Gas phase carbonylation of methane is studied in the presence of molecular oxygen over pure carbon carriers and carbon supported rhodium chalcogen halides. Activated carbons and fullerene blacks have been used as carb...Gas phase carbonylation of methane is studied in the presence of molecular oxygen over pure carbon carriers and carbon supported rhodium chalcogen halides. Activated carbons and fullerene blacks have been used as carbon supports. XPS and IR-spectroscopy data show the formation of rhodium chalcogen halides in solids prepared by different methods. We have found that the productivity of acetic acid by carbon supported rhodium chalcogen halides depends strongly on the carbon carrier and the method of the catalyst preparation. Namely, the catalyst with highest productivity for the acetic acid is prepared by synthesizing the rhodium chalcogen halide over the carbon support followed by thermal destruction. We have also found that rhodium chalcogen halides over activated carbons are more active compared with fullerene supported catalysts.展开更多
Colloidal synthesis method such as oleylamine(OAm)-stabilized process is of great interest for obtaining uniform and highly dispersed platinum nanoparticle catalysts, yet the ligand may unavoidably inhibit their elect...Colloidal synthesis method such as oleylamine(OAm)-stabilized process is of great interest for obtaining uniform and highly dispersed platinum nanoparticle catalysts, yet the ligand may unavoidably inhibit their electro-catalytic performance. Thus, fully removing these ligands is critical to activate catalyst surface. Previous research of OAm removal process pointed that thermal annealing was the most effective way in comparison with other methods such as chemical washing, UV–Ozone irradiation and cyclic voltammetry sweeping, but generally resulting in undesired growth of platinum nanoparticle. Few studies concerning a more efficient ligand removal process have been published yet. In this work we proposed a platinum in-situ catalytic OAm combustion strategy to elucidate the removal mechanism of OAm ligands in thermal process and the key experimental parameters were also optimized. In addition, heat flow signal based on differential scanning calorimetry(DSC) measurement as a sensitive indicator, is suggested to reveal the ligand removal efficiency, which is much more reliable than the traditional spectroscopy.In comparison with commercial Pt/C sample, such a surface clean Pt/C electrocatalyst has shown an enhanced specific activity for oxygen reduction reaction. Our removal strategy and the evaluation method are highly instructive to efficient removal of different organic ligands.展开更多
A series of high surface area graphitic carbon materials (HSGCs) were prepared by ball-milling method. Effect of the graphitic degree of HSGCs on the catalytic performance of Ba-Ru-K/HSGC-x (x is the ball-milling t...A series of high surface area graphitic carbon materials (HSGCs) were prepared by ball-milling method. Effect of the graphitic degree of HSGCs on the catalytic performance of Ba-Ru-K/HSGC-x (x is the ball-milling time in hour) catalysts was studied using ammonia synthesis as a probe reaction. The graphitic degree and pore structure of HSGC-x supports could be successfully tuned via the variation of ball-milling time. Ru nanoparticles of different Ba-Ru-K/HSGC-x catalysts are homogeneously distributed on the supports with the particle sizes ranging from 1.6 to 2.0 nm. The graphitic degree of the support is closely related to its facile electron transfer capability and so plays an important role in improving the intrinsic catalytic performance of Ba-Ru-K/HSGC-x catalyst.展开更多
The carbon supported PtRu alloy film electrodes having Pt about 0.10 mg/cm2 or even less were prepared by ion beam sputtering method (IBSM). It was valued on the hydrogen analyse performance, the temperature influen...The carbon supported PtRu alloy film electrodes having Pt about 0.10 mg/cm2 or even less were prepared by ion beam sputtering method (IBSM). It was valued on the hydrogen analyse performance, the temperature influence factor and the stability by electroanalysis hydrogen analyse method. It was found that the carbon supported PtRu alloy film electrodes had higher hydrogen evolution performance and stability, such as the hydrogen evolution exchange current density (j0) was increase as the temperature (T) rised, and it overrun 150 mA/cm2 as the trough voltage in about 0.68V, and it only had about 2.8% decline in 500 h electrolytic process. The results demonstrated that the carbon supported PtRu alloy film electrodes kept highly catalytic activity and stability, and it were successfully used in pilot plant for producing H2 on electrolysis of H2S.展开更多
