1 .Introduction Metal-matrix composites (MMCs) have developed since they first appeared in the 1960s. However, the high cost of current monolithic MMCs hampers their production on a large industrial cale Fro...1 .Introduction Metal-matrix composites (MMCs) have developed since they first appeared in the 1960s. However, the high cost of current monolithic MMCs hampers their production on a large industrial cale From the point of view of their application, the service life of components usually relies on their surface properties. It is展开更多
采用电渣熔铸技术,制备了以5Cr Ni Mo模具钢为基体,WC颗粒为硬质相的钢基复合材料。利用扫描电子显微镜、冲击试验机、摩擦磨损试验机等研究了复合材料的冲击韧度、断口形貌、摩擦系数、磨损量和磨损机制。结果表明,复合材料冲击韧度值...采用电渣熔铸技术,制备了以5Cr Ni Mo模具钢为基体,WC颗粒为硬质相的钢基复合材料。利用扫描电子显微镜、冲击试验机、摩擦磨损试验机等研究了复合材料的冲击韧度、断口形貌、摩擦系数、磨损量和磨损机制。结果表明,复合材料冲击韧度值较小,断裂方式均是脆性断裂。顶部和中部试样分布着沿晶或穿晶二次裂纹,为解理断裂。尾部试样部分区域具有一些韧性特征,断口为细韧窝和部分沿晶断口。热处理后试样的耐磨性得到很大提高,在干滑动磨损条件下,试样的磨损机制主要是粘着磨损引起的表面剥落及磨屑充当第三体引起的磨粒磨损。展开更多
文摘1 .Introduction Metal-matrix composites (MMCs) have developed since they first appeared in the 1960s. However, the high cost of current monolithic MMCs hampers their production on a large industrial cale From the point of view of their application, the service life of components usually relies on their surface properties. It is
文摘采用电渣熔铸技术,制备了以5Cr Ni Mo模具钢为基体,WC颗粒为硬质相的钢基复合材料。利用扫描电子显微镜、冲击试验机、摩擦磨损试验机等研究了复合材料的冲击韧度、断口形貌、摩擦系数、磨损量和磨损机制。结果表明,复合材料冲击韧度值较小,断裂方式均是脆性断裂。顶部和中部试样分布着沿晶或穿晶二次裂纹,为解理断裂。尾部试样部分区域具有一些韧性特征,断口为细韧窝和部分沿晶断口。热处理后试样的耐磨性得到很大提高,在干滑动磨损条件下,试样的磨损机制主要是粘着磨损引起的表面剥落及磨屑充当第三体引起的磨粒磨损。