Polyacrylonitrile （PAN） based carbon fibers with different surface morphology were electrochemically treated in 3 wt% NH4HCO3 aqueous solution with current density up to 3.47 A/m 2 at room temperature, and surface s...Polyacrylonitrile （PAN） based carbon fibers with different surface morphology were electrochemically treated in 3 wt% NH4HCO3 aqueous solution with current density up to 3.47 A/m 2 at room temperature, and surface structures, surface morphology and residual mechanical properties were characterized. The crystallite size （La） of carbon fibers would be interrupted due to excessive electrochemical etching, while the crystallite spacing （d（002）） increased as increasing current density. The disordered structures on the surface of carbon fiber with rough surface increased at the initial oxidation stage and then removed by further electrochemical etching, which resulting in continuous increase of the extent of graphitization on the fiber surface. However, the electrochemical etching was beneficial to getting ordered morphology on the surface for carbon fiber with smooth surface, especially when the current density was lower than 1.77 A/m 2 . The tensile strength and tensile modulus could be improved by 17.27% and 5.75%, respectively, and was dependent of surface morphology. The decreasing density of carbon fibers probably resulted from the volume expansion of carbon fibers caused by the abundant oxygen functional groups intercalated between the adjacent graphite layers.展开更多
In this work, a simple, low cost and sensitive voltammetric sensor was developed for the simultaneous detection of lead （Pb2＋）, cadmium （Cd2＋）, and zinc （Zn2＋） ions based on a disposable carbon fiber rod （CF...In this work, a simple, low cost and sensitive voltammetric sensor was developed for the simultaneous detection of lead （Pb2＋）, cadmium （Cd2＋）, and zinc （Zn2＋） ions based on a disposable carbon fiber rod （CFR）. The important factors to enhance the sensing property were creation of a clean surface by dealing with CFR at a high potential and electrochemical deposition of bismuth （Bi） film to improve the accumulation of heavy metal ions. The morphology and conductivity of such activated CFR was characterized by scanning electron microscopy and electrochemical impedance spectroscopy, respectively. In terms of application, differential pulse anodic stripping voltammetry （DPASV） was employed for the simultaneous detection of Pb2＋, Cd2＋, and Zn2＋ on Bi film-coated activated CFR. Experimental parameters, such as the pH value of buffer solution, stirring speed and enrichment factors were optimized. Under optimal conditions, the DPASV peak currents showed good linear relationships with Pb2＋, Cd2＋ and Zn2＋ concentrations in the range of 0.5-2.25 μg/L, 0.5-4.0 μg/L and 1.0- 4.0 μg/L with detection limits of 0.1, 0.3 and 1.0 μg/L （SIN = 3）, respectively. Finally, the proposed analysis system was successfully utilized for the simultaneous detection of Pb2＋, Cd2＋, and Zn2＋ contents in rice samples. This study indicated that Bi film-coated activated CFR based DPASV sensor can be a promising and reliable tool for rapid analysis of emergency Dollution affairs of heavv metal ions in food.展开更多
基金supported by the National Basic Research Program of China (No. 2011CB605602)
文摘Polyacrylonitrile （PAN） based carbon fibers with different surface morphology were electrochemically treated in 3 wt% NH4HCO3 aqueous solution with current density up to 3.47 A/m 2 at room temperature, and surface structures, surface morphology and residual mechanical properties were characterized. The crystallite size （La） of carbon fibers would be interrupted due to excessive electrochemical etching, while the crystallite spacing （d（002）） increased as increasing current density. The disordered structures on the surface of carbon fiber with rough surface increased at the initial oxidation stage and then removed by further electrochemical etching, which resulting in continuous increase of the extent of graphitization on the fiber surface. However, the electrochemical etching was beneficial to getting ordered morphology on the surface for carbon fiber with smooth surface, especially when the current density was lower than 1.77 A/m 2 . The tensile strength and tensile modulus could be improved by 17.27% and 5.75%, respectively, and was dependent of surface morphology. The decreasing density of carbon fibers probably resulted from the volume expansion of carbon fibers caused by the abundant oxygen functional groups intercalated between the adjacent graphite layers.
基金financially supported by the National Natural Science Foundation of China(Nos. 21675062, 21305050)the Science and Technology Planning Project of Fujian Province, China (No. 2017J05024)+2 种基金Program for New Century Excellent Talents in Fujian Province University(NCETFJ)Program for the Cultivation of Outstanding Young Scientific Researches in Fujian Universities (COYSRFJ)the opening project of Fujian Provincial EngineeringTechnology Research Center of Marine Functional Food(No. C11172)
文摘In this work, a simple, low cost and sensitive voltammetric sensor was developed for the simultaneous detection of lead （Pb2＋）, cadmium （Cd2＋）, and zinc （Zn2＋） ions based on a disposable carbon fiber rod （CFR）. The important factors to enhance the sensing property were creation of a clean surface by dealing with CFR at a high potential and electrochemical deposition of bismuth （Bi） film to improve the accumulation of heavy metal ions. The morphology and conductivity of such activated CFR was characterized by scanning electron microscopy and electrochemical impedance spectroscopy, respectively. In terms of application, differential pulse anodic stripping voltammetry （DPASV） was employed for the simultaneous detection of Pb2＋, Cd2＋, and Zn2＋ on Bi film-coated activated CFR. Experimental parameters, such as the pH value of buffer solution, stirring speed and enrichment factors were optimized. Under optimal conditions, the DPASV peak currents showed good linear relationships with Pb2＋, Cd2＋ and Zn2＋ concentrations in the range of 0.5-2.25 μg/L, 0.5-4.0 μg/L and 1.0- 4.0 μg/L with detection limits of 0.1, 0.3 and 1.0 μg/L （SIN = 3）, respectively. Finally, the proposed analysis system was successfully utilized for the simultaneous detection of Pb2＋, Cd2＋, and Zn2＋ contents in rice samples. This study indicated that Bi film-coated activated CFR based DPASV sensor can be a promising and reliable tool for rapid analysis of emergency Dollution affairs of heavv metal ions in food.