Developing platinum-group-metal(PGM)catalysts possessing strong metal-support interaction and controllable PGM size is urgent for the sluggish oxygen reduction reaction(ORR)in proton-exchange membrane fuel cells.Herei...Developing platinum-group-metal(PGM)catalysts possessing strong metal-support interaction and controllable PGM size is urgent for the sluggish oxygen reduction reaction(ORR)in proton-exchange membrane fuel cells.Herein,we propose an in-situ self-assembled reduction strategy to successfully induce highly-dispersed sub-3nm platinum nanoparticles(Pt NPs)to attach on resin-derived atomic Co coordinated by N-doped carbon substrate(Pt/Co_(SA)-N-C)for ORR.To be specific,the interfacial electron interaction effect,along with a highly robust Co_(SA)-N-C support endow the as-fabricated Pt/Co_(SA)-N-C catalyst with significantly enhanced catalytic properties,i.e.,a mass activity(MA)of 0.719 A/mgPt at 0.9 ViR-free and a reduction of 24.2%in MA after a 20,000-cycles test.Density functional theory(DFT)calculations demonstrate that the enhanced electron interaction between Pt and Co_(SA)-N-C support decreases the dband center of Pt,which is in favor of lowering the desorption energy of ^(*)OH on Pt/Co_(SA)-N-C surface and accelerating the formation of H_(2)O,thus enhance the instinct activity of ORR.Furthermore,the higher binding energy between Pt and Co_(SA)-N-C compared to Pt and C indicates that the migration of Pt has been suppressed,which theoretically explains the improved durability of Pt/Co_(SA)-N-C.Our work offers an enlightenment on constructing composite Pt-based catalysts with multiple active sites.展开更多
The Fischer–Tropsch to olefins(FTO) process is a method for the direct conversion of synthesis gas to lower C–Colefins. Carbon-supported iron carbide nanoparticles are attractive catalysts for this reaction.The ca...The Fischer–Tropsch to olefins(FTO) process is a method for the direct conversion of synthesis gas to lower C–Colefins. Carbon-supported iron carbide nanoparticles are attractive catalysts for this reaction.The catalytic activity can be improved and undesired formation of alkanes can be suppressed by the addition of sodium and sulfur as promoters but the influence of their content and ratio remains poorly understood and the promoted catalysts often suffer from rapid deactivation due to particle growth. A series of carbon black-supported iron catalysts with similar iron content and nominal sodium/sulfur loadings of 1–30/0.5–5 wt% with respect to iron are prepared and characterized under FTO conditions at 1and 10 bar syngas pressure to illuminate the influence of the promoter level on the catalytic properties.Iron particles and promoters undergo significant reorganization during FTO operation under industrially relevant conditions. Low sodium content(1–3 wt%) leads to a delay in iron carbide formation. Sodium contents of 15–30 wt% lead to rapid loss of catalytic activity due to the covering of the iron surface with promoters during particle growth under FTO operation. Higher activity and slower loss of activity are observed at low promoter contents(1–3 wt% sodium and 0.5–1 wt% sulfur) but a minimum amount of alkali is required to effectively suppress methane and C–Cparaffin formation. A reference catalyst support(carbide-derived carbon aerogel) shows that the optimum promoter level depends on iron particle size and support pore structure.展开更多
Carbon materials were used as supports for Ag catalysts that are prepared using the conventional wet impregnation method, and their catalytic properties for CO selective oxidation in excess hydrogen at temperatures be...Carbon materials were used as supports for Ag catalysts that are prepared using the conventional wet impregnation method, and their catalytic properties for CO selective oxidation in excess hydrogen at temperatures below 483 K were tested. A variety of techniques, e.g. N2 adsorption, XPS, TPD, UV-Vis DRS, TEM and SEM, were used to determine the influence of physical and chemical properties of the carbon on the properties of Ag catalyst. It was found that defects on the carbon surface served as nucleation sites for silver ions, while functional groups on carbon surface induced their reduction to the metallic form. The formation of silver particles on carbon was governed by homogeneous and/or heterogeneous nucleation during the impregnation and subsequent activation processes. The best catalytic performance was obtained with a Ag/carbon black catalyst with a uniform size distribution of silver nanoparticles (about 12 nm), moderate BET surface area (with a mesoporous structure), and a limited amount of carbon-oxygen groups. The research indicates that carbon materials are potentially good supports for silver catalysts for preferential oxidation of CO in excess hydrogen.展开更多
