The oxides Eu, Ho, Er and Dy were used to prepare the hydroxides of rare earth modified carbon black. Then natural rubber latex （NRL） was added into the reactor. The system reacted at 85 ℃ with stirring for 1 h to ...The oxides Eu, Ho, Er and Dy were used to prepare the hydroxides of rare earth modified carbon black. Then natural rubber latex （NRL） was added into the reactor. The system reacted at 85 ℃ with stirring for 1 h to prepare powdered HAF-Ln（OH）3/NR composites. The effects of the kind and content of Ln on the particle size distribution of P [ NR/HAF-Ln （OH）3 ] and mechanical properties of its vulcanizate were studied respectively. It is found that rare earth can help to get the powder of the composite, the product particle with a diameter less than 0.9mm will be get when the composites containing the compound of Ho, Er and Dy with dosage of 1.0, 1.0, O. 5 percent, respectively. The adding of Ln can improve the tensile strength and tear strength of the vulcanizate effectively, what＇s more, Er and Dy can decrease the permanent set of vulcanizate significantly. The SEM studies shows that P[ NR/HAF-Dy （OH）3 ] vulcanizate shows superior mechanical properties that depend primarily on the absence of free carbon black, the fine dispersion of carbon black in the rubber matrix and better polymer-filler interaction.展开更多
Natural rubber based composites containing different carbon nanofillers (fullerenes, carbon nanotubes (CNTs) and graphene nanoplatelets (GNPs)) at different concentrations have been prepared. Their dielectric properti...Natural rubber based composites containing different carbon nanofillers (fullerenes, carbon nanotubes (CNTs) and graphene nanoplatelets (GNPs)) at different concentrations have been prepared. Their dielectric properties (dielectric permittivity, dielectric loss) have been studied in the 1 - 12 GHz frequency range. Some factors (electromagnetic field frequency, fillers concentration, fillers intrinsic structure) influencing the dielectric behavior of the composites have been investigated. The dielectric properties of the developed natural rubber composites containing conductive fillers (fullerenes, CNTs, GNPs) indicate that these composites can be used as broadband microwave absorbing materials.展开更多
文摘The oxides Eu, Ho, Er and Dy were used to prepare the hydroxides of rare earth modified carbon black. Then natural rubber latex （NRL） was added into the reactor. The system reacted at 85 ℃ with stirring for 1 h to prepare powdered HAF-Ln（OH）3/NR composites. The effects of the kind and content of Ln on the particle size distribution of P [ NR/HAF-Ln （OH）3 ] and mechanical properties of its vulcanizate were studied respectively. It is found that rare earth can help to get the powder of the composite, the product particle with a diameter less than 0.9mm will be get when the composites containing the compound of Ho, Er and Dy with dosage of 1.0, 1.0, O. 5 percent, respectively. The adding of Ln can improve the tensile strength and tear strength of the vulcanizate effectively, what＇s more, Er and Dy can decrease the permanent set of vulcanizate significantly. The SEM studies shows that P[ NR/HAF-Dy （OH）3 ] vulcanizate shows superior mechanical properties that depend primarily on the absence of free carbon black, the fine dispersion of carbon black in the rubber matrix and better polymer-filler interaction.
文摘Natural rubber based composites containing different carbon nanofillers (fullerenes, carbon nanotubes (CNTs) and graphene nanoplatelets (GNPs)) at different concentrations have been prepared. Their dielectric properties (dielectric permittivity, dielectric loss) have been studied in the 1 - 12 GHz frequency range. Some factors (electromagnetic field frequency, fillers concentration, fillers intrinsic structure) influencing the dielectric behavior of the composites have been investigated. The dielectric properties of the developed natural rubber composites containing conductive fillers (fullerenes, CNTs, GNPs) indicate that these composites can be used as broadband microwave absorbing materials.
