Indirect mineral carbonation of titanium-bearing blast furnace slag coupled with recovery of TiO_2 and Al_2O_3

Large quantities of CO2 and blast furnace slag are discharged in the iron and steel industry. Mineral carbonation of blast furnace slag can offer substantial CO2 emission reduction and comprehensive utilization of the solid waste. This paper describes a novel route for indirect mineral carbonation of titanium-bearing blast furnace （TBBF） slag, in which the TBBF slag is roasted with recyclable （NH4）2SO4 （AS） at low temperatures and converted into the sulphates of various valuable metals, including calcium, magnesium, aluminium and titanium. High value added Ti-and Al-rich products can be obtained through stepwise precipitation of the leaching solution from the roasted slag. The NH3 produced during the roasting is used to capture CO2 from flue gases. The NH4HCO3 and （NH4）2CO3 thus obtained are used to carbonate the CaSO4-containing leaching residue and MgSO4-rich leaching solution, respectively. In this study, the process parameters and efficiency for the roasting, carbonation and Ti and Al recovery were investigated in detail. The results showed that the sulfation ratios of calcium, magnesium, titanium and aluminium reached 92.6%, 87% and 84.4%, respectively, after roasting at an AS-to-TBBF slag mass ratio of 2：1 and 350℃ for 2 h. The leaching solution was subjected to hydrolysis at 102℃ for 4 h with a Ti hydrolysis ratio of 95.7%and the purity of TiO2 in the calcined hydrolysate reached 98 wt%. 99.7% of aluminium in the Ti-depleted leaching solution was precipitated by using NH3. The carbonation products of Ca and Mg were CaCO3 and （NH4）2Mg（CO3）2·4H2O, respectively. The latter can be decomposed into MgCO3 at 100-200℃ with simultaneous recovery of the NH3 for reuse. In this process, approximately 82.1% of Ca and 84.2% of Mg in the TBBF slag were transformed into stable carbonates and the total CO2 sequestration capacity per ton of TBBF slag reached up to 239.7 kg. The TiO2 obtained can be used directly as an end product, while the Al-rich precipitate and the two carbonation products can act, respectively, as raw materials for electrolytic aluminium, cement and light magnesium carbonate production for the replacement of natural resources.

Carbon Ramming Materials for Blast Furnace Construction

1 Scope This standard specifies the definition, classifica- tion, technical requirements, test methods, quality ap- praisal procedure, packing, marking, transportation, stroage and quality certificate of carbon ramming mate- rials for blast furnace construction. This standard is applicable to carbon ramming materials for construction in leveling layer of blast furnace bottom, ramming layer upper or lower the cen- tral line of water cooling pipes, joints between carbon bricks, or joints between carbon bricks and cooling equipment.

Effect of Coke Reaction Index on Reduction and Permeability of Ore Layer in Blast Furnace Lumpy Zone Under Non-Isothermal Condition

Reasonable control on CRI（coke reaction index）is one of the key factors for BF（blast furnace）low-carbon smelting.However,there are contrary opinions.One is increasing CRI to improve reaction efficiency in BF and the other is decreasing CRI to suppress coke degradation in furnace.Different methods are adopted to realize effective catalysis（increasing CRI）and passivation（decreasing CRI）of coke.Simulation tests of coke in BF lumpy zone under gradual temperature rising have been done.Effect of CRI on gas composition,ore reduction,burden column permeability and heat reserve zone′s temperature under non-isothermal condition are studied.Then combined with iron making calculations,a novel BF operation suggestion is proposed as coke nut with small size be catalyzed and mixed with ore while skeletal coke with large size be passivated and separately charged into BF.

Medium oxygen enriched blast furnace with top gas recycling strategy

Top gas recycling oxygen blast furnace（TGR-OBF）process is a promising ironmaking process.The biggest challenge of the TGR-OBF in operation is the dramatic decrease of top gas volume（per ton hot metal）,which once led to hanging-up and shutdowns in practice of the Toulachermet.In order to avoid this weakness,the strategy of medium oxygen blast furnace was presented.The maneuverable zone of the TGR-OBF was determined by the top gas volume,which should not be far from the data of the traditional blast furnace.The deviation of ±12.5% was used,and then the maneuverable blast oxygen content is from 0.30 to 0.47 according to the calculation.The flame temperature and the top gas volume have no much difference compared to those of the traditional blast furnace.The minimum carbon consumption of 357 kg per ton hot metal in the maneuverable zone occurs at the oxygen content of 0.30（fuel saving of 14%）.In the unsteady evolution,the N2 accumulation could approach nearly zero after the recycling reached 6 times.Thus far,some TGR-OBF industrial trials have been carried out in different countries,but the method of medium oxygen enriched TGR-OBF has not been implemented,because the accumulation of N2 was worried about.The presented strategy of medium oxygen enriched TGR-OBF is applicable and the strategy with good operational performance is strongly suggested as a forerunner of the full oxygen blast furnace.