The activated carbon-supported TiO2 nanoparticles(TiO2/AC)were prepared by a properly controlled sol-gel method.The effects of activated carbons(AC)support on inactivated properties of TiO2 nanoparticles were evaluate...The activated carbon-supported TiO2 nanoparticles(TiO2/AC)were prepared by a properly controlled sol-gel method.The effects of activated carbons(AC)support on inactivated properties of TiO2 nanoparticles were evaluated by photocatalytic inactivation experiments of Escherichia coli.The key factors affecting the inactivation effciency were investigated,including electric power of lamp, temperature,and pH values.The results show that the TiO2/AC composites have high inactivation properties of E.coli in compari...展开更多
TiO2 sol was prepared by sol-gel technique with tetrabutyl titanate as precursor. Supported TiO2 catalysts on activated carbon were prepared by soak and sintering method. The aggregation of nano-TiO2 particles can be ...TiO2 sol was prepared by sol-gel technique with tetrabutyl titanate as precursor. Supported TiO2 catalysts on activated carbon were prepared by soak and sintering method. The aggregation of nano-TiO2 particles can be effectively suppressed by added polyethylene glycol (PEG) as a surface modifier. The average particle diameter of TiO2, specific surface area and absorbability of catalyst can be modified. Based on characteristics of the TiO2 photocatalyst with XRD, specific surface area, adsorption valves of methylene blue and the amount of TiO2 supported on the activated carbon, the photocatalytic degradation of L-acid was studied. The effect of the factors, such as pH of the solution, the initial concentration of L-acid on the photocatalytic degradation of L-acid, were studied also. It was found that when the pH of the solution is 1.95, the amount of photocatalyst is 0.5 g, the concentration of the L-acid solution is 1.34×10^3 mol/L and the illumination time is 7 h, the photocatalytic degradation efficiency of L-acid can reach 89,88%, The catalyst was reused 6 times and its degradation efficiency hardly changed.展开更多
Ten kinds of activated carbon from different raw materials were used as supports to prepare ruthenium catalysts. N_2 physisorption and CO chemisorption were carried out to investigate the pore size distribution and th...Ten kinds of activated carbon from different raw materials were used as supports to prepare ruthenium catalysts. N_2 physisorption and CO chemisorption were carried out to investigate the pore size distribution and the ruthenium dispersion of the catalysts. It was found that the Ru dispersion of the catalyst was closely related to not only the texture of carbon support but also the purity of activated carbon. The activities of a series of the carbon-supported barium-promoted Ru catalysts for ammonia synthesis were measured at 425 ℃, 10 0 MPa and 10 000 h -1. The result shows that the same raw material activated carbon, with a high purity, high surface area, large pore volume and reasonable pore size distribution might disperse ruthenium and promoter sufficiently, which activated carbon as support, could be used to manufacture ruthenium catalyst with a high activity for ammonia synthesis. The different raw material activated carbon as the support would greatly influence the catalytic properties of the ruthenium catalyst for ammonia synthesis. For example, with coconut shell carbon(AC1) as the support, the ammonia concentration in the effluent was 13 17% over 4%Ru-BaO/AC1 catalyst, while with the desulfurized coal carbon(AC10) as the support, that in the effluent was only 1 37% over 4%Ru-BaO/AC10 catalyst.展开更多
A carbon nanotube-supported NiP amorphous catalyst (NiP/CNT) was prepared by induced reduction. Benzene hydrogenation was used as a probe reaction for the study of catalytic activity. The effects of the support on t...A carbon nanotube-supported NiP amorphous catalyst (NiP/CNT) was prepared by induced reduction. Benzene hydrogenation was used as a probe reaction for the study of catalytic activity. The effects of the support on the activity and thermal stability of the supported catalyst were discussed based on various characterizations, including XRD, TEM, ICP, XPS, H2-TPD, and DTA. In comparison with the NiP amorphous alloy, the benzene conversion on NiP/CNT catalyst was lower, but the specific activity of NiP/CNT was higher, which is attributed to the dispersion produced by the support, an electron-donating effect, and the hydrogen-storage ability of CNT. The NiP/CNT thermal stability was improved because of the dispersion and electronic effects and the good heat-conduction ability of the CNT support.展开更多
The cyclohexene 1 was oxidized with polymer-supported 2.2-bipyridine cobalt(II) complex in the presence of CO2. The conversion and selectivity was sensitive to the pressure of CO2.
