: austenitizing temperature and time are 866 °C and 135 min, and austempering temperature and time are 279 °C and 135 min, respectively. The microstructure of ADI under the optimal austempering process consists of fi ne acicular ferrite and a small amount of retained austenite, and the hardness, tensile strength, yield strength, elongation and impact toughness of the bars are HBW 476, 1670 MPa, 1428 MPa, 2.93% and 25.7 J, respectively.展开更多
The equilibrium partition ratio, k, has been measured for Mn, Mo, Si, Ni and Cu in a ductile iron with composition(wt.%): 3.45 C, 0.25 Mn, 0.25 Mo, 2.45 Si, 0.5Ni and 0.5Cu with different nodule counts obtained from d...The equilibrium partition ratio, k, has been measured for Mn, Mo, Si, Ni and Cu in a ductile iron with composition(wt.%): 3.45 C, 0.25 Mn, 0.25 Mo, 2.45 Si, 0.5Ni and 0.5Cu with different nodule counts obtained from different section sizes of13, 25, 75 mm in the as cast, austenitized(at 870 °C for times 1, 4 and 6 hours) and austempered(at 375 °C for times 1 to 1,440 min) samples. Results show that Mn and Mo segregate positively at cell boundaries, but Si, Ni and Cu concentrate in an inverse manner in the vicinity ofgraphite nodules and there is a depletion ofthese elements at cell boundaries. Segregation curves for Ni and Cu are more smooth than for Si. Carbide formation has been observed at cell boundaries. Based on the results, the partition ratios for all elements decrease with increasing the nodule count. More carbide with coarser morphology has been observed in the microstructure with a lower nodule count. Austenitization for a longer time can decrease partition ratio, but cannot eliminate it entirely. Increasing the austenitization temperature has the same effect. Austenitizing parameters have no significant effect on carbides volume fraction. The kinetics ofaustempering is faster in higher nodule counts and subsequently better mechanical properties including higher ductility, strength and toughness have been observed for all austempering conditions studied.展开更多
The effect of Ca,Ba,Bi and Al on the amount of carbide in ductile iron weld metal,the microstructural characteristics of ADI weld metal and the effect of heat treatment process on the microstructure and mechanical pro...The effect of Ca,Ba,Bi and Al on the amount of carbide in ductile iron weld metal,the microstructural characteristics of ADI weld metal and the effect of heat treatment process on the microstructure and mechanical properties of ADI weld metal have been studied.On this basis the optimum composition of weld and the optimum heat treatment process of ADI weld metal were de- termined and a new electrode for arc cold-welding (i.e.,without preheat) of ADI was developed.The ductile iron welded joint free from eutectic carbide can be produced by using this electrode before austempering and the weld metal obtained after austempering has a microstructure and mechanical properties similar to those of ADI.The mechanical properties of welded joints can match the require- ment of ADI.展开更多
This paper describes a study of the effects of graphite nodule characteristics on a subsurface crack in austempered ductile iron(ADI).A representative specimen of ADI,subjected to sliding contact load,is modeled using...This paper describes a study of the effects of graphite nodule characteristics on a subsurface crack in austempered ductile iron(ADI).A representative specimen of ADI,subjected to sliding contact load,is modeled using finite elements aiming to obtain the shear stress intensity factor(KII).The parameters varied were(i)the nodule diameter(two different values were considered),(ii)the distance between the nodule and the tip of the crack and(iii)the position of the load relative to the tip of the crack.The results of the numerical simulations show that the smaller diameter nodule has a larger influence on KII,suggesting a higher contact fatigue crack propagation rate in the material with the smaller nodule.These results are the opposite of those observed in experimental studies and would appear to indicate that other factors should be also considered to ensure realistic estimates of the contact fatigue strength of ADI.展开更多
文摘Carbide formation in austempered ductile iron (ADI) alloyed with Ni and Cu has been studied by use of TEM. The results show that η carbide precipitates in the bainitic ferrite when austempered at 350℃.for 6h, but no carbide was found at the austenite/.ferrite interfaces. When austempered at 300℃, two kinds of. s carbides appear in the bainitic ferrite when austempering time reached I h, and X carbide also precipitates at the austenite /ferrite interfaces when austempering time was extended up to 6h. The bainitic. ferrite and the retained austenite follow the Nishiyama- Wasserman relationship,
