Silica-coated carbonyl iron particles （CIPs） are fabricated with the Stober method to improve their heat-resistance and wave-aSsorption properties. The morphology, heat-resistance, electromagnetic properties and mic...Silica-coated carbonyl iron particles （CIPs） are fabricated with the Stober method to improve their heat-resistance and wave-aSsorption properties. The morphology, heat-resistance, electromagnetic properties and microwave absorption of raw-CIPs and silica-coated CIPs are investigated using a scanning electron microscope, an energy dispersive spectrometer, a thermal-gravimetric analyzer, and a network analyzer. The results show that the heat-resistance of silica-coated CIPs is better than that of raw CIFs. The reflection losses exceeding -lOdB of silica-coated CIPs are obtained in the frequency range 9.5-12.4 GHz for the absorber thickness of 2.3 mm, and the same reflection losses of uncoated CIPs reach the data in the lower frequency range for the same thickness. The enhanced microwave absorption of silica-coated CIPs can be ascribed to the combination of proper electromagnetic impedance match and the decrease of dielectric permittivity.展开更多
The electromagnetic （EM） wave absorbing property of silicone rubber filled with carbonyl iron particles （CIPs） and multi-walled carbon nanotubes （MWCNTs） was examined. Absorbents including MWCNTs and spherical/ ...The electromagnetic （EM） wave absorbing property of silicone rubber filled with carbonyl iron particles （CIPs） and multi-walled carbon nanotubes （MWCNTs） was examined. Absorbents including MWCNTs and spherical/ flaky CIPs were added to silicone rubber using a two-roll mixer. The complex permittivity and complex permeability were measured over the frequency range of 1-18 GHz. The two EM parameters were verified and the uniform dispersion of MWCNTs and ClPs was confirmed by comparing the measured reflection loss （RL） with the calculated one. As the MWCNT weight percent increased, the RL of the spherical CIPs/silicone rubber composites changed insignificantly. It was attributed to the random distribution of spherical ClPs and less content of MWCNTs. On the contrary, for composites filled with flaky ClPs the absorption bandwidth increased at thickness 0.5 mm （RL value lower than -5 dB in 8-18 GHz） and the absorption ratio increased at lower frequency （minimum -35 dB at 3.5 GHz）. This effect was attributed to the oriented distribution of flaky CIPs caused by interactions between the two absorbents. Therefore, mixing MWCNTs and flaky CIPs could achieve wider-band and higher-absorption ratio absorbing materials.展开更多
文摘Silica-coated carbonyl iron particles （CIPs） are fabricated with the Stober method to improve their heat-resistance and wave-aSsorption properties. The morphology, heat-resistance, electromagnetic properties and microwave absorption of raw-CIPs and silica-coated CIPs are investigated using a scanning electron microscope, an energy dispersive spectrometer, a thermal-gravimetric analyzer, and a network analyzer. The results show that the heat-resistance of silica-coated CIPs is better than that of raw CIFs. The reflection losses exceeding -lOdB of silica-coated CIPs are obtained in the frequency range 9.5-12.4 GHz for the absorber thickness of 2.3 mm, and the same reflection losses of uncoated CIPs reach the data in the lower frequency range for the same thickness. The enhanced microwave absorption of silica-coated CIPs can be ascribed to the combination of proper electromagnetic impedance match and the decrease of dielectric permittivity.
基金supported by the National Natural Science Foundation of China (Grant No. 50805005)the National "863" Project of China (Grant No. 2009AA043804)the Foundation for the Author of National Excellent Doctoral Dissertation of PR China (Grant No. 2007B32)
文摘The electromagnetic （EM） wave absorbing property of silicone rubber filled with carbonyl iron particles （CIPs） and multi-walled carbon nanotubes （MWCNTs） was examined. Absorbents including MWCNTs and spherical/ flaky CIPs were added to silicone rubber using a two-roll mixer. The complex permittivity and complex permeability were measured over the frequency range of 1-18 GHz. The two EM parameters were verified and the uniform dispersion of MWCNTs and ClPs was confirmed by comparing the measured reflection loss （RL） with the calculated one. As the MWCNT weight percent increased, the RL of the spherical CIPs/silicone rubber composites changed insignificantly. It was attributed to the random distribution of spherical ClPs and less content of MWCNTs. On the contrary, for composites filled with flaky ClPs the absorption bandwidth increased at thickness 0.5 mm （RL value lower than -5 dB in 8-18 GHz） and the absorption ratio increased at lower frequency （minimum -35 dB at 3.5 GHz）. This effect was attributed to the oriented distribution of flaky CIPs caused by interactions between the two absorbents. Therefore, mixing MWCNTs and flaky CIPs could achieve wider-band and higher-absorption ratio absorbing materials.