Support vector regression (SVR) combined with particle swarm optimization for its parameter optimization is employed to establish a model for predicting the Henry constants of multi-walled carbon nanotubes (MWNTs)...Support vector regression (SVR) combined with particle swarm optimization for its parameter optimization is employed to establish a model for predicting the Henry constants of multi-walled carbon nanotubes (MWNTs) for adsorption of volatile organic compounds (VOCs). The prediction performance of SVR is compared with those of the model of theoretical linear salvation energy relationship (TLSER). By using leave-one-out cross validation of SVR test Henry constants for adsorption of 35 VOCs on MWNTs, the root mean square error is 0.080, the mean absolute percentage error is only 1.19~, and the correlation coefficient (R2) is as high as 0.997. Compared with the results of the TLSER model, it is shown that the estimated errors by SVR are ali smaller than those achieved by TLSER. It reveals that the generalization ability of SVR is superior to that of the TLSER model Meanwhile, multifactor analysis is adopted for investigation of the influences of each molecular structure descriptor on the Henry constants. According to the TLSER model, the adsorption mechanism of adsorption of carbon nanotubes of VOCs is mainly a result of van der Waals and interactions of hydrogen bonds. These can provide the theoretical support for the application of carbon nanotube adsorption of VOCs and can make up for the lack of experimental data.展开更多
Carbon-supported copper catalyst was prepared for the first time in one-step with copper nitrate and corn stalk through calcination under different temperatures. Uniformly dispersed nanoparticles were obtained and wer...Carbon-supported copper catalyst was prepared for the first time in one-step with copper nitrate and corn stalk through calcination under different temperatures. Uniformly dispersed nanoparticles were obtained and were identified to be Cu(0) and Cu(Ⅰ) in XRD patterns. Excellent catalytic activity and selectivity were achieved in the N-arylation of pyrazole under ligand and protection gas free conditions. About90.4% of product yield was achieved with only 0.5 mol% of copper catalyst(Cu-C-300), which was considerably more efficient than previous reports. XPS results suggested that the N-arylation of pyrazole activity was closely related to the surface Cu(Ⅰ) species.展开更多
The carbon nanotubes-coated cordierite (CNTs-cordierite) was fabricated by pyrolysis of ethine on cordierite with iron catalyst, which was penetrated into the cordierite substrate by vacuum impregnation. The cordier...The carbon nanotubes-coated cordierite (CNTs-cordierite) was fabricated by pyrolysis of ethine on cordierite with iron catalyst, which was penetrated into the cordierite substrate by vacuum impregnation. The cordierite substrate, carbon naontubes, and CNTs-cordierite were characterized by SEM, TEM/HREM, BET, and TGA. The results show that the carbon nanotubes were distributed uniformly on the surface of cordierite. A significant increase in BET surface area and pore volume was observed, and a suitable pore-size distribution was obtained. On the CNTs-cordierite, carbon nanotubes penetrated into the cordierite substrate, which led to a remarkable stability of the CNTs against ultrasound maltreatment. Growth time is an important factor for thermostability and texture of the sample. The mass increased but the purity decreased with the growth time, which caused the exothermic peak shift to low temperature, and the corresponding full width half maximum (FWHM) of the peak in DTG increased.展开更多
The adsorption and dissociation of methane and carbon dioxide for reforming on nickel catalyst were extensively investigated by TPSR and TPD experiments. It showed that the decomposition of methane results in the form...The adsorption and dissociation of methane and carbon dioxide for reforming on nickel catalyst were extensively investigated by TPSR and TPD experiments. It showed that the decomposition of methane results in the formation of at least three kinds of surface carbon species on supported nickel catalyst, while CO2 adsorbed on the catalyst weakly and only existed in one kind of adsorption state. Then the mechanism of interaction between the species dissociated from CH4 and CO2 during reforming was proposed.展开更多
The synthesis and properties of carbon xerogels are briefly described in this mini-review, emphasizing the methods used for tuning their surface chemistry and textural properties in order to design efficient electroca...The synthesis and properties of carbon xerogels are briefly described in this mini-review, emphasizing the methods used for tuning their surface chemistry and textural properties in order to design efficient electrocatalysts for fuel cells. In particular, the role played by the surface functional groups in determining the loading, dispersion, oxidation state and stability of the metal phases is addressed.展开更多
Methacrylic acid first was neutralized with an aqueous solution of NaOH to pH = 6.0 similar to 7.0, vinylene carbonate (VCA) was added to the solution, then monomers were copolymerized in paraffin oil by means of reve...Methacrylic acid first was neutralized with an aqueous solution of NaOH to pH = 6.0 similar to 7.0, vinylene carbonate (VCA) was added to the solution, then monomers were copolymerized in paraffin oil by means of reverse-phase suspension polymerization and hydrophilic copolymeric supports were prepared. The properties of the supports were determined using trypsin and results show that the amount of enzymes coupled to the supports and the specific activity of immobilized trypsin are related to the content of VCA structure units, reaction time and concentration of enzyme solution, etc.展开更多
In this paper,AgBF_4/[emim][BF_4] supported ionic liquid membranes(SILMs) were prepared successfully for CO/N_2 separation using nitrogen pressure immobilization procedures.The incorporation of AgBF_4 could decrease m...In this paper,AgBF_4/[emim][BF_4] supported ionic liquid membranes(SILMs) were prepared successfully for CO/N_2 separation using nitrogen pressure immobilization procedures.The incorporation of AgBF_4 could decrease membrane weight loss,improve the pressure-resistant ability,and keep the critical pressure(0.45 MPa) of the SILMs.The high viscosity and undissolved Ag BF_4 solids in membrane liquid would disturb gas molecular transport through membrane and give rise to the gas transport resistance.Therefore,the gas permeability decreased remarkably with increasing AgBF_4 carrier content in the membrane.When the molar ratio of AgBF_4 to [emim][BF_4] increased from 0:1 to 0.3:1,the CO/N_2 selectivity of the SILMs showed a great increase from ~1 to ~9 at 20 °C and 0.4 MPa,suggesting that AgBF_4 was an effective carrier for CO facilitated transport.The permeabilities of N_2 and CO increased at higher transmembrane pressure,indicating that molecular transport would dominate the transport process at high pressure.The temperature-dependent gas permeability followed the Arrhenius equation.Moreover,the differences between the activation energies of CO and N_2 became larger after introducing AgBF_4,resulting in more obvious decrease in the CO/N_2 selectivity at higher operating temperature.展开更多
文摘Gas phase carbonylation of methane is studied in the presence of molecular oxygen over pure carbon carriers and carbon supported rhodium chalcogen halides. Activated carbons and fullerene blacks have been used as carbon supports. XPS and IR-spectroscopy data show the formation of rhodium chalcogen halides in solids prepared by different methods. We have found that the productivity of acetic acid by carbon supported rhodium chalcogen halides depends strongly on the carbon carrier and the method of the catalyst preparation. Namely, the catalyst with highest productivity for the acetic acid is prepared by synthesizing the rhodium chalcogen halide over the carbon support followed by thermal destruction. We have also found that rhodium chalcogen halides over activated carbons are more active compared with fullerene supported catalysts.
