The working principle of cement roller press and current development of wear resistance on the cement grinding system status at home and abroad was described. The main improvement of previous research on the wear resi...The working principle of cement roller press and current development of wear resistance on the cement grinding system status at home and abroad was described. The main improvement of previous research on the wear resistance of roller press was proposed from three aspects of wear-resistant material, roller press roller structure, and surface morphology.展开更多
The performances of dry grinding fine cement (DFC) in grouting procedure were experimentally studied.The measurement of its fineness and simulated test for injectability showed that this DFC could be used to inject r...The performances of dry grinding fine cement (DFC) in grouting procedure were experimentally studied.The measurement of its fineness and simulated test for injectability showed that this DFC could be used to inject rock mass with micro fissure.In order to improve the grouting quality,the water cement ratio and discarding time of slurry should be controlled precisely.If the water cement ratio is over 2∶1 in slurry that is made from DFC,it is not suitable to grout.Finally,the influence of different mixing times on strength of hydrated cement made from the DFC is explained by microstructure analysis with SEM.展开更多
基金Supported by the Planning Project of Science and Technology Development of Jilin Province (09ZDGG001)~~
文摘The working principle of cement roller press and current development of wear resistance on the cement grinding system status at home and abroad was described. The main improvement of previous research on the wear resistance of roller press was proposed from three aspects of wear-resistant material, roller press roller structure, and surface morphology.
文摘The performances of dry grinding fine cement (DFC) in grouting procedure were experimentally studied.The measurement of its fineness and simulated test for injectability showed that this DFC could be used to inject rock mass with micro fissure.In order to improve the grouting quality,the water cement ratio and discarding time of slurry should be controlled precisely.If the water cement ratio is over 2∶1 in slurry that is made from DFC,it is not suitable to grout.Finally,the influence of different mixing times on strength of hydrated cement made from the DFC is explained by microstructure analysis with SEM.