The influences of Sn element and heat treat-ment on the microstructure and mechanical properties of Mg-7Al alloy prepared by vacuum die cast(VDC)were studied.The results indicate thatα-Mg dendrite and Mg_(17)Al_(12) ...The influences of Sn element and heat treat-ment on the microstructure and mechanical properties of Mg-7Al alloy prepared by vacuum die cast(VDC)were studied.The results indicate thatα-Mg dendrite and Mg_(17)Al_(12) are refined and new Mg_(2)Sn phase is formed in Mg-7Al alloy with 2 wt%Sn addition.The ultimate tensile strength(σ_(b))of Mg-7Al alloy increases from 205 to 258 MPa(i.e.,a 25%increase).The mechanical properties of Mg-7Al-2Sn(AT72)alloy are further improved through heat treatment because of the dense microstructures processed by VDC.In particular,the mechanical properties of AT72 alloy are greatly improved after solution treatment at 400℃for 20 h due to solution strengthening of Al and Sn elements and precipitation strengthening of Mg_(2)Sn phases.The precipitation strengthening effect of particle Mg_(2)Sn phases is more apparent due to the decomposition of Mg_(17)Al_(12) phases.In addition,from the view of microscopic theory,the effect of Sn on mechanical properties of Mg-7Al alloy was discussed by first-principle calculation.展开更多
基金financially supported by the Program for Liaoning Innovative Research Team in University (No. LT2013004)the Key Technologies Research and Development Program of Liaoning Province (No.2013201018)the Doctoral Starting up Foundation of Liaoning Province (No.20131083)
文摘The influences of Sn element and heat treat-ment on the microstructure and mechanical properties of Mg-7Al alloy prepared by vacuum die cast(VDC)were studied.The results indicate thatα-Mg dendrite and Mg_(17)Al_(12) are refined and new Mg_(2)Sn phase is formed in Mg-7Al alloy with 2 wt%Sn addition.The ultimate tensile strength(σ_(b))of Mg-7Al alloy increases from 205 to 258 MPa(i.e.,a 25%increase).The mechanical properties of Mg-7Al-2Sn(AT72)alloy are further improved through heat treatment because of the dense microstructures processed by VDC.In particular,the mechanical properties of AT72 alloy are greatly improved after solution treatment at 400℃for 20 h due to solution strengthening of Al and Sn elements and precipitation strengthening of Mg_(2)Sn phases.The precipitation strengthening effect of particle Mg_(2)Sn phases is more apparent due to the decomposition of Mg_(17)Al_(12) phases.In addition,from the view of microscopic theory,the effect of Sn on mechanical properties of Mg-7Al alloy was discussed by first-principle calculation.