The effect of HCO3^- concentration on CO2 corrosion was investigated by polarization measurement of potentiodynamic scans and weight-loss method, Under the conditions of high pressure and high temperature, the corrosi...The effect of HCO3^- concentration on CO2 corrosion was investigated by polarization measurement of potentiodynamic scans and weight-loss method, Under the conditions of high pressure and high temperature, the corrosion rate of steel X65 decreased with the increase of HCO3^- concentration, while pH of solution increased. SEM, EDS, and XRD results of the corrosion scales indir cated that the typical FeCO3 crystallite was found at low HCO3^- concentration but Ca（Fe,Mg）（CO3）2 was found at high HCO3^- con- centration. Ca^2＋ and Mg^2＋ are precipitated preferential to Fe^2＋ at high pH value. Potentiodynamic polarization curves showed that the cathodic current density decreases with the increase of HCO3^- concentration at low HCO3^- concentration. When the HCO3^- concentration reaches 0.126 mol/L, increasing HCO3^- concentration promotes cathodic reactions. Anodic behavior is an active process at low HCO3^- concentration and the anodic current density decreases with the increase of HCO3^- concentration. An evident active-passive behavior is exhibited in anodic process at 0.126 mol/L HCO3^-.展开更多
基金financially supported by the National Natural Science Foundation of China Key Program (No.50231020)the National Key Basic Research and Development Plan Program (No. G1999065004)
文摘The effect of HCO3^- concentration on CO2 corrosion was investigated by polarization measurement of potentiodynamic scans and weight-loss method, Under the conditions of high pressure and high temperature, the corrosion rate of steel X65 decreased with the increase of HCO3^- concentration, while pH of solution increased. SEM, EDS, and XRD results of the corrosion scales indir cated that the typical FeCO3 crystallite was found at low HCO3^- concentration but Ca（Fe,Mg）（CO3）2 was found at high HCO3^- con- centration. Ca^2＋ and Mg^2＋ are precipitated preferential to Fe^2＋ at high pH value. Potentiodynamic polarization curves showed that the cathodic current density decreases with the increase of HCO3^- concentration at low HCO3^- concentration. When the HCO3^- concentration reaches 0.126 mol/L, increasing HCO3^- concentration promotes cathodic reactions. Anodic behavior is an active process at low HCO3^- concentration and the anodic current density decreases with the increase of HCO3^- concentration. An evident active-passive behavior is exhibited in anodic process at 0.126 mol/L HCO3^-.