Self-propagating high-temperature synthesis(SHS) is a new kind of material synthesis technique, and has characteristics with respect to low energy consumption, short synthetizing time, high production quantity, high p...Self-propagating high-temperature synthesis(SHS) is a new kind of material synthesis technique, and has characteristics with respect to low energy consumption, short synthetizing time, high production quantity, high product purity and no environmental pollution. When SHS combines with centrifugal casting, ceramic-lined compound copper pipe(CLCCP) can be produced, the inner surface of copper pipe can produce ceramic coatings having good wear and corrosion resistance. In order to increase the densification degree, combining strength and toughness of ceramic layer, the effects of additives such as SiO2, CrO3, Na2B4O7 and ZrO2 are researched, adding SiO2 and CrO3 in thermite, the densification degree of ceramic layer increases, adding Na2 B4 O7 in thermite can increase combining strength, adding ZrO2 in thermite can increase the toughness of ceramic layer. CLCCP is used in tubular billet crystallizer, having excellent service effects and decreasing the production cost of tubular billet.展开更多
The ceramic lined pipes had been produced by gravitational separation SHS method and influential factors on combustion synthesis was investigated.The experimental results showed that the ceramic lined pipes had been...The ceramic lined pipes had been produced by gravitational separation SHS method and influential factors on combustion synthesis was investigated.The experimental results showed that the ceramic lined pipes had been produced easily under condition that selecting pipes well distributed on the wall thickness ,proper preheating temperature and appropriate additive.展开更多
The ceramic setting binders obtained by means of the raw mix mechano-chemical processing(mechanical dispersion and chemical interaction processes combination), used for bonding refractory concretes, become more availa...The ceramic setting binders obtained by means of the raw mix mechano-chemical processing(mechanical dispersion and chemical interaction processes combination), used for bonding refractory concretes, become more available with a subsequent increased interest in their properties because they develop initial strength during a heat up of the units within 8-10 h, in contrast to 24 h after placement for high Al_2O_3 cements(HAC). This strength development enables high temperature processing units to be relined with minimum turnaround time, thus providing a favored cost/performance ratio. The present paper identifies the predominant phosphate phases responsible for developing good mechanical-strength properties of zirconia and alumina concretes bonded with mechano-chemical binders. It sets out the colloid and crystalline phases resulted from interphase interaction that provide the basis for high concentrated bonding suspensions(HCBS) technology useful to the refractory industry.展开更多
To improve the surface properties,lining of magnesium alloys with hard powders by shot peening was carried out in order. The hard powders were tried to bond to the workpiece surface due to the collision of many shots....To improve the surface properties,lining of magnesium alloys with hard powders by shot peening was carried out in order. The hard powders were tried to bond to the workpiece surface due to the collision of many shots.In order to fix the hard powders to the surface of the workpiece,the powders were set on an uneven surface.To easily facilitate fixing of powders,lining of the workpiece with the powder sandwiched between two aluminum foil sheets was also attempted.In this experiment,a centrifugal shot peening machine with an electrical heater was employed.The workpieces were magnesium alloys AZ31B and AZ91D,and the hard powders were commercial cemented carbide,alumina,and zirconia.The joinability of hard powders near the lined surface was observed by a optical microscope.The wear resistance was also evaluated by a wear test.The hard powders were successfully bonded to the surface of workpieces by the shot lining process.The results show that the present method is effective in wear resistance of the magnesium alloys.展开更多
基于宽边耦合带状线结构,该文设计了一种基于低温共烧陶瓷(LTCC)技术的高隔离低插损3 dB 90°电桥。该电桥使用螺旋耦合线有效地减小了器件尺寸,同时以对称式结构建模更便于后期的优化调整。在宽边螺旋耦合带状线垂直方向引入一个...基于宽边耦合带状线结构,该文设计了一种基于低温共烧陶瓷(LTCC)技术的高隔离低插损3 dB 90°电桥。该电桥使用螺旋耦合线有效地减小了器件尺寸,同时以对称式结构建模更便于后期的优化调整。在宽边螺旋耦合带状线垂直方向引入一个伸入式可调隔离电容,极大地提高了该电桥的隔离度,使其可达27 dB,且插入损耗≤0.2 dB,较之传统的定向耦合器结构,其在提升性能的同时大幅减小了器件尺寸。对耦合线直角拐弯处的电场强度进行分析与优化,采用45°斜切的方式使拐角处的电场强度与直线处大致相等。对上接地金属板进行环形镂空处理,这将改善带内的幅度平衡度。该文设计的3 dB 90°电桥通带为0.96~1.53 GHz,插入损耗≤0.2 dB,幅度平衡度≤±0.7 dB,相位平衡度为90°±1°,隔离度≥27 dB,其具有良好的应用市场。展开更多
This research was aimed at investigating the reduction of DOM fractions and their trihalomethane formation potential （THMFP） by in-line coagulation with 0.1 μm ceramic membrane filtration. The combination of cerami...This research was aimed at investigating the reduction of DOM fractions and their trihalomethane formation potential （THMFP） by in-line coagulation with 0.1 μm ceramic membrane filtration. The combination of ceramic membrane filtration with a coagulation process is an alternative technology which can be applied to enhance conventional coagulation processes in the field of water treatment and drinking water production. The Ping River water （high turbidity water） was selected as the raw surface water because it is currently the main raw water source for water supply production in the urban and rural areas of Chiang Mai Province. From the investigation, the results showed that the highest percent reductions of DOC, UV-254, and THMFP （47.6%, 71.0%, and 67.4%, respectively） were achieved from in-line coagulation with ceramic membrane filtration at polyaluminum chloride dosage 40 mg/L. Resin adsorption techniques were employed to characterize the DOM in raw surface water and filtered water. The results showed that the use of a ceramic membrane with in-line coagulation was able to most efficiently reduce the hydrophobic fraction （HPOA） （68.5%）, which was then followed by the hydrophilic fraction （HPIA） （49.3%）. The greater mass DOC reduction of these two fractions provided the highest THMFP reductions （55.1% and 37.2%, respectively）. Furthermore, the in-line coagulation with ceramic membrane filtration was able to reduce the hydrophobic （HPOB） fraction which is characterized by high reactivity toward THM formation. The percent reduction of mass DOC and THMFP of HPOB by in-line coagulation with ceramic membrane filtration was 45.9% and 48.0%, respectively.展开更多