文摘Austempered ductile iron(ADI)is composed of an ausferritic matrix with graphite nodules and has a wide range of applications because of its high mechanical strength,fatigue resistance,and wear resistance compared to other cast irons.The amount and size of the nodules can be controlled by the chemical composition and austenitizing temperature.As the nodules have lower stiffness than the matrix and can act as stress concentrators,they influence crack propagation.However,the crack propagation mechanism in ADI is not yet fully understood.In this study,we describe a numerical investigation of crack propagation in ADIs subjected to cyclic loading.The numerical model used to calculate the stress intensity factors in the material under the given conditions is built with the aid of Abaqus commercial finite element code.The crack propagation routine,which is based on the Paris law,is implemented in Python.The results of the simulation show that the presence of a nodule generates a shear load on the crack tip.Consequently,even under uniaxial tensile loading,the presence of the nodule yields a non-zero stress intensity factor in mode II,resulting in a deviation in the crack propagation path.This is the primary factor responsible for changing the crack propagation direction towards the nodule.Modifying the parameters,for example,increasing the nodule size or decreasing the distance between the nodule and crack tip,can intensify this effect.In simulations comparing two different ADIs with the same graphite fraction area,the crack in the material with more nodules reaches another nodule in a shorter propagation time(or shorter number of cycles).This suggests that the high fatigue resistance observed in ADIs may be correlated with the number of nodules intercepted by a crack and the additional energy required to nucleate new cracks.In summary,these findings contribute to a better understanding of crack propagation in ADIs,provide insights into the relationship between the presence of nodules and the fatigue resistance of these materials,and support studies that associate the increased fatigue resistance with a higher number of graphite nodules.These results can also help justify the enhanced fatigue resistance of ADIs when compared to other cast irons.
文摘The fast cooling rate of thin ductile iron castings requires special consideration to produce carbide-free castings. Extraordinary care was taken to select the charge to produce castings of 100-mm long round bars with 16-mm diameter. The castings show the presence of carbides in the bars. Seven melts were made with different temperatures and with different compositions to get rid of carbides. After chemical analyses,it was found that the extra purity of the charge with less than 0.008wt% sulfur in the castings was the cause of carbides. To remove the carbides from the castings,sulfur should be added to the charge.
文摘The wear resistances of austempered ductile iron (ADI) were improved through intxoduction of a new phase (carbide) into the ma- txix by addition of chromium. In the present investigation, low-caxbon-equivalent ductile iron (LCEDI) (CE = 3.06%, and CE represents cax- bon-equivalent) with 2.42% chromium was selected. LCEDI was austeintized at two difl'erent temperatures (900 and 975~C) a^ld soaked for 1 h and then quenched in a salt bath at 325~C for 0 to 10 h. Samples were analyzed using optical microscopy and X-ray diffraction. Wear tests were carded out on a pin-on-disk-type machine. The efl'ect of austenization temperature on the wear resistance, impact strength, and the mi- crostructure was evaluated. A stxucture-property correlation based on the observations is established.
基金financially supported by the Hebei Province Science and Technology Support Program(No.14211007D)
文摘The formation mechanism of the spheroidal carbide in the ultra-low carbon ductile cast iron fabricated by the metal mold casting technique was systematically investigated. The results demonstrated that the spheroidal carbide belonged to eutectic carbide and crystallized in the isolated eutectic liquid phase area. The formation process of the spheroidal carbide was related to the contact and the intersection between the primary dendrite and the secondary dendrite of austenite. The oxides of magnesium, rare earths and other elements can act as heterogeneous nucleation sites for the spheroidal carbide. It was also found that the amount of the spheroidal carbide would increase with an increase in carbon content. The cooling rate has an important influence on the spheroidal carbide under the same chemical composition condition.