基金the financial support by DICP Grant no.ZZBS201705。
文摘Colloidal synthesis method such as oleylamine(OAm)-stabilized process is of great interest for obtaining uniform and highly dispersed platinum nanoparticle catalysts, yet the ligand may unavoidably inhibit their electro-catalytic performance. Thus, fully removing these ligands is critical to activate catalyst surface. Previous research of OAm removal process pointed that thermal annealing was the most effective way in comparison with other methods such as chemical washing, UV–Ozone irradiation and cyclic voltammetry sweeping, but generally resulting in undesired growth of platinum nanoparticle. Few studies concerning a more efficient ligand removal process have been published yet. In this work we proposed a platinum in-situ catalytic OAm combustion strategy to elucidate the removal mechanism of OAm ligands in thermal process and the key experimental parameters were also optimized. In addition, heat flow signal based on differential scanning calorimetry(DSC) measurement as a sensitive indicator, is suggested to reveal the ligand removal efficiency, which is much more reliable than the traditional spectroscopy.In comparison with commercial Pt/C sample, such a surface clean Pt/C electrocatalyst has shown an enhanced specific activity for oxygen reduction reaction. Our removal strategy and the evaluation method are highly instructive to efficient removal of different organic ligands.
基金supported by the Natural Science Foundation of China(NSFC Grant No.20803064)the Natural Science Foundation of Zhejiang Provence(Y4090348 and LY12B03007)Qianjiang Talent Project in Zhejiang Province(2010R10039 and 2013R10056)
文摘A series of high surface area graphitic carbon materials (HSGCs) were prepared by ball-milling method. Effect of the graphitic degree of HSGCs on the catalytic performance of Ba-Ru-K/HSGC-x (x is the ball-milling time in hour) catalysts was studied using ammonia synthesis as a probe reaction. The graphitic degree and pore structure of HSGC-x supports could be successfully tuned via the variation of ball-milling time. Ru nanoparticles of different Ba-Ru-K/HSGC-x catalysts are homogeneously distributed on the supports with the particle sizes ranging from 1.6 to 2.0 nm. The graphitic degree of the support is closely related to its facile electron transfer capability and so plays an important role in improving the intrinsic catalytic performance of Ba-Ru-K/HSGC-x catalyst.
文摘The carbon supported PtRu alloy film electrodes having Pt about 0.10 mg/cm2 or even less were prepared by ion beam sputtering method (IBSM). It was valued on the hydrogen analyse performance, the temperature influence factor and the stability by electroanalysis hydrogen analyse method. It was found that the carbon supported PtRu alloy film electrodes had higher hydrogen evolution performance and stability, such as the hydrogen evolution exchange current density (j0) was increase as the temperature (T) rised, and it overrun 150 mA/cm2 as the trough voltage in about 0.68V, and it only had about 2.8% decline in 500 h electrolytic process. The results demonstrated that the carbon supported PtRu alloy film electrodes kept highly catalytic activity and stability, and it were successfully used in pilot plant for producing H2 on electrolysis of H2S.
基金financially supported by the Natural Science Foundation of China(Nos.22169005,22209186,22068009 and 22262006)the Science and Technology Support Project of Guizhou Provincial Science and Technology Department(Nos.ZK[2023]050 and[2023]403)+2 种基金the Open Project of Institute of Dualcarbon and New Energy Technology Innovation and Development of Guizhou Province(No.DCRE-2023-06)Youth Innovation Promotion Association,CAS(No.2023343)Self-deployed Projects of Ganjiang Innovation Academy,CAS(No.E355F006).
