The purpose of this research is to investigate the hydration behavior and cementitious properties of the mixture of calcium carbonate and aluminate, and to explore whether it can be adopted as a new low-carbon cementi...The purpose of this research is to investigate the hydration behavior and cementitious properties of the mixture of calcium carbonate and aluminate, and to explore whether it can be adopted as a new low-carbon cementitious material. The composite system of calcium carbonate and aluminate minerals is studied by measuring the component of hydration products, the hydration heat, setting time and compressive strength.The results prove that the composite system has certain cementitious properties and is feasible to prepare new low-carbon cement.展开更多
To investigate the optimum calcination temperature and cementitious properties of gangue, the microstructure of clay-containing gangue calcined at different temperatures was analyzed by X-ray diffraction （XRD）, infr...To investigate the optimum calcination temperature and cementitious properties of gangue, the microstructure of clay-containing gangue calcined at different temperatures was analyzed by X-ray diffraction （XRD）, infrared spectroscopy （IR）, and magnetic angle spinning nuclear magnetic resonance （MAS NMR）. The results show that the structure of kaolinite in the gangue sample calcined at 500℃ is destroyed. The XRD spectra show the disappearance of illite at about 800℃ and the formation ofmullite at about 1000℃. With the increase in calcination temperature, octahedral （6-coordinated） aluminum is transformed to tetrahedral （4-coordinated） aluminum gradually. For the gangue sample calcined at 700℃, the 29Si MAS NMR sharp peak of Q4 （framework silicate-quartz） is left. Compared with kaolinite in gangue, the thermal transformed temperature of pure kaolinite is lagged. On the basis of the microstructure and cementitious properties of calcined gangue, the results can be concluded, in order to obtain metakaolinite, the optimum calcination temperature of this gangue is about 500℃, and the optimum temperature is about 700℃ for activated SiO2 and Al2O3.展开更多
Air quenched basic oxygen furnace steel slag （BOF-SS） is processed at very high cooling rate, which is expected to have different cementitious properties from conventional slowly cooled BOF-SS. For this purpose, the...Air quenched basic oxygen furnace steel slag （BOF-SS） is processed at very high cooling rate, which is expected to have different cementitious properties from conventional slowly cooled BOF-SS. For this purpose, the strength activity indexes of air quenched and slowly cooled BOF-SS are investigated. The results reveal that, under the specific surface area （S） of 490 m^2/kg, the compressive strength activity index reaches 1.24 after 28 days with replacement of 15% air quenched BOF-SS and reaches 1.05 after 28 days with replacement of 20% air quenched BOF-SS and 30%granulated blast furnace slag （GBFS）. The cementitious activity of air quenched BOF-SS is obviously higher than that of slowly cooled BOF-SS, mainly because it contains more C3 S and glassy phases.展开更多
基金Funded by the National Natural Science Foundation of China (Nos.51772033, 52002040)the National Key Research and Development Program of China (No. 2023YFB3711400)。
文摘The purpose of this research is to investigate the hydration behavior and cementitious properties of the mixture of calcium carbonate and aluminate, and to explore whether it can be adopted as a new low-carbon cementitious material. The composite system of calcium carbonate and aluminate minerals is studied by measuring the component of hydration products, the hydration heat, setting time and compressive strength.The results prove that the composite system has certain cementitious properties and is feasible to prepare new low-carbon cement.
基金supported by the Key Project of the Ministry of Railway of China(No.2008G031-N and No.2008G032-06)
文摘To investigate the optimum calcination temperature and cementitious properties of gangue, the microstructure of clay-containing gangue calcined at different temperatures was analyzed by X-ray diffraction （XRD）, infrared spectroscopy （IR）, and magnetic angle spinning nuclear magnetic resonance （MAS NMR）. The results show that the structure of kaolinite in the gangue sample calcined at 500℃ is destroyed. The XRD spectra show the disappearance of illite at about 800℃ and the formation ofmullite at about 1000℃. With the increase in calcination temperature, octahedral （6-coordinated） aluminum is transformed to tetrahedral （4-coordinated） aluminum gradually. For the gangue sample calcined at 700℃, the 29Si MAS NMR sharp peak of Q4 （framework silicate-quartz） is left. Compared with kaolinite in gangue, the thermal transformed temperature of pure kaolinite is lagged. On the basis of the microstructure and cementitious properties of calcined gangue, the results can be concluded, in order to obtain metakaolinite, the optimum calcination temperature of this gangue is about 500℃, and the optimum temperature is about 700℃ for activated SiO2 and Al2O3.
基金Item Sponsored by National Natural Science Foundation of China(51234003)
文摘Air quenched basic oxygen furnace steel slag （BOF-SS） is processed at very high cooling rate, which is expected to have different cementitious properties from conventional slowly cooled BOF-SS. For this purpose, the strength activity indexes of air quenched and slowly cooled BOF-SS are investigated. The results reveal that, under the specific surface area （S） of 490 m^2/kg, the compressive strength activity index reaches 1.24 after 28 days with replacement of 15% air quenched BOF-SS and reaches 1.05 after 28 days with replacement of 20% air quenched BOF-SS and 30%granulated blast furnace slag （GBFS）. The cementitious activity of air quenched BOF-SS is obviously higher than that of slowly cooled BOF-SS, mainly because it contains more C3 S and glassy phases.