文摘The aim of present work is to investigate the influencing factors on mechanical property stability of Cu-Mo-Ni alloyed austempered ductile iron (ADI). The results show that after austenitized at 900℃ for 2 h followed by austempered at 370℃for another 2 h, the mechanical property of the alloyed ADI can reach the Germanite GGG-100 standard, i.e. σb≮1000 MPa,δ≮5%, at 95% confidence level. And the satisfactory mechanical properties were obtained when the alloyed ADI was austenitized at 850℃ to 1 000 ℃ for 1-4 h, and austempered at 355℃ to 400℃ for another 1 h to 4 h. The microstructures, including nodule number, white bright zone content (martensite-containing interdendritic segregation zone) and retained austenite content, can significantly influence the mechanical properties of the ADI. In order to obtain the good combinations of strength and ductility, the volume fraction of white bright zone should he less than 5%, and the retained austenite contents maintain hetween 30 % and 40%. The application of inoculation techniques to increase graphite nodule number can effectively reduce the white bright zone content in the structure.
文摘Austempered ductile iron(ADI) parts have a unique combination of high strength and toughness with excellent design flexibility and low cost. These excellent properties are directly related to its microstructure called "ausferrite" that is the result of austempering heat treatment applied to ductile irons. Alloying elements increase ADI austemperability and change speeds of austempering reactions. Thus, they can affect ADI resultant microstructure and mechanical properties. In this paper, the effects of alloying elements on ADI mechanical properties, microstructural changes, two-stage austempering reactions, processing windows, austemperability, and other aspects are reviewed.
基金supported by the key project for Science and Technology of Hubei Provincial Department of Education(No.D20101606)the Scientific and Technological Project of China Textile Industry Association(No.2008085)
文摘This paper presents the effects of chemical compositions of austempered ductile iron(ADI)on casting quality,heat treatment process parameters and mechanical properties of final products.Through experiment and production practice,the impacts of carbon equivalent on ADI and its mechanical properties have been studied. Proper content ranges for carbon and silicon have been obtained to avoid ADI casting shrinkage and graphite floatation,as well as to achieve the optimal mechanical properties.According to the impact of silicon content on austenite phase transformation,the existing form of carbon in ADI has been analyzed,and also the formula and diagram showing the relationship between austenitizing temperature and carbon content in austenite have been deduced.The chemical composition range for high performance ADI and its control points have been recommended, to serve as a reference for production process.
基金the Sahand University of Technology for providing the research facilities and financial support
文摘Measurements of dry sliding wear are presented for ductile irons with composition Fe-3.56C-2.67Si-0.25Mo-0.5Cu and Ni contents of 0.8 and 1.5 in wt.% with applied loads of 50, 100 and 150 N for austempering temperatures of 270, 320, and 370 °C after austenitizing at 870 °C for 120 min. The mechanical property measurements show that the grades of the ASTM 897M: 1990 Standard can be satisfied for the selected austempering conditions. The results show that wear resistance is independent of austempering temperature with an applied load of 50 N, but there is a strong dependence at higher austempering temperatures with applied loads of 100 and 150 N. Observations indicate that wear is due to subsurface fatigue with cracks nucleated at deformed graphite nodules.
文摘Effects of graphite nodule diameter on the water embrittlement of austempered ductile iron (ADI) is studied. The water embrittlement mechanism is discussed. Due to water adhesion, local embrittlement occurs on the surface of ADI specimen, resulting in early fracture and significant reduction in tensile strength and elongation. The water embrittlement is the cracking of stress induced martensite formed during tensile deformation caused by hydrogen diffusion decomposed from water and as a result tensile strength and elongation of ADI are remarkably reduced. The segregation of alloying elements in ductile iron is weakened with decreasing nodule diameter, reducing the residual austenite in grain boundaries, then decreasing the amount of stress induced martensite during tensile plastic deformation and finally restraining ADI water embrittlement.
基金the National Science Council(No.NSC 93-2216-E-006-034).
文摘The erosion behavior of austempered ductile irons austenized at different temperatures was studied. The results indicate that the erosion rate well correlates with the mechanical properties. At high impact angles, increasing ductility and mechanical energy density results in decreasing erosion rate, whereas increasing hardness reduces the erosion rate at low impact angles. 2008 University of Science and Technology Beijing. All rights reserved.