文摘Self-propagating high-temperature synthesis(SHS) is a new kind of material synthesis technique, and has characteristics with respect to low energy consumption, short synthetizing time, high production quantity, high product purity and no environmental pollution. When SHS combines with centrifugal casting, ceramic-lined compound copper pipe(CLCCP) can be produced, the inner surface of copper pipe can produce ceramic coatings having good wear and corrosion resistance. In order to increase the densification degree, combining strength and toughness of ceramic layer, the effects of additives such as SiO2, CrO3, Na2B4O7 and ZrO2 are researched, adding SiO2 and CrO3 in thermite, the densification degree of ceramic layer increases, adding Na2 B4 O7 in thermite can increase combining strength, adding ZrO2 in thermite can increase the toughness of ceramic layer. CLCCP is used in tubular billet crystallizer, having excellent service effects and decreasing the production cost of tubular billet.
文摘The ceramic lined pipes had been produced by gravitational separation SHS method and influential factors on combustion synthesis was investigated.The experimental results showed that the ceramic lined pipes had been produced easily under condition that selecting pipes well distributed on the wall thickness ,proper preheating temperature and appropriate additive.
文摘The ceramic setting binders obtained by means of the raw mix mechano-chemical processing(mechanical dispersion and chemical interaction processes combination), used for bonding refractory concretes, become more available with a subsequent increased interest in their properties because they develop initial strength during a heat up of the units within 8-10 h, in contrast to 24 h after placement for high Al_2O_3 cements(HAC). This strength development enables high temperature processing units to be relined with minimum turnaround time, thus providing a favored cost/performance ratio. The present paper identifies the predominant phosphate phases responsible for developing good mechanical-strength properties of zirconia and alumina concretes bonded with mechano-chemical binders. It sets out the colloid and crystalline phases resulted from interphase interaction that provide the basis for high concentrated bonding suspensions(HCBS) technology useful to the refractory industry.
文摘To improve the surface properties,lining of magnesium alloys with hard powders by shot peening was carried out in order. The hard powders were tried to bond to the workpiece surface due to the collision of many shots.In order to fix the hard powders to the surface of the workpiece,the powders were set on an uneven surface.To easily facilitate fixing of powders,lining of the workpiece with the powder sandwiched between two aluminum foil sheets was also attempted.In this experiment,a centrifugal shot peening machine with an electrical heater was employed.The workpieces were magnesium alloys AZ31B and AZ91D,and the hard powders were commercial cemented carbide,alumina,and zirconia.The joinability of hard powders near the lined surface was observed by a optical microscope.The wear resistance was also evaluated by a wear test.The hard powders were successfully bonded to the surface of workpieces by the shot lining process.The results show that the present method is effective in wear resistance of the magnesium alloys.
基金the Center of Excellence on Hazardous Substance Management,Chulalongkorn University,Bangkok,Thailand for financial support
文摘This research was aimed at investigating the reduction of DOM fractions and their trihalomethane formation potential （THMFP） by in-line coagulation with 0.1 μm ceramic membrane filtration. The combination of ceramic membrane filtration with a coagulation process is an alternative technology which can be applied to enhance conventional coagulation processes in the field of water treatment and drinking water production. The Ping River water （high turbidity water） was selected as the raw surface water because it is currently the main raw water source for water supply production in the urban and rural areas of Chiang Mai Province. From the investigation, the results showed that the highest percent reductions of DOC, UV-254, and THMFP （47.6%, 71.0%, and 67.4%, respectively） were achieved from in-line coagulation with ceramic membrane filtration at polyaluminum chloride dosage 40 mg/L. Resin adsorption techniques were employed to characterize the DOM in raw surface water and filtered water. The results showed that the use of a ceramic membrane with in-line coagulation was able to most efficiently reduce the hydrophobic fraction （HPOA） （68.5%）, which was then followed by the hydrophilic fraction （HPIA） （49.3%）. The greater mass DOC reduction of these two fractions provided the highest THMFP reductions （55.1% and 37.2%, respectively）. Furthermore, the in-line coagulation with ceramic membrane filtration was able to reduce the hydrophobic （HPOB） fraction which is characterized by high reactivity toward THM formation. The percent reduction of mass DOC and THMFP of HPOB by in-line coagulation with ceramic membrane filtration was 45.9% and 48.0%, respectively.