文摘Developing platinum-group-metal(PGM)catalysts possessing strong metal-support interaction and controllable PGM size is urgent for the sluggish oxygen reduction reaction(ORR)in proton-exchange membrane fuel cells.Herein,we propose an in-situ self-assembled reduction strategy to successfully induce highly-dispersed sub-3nm platinum nanoparticles(Pt NPs)to attach on resin-derived atomic Co coordinated by N-doped carbon substrate(Pt/Co_(SA)-N-C)for ORR.To be specific,the interfacial electron interaction effect,along with a highly robust Co_(SA)-N-C support endow the as-fabricated Pt/Co_(SA)-N-C catalyst with significantly enhanced catalytic properties,i.e.,a mass activity(MA)of 0.719 A/mgPt at 0.9 ViR-free and a reduction of 24.2%in MA after a 20,000-cycles test.Density functional theory(DFT)calculations demonstrate that the enhanced electron interaction between Pt and Co_(SA)-N-C support decreases the dband center of Pt,which is in favor of lowering the desorption energy of ^(*)OH on Pt/Co_(SA)-N-C surface and accelerating the formation of H_(2)O,thus enhance the instinct activity of ORR.Furthermore,the higher binding energy between Pt and Co_(SA)-N-C compared to Pt and C indicates that the migration of Pt has been suppressed,which theoretically explains the improved durability of Pt/Co_(SA)-N-C.Our work offers an enlightenment on constructing composite Pt-based catalysts with multiple active sites.
基金supported by a Post Doc grant of the German Academic Exchange Service(Deutscher Akademischer Austauschdienst,DAAD grant no.91552012)by the European Research Council(EU FP7 ERC advanced grant no.338846)
文摘The Fischer–Tropsch to olefins(FTO) process is a method for the direct conversion of synthesis gas to lower C–Colefins. Carbon-supported iron carbide nanoparticles are attractive catalysts for this reaction.The catalytic activity can be improved and undesired formation of alkanes can be suppressed by the addition of sodium and sulfur as promoters but the influence of their content and ratio remains poorly understood and the promoted catalysts often suffer from rapid deactivation due to particle growth. A series of carbon black-supported iron catalysts with similar iron content and nominal sodium/sulfur loadings of 1–30/0.5–5 wt% with respect to iron are prepared and characterized under FTO conditions at 1and 10 bar syngas pressure to illuminate the influence of the promoter level on the catalytic properties.Iron particles and promoters undergo significant reorganization during FTO operation under industrially relevant conditions. Low sodium content(1–3 wt%) leads to a delay in iron carbide formation. Sodium contents of 15–30 wt% lead to rapid loss of catalytic activity due to the covering of the iron surface with promoters during particle growth under FTO operation. Higher activity and slower loss of activity are observed at low promoter contents(1–3 wt% sodium and 0.5–1 wt% sulfur) but a minimum amount of alkali is required to effectively suppress methane and C–Cparaffin formation. A reference catalyst support(carbide-derived carbon aerogel) shows that the optimum promoter level depends on iron particle size and support pore structure.
基金the Chinese Ministry of Science and Technology (2003CB6 15806) the Natural Science Foundation of China (National Key Project: 90206036).
文摘Carbon materials were used as supports for Ag catalysts that are prepared using the conventional wet impregnation method, and their catalytic properties for CO selective oxidation in excess hydrogen at temperatures below 483 K were tested. A variety of techniques, e.g. N2 adsorption, XPS, TPD, UV-Vis DRS, TEM and SEM, were used to determine the influence of physical and chemical properties of the carbon on the properties of Ag catalyst. It was found that defects on the carbon surface served as nucleation sites for silver ions, while functional groups on carbon surface induced their reduction to the metallic form. The formation of silver particles on carbon was governed by homogeneous and/or heterogeneous nucleation during the impregnation and subsequent activation processes. The best catalytic performance was obtained with a Ag/carbon black catalyst with a uniform size distribution of silver nanoparticles (about 12 nm), moderate BET surface area (with a mesoporous structure), and a limited amount of carbon-oxygen groups. The research indicates that carbon materials are potentially good supports for silver catalysts for preferential oxidation of CO in excess hydrogen.
基金supported by the Educational and Tech-nological Department of Hunan Province(No.08B063)the Natural Science Foundation of Science and Technology Department of Hunan Government(No.2007GK3060)the Doctor Foundation of Jishou University(No.JSDXKYZZ200648).
文摘The activated carbon-supported TiO2 nanoparticles(TiO2/AC)were prepared by a properly controlled sol-gel method.The effects of activated carbons(AC)support on inactivated properties of TiO2 nanoparticles were evaluated by photocatalytic inactivation experiments of Escherichia coli.The key factors affecting the inactivation effciency were investigated,including electric power of lamp, temperature,and pH values.The results show that the TiO2/AC composites have high inactivation properties of E.coli in compari...
