The mechanism of grain fracturing in a zirconia metering nozzle used in the continuous casting process was studied. The phase composition, microstructure, and chemical composition of the residual samples were studied ...The mechanism of grain fracturing in a zirconia metering nozzle used in the continuous casting process was studied. The phase composition, microstructure, and chemical composition of the residual samples were studied using an X-ray fluorescence analyzer, scanning electron microscope, and electron probe. Results revealed that the composition, structure, and mineral phase of the original layer, transition layer, and affected layer of the metering nozzle differed because of stabilizer precipitation and steel slag permeation. The stabilizer MgO formed low-melting phases with steel slag and impure SiO2 on the boundaries（pores） of zirconia grains; consequently, grain fracturing occurred and accelerated damage to the metering nozzle was observed.展开更多
The long nozzle,stopper,and submerged entry nozzle play an important role in continuous casting. They are of the similar composition and are mainly damaged by liquid steel thermal shock which leads to immediate cracks...The long nozzle,stopper,and submerged entry nozzle play an important role in continuous casting. They are of the similar composition and are mainly damaged by liquid steel thermal shock which leads to immediate cracks or fracture in their combined area because of the thermal mechanical properties mismatch,or damaged by corrosion on their interface. The failure mechanisms are the thermal shock damage and continuous reaction corrosion. High efficiency and long life of the long nozzle,stopper,and submerged entry nozzle can be realized by optimizing the thermal mechanical properties,the key erosion step,and the combination match.展开更多
Flow field,heat transfer and inclusion behavior in a 700 mm round bloom mold under the effect of a swirling flow submerged entry nozzle(SEN)were investigated with the aim to enhance the casting process.The results ind...Flow field,heat transfer and inclusion behavior in a 700 mm round bloom mold under the effect of a swirling flow submerged entry nozzle(SEN)were investigated with the aim to enhance the casting process.The results indicate that the impinging flow phenomenon,which is commonly observed in conventional single-port SEN casting,was completely suppressed by the swirling flow SEN coming from a novel swirling flow generator design in tundish.Steel from the SEN port moved towards the mold wall in 360 direction,leading to a uniform temperature distribution in the mold.Compared to a conventional single-port SEN casting,the steel super-heat was decreased by about 5 K at the mold center,and the temperature was increased by around 3.5 K near the meniscus.In addition,the removal ratio of inclusions to the mold top surface in the swirling flow SEN casting was found to be increased.Specifically,the removal ratio of spherical inclusions with diameters of 1,10,50 and 100μm was increased by 18.2%,18.5%,22.6% and 42.7%,respectively.Furthermore,the ratio was raised by 18.2%,20.8%,21.5% and 44.1%for non-spherical inclusions,respectively.展开更多
基金funded by the National Natural Science Foundation of China(51372193)the Natural Science Basic Research Plan in the Shaanxi Province of China(2014JM6224)
文摘The mechanism of grain fracturing in a zirconia metering nozzle used in the continuous casting process was studied. The phase composition, microstructure, and chemical composition of the residual samples were studied using an X-ray fluorescence analyzer, scanning electron microscope, and electron probe. Results revealed that the composition, structure, and mineral phase of the original layer, transition layer, and affected layer of the metering nozzle differed because of stabilizer precipitation and steel slag permeation. The stabilizer MgO formed low-melting phases with steel slag and impure SiO2 on the boundaries（pores） of zirconia grains; consequently, grain fracturing occurred and accelerated damage to the metering nozzle was observed.
文摘The long nozzle,stopper,and submerged entry nozzle play an important role in continuous casting. They are of the similar composition and are mainly damaged by liquid steel thermal shock which leads to immediate cracks or fracture in their combined area because of the thermal mechanical properties mismatch,or damaged by corrosion on their interface. The failure mechanisms are the thermal shock damage and continuous reaction corrosion. High efficiency and long life of the long nozzle,stopper,and submerged entry nozzle can be realized by optimizing the thermal mechanical properties,the key erosion step,and the combination match.
基金supported by the National Natural Science Foundation of China(Grant No.51704062)the Fundamental Research Funds for the Central Universities(Grant No.N2025019).
文摘Flow field,heat transfer and inclusion behavior in a 700 mm round bloom mold under the effect of a swirling flow submerged entry nozzle(SEN)were investigated with the aim to enhance the casting process.The results indicate that the impinging flow phenomenon,which is commonly observed in conventional single-port SEN casting,was completely suppressed by the swirling flow SEN coming from a novel swirling flow generator design in tundish.Steel from the SEN port moved towards the mold wall in 360 direction,leading to a uniform temperature distribution in the mold.Compared to a conventional single-port SEN casting,the steel super-heat was decreased by about 5 K at the mold center,and the temperature was increased by around 3.5 K near the meniscus.In addition,the removal ratio of inclusions to the mold top surface in the swirling flow SEN casting was found to be increased.Specifically,the removal ratio of spherical inclusions with diameters of 1,10,50 and 100μm was increased by 18.2%,18.5%,22.6% and 42.7%,respectively.Furthermore,the ratio was raised by 18.2%,20.8%,21.5% and 44.1%for non-spherical inclusions,respectively.