Cardanol-aldehyde condensation polymer containing boron-nitrogen coordinate bond (CFBN) has been synthesized and characterized by IR, XPS, HPLC and DTA-TG. Its properties were also investigated. The results show tha...Cardanol-aldehyde condensation polymer containing boron-nitrogen coordinate bond (CFBN) has been synthesized and characterized by IR, XPS, HPLC and DTA-TG. Its properties were also investigated. The results show that the coating film of CFBN has excellent physico-mechanical properties, good anticorrosive properties and stable at high temperature. (Author abstract) 8 Refs.展开更多
A new kind of flocculants, named Polymer Silicate Phosphate Ferric Sulfate(PSPFS), was synthesized by ferrous sulfate used as the main material and activated silicic acid as additive. In this paper, High-Viscosity Oil...A new kind of flocculants, named Polymer Silicate Phosphate Ferric Sulfate(PSPFS), was synthesized by ferrous sulfate used as the main material and activated silicic acid as additive. In this paper, High-Viscosity Oil Refining wastewater from Liaohe Petrochemical Corporation was the treatment object. Overall, the in-fluencing factors and synthesis technology conditions of PSPFS were determined by experiments. First of all, the conditions of influencing factors were showed as follows: the mass percent concentration of ferrous sulfate 55%,concentration of sodium silicate 15% , the molar ratio of ferrous sulfate and hydrogen peroxide 1.2:1, oxidation temperature 40 degree Celsius, oxidation time 4 hours, polymerization temperature 60 de-gree Celsius and polymerization time 2 hours. Secondly, the optimal ratios of components were determined by uniform design method. The molar ratio of Fe/Si is 5.0:1, Fe/H2SO4 is 3.2:1, and Fe/P is 18.0:1. At last, the optimal experimental condition was determined as follows: the dosing quantity 200mg/L, pH value 5.5~9, temperature 25~45℃, stirring time 2 min, and standing time 3 min, according to the result of floc-culation experiments with PSPFS. Besides, the result of the comparative experiments showed that the effi-ciency of PSPFS was much better than the reference flocculants.展开更多
Bio-inspired hierarchical self-assembly provides elegant and powerful bottom-up strategies for the creation of complex materials.However,the current self-assembly approaches for natural bio-compounds often result in m...Bio-inspired hierarchical self-assembly provides elegant and powerful bottom-up strategies for the creation of complex materials.However,the current self-assembly approaches for natural bio-compounds often result in materials with limited diversity and complexity in architecture as well as microstructure.Here,we develop a novel coordination polymerization-driven hierarchical assembly of micelle strategy,using phytic acid-based natural compounds as an example,for the spatially controlled fabrication of metal coordination bio-derived polymers.The resultant ferric phytate polymer nanospheres feature hollow architecture,ordered meso-channels of^12 nm,high surface area of 401 m2 g−1,and large pore volume of 0.53 cm3 g−1.As an advanced anode material,this bio-derivative polymer delivers a remarkable reversible capacity of 540 mAh g−1 at 50 mA g−1,good rate capability,and cycling stability for sodium-ion batteries.This study holds great potential of the design of new complex bio-materials with supramolecular chemistry.展开更多
In this article, a new type of coagulant material has been investigated and the performance of the coagulation process using this type of coagulant was evaluated. This new type is a combination of zinc oxide nanoparti...In this article, a new type of coagulant material has been investigated and the performance of the coagulation process using this type of coagulant was evaluated. This new type is a combination of zinc oxide nanoparticles and polyferric sulfate (ZnOPFS). The structure of zinc oxide nanoparticles was determined by spectroscopic, X-ray and electron microscopy methods, and based on this, it was determined that ZnOPFS is a complex and mixed compound that is mainly composed of zinc oxide nanoparticles and ferric sulfate. The effects of Zn/Fe (Zn/Fe) molar ratio and aging (time) on acidity and zeta potential were also evaluated using a specific method. The obtained results showed that in the simultaneous deposition process, zinc ions can prevent the formation of polyferric acid coagulation and subsequently improve the stability of ZnOPFS.展开更多
对采用硫铁矿烧渣为主要原料,生产制备新型聚合双酸铁铝混凝剂及其水处理混凝性能进行了研究。对影响烧渣中铁溶出率的反应温度和反应时间进行了考察,并以城市污水和染色工业废水为处理对象,考察了新型聚合双酸铁铝的混凝性能。结果表明...对采用硫铁矿烧渣为主要原料,生产制备新型聚合双酸铁铝混凝剂及其水处理混凝性能进行了研究。对影响烧渣中铁溶出率的反应温度和反应时间进行了考察,并以城市污水和染色工业废水为处理对象,考察了新型聚合双酸铁铝的混凝性能。结果表明,在反应温度为110℃和反应时间为70 m in时,烧渣中铁的溶出率达到95%左右,经水解聚合反应后所得的聚合双酸铁铝比聚合硫酸铁具有更好的混凝性能和更低的成本。与聚合硫酸铁相比,聚合双酸铁铝具有混凝性能优、成本低廉的特点。展开更多
基金This work is supported by the National Science Foundation of China.