基金The State Education Ministry "211" Project, the Natural Science Foundation of the Education Commission of Jiangsu Province(2005103TSJB156) and the Funding of the Environment Friendship Laboratory of Nanjing Normal University
文摘TiO2 sol was prepared by sol-gel technique with tetrabutyl titanate as precursor. Supported TiO2 catalysts on activated carbon were prepared by soak and sintering method. The aggregation of nano-TiO2 particles can be effectively suppressed by added polyethylene glycol (PEG) as a surface modifier. The average particle diameter of TiO2, specific surface area and absorbability of catalyst can be modified. Based on characteristics of the TiO2 photocatalyst with XRD, specific surface area, adsorption valves of methylene blue and the amount of TiO2 supported on the activated carbon, the photocatalytic degradation of L-acid was studied. The effect of the factors, such as pH of the solution, the initial concentration of L-acid on the photocatalytic degradation of L-acid, were studied also. It was found that when the pH of the solution is 1.95, the amount of photocatalyst is 0.5 g, the concentration of the L-acid solution is 1.34×10^3 mol/L and the illumination time is 7 h, the photocatalytic degradation efficiency of L-acid can reach 89,88%, The catalyst was reused 6 times and its degradation efficiency hardly changed.
基金Supported by the Science &Technical Ministry of China( No.2 0 0 1BA3 2 2 C) ,the Science &Technical Department ofFujian Province( No.2 0 0 0 F0 0 2 ) and the Science &Technical Development Foundation of Fuzhou U niversity( No.XKJQD-0 10 2 )
文摘Ten kinds of activated carbon from different raw materials were used as supports to prepare ruthenium catalysts. N_2 physisorption and CO chemisorption were carried out to investigate the pore size distribution and the ruthenium dispersion of the catalysts. It was found that the Ru dispersion of the catalyst was closely related to not only the texture of carbon support but also the purity of activated carbon. The activities of a series of the carbon-supported barium-promoted Ru catalysts for ammonia synthesis were measured at 425 ℃, 10 0 MPa and 10 000 h -1. The result shows that the same raw material activated carbon, with a high purity, high surface area, large pore volume and reasonable pore size distribution might disperse ruthenium and promoter sufficiently, which activated carbon as support, could be used to manufacture ruthenium catalyst with a high activity for ammonia synthesis. The different raw material activated carbon as the support would greatly influence the catalytic properties of the ruthenium catalyst for ammonia synthesis. For example, with coconut shell carbon(AC1) as the support, the ammonia concentration in the effluent was 13 17% over 4%Ru-BaO/AC1 catalyst, while with the desulfurized coal carbon(AC10) as the support, that in the effluent was only 1 37% over 4%Ru-BaO/AC10 catalyst.
基金Supported by the National Natural Science Foundation of China (No. 20263003)Natural Science Foundation of Jiangxi province (No. 0250009)
文摘A carbon nanotube-supported NiP amorphous catalyst (NiP/CNT) was prepared by induced reduction. Benzene hydrogenation was used as a probe reaction for the study of catalytic activity. The effects of the support on the activity and thermal stability of the supported catalyst were discussed based on various characterizations, including XRD, TEM, ICP, XPS, H2-TPD, and DTA. In comparison with the NiP amorphous alloy, the benzene conversion on NiP/CNT catalyst was lower, but the specific activity of NiP/CNT was higher, which is attributed to the dispersion produced by the support, an electron-donating effect, and the hydrogen-storage ability of CNT. The NiP/CNT thermal stability was improved because of the dispersion and electronic effects and the good heat-conduction ability of the CNT support.
文摘The cyclohexene 1 was oxidized with polymer-supported 2.2-bipyridine cobalt(II) complex in the presence of CO2. The conversion and selectivity was sensitive to the pressure of CO2.
基金Supported by the Innovative Talent Funds for Project 985 under Grant No WLYJSBJRCTD201102the Fundamental Research Funds for the Central Universities under Grant No CQDXWL-2013-014+1 种基金the Natural Science Foundation of Chongqing under Grant No CSTC2006BB5240the Program for New Century Excellent Talents in Universities of China under Grant No NCET-07-0903
文摘Support vector regression (SVR) combined with particle swarm optimization for its parameter optimization is employed to establish a model for predicting the Henry constants of multi-walled carbon nanotubes (MWNTs) for adsorption of volatile organic compounds (VOCs). The prediction performance of SVR is compared with those of the model of theoretical linear salvation energy relationship (TLSER). By using leave-one-out cross validation of SVR test Henry constants for adsorption of 35 VOCs on MWNTs, the root mean square error is 0.080, the mean absolute percentage error is only 1.19~, and the correlation coefficient (R2) is as high as 0.997. Compared with the results of the TLSER model, it is shown that the estimated errors by SVR are ali smaller than those achieved by TLSER. It reveals that the generalization ability of SVR is superior to that of the TLSER model Meanwhile, multifactor analysis is adopted for investigation of the influences of each molecular structure descriptor on the Henry constants. According to the TLSER model, the adsorption mechanism of adsorption of carbon nanotubes of VOCs is mainly a result of van der Waals and interactions of hydrogen bonds. These can provide the theoretical support for the application of carbon nanotube adsorption of VOCs and can make up for the lack of experimental data.
