The thermal fatigue behavior of wear resistance cast iron with different quantity of deformation has been investigated. The results show that eutectic carbide is the main location and passage for initiation and extens...The thermal fatigue behavior of wear resistance cast iron with different quantity of deformation has been investigated. The results show that eutectic carbide is the main location and passage for initiation and extension of thermal fatigue cracks, approving that the more serious, the carbide breaks. The higher thermal fatigue resistance of wear resistance cast iron will be and thermal fatigue fracture belongs mainly to brittleness.展开更多
The effects of squeeze casting process on microstructure and flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy were investigated and the hot-compression tests of gravity casting and squeeze casting alloy were carried ...The effects of squeeze casting process on microstructure and flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy were investigated and the hot-compression tests of gravity casting and squeeze casting alloy were carried out at 350-500°C and 0.001-5s-1.The results show that microstructures of Al-17.5Si-4Cu-0.5Mg alloys were obviously improved by squeeze casting.Due to the decrease of coarse primary Si particles,softα-Al dendrite as well as the fine microstructures appeared,and the mechanical properties of squeeze casting alloys were improved.However,when the strain rate rises or the deformation temperature decreases,the flow stress increases and it was proved that the alloy is a positive strain rate sensitive material.It was deduced that compared with the gravity casting alloy,squeeze casting alloy（solidified at 632 MPa）is more difficult to deform since the flow stress of squeeze casting alloy is higher than that of gravity casting alloy when the deformation temperature exceeds 400°C.Flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy can be described by a hyperbolic sine form with Zener-Hollomon parameter,and the average hot deformation activation energy Q of gravity casting alloy and squeeze casting alloy is 278.97 and 308.77kJ/mol,respectively.展开更多
文摘The thermal fatigue behavior of wear resistance cast iron with different quantity of deformation has been investigated. The results show that eutectic carbide is the main location and passage for initiation and extension of thermal fatigue cracks, approving that the more serious, the carbide breaks. The higher thermal fatigue resistance of wear resistance cast iron will be and thermal fatigue fracture belongs mainly to brittleness.
基金supported by National Natural Science Foundation of China(51674168)Shenyang City Application Basic Research Foundation(F14-231-1-23)
文摘The effects of squeeze casting process on microstructure and flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy were investigated and the hot-compression tests of gravity casting and squeeze casting alloy were carried out at 350-500°C and 0.001-5s-1.The results show that microstructures of Al-17.5Si-4Cu-0.5Mg alloys were obviously improved by squeeze casting.Due to the decrease of coarse primary Si particles,softα-Al dendrite as well as the fine microstructures appeared,and the mechanical properties of squeeze casting alloys were improved.However,when the strain rate rises or the deformation temperature decreases,the flow stress increases and it was proved that the alloy is a positive strain rate sensitive material.It was deduced that compared with the gravity casting alloy,squeeze casting alloy（solidified at 632 MPa）is more difficult to deform since the flow stress of squeeze casting alloy is higher than that of gravity casting alloy when the deformation temperature exceeds 400°C.Flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy can be described by a hyperbolic sine form with Zener-Hollomon parameter,and the average hot deformation activation energy Q of gravity casting alloy and squeeze casting alloy is 278.97 and 308.77kJ/mol,respectively.