文摘The Impact toughness and fracture toughness of Austempered Ductile Iron (ADI) are described. The notched and un-notched Charpy impact toughness of ADI at room temperature are somewhat lower than that of steel castings or forged steel pieces, however, they are approximately three times higher than that of normal pearlitic ductile iron. The impact toughness of ADI decreases with decreasing temperature; but at-40℃ it still maintains about 70% of the value at room temperature. The properties of fracture toughness are important in safety design and failure analysis. In this study all fracture toughness data of ADI are higher than that of conventional ductile iron, and are equivalent to or better than that of steel castings or forged steel pieces with the tensile strength equivalent to ADI.
基金supported financially by the research council of Sahand University of Technology
文摘Shot peening is one of the most common surface treatments to improve the fatigue behavior of metallic parts. In this study the effect of shot peening process on the fatigue behavior of an alloyed austempered ductile iron (ADI) has been studied. Austempering heat treatment consisted of austenitizing at 875℃ for 90 min followed by austempering at three different temperatures of 320, 365 and 400℃. Rotating-bending fatigue test was carried out on samples after shot peening by 0.4-0.6 mm shots. XRD and SEM analysis, micro hardness and roughness tests were carried out to study the fatigue behavior of the samples. Results indicate that the fatigue strengths of samples austempered at 320, 365 and 400℃ are increased by 27.3%, 33.3% and 48.4%, respectively, after shot peening process.
文摘The effect of sub-zero cooling on microstructure and mechanical properties of a low alloyed austempered ductile iron has been investigated. Austempering of samples was performed at 325℃and 400℃after austenitizing at 875℃and 950℃. The sub-zero treatments were carried out by cooling down the samples to -30℃, -70℃and -196℃. The changes in volume fraction of austenite and mechanical properties were determined after cooling to each temperature. The austenite volume fraction of samples which were austenitized at 875℃and austempered at 325℃remained unchanged, whilst it reduced in samples austenitized at 950℃and 875℃for austempering temperature of 400℃. In these specimens, some austenite transformed to martensite after subzero cooling. Mechanical property measurements showed a slight increase in strength and hardness and decrease in elongation and toughness due to this transformation behavior.
文摘This study focused on the development of austempered ductile iron(ADI)with desirable combination of mechanical properties for crankshaft applications by the combined effect of vanadium(V)alloying and an optimized heat treatment process.The produced unalloyed GGG60,0.15%V-alloyed GGG60(V-15),and 0.30%V-alloyed GGG60 samples were subjected to austenitizing at 900℃for 1 h and subsequent austempering processes at 250,300,and 350℃for 15,30,60,90,and 180 min.As a result of these austempering processes,different bainitic structures were obtained,which led to the formation of diverse combinations of mechanical properties.The mechanical properties of the austempered samples were tested comprehensively,and the results were correlated with their microstructures and the stability of the retained austenite phases.From the microstructural observations,the V-alloyed samples exhibited a finer microstructure and a more acicular ferrite phase than unalloyed samples.The V addition delayed the coarsening of the acicular ferrite structures and considerably contributed to the improvement of the mechanical properties of GGG60.Moreover,the X-ray diffraction results revealed that the retained austenite volume and the carbon enrichment of austenite phases in ADI samples were remarkably affected by the addition of vanadium.The increase in volume fraction of retained austenite and its carbon content provided favorable ductility and toughness to V-15,as confirmed by the elongation and impact test results.Consequently,the dual-phase ausferrite microstructure of V-15 that was austempered at 300℃for 60 min exhibited high strength with substantial ductility and toughness for crankshaft applications.