基金supported by the Natural Science Foundation of China(91645115 and 21473003)High-level talents funding project of Hebei(CL201601,E2016100015)science technology research and development guidance program project of Baoding City(No.16ZF027)
文摘Carbon-supported copper catalyst was prepared for the first time in one-step with copper nitrate and corn stalk through calcination under different temperatures. Uniformly dispersed nanoparticles were obtained and were identified to be Cu(0) and Cu(Ⅰ) in XRD patterns. Excellent catalytic activity and selectivity were achieved in the N-arylation of pyrazole under ligand and protection gas free conditions. About90.4% of product yield was achieved with only 0.5 mol% of copper catalyst(Cu-C-300), which was considerably more efficient than previous reports. XPS results suggested that the N-arylation of pyrazole activity was closely related to the surface Cu(Ⅰ) species.
基金This study was supported by the National Natural Science Foundation of China (20576021)Science & Technology Priority Project of Fujian Province (2005H201-2).
文摘The carbon nanotubes-coated cordierite (CNTs-cordierite) was fabricated by pyrolysis of ethine on cordierite with iron catalyst, which was penetrated into the cordierite substrate by vacuum impregnation. The cordierite substrate, carbon naontubes, and CNTs-cordierite were characterized by SEM, TEM/HREM, BET, and TGA. The results show that the carbon nanotubes were distributed uniformly on the surface of cordierite. A significant increase in BET surface area and pore volume was observed, and a suitable pore-size distribution was obtained. On the CNTs-cordierite, carbon nanotubes penetrated into the cordierite substrate, which led to a remarkable stability of the CNTs against ultrasound maltreatment. Growth time is an important factor for thermostability and texture of the sample. The mass increased but the purity decreased with the growth time, which caused the exothermic peak shift to low temperature, and the corresponding full width half maximum (FWHM) of the peak in DTG increased.
文摘The adsorption and dissociation of methane and carbon dioxide for reforming on nickel catalyst were extensively investigated by TPSR and TPD experiments. It showed that the decomposition of methane results in the formation of at least three kinds of surface carbon species on supported nickel catalyst, while CO2 adsorbed on the catalyst weakly and only existed in one kind of adsorption state. Then the mechanism of interaction between the species dissociated from CH4 and CO2 during reforming was proposed.
基金supported by project PEstC/EQB/LA0020/2011 financed by FEDER through COMPETE-Programa Operacional Factores de CompetitividadeFCT-Fundao para a Ciência e a Tecnologia
文摘The synthesis and properties of carbon xerogels are briefly described in this mini-review, emphasizing the methods used for tuning their surface chemistry and textural properties in order to design efficient electrocatalysts for fuel cells. In particular, the role played by the surface functional groups in determining the loading, dispersion, oxidation state and stability of the metal phases is addressed.
文摘Methacrylic acid first was neutralized with an aqueous solution of NaOH to pH = 6.0 similar to 7.0, vinylene carbonate (VCA) was added to the solution, then monomers were copolymerized in paraffin oil by means of reverse-phase suspension polymerization and hydrophilic copolymeric supports were prepared. The properties of the supports were determined using trypsin and results show that the amount of enzymes coupled to the supports and the specific activity of immobilized trypsin are related to the content of VCA structure units, reaction time and concentration of enzyme solution, etc.
基金Financial support from the National Natural Science Foundation of China (21406235)
文摘In this paper,AgBF_4/[emim][BF_4] supported ionic liquid membranes(SILMs) were prepared successfully for CO/N_2 separation using nitrogen pressure immobilization procedures.The incorporation of AgBF_4 could decrease membrane weight loss,improve the pressure-resistant ability,and keep the critical pressure(0.45 MPa) of the SILMs.The high viscosity and undissolved Ag BF_4 solids in membrane liquid would disturb gas molecular transport through membrane and give rise to the gas transport resistance.Therefore,the gas permeability decreased remarkably with increasing AgBF_4 carrier content in the membrane.When the molar ratio of AgBF_4 to [emim][BF_4] increased from 0:1 to 0.3:1,the CO/N_2 selectivity of the SILMs showed a great increase from ~1 to ~9 at 20 °C and 0.4 MPa,suggesting that AgBF_4 was an effective carrier for CO facilitated transport.The permeabilities of N_2 and CO increased at higher transmembrane pressure,indicating that molecular transport would dominate the transport process at high pressure.The temperature-dependent gas permeability followed the Arrhenius equation.Moreover,the differences between the activation energies of CO and N_2 became larger after introducing AgBF_4,resulting in more obvious decrease in the CO/N_2 selectivity at higher operating temperature.