文摘Cardanol-aldehyde condensation polymer containing boron-nitrogen coordinate bond (CFBN) has been synthesized and characterized by IR, XPS, HPLC and DTA-TG. Its properties were also investigated. The results show that the coating film of CFBN has excellent physico-mechanical properties, good anticorrosive properties and stable at high temperature. (Author abstract) 8 Refs.
文摘A new kind of flocculants, named Polymer Silicate Phosphate Ferric Sulfate(PSPFS), was synthesized by ferrous sulfate used as the main material and activated silicic acid as additive. In this paper, High-Viscosity Oil Refining wastewater from Liaohe Petrochemical Corporation was the treatment object. Overall, the in-fluencing factors and synthesis technology conditions of PSPFS were determined by experiments. First of all, the conditions of influencing factors were showed as follows: the mass percent concentration of ferrous sulfate 55%,concentration of sodium silicate 15% , the molar ratio of ferrous sulfate and hydrogen peroxide 1.2:1, oxidation temperature 40 degree Celsius, oxidation time 4 hours, polymerization temperature 60 de-gree Celsius and polymerization time 2 hours. Secondly, the optimal ratios of components were determined by uniform design method. The molar ratio of Fe/Si is 5.0:1, Fe/H2SO4 is 3.2:1, and Fe/P is 18.0:1. At last, the optimal experimental condition was determined as follows: the dosing quantity 200mg/L, pH value 5.5~9, temperature 25~45℃, stirring time 2 min, and standing time 3 min, according to the result of floc-culation experiments with PSPFS. Besides, the result of the comparative experiments showed that the effi-ciency of PSPFS was much better than the reference flocculants.
基金financially supported by the Natural Science Foundation of China (Grant Nos.51773062 and 61831021)
文摘Bio-inspired hierarchical self-assembly provides elegant and powerful bottom-up strategies for the creation of complex materials.However,the current self-assembly approaches for natural bio-compounds often result in materials with limited diversity and complexity in architecture as well as microstructure.Here,we develop a novel coordination polymerization-driven hierarchical assembly of micelle strategy,using phytic acid-based natural compounds as an example,for the spatially controlled fabrication of metal coordination bio-derived polymers.The resultant ferric phytate polymer nanospheres feature hollow architecture,ordered meso-channels of^12 nm,high surface area of 401 m2 g−1,and large pore volume of 0.53 cm3 g−1.As an advanced anode material,this bio-derivative polymer delivers a remarkable reversible capacity of 540 mAh g−1 at 50 mA g−1,good rate capability,and cycling stability for sodium-ion batteries.This study holds great potential of the design of new complex bio-materials with supramolecular chemistry.
文摘In this article, a new type of coagulant material has been investigated and the performance of the coagulation process using this type of coagulant was evaluated. This new type is a combination of zinc oxide nanoparticles and polyferric sulfate (ZnOPFS). The structure of zinc oxide nanoparticles was determined by spectroscopic, X-ray and electron microscopy methods, and based on this, it was determined that ZnOPFS is a complex and mixed compound that is mainly composed of zinc oxide nanoparticles and ferric sulfate. The effects of Zn/Fe (Zn/Fe) molar ratio and aging (time) on acidity and zeta potential were also evaluated using a specific method. The obtained results showed that in the simultaneous deposition process, zinc ions can prevent the formation of polyferric acid coagulation and subsequently improve the stability of ZnOPFS.
文摘对采用硫铁矿烧渣为主要原料,生产制备新型聚合双酸铁铝混凝剂及其水处理混凝性能进行了研究。对影响烧渣中铁溶出率的反应温度和反应时间进行了考察,并以城市污水和染色工业废水为处理对象,考察了新型聚合双酸铁铝的混凝性能。结果表明,在反应温度为110℃和反应时间为70 m in时,烧渣中铁的溶出率达到95%左右,经水解聚合反应后所得的聚合双酸铁铝比聚合硫酸铁具有更好的混凝性能和更低的成本。与聚合硫酸铁相比,聚合双酸铁铝具有混凝性能优、成本低廉的特点。