基金financially supported by the fund of the Key Projects of Shaanxi Provincial International Technology Cooperation Plan(2013KW16)the Scientific Research Program funded by Shaanxi Provincial Education Department(2013JK0914)+2 种基金the State Key Laboratory of Solidifi cation Processing in NWPU(SKLSP201115)the Scientific Research Project of Xi'an University of Technology(2013CX004)the fund of the Key Laboratory of Electrical Materials and Infi ltration Technology of Shaanxi Province,China(2014)
文摘In the present research, the orthogonal experiment was carried out to investigate the influence of different austempering process parameters(i.e. austenitizing temperature and time, and austempering temperature and time) on microstructure and mechanical properties of LZQT500-7 ductile iron dense bars with 172 mm in diameter which were produced by horizontal continuous casting(HCC). The results show that the major factors influencing the hardness of austempered ductile iron(ADI) are austenitizing temperature and austempering temperature. The fraction of retained austenite increases as the austenitizing and austempering temperatures increase. When austenitizing temperature is low, acicular ferrite and retained austenite can be effi ciently obtained by appropriately extending the austenitizing time. The proper austmepering time could ensure enough stability of retained austenite and prevent high carbon austenite decomposition. The optimal mechanical properties of ADI can be achieved with the following process parameters: austenitizing temperature and time are 866 °C and 135 min, and austempering temperature and time are 279 °C and 135 min, respectively. The microstructure of ADI under the optimal austempering process consists of fi ne acicular ferrite and a small amount of retained austenite, and the hardness, tensile strength, yield strength, elongation and impact toughness of the bars are HBW 476, 1670 MPa, 1428 MPa, 2.93% and 25.7 J, respectively.
基金the Sahand University of Technology for providing the research facilities and financial support
文摘The equilibrium partition ratio, k, has been measured for Mn, Mo, Si, Ni and Cu in a ductile iron with composition(wt.%): 3.45 C, 0.25 Mn, 0.25 Mo, 2.45 Si, 0.5Ni and 0.5Cu with different nodule counts obtained from different section sizes of13, 25, 75 mm in the as cast, austenitized(at 870 °C for times 1, 4 and 6 hours) and austempered(at 375 °C for times 1 to 1,440 min) samples. Results show that Mn and Mo segregate positively at cell boundaries, but Si, Ni and Cu concentrate in an inverse manner in the vicinity ofgraphite nodules and there is a depletion ofthese elements at cell boundaries. Segregation curves for Ni and Cu are more smooth than for Si. Carbide formation has been observed at cell boundaries. Based on the results, the partition ratios for all elements decrease with increasing the nodule count. More carbide with coarser morphology has been observed in the microstructure with a lower nodule count. Austenitization for a longer time can decrease partition ratio, but cannot eliminate it entirely. Increasing the austenitization temperature has the same effect. Austenitizing parameters have no significant effect on carbides volume fraction. The kinetics ofaustempering is faster in higher nodule counts and subsequently better mechanical properties including higher ductility, strength and toughness have been observed for all austempering conditions studied.
文摘The effect of Ca,Ba,Bi and Al on the amount of carbide in ductile iron weld metal,the microstructural characteristics of ADI weld metal and the effect of heat treatment process on the microstructure and mechanical properties of ADI weld metal have been studied.On this basis the optimum composition of weld and the optimum heat treatment process of ADI weld metal were de- termined and a new electrode for arc cold-welding (i.e.,without preheat) of ADI was developed.The ductile iron welded joint free from eutectic carbide can be produced by using this electrode before austempering and the weld metal obtained after austempering has a microstructure and mechanical properties similar to those of ADI.The mechanical properties of welded joints can match the require- ment of ADI.
文摘This paper describes a study of the effects of graphite nodule characteristics on a subsurface crack in austempered ductile iron(ADI).A representative specimen of ADI,subjected to sliding contact load,is modeled using finite elements aiming to obtain the shear stress intensity factor(KII).The parameters varied were(i)the nodule diameter(two different values were considered),(ii)the distance between the nodule and the tip of the crack and(iii)the position of the load relative to the tip of the crack.The results of the numerical simulations show that the smaller diameter nodule has a larger influence on KII,suggesting a higher contact fatigue crack propagation rate in the material with the smaller nodule.These results are the opposite of those observed in experimental studies and would appear to indicate that other factors should be also considered to ensure realistic estimates of the contact fatigue strength of ADI.