Optical and electrical properties of BaSnO_(3) and In_2O_(3) mixed transparent conductive films deposited by filtered cathodic vacuum arc technique at room temperature

For the crystalline temperature of BaSnO_(3)(BTO)was above 650℃,the transparent conductive BTO-based films were always deposited above this temperature on epitaxy substrates by pulsed laser deposition or molecular beam epitaxy till now which limited there application in low temperature device process.In the article,the microstructure,optical and electrical of BTO and In_(2)O_(3) mixed transparent conductive BaInSnO_(x)(BITO)film deposited by filtered cathodic vacuum arc technique(FCVA)on glass substrate at room temperature were firstly reported.The BITO film with thickness of 300 nm had mainly In_(2)O_(3) polycrystalline phase,and minor polycrystalline BTO phase with(001),(011),(111),(002),(222)crystal faces which were first deposited at room temperature on amorphous glass.The transmittance was 70%–80%in the visible light region with linear refractive index of 1.94 and extinction coefficient of 0.004 at 550-nm wavelength.The basic optical properties included the real and imaginary parts,high frequency dielectric constants,the absorption coefficient,the Urbach energy,the indirect and direct band gaps,the oscillator and dispersion energies,the static refractive index and dielectric constant,the average oscillator wavelength,oscillator length strength,the linear and the third-order nonlinear optical susceptibilities,and the nonlinear refractive index were all calculated.The film was the n-type conductor with sheet resistance of 704.7Ω/□,resistivity of 0.02Ω⋅cm,mobility of 18.9 cm2/V⋅s,and carrier electron concentration of 1.6×10^(19) cm^(−3) at room temperature.The results suggested that the BITO film deposited by FCVA had potential application in transparent conductive films-based low temperature device process.

Tribological properties of multilayer tetrahedral amorphous carbon coatings deposited by filtered cathodic vacuum arc deposition

Tetrahedral amorphous carbon(ta‐C)has emerged as an excellent coating material for improving the reliability of application components under high normal loads.Herein,we present the results of our investigations regarding the mechanical and tribological properties of a 2‐μm‐thick multilayer ta‐C coating on high‐speed steel substrates.Multilayers composed of alternating soft and hard layers are fabricated using filtered a cathodic vacuum arc with alternating substrate bias voltages(0 and 100 V or 0 and 150 V).The thickness ratio is discovered to be 1:3 for the sp2‐rich and sp3‐rich layers.The results show that the hardness and elastic modulus of the multilayer ta‐C coatings increase with the sp3 content of the hard layer.The hardness reached approximately 37 GPa,whereas an improved toughness and a higher adhesion strength(>29 N)are obtained.The friction performance(μ=0.07)of the multilayer coating is similar to that of the single layer ta‐C thick coating,but the wear rate(0.13×10^(–6) mm^(3)/(N∙m))improved under a high load of 30 N.We further demonstrate the importance of the multilayer structure in suppressing crack propagation and increasing the resistance to plastic deformation(H3/E2)ratio.

STUDY ON COMPOSITION, MICROSTRUCTURE AND HARDNESS OF DLC FILMS BY VCAD

DLC super-hard films have been deposited on the substrates of single crystalline Si, pure Ti and stainless steel 18-8 by a method of vacuum cathode arc deposition (VCAD). The composition, microstructure and micro-hardness of the films have been studied in this paper. The results indicate that hardness of the DLC films is different on the different substrates. Hardness of the films increases with decreasing in surface roughness of the films. The maximum value of micro-hardness belongs to the DLC films deposited under the hydrogen pressure of 0.35Pa and the negative bias of 100V.