With Al2O3, Dy2O3, and SiO2 as starting materials, the basic glass of Al2O3-Dy2O3-SiO2 system was prepared by conventional melting technology, and their thermal expansion coefficients （TECs） at different anneal time...With Al2O3, Dy2O3, and SiO2 as starting materials, the basic glass of Al2O3-Dy2O3-SiO2 system was prepared by conventional melting technology, and their thermal expansion coefficients （TECs） at different anneal time were investigated. TECs of the basic glass, which were heat-treated under different temperature, were also investigated. The result showed that TECs of the basic glass gradually approached a fixed value as the anneal time was extended, which suggested that most of the inner stress had been eliminated. After heat treatment, the contents of Dy2O3, Dy2Si2O7, and a new crystal increased up to 1200 ℃ and decreased below 1250 ℃, which was consistent with the TEC change of crystallized samples. This suggests that the crystal has a direct effect on TECs of the crystallized samples.展开更多
Employing Dy2O3, Al2O3, and SiO2 as starting materials, several series of Dy2O3-Al2O3-SiO2 sealing glass were prepared. The relationship between their coefficients of thermal expansion and the contents of Dy2O3, Al2O3...Employing Dy2O3, Al2O3, and SiO2 as starting materials, several series of Dy2O3-Al2O3-SiO2 sealing glass were prepared. The relationship between their coefficients of thermal expansion and the contents of Dy2O3, Al2O3, and SiO2 were studied respectively. Experimental results showed that Dy2O3 and Al2O3 had a positive effect on the coefficient of thermal expansion of glass, whereas, SiO2 had a negative effect. The coefficient of thermal expansion of glass showed an apparent linear relation to the contents of these three raw materials, from which an estimation model was built, to calculate the coefficient of thermal expansion of sealing glass. Relative errors of the calculating results to testing results were no more than 2%, which suggested that the estimation model was reasonable. This study provides a good theory reference for the practical utilizing of this sealing material, through which a proper glass composition for good sealing could be easily found.展开更多
基金Project supported by the Ministry of Science and Technology of China (2006CB601104)
文摘With Al2O3, Dy2O3, and SiO2 as starting materials, the basic glass of Al2O3-Dy2O3-SiO2 system was prepared by conventional melting technology, and their thermal expansion coefficients （TECs） at different anneal time were investigated. TECs of the basic glass, which were heat-treated under different temperature, were also investigated. The result showed that TECs of the basic glass gradually approached a fixed value as the anneal time was extended, which suggested that most of the inner stress had been eliminated. After heat treatment, the contents of Dy2O3, Dy2Si2O7, and a new crystal increased up to 1200 ℃ and decreased below 1250 ℃, which was consistent with the TEC change of crystallized samples. This suggests that the crystal has a direct effect on TECs of the crystallized samples.
基金Project supported by the Ministry of Science and Technology of China (2006CB601104)
文摘Employing Dy2O3, Al2O3, and SiO2 as starting materials, several series of Dy2O3-Al2O3-SiO2 sealing glass were prepared. The relationship between their coefficients of thermal expansion and the contents of Dy2O3, Al2O3, and SiO2 were studied respectively. Experimental results showed that Dy2O3 and Al2O3 had a positive effect on the coefficient of thermal expansion of glass, whereas, SiO2 had a negative effect. The coefficient of thermal expansion of glass showed an apparent linear relation to the contents of these three raw materials, from which an estimation model was built, to calculate the coefficient of thermal expansion of sealing glass. Relative errors of the calculating results to testing results were no more than 2%, which suggested that the estimation model was reasonable. This study provides a good theory reference for the practical utilizing of this sealing material, through which a proper glass composition for good sealing could be easily found.